CN107618312A - A kind of preparation method of silver-colored painted enamel jewellery - Google Patents
A kind of preparation method of silver-colored painted enamel jewellery Download PDFInfo
- Publication number
- CN107618312A CN107618312A CN201710683639.8A CN201710683639A CN107618312A CN 107618312 A CN107618312 A CN 107618312A CN 201710683639 A CN201710683639 A CN 201710683639A CN 107618312 A CN107618312 A CN 107618312A
- Authority
- CN
- China
- Prior art keywords
- silver
- enamel
- finished product
- colored
- semi
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
It is by mould that silver material is molded the invention discloses a kind of preparation method of silver-colored painted enamel jewellery, silver-colored tire is made, and silver-colored tire is polished smooth, first painted enamel background color, secondary drawing then is carried out with advanced enamel material, 5min is fired under the conditions of 850 DEG C, finally it is polished, finished product is obtained, enamel silverware products appearance color made by the present invention is more colorful, attractive in appearance, and glossiness is high, surface is smooth even bright, and the product holding time is also longer.
Description
Technical field
The present invention relates to silver jeweleries processing technique field, more particularly to a kind of preparation method of silver-colored painted enamel jewellery.
Background technology
Silver Jewelry by self-characteristic due to being limited, either ornaments and articles for daily use, in use for some time
Occur that color reduction, hair crow etc. influences the defects of attractive in appearance, and the color that silverware is presented is more single, visual impact
Degree is not strong；As people have new requirement, the system of traditional silver-colored painted enamel to the sight and artistic value of daily ornaments
The demand of standby technique unsuitable modern aesthetic viewpoint, these factors affect the extensive succession of silverware.
The content of the invention
It is an object of the invention to provide a kind of preparation method of silver-colored painted enamel jewellery, this method is made outside silverware jewellery
Shape beautiful appearance, product holding time length.
To achieve the above object, the present invention adopts the following technical scheme that：
A kind of preparation method of silver-colored painted enamel jewellery, comprises the following steps：
(1) silver-colored tire is made：It is by mould that silver material is molded, silver-colored tire is made；
(2) beat and wipe silver-colored tire：It is smooth that silver-colored tire with 240-400 mesh sand paper is polishing to surface；
(3) background color enamel is drawn：The enamel material reconciled is subjected to drawing background color to silver-colored tire, semi-finished product tire of once being painted
Body, the once drawing semi-finished product carcass finished is placed, it is standby after drying；
(4) secondary painted enamel：With advanced enamel material secondary paint is carried out on the once drawing semi-finished product carcass of step (3)
Draw, obtain secondary drawing semi-finished product carcass, the secondary drawing semi-finished product carcass finished is placed, it is standby after drying completely；
(5) enamel is fired：The secondary drawing semi-finished product carcass after drying will be placed in step (4) to be positioned on stainless steel frame
Stove is put into, kiln temperature is set, carries out high temperature sintering, 2-5min is fired under the conditions of 830-870 DEG C, closes stove power supply,
When kiln temperature is down to normal temperature, takes out and obtain burned product carcass after firing；
(6) polish：Unnecessary enamel material on burned product carcass is wiped with 800 mesh sand paper, is then processed by shot blasting, finally uses
Agate knife dips in clean water and gently presses silver-colored tire surface repeatedly, extremely obtains finished product after light.
Preferably, before drawing, by enamel abrasive lapping to 600-1000 mesh, and every part of enamel is pressed in ground enamel material
Material adds 0.4 part of turpentine oil and 0.6 portion of frankincense oil is reconciled.
Beneficial effects of the present invention：Enamel silverware products appearance color is more colorful, attractive in appearance made by the present invention, glossiness
Height, surface is smooth even bright, and the product holding time is also longer.
Embodiment
In order to be better understood from the present invention, below in conjunction with embodiment, the present invention will be further described.
Embodiment 1
A kind of preparation method of silver-colored painted enamel jewellery, comprises the following steps：
(1) silver-colored tire is made：It is by mould that silver material is molded, silver-colored tire is made；
(2) beat and wipe silver-colored tire：It is smooth that silver-colored tire with 400 mesh sand paper is polishing to surface；
(3) background color enamel is drawn：Before drawing, by enamel abrasive lapping to 1000 mesh, and every part is pressed in ground enamel material
Enamel material adds 0.4 part of turpentine oil and 0.6 portion of frankincense oil is reconciled, and the enamel material reconciled is carried out into drawing bottom to silver-colored tire
Color, semi-finished product carcass of once being painted, the once drawing semi-finished product carcass finished is placed, it is standby after drying；
(4) secondary painted enamel：With advanced enamel material secondary paint is carried out on the once drawing semi-finished product carcass of step (3)
Draw, obtain secondary drawing semi-finished product carcass, the secondary drawing semi-finished product carcass finished is placed, it is standby after drying completely；
(5) enamel is fired：The secondary drawing semi-finished product carcass after drying will be placed in step (4) to be positioned on stainless steel frame
Stove is put into, kiln temperature is set, carries out high temperature sintering, 5min is fired under the conditions of 850 DEG C, stove power supply is closed, works as stove
When temperature is down to normal temperature, takes out and obtain burned product carcass after firing；
(6) polish：Unnecessary enamel material on burned product carcass is wiped with 800 mesh sand paper, is then processed by shot blasting, finally uses
Agate knife dips in clean water and gently presses silver-colored tire surface repeatedly, extremely obtains finished product after light.
Claims (2)
1. a kind of preparation method of silver-colored painted enamel jewellery, it is characterised in that comprise the following steps：
(1) silver-colored tire is made：It is by mould that silver material is molded, silver-colored tire is made；
(2) beat and wipe silver-colored tire：It is smooth that silver-colored tire with 240-400 mesh sand paper is polishing to surface；
(3) background color enamel is drawn：The enamel material reconciled is subjected to drawing background color to silver-colored tire, semi-finished product carcass of once being painted,
The once drawing semi-finished product carcass finished is placed, it is standby after drying；
(4) secondary painted enamel：Secondary drawing is carried out on the once drawing semi-finished product carcass of step (3) with advanced enamel material, is obtained
To secondary drawing semi-finished product carcass, the secondary drawing semi-finished product carcass finished is placed, it is standby after drying completely；
(5) enamel is fired：The middle secondary drawing semi-finished product carcass placed after drying of step (4) is positioned on stainless steel frame and is put into
Stove, kiln temperature is set, carries out high temperature sintering, 2-5min is fired under the conditions of 830-870 DEG C, stove power supply is closed, works as stove
When kiln temperature degree is down to normal temperature, takes out and obtain burned product carcass after firing；
(6) polish：Unnecessary enamel material on burned product carcass is wiped with 800 mesh sand paper, is then processed by shot blasting, finally uses agate
Knife dips in clean water and gently presses silver-colored tire surface repeatedly, extremely obtains finished product after light.
2. the preparation method of silver-colored painted enamel jewellery according to claim 1, it is characterised in that before drawing, by enamel material
600-1000 mesh is ground to, and 0.4 part of turpentine oil and 0.6 portion of frankincense oil are added by every part of enamel material in ground enamel material
Reconciled.