CN107502200A - A kind of automobile polishing wax and its manufacture method - Google Patents
A kind of automobile polishing wax and its manufacture method Download PDFInfo
- Publication number
- CN107502200A CN107502200A CN201710799591.7A CN201710799591A CN107502200A CN 107502200 A CN107502200 A CN 107502200A CN 201710799591 A CN201710799591 A CN 201710799591A CN 107502200 A CN107502200 A CN 107502200A
- Authority
- CN
- China
- Prior art keywords
- polishing wax
- automobile polishing
- automobile
- peregal
- wax according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of automobile polishing wax and its manufacture method, include the component of following parts by weight：Solid paraffin 10~40%, emulsifying agent 5~15%, grinding agent 15~55%, brightener 1~2% and deionized water surplus.The automobile polishing wax has more preferable detergency and glossiness, and stability is more preferable for not hurting the cut of priming paint.
Description
Technical field
The invention belongs to Automobile Products and its manufacturing field, and in particular to a kind of automobile polishing wax and its manufacture method.
Background technology
As the improvement of people's living standards, the use of automobile is increasingly popularized.The vehicle body of Hyundai Motor is typically using gold
Category paint, metallic paint by it is permanent expose to the weather after color can produce and take off change, in addition, automobile is in use, due to roadside
Handstone contact with the branch in roadside, certain cut can be produced, these can all influence the outward appearance of automobile.
In order that vehicle body keeps beautiful clean and tidy, car owner can be usually to be polished the maintenances such as waxing.Polishing is to utilize
The method of physics either chemistry makes workpiece surface reach certain smoothness, removes process that is coarse and obtaining flat smooth.
Automobile finish polishing is to carry out modification processing to automobile finish using flexible polishing instrument and grinding agent.Buffing wax is grinding agent
One of carrying form, it is a lot of in auto industry dosage.
Existing polishing and waxing operation generally requires to be carried out by polishing machine, and operation is wasted time and energy, and cost is not low,
Car owner's inconvenience is voluntarily operated.If it is possible to provide it is a can the polishing that fast handles of the cut slight to vehicle body
Wax, reach and repair cut, the effect of upper wax polishing, the maintenance field in market, will have great importance after automobile.
The content of the invention
The invention provides a kind of automobile polishing wax and its manufacture method, and the automobile polishing wax is not for hurting priming paint
Cut, there is more preferable detergency and glossiness, and stability is more preferable.
The invention provides a kind of automobile polishing wax, include the component of following parts by weight：
Preferably, described emulsifying agent is at least one in AEO and APES
Kind.As it is further preferably, described emulsifying agent is paregal O -10, paregal O -15, paregal O -20, paregal O -
25th, at least one of peregal SA20, peregal A20, paregal O S15, peregal C-125, OP-10, OP-25.
Preferably, described grinding agent is nano aluminium oxide.As further preferred, described nano aluminium oxide
Preparation method is as follows：
(1) under the conditions of being stirred at room temperature, the Aluminum Chloride Hexahydrate aqueous solution is added drop-wise in aqueous sodium carbonate, then passed through
Filter, wash, be dried to obtain presoma；
(2) solid precursor that step (1) obtains is added in Muffle furnace, calcined 2~3 hours in 500~600 DEG C,
Obtain Nano-sized Alumina Powder.
As it is further preferably, in step (1), PEG2000 is added in described aqueous sodium carbonate.
Preferably, described brightener is dimethyl silicone polymer.
Present invention also offers a kind of manufacture method of described automobile polishing wax, including：By solid paraffin and grinding agent
It is added to the water, stirs, then adds emulsifying agent and brightener is well mixed and obtains described automobile polishing wax.
Compared with the existing technology, beneficial effects of the present invention are embodied in：
(1) detergency and glossiness of product are effectively improved using the buffing wax of the present invention, performance attractive in appearance is preferable；
(2) acid resistance and alkali resistance of product are effectively improved using the buffing wax of the present invention so that the throwing of buffing wax
Optical property is more lasting.
