CN104448709B - 一种用于文具的色母粒材料及其制备方法 - Google Patents
一种用于文具的色母粒材料及其制备方法 Download PDFInfo
- Publication number
- CN104448709B CN104448709B CN201410714933.7A CN201410714933A CN104448709B CN 104448709 B CN104448709 B CN 104448709B CN 201410714933 A CN201410714933 A CN 201410714933A CN 104448709 B CN104448709 B CN 104448709B
- Authority
- CN
- China
- Prior art keywords
- parts
- stationery
- masterbatch material
- preparation
- toner
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种用于文具的色母粒材料及其制备方法。该色母粒材料，由包含以下重量份的组分制成：双酚A型环氧树脂78‑85份、丙三醇10‑12份、聚丙烯酸钠5‑7份、甲撑二异丙基萘磺酸钾3‑7份、四氯化碳3‑6份、无机盐2‑3份、三聚磷酸钠0.5‑1.5份和色粉0.5‑1份。本发明还提供了一种用于文具的色母粒材料的制备方法，包括以下步骤：(1)称取双酚A型环氧树脂78‑85份、聚丙烯酸钠5‑7份、甲撑二异丙基萘磺酸钾3‑7份、无机盐2‑3份、三聚磷酸钠0.5‑1.5份和色粉0.5‑1份；(2)将上述组分加入三辊研磨机中进行研磨，将研磨后的混合物、丙三醇10‑12份和四氯化碳3‑6份加入到反应容器中，在温度120‑150℃，搅拌0.5‑1小时；(3)将步骤2的产物在真空条件下脱泡2‑4小时，得到用于文具的色母粒材料。
Description
技术领域
本发明涉及一种色母粒材料领域，特别是一种用于文具的色母粒材料及其制备方法。
背景技术
环氧树脂是指分子中至少含有两个反应性环氧基团的树脂化合物。环氧树脂对各种材料，特别是对金属的黏着力很强，具有很强的耐化学腐蚀性、电绝缘性好、耐腐蚀等。
双酚A型环氧树脂是由双酚A、环氧氯丙烷在碱性条件下缩合，经水洗，脱溶剂精制而成的高分子化合物。因环氧树脂的制成品具有良好的物理机械性能，耐化学药品性，电气绝缘性能，故广泛应用于涂料、胶粘剂、玻璃钢、层压板、电子浇铸、灌封、包封等领域。
随着涂层材料的应用越来越广泛，对现有涂层材料的附着性能和耐候性能受到了人们的广泛关注。特别对由于紫外线照射引起的涂层材料表面的脱落和颜色牢度差的问题，迟迟没有得到很好的解决。
发明内容
针对上述的需求，本发明特别提供了一种用于文具的色母粒材料及其制备方法。
本发明的目的可以通过以下技术方案实现：
一种用于文具的色母粒材料，由包含以下重量份的组分制成：
双酚A型环氧树脂 78-85份，
丙三醇 10-12份，
聚丙烯酸钠 5-7份，
甲撑二异丙基萘磺酸钾 3-7份，
四氯化碳 3-6份，
无机盐 2-3份，
三聚磷酸钠 0.5-1.5份，
色粉 0.5-1份。
所述无机盐选自碳酸镁、碳酸钙、碳酸钾、碳酸钡、硫酸镁、硫酸锌中的一种或几种的混合。
所述无机盐为硫酸镁、硫酸锌和碳酸镁质量比为1:1:1的混合物。
所述色粉选自绿G色粉、黄3G色粉、BK2色粉和橙R色粉中的一种或几种的混合。
一种用于文具的色母粒材料的制备方法，包括以下步骤：
(1)称取双酚A型环氧树脂78-85份、聚丙烯酸钠5-7份、甲撑二异丙基萘磺酸钾3-7份、无机盐2-3份、三聚磷酸钠0.5-1.5份和色粉0.5-1份；
