CN104497428A - 一种聚苯乙烯塑料阻燃剂的制备方法 - Google Patents
一种聚苯乙烯塑料阻燃剂的制备方法 Download PDFInfo
- Publication number
- CN104497428A CN104497428A CN201410677901.4A CN201410677901A CN104497428A CN 104497428 A CN104497428 A CN 104497428A CN 201410677901 A CN201410677901 A CN 201410677901A CN 104497428 A CN104497428 A CN 104497428A
- Authority
- CN
- China
- Prior art keywords
- fire retardant
- preparation
- polystyrene plastic
- naoh
- polystyrene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种聚苯乙烯塑料阻燃剂的制备方法,其特征在于,包括如下步骤:S01:将NaOH、三溴苯酚、纯硅酮塑料改性添加剂和异丙醇加入水中进行搅拌;S02:对搅拌后的混合物进行加热;S03:加入1,4-二氯-2-丁烯形成沉淀物;S04:搅拌沉淀物,并在烧结玻璃漏斗上进行热过滤;S05:用水清洗后,进行干燥得到粉末状阻燃剂。在提高聚苯乙烯塑料阻燃效率的同时还保持良好的机械性能。
Description
技术领域
本发明涉及一种聚苯乙烯塑料阻燃剂的制备方法。
背景技术
聚苯乙烯(PS)是由苯乙烯单体聚合而成的线型结构的塑料,广泛应用于光学仪器、化工部门及日用品方面。在聚苯乙烯塑料的制备过程中需要添加各种塑料助剂,比如增塑剂、热稳定剂、阻燃剂等。其中,传统的阻燃剂制得的聚苯乙烯塑料阻燃效率低,机械性能也不佳。
发明内容
针对上述问题,本发明提供一种聚苯乙烯塑料阻燃剂的制备方法,在提高聚苯乙烯塑料阻燃效率的同时还保持良好的机械性能。
为实现上述技术目的,达到上述技术效果,本发明通过以下技术方案实现:
一种聚苯乙烯塑料阻燃剂的制备方法,其特征在于,包括如下步骤:
S01:将NaOH、三溴苯酚、纯硅酮塑料改性添加剂和异丙醇加入水中进行搅拌;
S02:对搅拌后的混合物进行加热;
S03:加入1,4-二氯-2-丁烯形成沉淀物;
S04:搅拌沉淀物,并在烧结玻璃漏斗上进行热过滤;
S05:用水清洗后,进行干燥得到粉末状阻燃剂。
优选,所述NaOH的质量体积浓度为40%-45%。
优选,所述三溴苯酚、异丙醇、纯硅酮塑料改性添加剂和NaOH的质量份数分别是:三溴苯酚是40-50份,异丙醇是100-130份,NaOH是20-25份,纯硅酮塑料改性添加剂是5-10份。
聚苯乙烯燃烧时发生解聚,产生苯乙烯单体,其引火性非常大,所以PS的阻燃性能提高很困难,通过上述方法制得的阻燃剂可提高PS的阻燃效率,其发热速度、CO、发烟的各种效果都有提高,同时还保持良好的机械性能。
本发明的有益效果是:工艺简单,方便批量生产,在提高聚苯乙烯塑料阻燃效率的同时还保持良好的机械性能。
具体实施方式
下面结合具体的实施例对本发明技术方案作进一步的详细描述,以使本领域的技术人员可以更好的理解本发明并能予以实施,但所举实施例不作为对本发明的限定。
一种聚苯乙烯塑料阻燃剂的制备方法,其特征在于,包括如下步骤:
S01:将NaOH、三溴苯酚、纯硅酮塑料改性添加剂和异丙醇加入水中进行搅拌;
S02:对搅拌后的混合物进行加热;
S03:加入1,4-二氯-2-丁烯形成沉淀物;
S04:搅拌沉淀物,并在烧结玻璃漏斗上进行热过滤;
S05:用水清洗后,进行干燥得到粉末状阻燃剂。
优选,所述NaOH的质量体积浓度为40%-45%。
优选,所述三溴苯酚、异丙醇、纯硅酮塑料改性添加剂和NaOH的质量份数分别是:三溴苯酚是40-50份,异丙醇是100-130份,NaOH是20-25份,纯硅酮塑料改性添加剂是5-10份。
优选,步骤S02中,加热温度为60-70℃。
优选,步骤S05中,在烘箱中进行干燥。
优选,烘箱的干燥温度为100-110℃。
上述材料均可在市场上买到。聚苯乙烯燃烧时发生解聚,产生苯乙烯单体,其引火性非常大,所以PS的阻燃性能提高很困难,通过上述方法制得的阻燃剂可提高PS的阻燃效率,其发热速度、CO、发烟的各种效果都有提高,同时还保持良好的机械性能。
以上仅为本发明的优选实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书内容所作的等效结构或者等效流程变换,或者直接或间接运用在其他相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (6)
1.一种聚苯乙烯塑料阻燃剂的制备方法,其特征在于,包括如下步骤:
S01:将NaOH、三溴苯酚、纯硅酮塑料改性添加剂和异丙醇加入水中进行搅拌;
S02:对搅拌后的混合物进行加热;
S03:加入1,4-二氯-2-丁烯形成沉淀物;
S04:搅拌沉淀物,并在烧结玻璃漏斗上进行热过滤;
S05:用水清洗后,进行干燥得到粉末状阻燃剂。
2.根据权利要求1所述的一种聚苯乙烯塑料阻燃剂的制备方法,其特征在于,所述NaOH的质量体积浓度为40%-45%。
3.根据权利要求2所述的一种聚苯乙烯塑料阻燃剂的制备方法,其特征在于,所述三溴苯酚、异丙醇、纯硅酮塑料改性添加剂和NaOH的质量份数分别是:三溴苯酚是40-50份,异丙醇是100-130份,NaOH是20-25份,纯硅酮塑料改性添加剂是5-10份。
4.根据权利要求2所述的一种聚苯乙烯塑料阻燃剂的制备方法,其特征在于,步骤S02中,加热温度为60-70℃。
5.根据权利要求4所述的一种聚苯乙烯塑料阻燃剂的制备方法,其特征在于,步骤S05中,在烘箱中进行干燥。
6.根据权利要求5所述的一种聚苯乙烯塑料阻燃剂的制备方法,其特征在于,烘箱的干燥温度为100-110℃。