CN104473392B - A kind of manufacturing process of silver-colored painted enamel - Google Patents
A kind of manufacturing process of silver-colored painted enamel Download PDFInfo
- Publication number
- CN104473392B CN104473392B CN201410661469.XA CN201410661469A CN104473392B CN 104473392 B CN104473392 B CN 104473392B CN 201410661469 A CN201410661469 A CN 201410661469A CN 104473392 B CN104473392 B CN 104473392B
- Authority
- CN
- China
- Prior art keywords
- silver
- enamel
- carcass
- finished product
- colored
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of manufacturing process of silver-colored painted enamel, adopt colour enamels modulation, handwritten drawings silver carcass, make silver-colored painted enamel goods, preparation method is simple, and product is vividly changeable, a kind of new technique is opened again to silver jeweleries industry, has saved a kind of ancient technique of lost upper a century.Product design beautiful appearance, the product holding time is long, and goods degree of spreading is wide, and color is no longer single; Perfectly be combined with silverware by colour enamels by special treatment process and transmutation, color adhesive ability is strong, and the holding time is of a specified duration; Drawing adopts artificial drafting, and lines are exquisite, pure manual drawing, good looking appearance, and pattern is lively; There is good Social and economic benef.
Description
Technical field
The present invention relates to silver jeweleries industry, be specifically related to a kind of manufacturing process of Silver Jewelry, be specifically related to a kind of manufacturing process of silver-colored painted enamel.
Background technology
The shortcoming that traditional Silver Jewelry exists is that color is incomplete, and color is rendered as single color.The many silvery whites yellow in micro-band of silver jewellery, in soft metallic luster.Because of oxidizable, of long duration, color and luster can become dark yellow-white.Silver is a kind of more active precious metal, very easily reacts with sulphur or hydrogen sulfide and generates the silver sulfide of black in atmosphere.Here it is, and why silver jewellery there will be the phenomenon sending out bird blackening after a procedure.The silver jewellery of Long-Time Service is seldom rubbed due to surface, and after placing, to turn black phenomenon more serious for this blackout.Silver Jewelry wear time is of a specified duration to be needed to clear up, time-consuming during cleaning, very easily causes precious metal to run off.And necessary exercise due diligence, generally has a bath, sleeps and had better not wear, avoid the air of contact flow when not wearing on wearing, casket or sealing bag should be put into, not with swimming, particularly in the sea, the people that sweat is many is especially not suitable for wearing silver jeweleries.
Painted enamel is also called " enamel ", is one of enamel handicraft kind, is all generally refer in particular to copper painted enamel.Painted enamel is also the goods having other carcass, metal matrix have golden painted enamel, silver-colored painted enamel etc., other carcass comprise enamel painting on porcelain, glass painted enamel etc.Painted enamel is directly coated with enamel glaze to be drawn on metal matrix, shows a kind of champleve enamel ware works of cloisonne enamel picture after firing.The manufacture technique of painted enamel originates from the Fo Langdesi area of the 15th century middle period Europe Belgium, France, Dutch three states boundaries, imports China into period, and develop rapidly Qing Dynasty Kangxu.Although the painted enamel of China imports into from west, but be through domestic cloisonne handicraft and make the development of great master and the painted enamel in west has had very large difference, in the scope of application of the subject matter of pattern, style and implements, and the raw material sources component ratio aspect of enamel, all there is the feature of oneself, so China's painted enamel does not resemble the painted enamel of west strong glass light, and simpler and more honest, very alike with the powder enamel in China porcelain.The painted enamel of China is that Kangxu starts to fire period, and it is the most prevailing in the Yongzheng's reign, this and Yongzheng Supreme Being like ardently painted enamel very large relation, and after Jiaqing, because financial, the problems such as materials no longer or seldom fire painted enamel, from the Yongzheng's reign, derived enamel ceramics from painted enamel, colour enamels has very high collection and ornamental value, auction is in recent years all the personal value up to a million.
Silver Jewelry is owing to being subject to the restriction of self-characteristic, no matter be ornaments and articles for daily use, all there will be color in use for some time to reduce, send out the defect that crow waits impact attractive in appearance, and the color that silverware presents is comparatively single, visual impact dynamics is not strong, current market does not occur yet the fine work device of new silver-colored painted enamel, the preparation technology of traditional silver-colored painted enamel has been not suitable for the demand of modern aesthetic viewpoint, and these factors affect the extensive succession of silverware.
Therefore, produce a kind of preparation technology simply, product design beautiful appearance, the product holding time is long, and goods degree of spreading is wide, and the manufacturing process of the silver-colored painted enamel that color is no longer single, has wide market prospects.
summary of the invention
For the deficiencies in the prior art, the invention provides a kind of preparation technology simple, product design beautiful appearance, the product holding time is long, and goods degree of spreading is wide, the manufacturing process of the silver-colored painted enamel that color is no longer single.
