CN104464889A - 一种内埋电阻浆料 - Google Patents
一种内埋电阻浆料 Download PDFInfo
- Publication number
- CN104464889A CN104464889A CN201410826247.9A CN201410826247A CN104464889A CN 104464889 A CN104464889 A CN 104464889A CN 201410826247 A CN201410826247 A CN 201410826247A CN 104464889 A CN104464889 A CN 104464889A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- ultra
- fine
- ethylene glycol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种内埋电阻浆料,所述的配方按质量份数:线性酚醛树脂 20-30;磷酸三丁酯 0.5-2;导电相石墨粉 10-15;超细贱金属合金粉导电填料 3-5;邻甲基酚醛环氧树脂 30-35;硬脂酸盐热稳定剂 0.5-1;陶瓷粉 10-15;端羟基液体丁晴橡胶 20-30;乙二醇二缩水甘油醚 10-15;铝粉 5-8;硅系远红外辐射材料 2-3;超细云母粒 3-4。本发明不仅实现了阻燃、耐热、抗老化、热辐射、环保等复合功能,而且提高了体系的稳定性。
Description
技术领域
本发明涉及电子领域,具体涉及一种内埋电阻浆料。
背景技术
电阻时一种常用的电气元件,应用领域广泛,例如使用在集成电路、芯片中,但是随着集成电路以及芯片的迅速发展,目前的电阻存在着诸多缺点,已不能满足集成化的需要,电阻浆料成为解决这一问题的一个方向。
作为电阻浆料的主要成分,通常由玻璃组合物、导电材料、有机载体来构成,包含玻璃组合物是为了调节电阻值和增加浆料的粘接性。在基板上印刷电阻浆料之后,通过烧结,形成厚度约5-20um的厚膜电阻,并且,在此种电阻浆料中,通常可使用氧化钌和铅钌氧化物作为导电材料,可使用氧化铅类玻璃等作为玻璃。
近年来,正积极地探讨环境问题,正推进从电子部件中排除铅等有害物质。上述电阻浆料也不例外,正在进行着无铅化的研究。
作为电阻浆料的无铅化中的课题之一,特别是对于高电阻的电阻浆料中,例如有温度特性和耐压特性的兼顾,例如,在将通过添加在现有的铅类电阻浆料中使用的金属氧化物来调节TCR,原样应用在无铅成分的情况下,由于与铅类成分比较,因电压施加而导致的电阻值变动较大,所以结果就难于实现TCR和STOL的兼顾。
发明内容
发明目的:针对上述现有技术存在的问题和不足,本发明的目的是提供一种内埋电阻浆料。
技术方案:本发明公开了一种内埋电阻浆料,所述的配方按质量份数:线性酚醛树脂 20-30;磷酸三丁酯 0.5-2;导电相石墨粉 10-15;超细贱金属合金粉导电填料 3-5;邻甲基酚醛环氧树脂 30-35;硬脂酸盐热稳定剂 0.5-1;陶瓷粉 10-15;端羟基液体丁晴橡胶 20-30;乙二醇二缩水甘油醚 10-15;铝粉 5-8;硅系远红外辐射材料 2-3;超细云母粒 3-4。
作为本发明的进一步优化,本发明所述的配方按质量份数:线性酚醛树脂 20;磷酸三丁酯 0.5;导电相石墨粉 10;超细贱金属合金粉导电填料 3;邻甲基酚醛环氧树脂 30;硬脂酸盐热稳定剂 0.5;陶瓷粉 10;端羟基液体丁晴橡胶 20;乙二醇二缩水甘油醚 10;铝粉 5;硅系远红外辐射材料 2;超细云母粒 3。
作为本发明的进一步优化,本发明所述的配方按质量份数:线性酚醛树脂30;磷酸三丁酯2;导电相石墨粉15;超细贱金属合金粉导电填料5;邻甲基酚醛环氧树脂35;硬脂酸盐热稳定剂 1;陶瓷粉15;端羟基液体丁晴橡胶30;乙二醇二缩水甘油醚15;铝粉8;硅系远红外辐射材料3;超细云母粒4。
