CN103571386A - 一种透气性热熔胶 - Google Patents

一种透气性热熔胶 Download PDF

Info

Publication number
CN103571386A
CN103571386A CN201310505571.6A CN201310505571A CN103571386A CN 103571386 A CN103571386 A CN 103571386A CN 201310505571 A CN201310505571 A CN 201310505571A CN 103571386 A CN103571386 A CN 103571386A
Authority
CN
China
Prior art keywords
parts
hot melt
melt adhesive
mix
kneader
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310505571.6A
Other languages
English (en)
Inventor
项孝泓
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Zhongli Parts Co Ltd
Original Assignee
Wuhu Zhongli Parts Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Zhongli Parts Co Ltd filed Critical Wuhu Zhongli Parts Co Ltd
Priority to CN201310505571.6A priority Critical patent/CN103571386A/zh
Publication of CN103571386A publication Critical patent/CN103571386A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种透气性热熔胶，其是由下述重量份的原料制得：EVA50-55、叔丁基酚醛树脂20425-38、尼龙661-2，抗氧剂11351-2、抗氧剂6260.2-0.4、石蜡6-8、聚二甲基硅氧烷4-8，丙烯酸酯类抗冲改性剂ACR1-3、当归油 0.05-0.08,硬脂酸1.2～2.3，复合填料3-6，三氟化硼1-2。本发明热熔胶采用新配方原料组合,不仅提高了热熔胶透气性，同时增加了热熔胶粘结强度,可以完全满足汽车内饰件粘结塑料等材料对热熔胶性能的要求。

Description

一种透气性热熔胶
技术领域
本发明属粘结剂领域，尤其涉及一种透气性热熔胶。
背景技术
    近几年，复合材料和塑料等新材料在汽车上的应用使得汽车用胶粘剂和密封胶用量也持续增长，其中汽车内饰件是胶粘剂用量迅速增长的一个领域。 汽车内饰件热熔胶的需求越来越多。
发明内容
本发明的目的是提供一种透气性热熔胶。
为了实现上述目的本发明采用如下技术方案：
一种透气性热熔胶，其特征在于，其是由下述重量份的原料制得：
 EVA 50-55、叔丁基酚醛树脂204 25-38、尼龙66 1-2，抗氧剂1135 1-2、抗氧剂626 0.2-0.4、石蜡6-8、聚二甲基硅氧烷4-8，丙烯酸酯类抗冲改性剂ACR 1-3、当归油  0.05-0.08,硬脂酸1.2～2.3，复合填料3-6，三氟化硼1-2;
复合填料由下述重量份的原料制得：膨润土15-28、重晶石粉8-10、凹凸棒土15-22，氧化镁粉末1-2、偏硅酸钠0.2-0.4、磷酸氢二铵0.1-0.2、邻苯二甲酸二正辛酯0.1-0.2、纳米碳粉1-2、稻壳炭粉1-2、烷基糖苷1-2、硅烷偶联剂KH570 1.3-1.5，抗氧剂1010 0.6-1.4；
所述的复合填料的制备方法为：制备方法是将膨润土、重晶石粉、凹凸棒土混匀，在清水中浸泡1-2天，取出，烘干，再在700-750℃下煅烧2-3小时，然后，取出，加10-15%盐酸溶液调PH为5.8-6.5，研磨浆料至400-500目后，再加氢氧化钠溶液调为中性，干燥，再与剩余原料混合，混合均匀即得。
所述的一种透气性热熔胶，其特征在于：
制备步骤是:
（1）将EVA、尼龙66、聚二甲基硅氧烷放入捏合机中180-195℃捏合8-10分钟;
（2）再将石蜡、叔丁基酚醛树脂204、硬脂酸放入捏合机中190-200℃捏合5-7分钟;
（3）将其余原料放入捏合机中，189-197℃下捏合6-8分钟，取出冷却即得。
     本发明的有益效果：本发明热熔胶采用新配方原料组合,不仅提高了热熔胶透气性，同时增加了热熔胶粘结强度,可以完全满足汽车内饰件粘结塑料等材料对热熔胶性能的要求。稻壳炭的加入，变废为宝，增加了本发明的透气性的同时，不影响本发明的粘结强度。
具体实施方式、
一种透气性热熔胶，其是由下述重量kg的原料制得：
 EVA  55、叔丁基酚醛树脂204  28、尼龙66  1，抗氧剂1135  1、抗氧剂626 0.2、石蜡6、聚二甲基硅氧烷4，丙烯酸酯类抗冲改性剂ACR 1、当归油  0.08,硬脂酸1.2，复合填料3，三氟化硼1;
复合填料由下述重量kg的原料制得：膨润土17、重晶石粉10、凹凸棒土15，氧化镁粉末2、偏硅酸钠0.4、磷酸氢二铵0.1、邻苯二甲酸二正辛酯0.2、纳米碳粉1、稻壳炭粉2、烷基糖苷2、硅烷偶联剂KH570   1.5，抗氧剂1010  0.8；
所述的复合填料的制备方法为：制备方法是将膨润土、重晶石粉、凹凸棒土混匀，在清水中浸泡2天，取出，烘干，再在720℃下煅烧2小时，然后，取出，加12%盐酸溶液调PH为6.5，研磨浆料至500目后，再加氢氧化钠溶液调为中性，干燥，再与剩余原料混合，混合均匀即得。
所述的一种透气性热熔胶，
制备步骤是:
（1）将EVA、尼龙66、聚二甲基硅氧烷放入捏合机中195℃捏合8分钟;
（2）再将石蜡、叔丁基酚醛树脂204、硬脂酸放入捏合机中200℃捏合7分钟;
（3）将其余原料放入捏合机中，189℃下捏合8分钟，取出冷却即得。
本实施例的粘结剂的表观粘度为4900MPa.s，剥离强度51N/2.5cm2，初粘力达到5号钢球，开放时间41s，24小时热稳定性状稳定。