(2)将上述组分加入三辊研磨机中进行研磨，将研磨后的混合物、丙三醇10-12份和四氯化碳3-6份加入到反应容器中，在温度120-150℃，搅拌0.5-1小时；
(3)将步骤2的产物在真空条件下脱泡2-4小时，得到用于文具的色母粒材料。
所述研磨时间为10-15分钟。
本发明与现有技术相比，其有益效果为：
(1)本发明制得的色母粒材料不仅具有良好的固色性能，而且具有优良的附着力，能与基体材料很好的融合，可用于制备金属表面的涂层材料。
(2)本发明制得的色母粒材料由于在制备过程中没有加入易燃的有机溶剂，因而不会在储存中发生易燃等安全性问题。
(3)本发明的色母粒材料的耐候性、耐热性和抗紫外线性能好。
(4)本发明的色母粒材料其制备方法简单、环保无污染，适合大规模生产。
具体实施方式
以下结合实施例对本发明作进一步的说明。
实施例1
(1)称取双酚A型环氧树脂78kg、聚丙烯酸钠5kg、甲撑二异丙基萘磺酸钾3kg、碳酸钙2kg、三聚磷酸钠0.5kg和绿G色粉0.5kg；
(2)将上述组分加入三辊研磨机中研磨10分钟，将研磨后的混合物、丙三醇10kg和四氯化碳3kg加入到反应容器中，在温度120℃，搅拌0.7小时；
(3)将步骤2的产物在真空条件下脱泡2小时，得到用于文具的色母粒材料。
制得用于文具的色母粒材料的性能测试结果如表1所示。
实施例2
(1)称取双酚A型环氧树脂85kg、聚丙烯酸钠6kg、甲撑二异丙基萘磺酸钾7kg、碳酸钾3kg、三聚磷酸钠1kg和黄3G色粉1kg；
(2)将上述组分加入三辊研磨机中研磨15分钟，将研磨后的混合物、丙三醇12kg和四氯化碳3kg加入到反应容器中，在温度150℃，搅拌0.5小时；
(3)将步骤2的产物在真空条件下脱泡4小时，得到用于文具的色母粒材料。
制得用于文具的色母粒材料的性能测试结果如表1所示。
实施例3
(1)称取双酚A型环氧树脂80kg、聚丙烯酸钠7kg、甲撑二异丙基萘磺酸钾4kg、硫酸镁2kg、三聚磷酸钠1.5kg、BK2色粉0.2kg和橙R色粉0.5kg；
(2)将上述组分加入三辊研磨机中研磨12分钟，将研磨后的混合物、丙三醇10kg和四氯化碳5kg加入到反应容器中，在温度130℃，搅拌1小时；
(3)将步骤2的产物在真空条件下脱泡2小时，得到用于文具的色母粒材料。
制得用于文具的色母粒材料的性能测试结果如表1所示。
实施例4
(1)称取双酚A型环氧树脂82kg、聚丙烯酸钠5kg、甲撑二异丙基萘磺酸钾5kg、硫酸镁1kg、硫酸锌1kg、碳酸镁1kg、三聚磷酸钠0.5kg和橙R色粉0.5kg；
(2)将上述组分加入三辊研磨机中研磨10分钟，将研磨后的混合物、丙三醇12kg和四氯化碳6kg加入到反应容器中，在温度140℃，搅拌0.5小时；
(3)将步骤2的产物在真空条件下脱泡2小时，得到用于文具的色母粒材料。
制得用于文具的色母粒材料的性能测试结果如表1所示。
表1
本发明不限于这里的实施例，本领域技术人员根据本发明的揭示，不脱离本发明范畴所做出的改进和修改都应该在本发明的保护范围之内。
Claims (1)
1.一种用于文具的色母粒材料的制备方法，其特征在于包括以下步骤：
(1)称取双酚A型环氧树脂80kg、聚丙烯酸钠7kg、甲撑二异丙基萘磺酸钾4kg、硫酸镁2kg、三聚磷酸钠1.5kg、BK2色粉0.2kg和橙R色粉0.5kg；
(2)将上述组分加入三辊研磨机中研磨12分钟，将研磨后的混合物、丙三醇10kg和四氯化碳5kg加入到反应容器中，在温度130℃，搅拌1小时；
(3)将步骤2的产物在真空条件下脱泡2小时，得到用于文具的色母粒材料。