CN104445303A - 氢氧化镁的制备方法 - Google Patents
氢氧化镁的制备方法 Download PDFInfo
- Publication number
- CN104445303A CN104445303A CN201410604258.2A CN201410604258A CN104445303A CN 104445303 A CN104445303 A CN 104445303A CN 201410604258 A CN201410604258 A CN 201410604258A CN 104445303 A CN104445303 A CN 104445303A
- Authority
- CN
- China
- Prior art keywords
- preparation
- magnesium hydrate
- magnesium hydroxide
- magnesium
- monostearate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种氢氧化镁的制备方法,包括如下步骤:1)在水溶液中加入15g/l的硫酸镁、6g/l的氢氧化钠,搅拌75min;2)再加入0.4g/l的乙二醇单硬脂酸酯、0.8g/l的聚甘油单硬脂酸酯、0.7g/l的失水山梨醇脂肪酸酯;3)将混合液置入高压反应釜,保持搅拌200r/min,在230℃保温7.5h;4)冷却后,通过高压自动隔膜压滤机过滤,使用无离子水洗涤,最后干燥粉碎,即可获得氢氧化镁成品。本发明氢氧化镁的制备方法,其制备的氢氧化镁纯度比较高,颗粒比较细,还大大提高了氢氧化镁的表面活性。
Description
技术领域
本发明涉及氢氧化镁的制备方法。
背景技术
现有氢氧化镁的制备方法,其制备的氢氧化镁纯度不够高,颗粒不够细,表面活性不好。
发明内容
本发明的目的在于提供一种氢氧化镁的制备方法,其制备的氢氧化镁纯度比较高,颗粒比较细,还大大提高了氢氧化镁的表面活性。
为实现上述目的,本发明的技术方案是设计一种氢氧化镁的制备方法,包括如下步骤:
1)在水溶液中加入15g/l的硫酸镁、6g/l的氢氧化钠,搅拌75min;
2)再加入0.4g/l的乙二醇单硬脂酸酯、0.8g/l的聚甘油单硬脂酸酯、0.7g/l的失水山梨醇脂肪酸酯;
3)将混合液置入高压反应釜,保持搅拌200r/min,在230℃保温7.5h;
4)冷却后,通过高压自动隔膜压滤机过滤,使用无离子水洗涤,最后干燥粉碎,即可获得氢氧化镁成品。
本发明的优点和有益效果在于:提供一种氢氧化镁的制备方法,其制备的氢氧化镁纯度比较高,颗粒比较细,还大大提高了氢氧化镁的表面活性。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是:
一种氢氧化镁的制备方法,包括如下步骤:
1)在水溶液中加入15g/l的硫酸镁、6g/l的氢氧化钠,搅拌75min;
2)再加入0.4g/l的乙二醇单硬脂酸酯、0.8g/l的聚甘油单硬脂酸酯、0.7g/l的失水山梨醇脂肪酸酯;
3)将混合液置入高压反应釜,保持搅拌200r/min,在230℃保温7.5h;
4)冷却后,通过高压自动隔膜压滤机过滤,使用无离子水洗涤,最后干燥粉碎,即可获得氢氧化镁成品。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.氢氧化镁的制备方法,其特征在于,包括如下步骤:
1)在水溶液中加入15g/l的硫酸镁、6g/l的氢氧化钠,搅拌75min;
2)再加入0.4g/l的乙二醇单硬脂酸酯、0.8g/l的聚甘油单硬脂酸酯、0.7g/l的失水山梨醇脂肪酸酯;
3)将混合液置入高压反应釜,保持搅拌200r/min,在230℃保温7.5h;
4)冷却后,通过高压自动隔膜压滤机过滤,使用无离子水洗涤,最后干燥粉碎,即可获得氢氧化镁成品。