Technical scheme of the present invention is achieved in that a kind of manufacturing process of silver-colored painted enamel, and its manufacturing process comprises the steps:
1) make silver-colored tire: with tablet press machine, silver strip is pressed into 0.75mm, circle of contact tempering, by mould silver strip rotary press modelling, make silver-colored tire;
2) beat and wipe silver-colored tire: the silver-colored tire in step 1) is stuck in whipper mould, first uses 320 order sand paper wipings silver carcasses one time, and then with 600 order sand paper wipings silver carcass second time, until carcass is without cheating trace;
3) silver-colored tire is welded: by through step 2) silver-colored tire after twice wiping glues borax water and burns red, is welded on silver-colored tire with 90 welding agent by accessory;
4) enamel material is ground: 100 object enamel material mills are ground to 1200 orders;
5) modulate enamel material: get 5 parts, enamel material ground in step 4), add 2 parts of turpentine oil and mix well, then add 3 portions of frankincense oils and be in harmonious proportion, obtain mixing enamel material;
6) painted enamel: by the various writing brush of mixing enamel material that is in harmonious proportion in step 5) and hook line pen, the silver-colored tire adding accessory in step 3) is painted, once to be painted semi-finished product carcass, the once drawing semi-finished product carcass finished is placed, for subsequent use after turpentine oil dries completely;
7. fire enamel: the once drawing semi-finished product carcass after placement in step 6) being dried is positioned on stainless steel frame puts into stove, kiln temperature is set, constant temperature 10 minutes when normal temperature rises to 120 degree, constant temperature 15 minutes when rising to 300 degree, then, time to 730 degree, stove power supply is closed, when kiln temperature is down to normal temperature, take out the once drawing semi-finished product carcass after firing, obtain a burned product carcass;
8) secondary painted enamel: time burned product carcass of in step 7) is carried out secondary drawing by the technique of painting in step 6), obtains secondary drawing semi-finished product carcass, is placed by the secondary drawing semi-finished product carcass finished, for subsequent use after turpentine oil dries completely;
9) secondary fires enamel: the secondary drawing semi-finished product carcass after placement in step 8) being dried is positioned on stainless steel frame puts into stove, kiln temperature is set, constant temperature 10 minutes when normal temperature rises to 120 degree, constant temperature 15 minutes when rising to 300 degree, then, time to 750 degree, stove power supply is closed, when kiln temperature is down to normal temperature, take out the secondary drawing semi-finished product carcass after firing, obtain secondary burned product carcass;
10) play wiping: wipe unnecessary welding agent and enamel material on secondary burned product carcass with 800 order sand paper, then carry out polishing, finally dip in clean water with agate cutter and repeatedly gently press silver-colored tire surface, to light, obtain finished product.
The present invention has following good effect: preparation method of the present invention is simple, and product is vividly changeable, opens again a kind of new technique to silver jeweleries industry, has saved a kind of ancient technique of lost upper a century; Product design beautiful appearance, the product holding time is long, and goods degree of spreading is wide, and color is no longer single; Perfectly be combined with silverware by colour enamels by special treatment process and transmutation, color adhesive ability is strong, and the holding time is of a specified duration; Drawing adopts artificial drafting, and lines are exquisite, and pure manual drawing, good looking appearance, pattern is lively.