Claims (2)

1.一种透气性热熔胶，其特征在于，其是由下述重量份的原料制得：
 EVA 50-55、叔丁基酚醛树脂204  25-38、尼龙66 1-2，抗氧剂1135 1-2、抗氧剂626 0.2-0.4、石蜡6-8、聚二甲基硅氧烷4-8，丙烯酸酯类抗冲改性剂ACR 1-3、当归油  0.05-0.08,硬脂酸1.2～2.3，复合填料3-6，三氟化硼1-2;
复合填料由下述重量份的原料制得：膨润土15-28、重晶石粉8-10、凹凸棒土15-22，氧化镁粉末1-2、偏硅酸钠0.2-0.4、磷酸氢二铵0.1-0.2、邻苯二甲酸二正辛酯0.1-0.2、纳米碳粉1-2、稻壳炭粉1-2、烷基糖苷1-2、硅烷偶联剂KH570 1.3-1.5，抗氧剂1010 0.6-1.4；
所述的复合填料的制备方法为：制备方法是将膨润土、重晶石粉、凹凸棒土混匀，在清水中浸泡1-2天，取出，烘干，再在700-750℃下煅烧2-3小时，然后，取出，加10-15%盐酸溶液调PH为5.8-6.5，研磨浆料至400-500目后，再加氢氧化钠溶液调为中性，干燥，再与剩余原料混合，混合均匀即得。
2.根据权利要求1所述的一种透气性热熔胶，其特征在于：
制备步骤是:
（1）将EVA、尼龙66、聚二甲基硅氧烷放入捏合机中180-195℃捏合8-10分钟;
（2）再将石蜡、叔丁基酚醛树脂204、硬脂酸放入捏合机中190-200℃捏合5-7分钟;
（3）将其余原料放入捏合机中，189-197℃下捏合6-8分钟，取出冷却即得。
CN201310505571.6A 2013-10-24 2013-10-24 一种透气性热熔胶 Pending CN103571386A (zh)