CN104403572B - A kind of liquor finish wax and preparation method thereof - Google Patents
A kind of liquor finish wax and preparation method thereof Download PDFInfo
- Publication number
- CN104403572B CN104403572B CN201410682001.9A CN201410682001A CN104403572B CN 104403572 B CN104403572 B CN 104403572B CN 201410682001 A CN201410682001 A CN 201410682001A CN 104403572 B CN104403572 B CN 104403572B
- Authority
- CN
- China
- Prior art keywords
- liquid
- parts
- stir
- wax
- liquor finish
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of liquor finish wax, the most composed of the following components: stearic acid 10～20 parts, liquid paraffin 20～30 parts, brightener 6～10 parts, emulsifying agent 5～10 parts, aluminium oxide 10～15 parts, silica flour 15～20 parts, water 15～20 parts, compared with prior art, present invention employs different raw material, proportioning and processing technology, 1～2 times is enhanced than common liquor finish wax polishing effect, the use time shortens 1～2 times, thus is effectively improved work efficiency, provide significant conservation production cost.
Description
Technical field
The present invention relates to polished exterior surface buffing wax field, a kind of environment-friendly high-efficiency liquid coordinating Full-automatic polishing machine to be used
Body buffing wax and preparation method thereof.
Background technology
Polishing refers to, with polishing material, subject surface is carried out leveling process, reduces roughness, improves lustrous surface and presentation quality
Process.Buffing wax (also known as polishing cured, antiscuffing paste, polishing rod) is the solid form of polishing material, applies the widest at home.
It is mainly made up of abrasive material and oils and fats.
Polishing be surface should in one of important procedure, due to the rising of human cost, and product quality requires more to come
The highest, so replacement the most slowly is manually polished by full automatic polishing, and liquor finish wax substitutes solid polishing wax therewith.This liquid
Body buffing wax feature is that it is adapted to different base materials and different workpiece is polished, and compares solid polishing wax use
Pollute less, more environmentally friendly, more efficient.
Summary of the invention
It is an object of the present invention to provide a kind of liquor finish wax and preparation method thereof.
A kind of liquor finish wax, the most composed of the following components:
Wherein said aluminium oxide is calcined alumina powder body.
Preferably, described brightener is animal oil and/or Vegetable oil lipoprotein.
Preferably, described emulsifying agent is in alkylphenol polyoxyethylene, NPE, fatty alcohol-polyoxyethylene ether
One or more.
Preferably, described calcined alumina powder body, particle diameter is 800-1200 mesh.
Preferably, the particle diameter of described silica flour is 500-700 mesh.
Another object of the present invention is to provide the preparation method of the preparation method of a kind of aforesaid liquid buffing wax, the method include with
Lower step:
(1) stearic acid and water being mixed, stir to obtain A liquid；
(2) liquid paraffin adding A liquid, stir to obtain B liquid；
(3) brightener adding B liquid, stir to obtain C liquid；
(4) aluminium oxide adding C liquid, stir to obtain D liquid；
(5) silica flour adding D liquid, stir to obtain E liquid；
(6) emulsifying agent adding E liquid, stir liquor finish wax.
Described liquor finish wax coordinates Full-automatic polishing machine to use.Compared with prior art, present invention employs different raw material,
Proportioning and processing technology, enhance more than 1-2 times than common liquor finish wax polishing effect, and the use time shortens 1-2 times
Above, thus it is effectively improved work efficiency, provide significant conservation production cost.
Detailed description of the invention
Embodiment 1:
A kind of liquor finish wax, the most composed of the following components:
Wherein said aluminium oxide is calcined alumina powder body.
Described brightener is animal oil；
Described emulsifying agent is alkylphenol polyoxyethylene；
Described calcined alumina powder body, particle diameter is 800 mesh；
The particle diameter of described silica flour is 500 mesh.
The preparation method of liquor finish wax comprises the following steps:
(1) stearic acid and water being mixed, stir to obtain A liquid；
(2) liquid paraffin adding A liquid, stir to obtain B liquid；
(3) brightener adding B liquid, stir to obtain C liquid；
(4) aluminium oxide adding C liquid, stir to obtain D liquid；
(5) silica flour adding D liquid, stir to obtain E liquid；
(6) emulsifying agent adding E liquid, stir liquor finish wax.
