CN104450062A - 一种铜带轧制油及其制备方法 - Google Patents

一种铜带轧制油及其制备方法 Download PDF

Info

Publication number
CN104450062A
CN104450062A CN201410644365.8A CN201410644365A CN104450062A CN 104450062 A CN104450062 A CN 104450062A CN 201410644365 A CN201410644365 A CN 201410644365A CN 104450062 A CN104450062 A CN 104450062A
Authority
CN
China
Prior art keywords
rolling oil
sodium
copper strips
oil
copper strip
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410644365.8A
Other languages
English (en)
Inventor
邓义增
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuxi Hebang Metal Products Co Ltd
Original Assignee
Wuxi Hebang Metal Products Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuxi Hebang Metal Products Co Ltd filed Critical Wuxi Hebang Metal Products Co Ltd
Priority to CN201410644365.8A priority Critical patent/CN104450062A/zh
Publication of CN104450062A publication Critical patent/CN104450062A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种铜带轧制油，所述铜带轧制油由以下质量份数的各组分组成：棕榈油5-6份、十二烷基磺酸钠0.2-0.4份、山梨醇0.8-1.2份、甘油0.2-0.4份、硅酸钙0.2-0.3份、月桂酸二乙醇酰胺0.2-0.3份、硫酸钠0.1-0.2份、聚丙烯酰胺0.2-0.4份、三聚磷酸钠0.3-0.5份、硼酸钠0.2-0.4份、硬脂酸丁酯0.1-0.3份。本发明还提供其制备方法。采用本发明的铜带轧制油轧制的铜带光泽度高，没有划痕产生，润滑性能好。而且本发明的铜带轧制油的制备方法简单，适合推广使用。