作为本发明的进一步优化,本发明所述的配方按质量份数:线性酚醛树脂 25;磷酸三丁酯 1.5;导电相石墨粉 12;超细贱金属合金粉导电填料 4;邻甲基酚醛环氧树脂 32;硬脂酸盐热稳定剂 0.6;陶瓷粉 12;端羟基液体丁晴橡胶 25;乙二醇二缩水甘油醚 12;铝粉 6;硅系远红外辐射材料 2.5;超细云母粒 3.5。
有益效果:本发明的电阻浆料,具有低温固化、高温使用的特性,印刷性及浸润性良好,与基材的附着力强,本发明不仅实现了阻燃、耐热、抗老化、热辐射、环保等复合功能,而且提高了体系的稳定性,热辐射效能优良,发热量大,耐温性能好,节能效果显著。由本发明制备的电阻经过测试分析,显示电阻性能良好,而且该方法工艺要求简单,制造成本低。
具体实施方式
下面结合实施例进一步阐明本发明。
实施例1:
本实施例的一种内埋电阻浆料的配方按质量份数:线性酚醛树脂 20;磷酸三丁酯 0.5;导电相石墨粉 10;超细贱金属合金粉导电填料 3;邻甲基酚醛环氧树脂 30;硬脂酸盐热稳定剂 0.5;陶瓷粉 10;端羟基液体丁晴橡胶 20;乙二醇二缩水甘油醚 10;铝粉 5;硅系远红外辐射材料 2;超细云母粒 3。
由本实施例所制备的电阻经过测试分析,显示电阻性能良好。
实施例2:
本实施例的一种内埋电阻浆料的配方按质量份数:线性酚醛树脂30;磷酸三丁酯2;导电相石墨粉15;超细贱金属合金粉导电填料5;邻甲基酚醛环氧树脂35;硬脂酸盐热稳定剂 1;陶瓷粉15;端羟基液体丁晴橡胶30;乙二醇二缩水甘油醚15;铝粉8;硅系远红外辐射材料3;超细云母粒4。
由本实施例所制备的电阻经过测试分析,显示电阻性能良好。
实施例3:
本实施例的一种内埋电阻浆料的配方按质量份数:线性酚醛树脂 25;磷酸三丁酯 1.5;导电相石墨粉 12;超细贱金属合金粉导电填料 4;邻甲基酚醛环氧树脂 32;硬脂酸盐热稳定剂 0.6;陶瓷粉 12;端羟基液体丁晴橡胶 25;乙二醇二缩水甘油醚 12;铝粉 6;硅系远红外辐射材料 2.5;超细云母粒 3.5。
由本实施例所制备的电阻经过测试分析,显示电阻性能良好。
Claims (4)
1.一种内埋电阻浆料,其特征在于:所述的配方按质量份数:线性酚醛树脂 20-30;磷酸三丁酯 0.5-2;导电相石墨粉 10-15;超细贱金属合金粉导电填料 3-5;邻甲基酚醛环氧树脂 30-35;硬脂酸盐热稳定剂 0.5-1;陶瓷粉 10-15;端羟基液体丁晴橡胶 20-30;乙二醇二缩水甘油醚 10-15;铝粉 5-8;硅系远红外辐射材料 2-3;超细云母粒 3-4。
2.根据权利要求1所述的一种内埋电阻浆料,其特征在于:所述的配方按质量份数:线性酚醛树脂 20;磷酸三丁酯 0.5;导电相石墨粉 10;超细贱金属合金粉导电填料 3;邻甲基酚醛环氧树脂 30;硬脂酸盐热稳定剂 0.5;陶瓷粉 10;端羟基液体丁晴橡胶 20;乙二醇二缩水甘油醚 10;铝粉 5;硅系远红外辐射材料 2;超细云母粒 3。
3.根据权利要求1所述的一种内埋电阻浆料,其特征在于:所述的配方按质量份数:线性酚醛树脂30;磷酸三丁酯2;导电相石墨粉15;超细贱金属合金粉导电填料5;邻甲基酚醛环氧树脂35;硬脂酸盐热稳定剂 1;陶瓷粉15;端羟基液体丁晴橡胶30;乙二醇二缩水甘油醚15;铝粉8;硅系远红外辐射材料3;超细云母粒4。
4.根据权利要求1所述的一种内埋电阻浆料,其特征在于:所述的配方按质量份数:线性酚醛树脂 25;磷酸三丁酯 1.5;导电相石墨粉 12;超细贱金属合金粉导电填料 4;邻甲基酚醛环氧树脂 32;硬脂酸盐热稳定剂 0.6;陶瓷粉 12;端羟基液体丁晴橡胶 25;乙二醇二缩水甘油醚 12;铝粉 6;硅系远红外辐射材料 2.5;超细云母粒 3.5。