Detailed description of the invention
A manufacturing process for silver-colored painted enamel, its manufacturing process comprises the steps:
1) make silver-colored tire: with tablet press machine, silver strip is pressed into 0.75mm, circle of contact tempering, by mould silver strip rotary press modelling, make silver-colored tire;
2) beat and wipe silver-colored tire: the silver-colored tire in step 1) is stuck in whipper mould, first uses 320 order sand paper wipings silver carcasses one time, and then with 600 order sand paper wipings silver carcass second time, until carcass is without cheating trace;
3) silver-colored tire is welded: by through step 2) silver-colored tire after twice wiping glues borax water and burns red, is welded on silver-colored tire with 90 welding agent by accessory;
4) enamel material is ground: 100 object enamel material mills are ground to 1200 orders;
5) modulate enamel material: get 20 grams, enamel material ground in step 4), add 8 grams of turpentine oil and mix well, then add 12 grams of frankincense oils and be in harmonious proportion, obtain mixing enamel material;
6) painted enamel: by the various writing brush of mixing enamel material that is in harmonious proportion in step 5) and hook line pen, the silver-colored tire adding accessory in step 3) is painted, once to be painted semi-finished product carcass, the once drawing semi-finished product carcass finished is placed, for subsequent use after turpentine oil dries completely;
7. fire enamel: the once drawing semi-finished product carcass after placement in step 6) being dried is positioned on stainless steel frame puts into stove, kiln temperature is set, constant temperature 10 minutes when normal temperature rises to 120 degree, constant temperature 15 minutes when rising to 300 degree, then, time to 730 degree, stove power supply is closed, when kiln temperature is down to normal temperature, take out the once drawing semi-finished product carcass after firing, obtain a burned product carcass;
8) secondary painted enamel: time burned product carcass of in step 7) is carried out secondary drawing by the technique of painting in step 6), obtains secondary drawing semi-finished product carcass, is placed by the secondary drawing semi-finished product carcass finished, for subsequent use after turpentine oil dries completely;
9) secondary fires enamel: the secondary drawing semi-finished product carcass after placement in step 8) being dried is positioned on stainless steel frame puts into stove, kiln temperature is set, constant temperature 10 minutes when normal temperature rises to 120 degree, constant temperature 15 minutes when rising to 300 degree, then, time to 750 degree, stove power supply is closed, when kiln temperature is down to normal temperature, take out the secondary drawing semi-finished product carcass after firing, obtain secondary burned product carcass;
10) play wiping: wipe unnecessary welding agent and enamel material on secondary burned product carcass with 800 order sand paper, then carry out polishing, finally dip in clean water with agate cutter and repeatedly gently press silver-colored tire surface, to light, obtain finished product.
The present invention adopts colour enamels to modulate, and handwritten drawings silver carcass, make silver-colored painted enamel goods, preparation method is simple, and product is vividly changeable, opens again a kind of new technique to silver jeweleries industry, has saved a kind of ancient technique of lost upper a century.Product design beautiful appearance, the product holding time is long, and goods degree of spreading is wide, and color is no longer single.Perfectly be combined with silverware by colour enamels by special treatment process and transmutation, color adhesive ability is strong, and the holding time is of a specified duration.Drawing adopts artificial drafting, and lines are exquisite, and pure manual drawing, good looking appearance, pattern is lively.There is good Social and economic benef.
Claims (1)
1. a manufacturing process for silver-colored painted enamel, is characterized in that, its manufacturing process comprises the steps: 1) make silver-colored tire: with tablet press machine, silver strip is pressed into 0.75mm, circle of contact tempering, by mould silver strip rotary press modelling, makes silver-colored tire;
2) beat and wipe silver-colored tire: the silver-colored tire in step 1) is stuck in whipper mould, first uses 320 order sand paper wipings silver carcasses one time, and then with 600 order sand paper wipings silver carcass second time, until carcass is without cheating trace;
3) silver-colored tire is welded: by through step 2) silver-colored tire after twice wiping glues borax water and burns red, is welded on silver-colored tire with 90# welding agent by accessory;
4) enamel material is ground: 100 object enamel material mills are ground to 1200 orders;
5) modulate enamel material: get 5 parts, enamel material ground in step 4), add 2 parts of turpentine oil and mix well, then add 3 portions of frankincense oils and be in harmonious proportion, obtain mixing enamel material;
6) painted enamel: by the various writing brush of mixing enamel material that is in harmonious proportion in step 5) and hook line pen, the silver-colored tire adding accessory in step 3) is painted, once to be painted semi-finished product carcass, the once drawing semi-finished product carcass finished is placed, for subsequent use after turpentine oil dries completely;
7) enamel is fired: the once drawing semi-finished product carcass after placement in step 6) being dried is positioned on stainless steel frame puts into stove, kiln temperature is set, constant temperature 10 minutes when normal temperature rises to 120 degree, constant temperature 15 minutes when rising to 300 degree, then, time to 730 degree, stove power supply is closed, when kiln temperature is down to normal temperature, take out the once drawing semi-finished product carcass after firing, obtain a burned product carcass;
8) secondary painted enamel: time burned product carcass of in step 7) is carried out secondary drawing by the technique of painting in step 6), obtains secondary drawing semi-finished product carcass, is placed by the secondary drawing semi-finished product carcass finished, for subsequent use after turpentine oil dries completely;
9) secondary fires enamel: the secondary drawing semi-finished product carcass after placement in step 8) being dried is positioned on stainless steel frame puts into stove, kiln temperature is set, constant temperature 10 minutes when normal temperature rises to 120 degree, constant temperature 15 minutes when rising to 300 degree, then, time to 750 degree, stove power supply is closed, when kiln temperature is down to normal temperature, take out the secondary drawing semi-finished product carcass after firing, obtain secondary burned product carcass;
10) play wiping: wipe unnecessary welding agent and enamel material on secondary burned product carcass with 800 order sand paper, then carry out polishing, finally dip in clean water with agate cutter and repeatedly gently press silver-colored tire surface, to light, obtain finished product.