CN104409178A - 耐腐蚀电缆的制备方法 - Google Patents
耐腐蚀电缆的制备方法 Download PDFInfo
- Publication number
- CN104409178A CN104409178A CN201410729613.9A CN201410729613A CN104409178A CN 104409178 A CN104409178 A CN 104409178A CN 201410729613 A CN201410729613 A CN 201410729613A CN 104409178 A CN104409178 A CN 104409178A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight portion
- cable
- weight
- corrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐腐蚀电缆的制备方法，包括如下步骤：1）将铜单丝拉制、退火；2）将多根铜单丝绞合；3）将19.1重量份丙烯腈-丁二烯-苯乙烯共聚物、0.9重量份1,2-二氢-2,2,4-三甲基喹啉的均聚物、3.4重量份β-(3,5-二叔丁基-4-羟基苯基)丙酸正十八碳醇酯、1.7重量份γ-环氧丙基醚基三甲氧基硅烷、1.4重量份甲基三乙氧基硅烷、0.6重量份甲基硅油投入挤出机共混挤出，包覆导体。本发明制备的电缆具有优良的机械性能、电性能、耐腐蚀性能和柔软性。
Description
技术领域
本发明涉及耐腐蚀电缆的制备方法。
背景技术
现有电缆的机械性能、电性能、耐腐蚀性能、柔软性有待提高。
发明内容
本发明的目的在于提供一种耐腐蚀电缆的制备方法，其制备的电缆具有优良的机械性能、电性能、耐腐蚀性能和柔软性。
为实现上述目的，本发明的技术方案是设计一种耐腐蚀电缆的制备方法，包括如下步骤：
1）将铜单丝拉制、退火；
2）将多根铜单丝绞合；
3）将19.1重量份丙烯腈-丁二烯-苯乙烯共聚物、0.9重量份1,2-二氢-2,2,4-三甲基喹啉的均聚物、3.4重量份β-(3,5-二叔丁基-4-羟基苯基)丙酸正十八碳醇酯、1.7重量份γ-环氧丙基醚基三甲氧基硅烷、1.4重量份甲基三乙氧基硅烷、0.6重量份甲基硅油投入挤出机共混挤出，包覆导体。
本发明的优点和有益效果在于：提供一种耐腐蚀电缆的制备方法，其制备的电缆具有优良的机械性能、电性能、耐腐蚀性能和柔软性。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是：
一种耐腐蚀电缆的制备方法，包括如下步骤：
1）将铜单丝拉制、退火；
2）将多根铜单丝绞合；
3）将19.1重量份丙烯腈-丁二烯-苯乙烯共聚物、0.9重量份1,2-二氢-2,2,4-三甲基喹啉的均聚物、3.4重量份β-(3,5-二叔丁基-4-羟基苯基)丙酸正十八碳醇酯、1.7重量份γ-环氧丙基醚基三甲氧基硅烷、1.4重量份甲基三乙氧基硅烷、0.6重量份甲基硅油投入挤出机共混挤出，包覆导体。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.耐腐蚀电缆的制备方法，其特征在于，包括如下步骤：
1）将铜单丝拉制、退火；
2）将多根铜单丝绞合；
3）将19.1重量份丙烯腈-丁二烯-苯乙烯共聚物、0.9重量份1,2-二氢-2,2,4-三甲基喹啉的均聚物、3.4重量份β-(3,5-二叔丁基-4-羟基苯基)丙酸正十八碳醇酯、1.7重量份γ-环氧丙基醚基三甲氧基硅烷、1.4重量份甲基三乙氧基硅烷、0.6重量份甲基硅油投入挤出机共混挤出，包覆导体。