Embodiment 2:
A kind of liquor finish wax, the most composed of the following components:
Wherein said aluminium oxide is calcined alumina powder body.
Described brightener is Vegetable oil lipoprotein；
Described emulsifying agent is alkylphenol polyoxyethylene and NPE；
Described calcined alumina powder body, particle diameter is 1000 mesh；
The particle diameter of described silica flour is 600 mesh.
The preparation method of liquor finish wax comprises the following steps:
(1) stearic acid and water being mixed, stir to obtain A liquid；
(2) liquid paraffin adding A liquid, stir to obtain B liquid；
(3) brightener adding B liquid, stir to obtain C liquid；
(4) aluminium oxide adding C liquid, stir to obtain D liquid；
(5) silica flour adding D liquid, stir to obtain E liquid；
(6) emulsifying agent adding E liquid, stir liquor finish wax.
Embodiment 3:
A kind of liquor finish wax, the most composed of the following components:
Wherein said aluminium oxide is calcined alumina powder body.
Described brightener is Vegetable oil lipoprotein and animal oil；
Described emulsifying agent is alkylphenol polyoxyethylene, NPE and fatty alcohol-polyoxyethylene ether；
Described calcined alumina powder body, particle diameter is 1200 mesh；
Preferably, the particle diameter of described silica flour is 700 mesh.
The preparation method of liquor finish wax comprises the following steps:
(1) stearic acid and water being mixed, stir to obtain A liquid；
(2) liquid paraffin adding A liquid, stir to obtain B liquid；
(3) brightener adding B liquid, stir to obtain C liquid；
(4) aluminium oxide adding C liquid, stir to obtain D liquid；
(5) silica flour adding D liquid, stir to obtain E liquid；
(6) emulsifying agent adding E liquid, stir liquor finish wax.
Embodiment 4:
The effect experimental of the present composition
In order to prove product effect, the liquor finish wax taking the embodiment of the present invention 2 carries out effect mensuration, has carried out polishing effect real
Testing, concrete assay method and measurement result are specific as follows:
Choosing two pieces of the same workpiece of surface roughness value, experimental group utilizes the liquor finish wax of inventive embodiments 2 to be polished,
Contrast groups utilizes common liq buffing wax to be polished, and at 5 minutes, 10 minutes, within 30 minutes, 3 time points measured workpiece respectively
Surface roughness, its numerical value is as follows:
Table one surface roughness is tested
| Time | Experimental group surface roughness | Contrast groups surface roughness |
| 5 minutes | 0.03μm | 0.08μm |
| 10 minutes | 0.009μm | 0.05μm |
| 30 minutes | 0.005μm | 0.02μm |
Above-mentioned test shows: the liquor finish wax of the application is thrown and enhanced more than 1-2 times than common liquor finish wax polishing effect,
The use time shortens more than 1-2 times, thus is effectively improved work efficiency.
Claims (2)
1. a liquor finish wax, it is characterised in that: by weight, by 15 parts of stearic acid, 25 parts of liquid paraffin,
8 parts of brighteners, 7 parts of emulsifying agents, 12 parts of aluminium oxidies, 18 parts of silica flours and 18 parts of water compositions；Described aluminium oxide is
Calcined alumina powder body, particle diameter is 1000 mesh；Described brightener is Vegetable oil lipoprotein；Described emulsifying agent is that alkyl phenol gathers
Oxygen vinyl Ether and NPE；The particle diameter of described silica flour is 600 mesh.
The preparation method of a kind of liquor finish wax the most according to claim 1, it is characterised in that include following
Step:
(1) stearic acid and water being mixed, stir to obtain A liquid；
(2) liquid paraffin adding A liquid, stir to obtain B liquid；
(3) brightener adding B liquid, stir to obtain C liquid；
(4) aluminium oxide adding C liquid, stir to obtain D liquid；
(5) silica flour adding D liquid, stir to obtain E liquid；
(6) emulsifying agent adding E liquid, stir to obtain liquor finish wax.