Description

一种铜带轧制油及其制备方法
技术领域
本发明涉及一种铜带轧制油。
背景技术
轧制是将金属通过轧机上两个相对回转轧辊之间的空隙，进行压延变形成为型材（如钢板、圆钢、角钢等）的加工方法。轧制油的主要作用是减小轧辊与铜带箔之间的摩擦，提供稳定的摩擦界面，实现稳定轧制，提高表面质量。采用现有的铜带轧制油轧制的产品光泽度低，且容易产生划痕。
发明内容
本发明提供了一种铜带轧制油，使用本发明的铜带轧制油轧制的铜带具有很好的光泽度，没有划痕产生；为此，本发明还提供其制备方法。
本发明提供一种铜带轧制油，所述铜带轧制油由以下质量份数的各组分组成：棕榈油5-6份、十二烷基磺酸钠0.2-0.4份、山梨醇0.8-1.2份、甘油0.2-0.4份、硅酸钙0.2-0.3份、月桂酸二乙醇酰胺0.2-0.3份、硫酸钠0.1-0.2份、聚丙烯酰胺0.2-0.4份、三聚磷酸钠0.3-0.5份、硼酸钠0.2-0.4份、硬脂酸丁酯0.1-0.3份。
优选地，所述铜带轧制油由以下质量份数的各组分组成：棕榈油5.5份、十二烷基磺酸钠0.3份、山梨醇1.1份、甘油0.3份、硅酸钙0.25份、月桂酸二乙醇酰胺0.25份、硫酸钠0.15份、聚丙烯酰胺0.3份、三聚磷酸钠0.4份、硼酸钠0.3份、硬脂酸丁酯0.2份。
本发明还提供上述铜带轧制油的制备方法，步骤如下：将配方量的棕榈油、十二烷基磺酸钠、山梨醇、硅酸钙、月桂酸二乙醇酰胺、硫酸钠、聚丙烯酰胺、三聚磷酸钠混合，加热至65-75℃，搅拌25-30min；加入配方量的其余组分，搅拌20-25℃，冷却至室温即得。
采用本发明的铜带轧制油轧制的铜带光泽度高，没有划痕产生，润滑性能好。而且本发明的铜带轧制油的制备方法简单，适合推广使用。
具体实施方式
以下的实施例便于更好地理解本发明，但并不限定本发明。下述实施例中的实验方法，如无特殊说明，均为常规方法。
实施例1
本发明的铜带轧制油的配方如下：
棕榈油5.5kg、十二烷基磺酸钠0.3kg、山梨醇1.1kg、甘油0.3kg、硅酸钙0.25kg、月桂酸二乙醇酰胺0.25kg、硫酸钠0.15kg、聚丙烯酰胺0.3kg、三聚磷酸钠0.4kg、硼酸钠0.3kg、硬脂酸丁酯0.2kg。
本发明的铜带轧制油的制备方法如下：
将棕榈油5.5kg、十二烷基磺酸钠0.3kg、山梨醇1.1kg、硅酸钙0.25kg、月桂酸二乙醇酰胺0.25kg、硫酸钠0.15kg、聚丙烯酰胺0.3kg、三聚磷酸钠0.4kg混合，加热至70℃，搅拌28min；加入甘油0.3kg、硼酸钠0.3kg、硬脂酸丁酯0.2kg，搅拌22℃，冷却至室温即得。
实施例2
本发明的铜带轧制油的配方如下：
棕榈油5kg、十二烷基磺酸钠0.2kg、山梨醇1.2kg、甘油0.4kg、硅酸钙0.2kg、月桂酸二乙醇酰胺0.2kg、硫酸钠0.1kg、聚丙烯酰胺0.4kg、三聚磷酸钠0.5kg、硼酸钠0.2kg、硬脂酸丁酯0.1kg。
本发明的铜带轧制油的制备方法如下：
将棕榈油5kg、十二烷基磺酸钠0.2kg、山梨醇1.2kg、硅酸钙0.2kg、月桂酸二乙醇酰胺0.2kg、硫酸钠0.1kg、聚丙烯酰胺0.4kg、三聚磷酸钠0.5kg混合，加热至65℃，搅拌30min；加入甘油0.4kg、硼酸钠0.2kg、硬脂酸丁酯0.1kg，搅拌20℃，冷却至室温即得。
实施例3
本发明的铜带轧制油的配方如下：
棕榈油6kg、十二烷基磺酸钠0.4kg、山梨醇0.8kg、甘油0.2kg、硅酸钙0.3kg、月桂酸二乙醇酰胺0.3kg、硫酸钠0.2kg、聚丙烯酰胺0.2kg、三聚磷酸钠0.3kg、硼酸钠0.4kg、硬脂酸丁酯0.3kg。
本发明的铜带轧制油的制备方法如下：
将棕榈油6kg、十二烷基磺酸钠0.4kg、山梨醇0.8kg、硅酸钙0.3kg、月桂酸二乙醇酰胺0.3kg、硫酸钠0.2kg、聚丙烯酰胺0.2kg、三聚磷酸钠0.3kg混合，加热至75℃，搅拌25min；加入甘油0.2kg、硼酸钠0.4kg、硬脂酸丁酯0.3kg，搅拌25℃，冷却至室温即得。
实施例4
本发明的铜带轧制油的配方如下：
棕榈油5.6kg、十二烷基磺酸钠0.25kg、山梨醇0.9kg、甘油0.25kg、硅酸钙0.26kg、月桂酸二乙醇酰胺0.23kg、硫酸钠0.12kg、聚丙烯酰胺0.35kg、三聚磷酸钠0.35kg、硼酸钠0.24kg、硬脂酸丁酯0.25kg。
本发明的铜带轧制油的制备方法如下：
将棕榈油5.6kg、十二烷基磺酸钠0.25kg、山梨醇0.9kg、硅酸钙0.26kg、月桂酸二乙醇酰胺0.23kg、硫酸钠0.12kg、聚丙烯酰胺0.35kg、三聚磷酸钠0.35kg混合，加热至75℃，搅拌25min；加入甘油0.25kg、硼酸钠0.24kg、硬脂酸丁酯0.25kg，搅拌25℃，冷却至室温即得。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (3)

1.一种铜带轧制油，其特征在于：所述铜带轧制油由以下质量份数的各组分组成：棕榈油5-6份、十二烷基磺酸钠0.2-0.4份、山梨醇0.8-1.2份、甘油0.2-0.4份、硅酸钙0.2-0.3份、月桂酸二乙醇酰胺0.2-0.3份、硫酸钠0.1-0.2份、聚丙烯酰胺0.2-0.4份、三聚磷酸钠0.3-0.5份、硼酸钠0.2-0.4份、硬脂酸丁酯0.1-0.3份。
2.根据权利要求1所述的铜带轧制油，其特征在于：所述铜带轧制油由以下质量份数的各组分组成：棕榈油5.5份、十二烷基磺酸钠0.3份、山梨醇1.1份、甘油0.3份、硅酸钙0.25份、月桂酸二乙醇酰胺0.25份、硫酸钠0.15份、聚丙烯酰胺0.3份、三聚磷酸钠0.4份、硼酸钠0.3份、硬脂酸丁酯0.2份。
3.权利要求1或2所述的铜带轧制油的制备方法，其特征在于：步骤如下：将配方量的棕榈油、十二烷基磺酸钠、山梨醇、硅酸钙、月桂酸二乙醇酰胺、硫酸钠、聚丙烯酰胺、三聚磷酸钠混合，加热至65-75℃，搅拌25-30min；加入配方量的其余组分，搅拌20-25℃，冷却至室温即得。
CN201410644365.8A 2014-11-14 2014-11-14 一种铜带轧制油及其制备方法 Pending CN104450062A (zh)