CN104458741A - 一种水泥熟料的岩相分析方法 - Google Patents

一种水泥熟料的岩相分析方法 Download PDF

Info

Publication number
CN104458741A
CN104458741A CN201410432064.9A CN201410432064A CN104458741A CN 104458741 A CN104458741 A CN 104458741A CN 201410432064 A CN201410432064 A CN 201410432064A CN 104458741 A CN104458741 A CN 104458741A
Authority
CN
China
Prior art keywords
polishing
analysis method
petrographic analysis
plane
cement clinker
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410432064.9A
Other languages
English (en)
Inventor
丁兆年
杨光
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qingdao Yongtong Elevator Engineering Co Ltd
Original Assignee
Qingdao Yongtong Elevator Engineering Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qingdao Yongtong Elevator Engineering Co Ltd filed Critical Qingdao Yongtong Elevator Engineering Co Ltd
Priority to CN201410432064.9A priority Critical patent/CN104458741A/zh
Publication of CN104458741A publication Critical patent/CN104458741A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种岩相分析方法，尤其是一种水泥熟料的岩相分析方法。其步骤包括镶样、粗磨、细磨、抛光、浸蚀、岩相分析。它具有操作步骤简单、取材方便、省时、成本低廉的特点，是一种优异的水泥熟料的岩相分析方法。

Description

一种水泥熟料的岩相分析方法
技术领域
本发明涉及一种岩相分析方法，尤其是一种水泥熟料的岩相分析方法。
背景技术
岩相分析是利用光学显微镜对天然岩石或硅酸盐材料中的物相进行晶体光学性质、显微结构和物相的种类、含量、形态、聚集状态等分析的方法。水泥在土木、桥梁、基础建设发挥着重要作用，因此研究水泥熟料的岩相结构，对后续水泥生产工艺、产品质量的改进等有着重要意义。
发明内容
本发明旨在提供一种水泥熟料的岩相分析方法，用以找出生料设备、熟料煅烧等工艺过程中的毛病，改进生产工艺、水泥质量，是一款通用的水泥岩相分析方法，其采用的技术方案如下：
一种水泥熟料的岩相分析方法，其步骤依次为：
(1)镶样：将待测水泥熟料块割制成一定形状，然后用树脂镶嵌样块；
(2)粗磨：用150号金刚砂纸和水粗磨出一个较好的平面，然后用水洗净；
(3)细磨：用600号金刚砂纸(或1000号砂纸)和水把此平面细磨二十分钟，直到表面有光泽，无明显划痕，再用水冲洗干净；
(4)抛光：用3μAl2O3粉和无水乙醇擦拭磨光的平面，在抛光盘上进行抛光，二十分钟后将抛光的平面用丝绒擦拭；
(5)浸蚀：将抛光好的光片用1％硝酸—酒精溶液侵蚀3～5秒；
(6)岩相分析：将浸蚀后的样块在金相显微镜下观察，记录熟料中主要矿物及其分布情况。
本发明具有如下优点：操作步骤简单、取材方便、省时、成本低廉的特点，是一种优异的水泥熟料的岩相分析方法。
具体实施方式
下面结合实例对本发明作进一步说明，以使本发明的优点和特征更易于本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
一种水泥熟料的岩相分析方法，其步骤依次为：
(1)镶样：将待测水泥熟料块割制成一定形状，然后用树脂镶嵌样块；
(2)粗磨：用150号金刚砂纸和水粗磨出一个较好的平面，然后用水洗净；
(3)细磨：用600号金刚砂纸(或1000号砂纸)和水把此平面细磨二十分钟，直到表面有光泽，无明显划痕，再用水冲洗干净；
(4)抛光：用3μAl2O3粉和无水乙醇擦拭磨光的平面，在抛光盘上进行抛光，二十分钟后将抛光的平面用丝绒擦拭；
(5)浸蚀：将抛光好的光片用1％硝酸—酒精溶液侵蚀3～5秒；
(6)岩相分析：将浸蚀后的样块在金相显微镜下观察，记录熟料中主要矿物及其分布情况。
上面以举例方式对本发明进行了说明，但本发明不限于上述具体实施例，凡基于本发明所做的任何改动或变型均属于本发明要求保护的范围。

Claims (1)

1.一种水泥熟料的岩相分析方法，其特征在于，所述岩相分析方法的步骤依次为：
(1)镶样：将待测水泥熟料块割制成一定形状，然后用树脂镶嵌样块；
(2)粗磨：用150号金刚砂纸和水粗磨出一个较好的平面，然后用水洗净；
(3)细磨：用600号金刚砂纸(或1000号砂纸)和水把此平面细磨二十分钟，直到表面有光泽，无明显划痕，再用水冲洗干净；
(4)抛光：用3μAl2O3粉和无水乙醇擦拭磨光的平面，在抛光盘上进行抛光，二十分钟后将抛光的平面用丝绒擦拭；
(5)浸蚀：将抛光好的光片用1％硝酸—酒精溶液侵蚀3～5秒；
(6)岩相分析：将浸蚀后的样块在金相显微镜下观察，记录熟料中主要矿物及其分布情况。
CN201410432064.9A 2014-08-28 2014-08-28 一种水泥熟料的岩相分析方法 Pending CN104458741A (zh)