Embodiment
Embodiment 1
Component：
The preparation method of nano aluminium oxide：
(1) 24g Aluminum Chloride Hexahydrates are dissolved in 200mL water, obtain the Aluminum Chloride Hexahydrate aqueous solution；
(2) 18g sodium carbonate is dissolved in 150mL water, then adds 2g PEG2000, obtain aqueous sodium carbonate；
(3) under the conditions of being stirred at room temperature, the Aluminum Chloride Hexahydrate aqueous solution that step (1) obtains is added drop-wise to step (2) and obtained
Aqueous sodium carbonate in, time for adding is 20 minutes, after being added dropwise to complete, stirs 2 hours, then by filtering, washing, alcohol washes
Solid precursor is obtained with microwave drying；
(4) solid precursor that step (3) obtains is added in Muffle furnace, calcines 2~3 hours, received in 500 DEG C
Rice alumina powder.
The preparation method of buffing wax：
Solid paraffin and the Nano-sized Alumina Powder being prepared are added to the water, stirs, then adds breast
Agent and brightener, which are well mixed, obtains described automobile polishing wax.
Embodiment 2
Component：
Preparation method：Solid paraffin and commercially available nano aluminium oxide (PAP-A50) are added to the water, stirred, then
Add emulsifying agent and brightener is well mixed and obtains described automobile polishing wax.
Embodiment 3
Component：
Preparation method：Solid paraffin and grinding agent diatomite are added to the water, stirred, then adds emulsifying agent
Well mixed with brightener is to obtain described automobile polishing wax.
Embodiment 4
Component：
Preparation method：Solid paraffin and abrasive silica are added to the water, stirred, then adds emulsification
Agent and brightener, which are well mixed, obtains described automobile polishing wax.
Dirt-removing power, glossiness test and the acid and alkali resistance for the automobile polishing wax that detection embodiment 1~4 obtains.
1st, dirt-removing power is tested：By outside reference white car paint panel 120mm × 50mm holding chambers, natural dust stratification 7d.With
Quantitative automobile polish clear glazing on panel, whiteness Wg is measured with whiteness, and calculate automobile polish to white car
Paint the detergency of plate.
Detergency=(whiteness value before whiteness value-cleaning after cleaning)/(whiteness before blank plate whiteness value-cleaning
Value) * 100%
2nd, glossiness test is by outside reference white and colored car paint panel 150mm × 80mm holding chambers, natural dust stratification 7d,
Glazing is cleaned using a certain amount of automobile polish, its glossiness is tested using vancometer.
3rd, acid resistance is tested：The sulfuric acid solution even application that mass fraction is 25% is being smeared into vehicle glazing emulsion
On standard paint plate, 72h is placed, whether breakage tarnishes the lacquer painting situation of observation paint plate, if lacquer painting retains more than 90% preferably,
It is qualified to retain more than 70%, and less than 70% is poor.
4th, the sodium hydroxide solution even application that mass fraction is 25% is being smeared vehicle glazing emulsion by alkali resistance
On standard paint plate, 30d is stood, whether breakage tarnishes the lacquer painting of observation paint plate, if lacquer painting retains more than 90% preferably, retains
More than 70% is qualified, and less than 70% is poor.
From the testing result of embodiment 1~4, the species of grinding agent is to detergency, glossiness, acid resistance and alkali resistance
Have a great influence, most suitable grinding agent is nano aluminium oxide.
Claims (8)
1. a kind of automobile polishing wax, it is characterised in that include the component of following parts by weight：
2. automobile polishing wax according to claim 1, it is characterised in that described emulsifying agent is AEO
At least one of with APES.
3. automobile polishing wax according to claim 2, it is characterised in that described emulsifying agent is paregal O -10, average
Add O-15, paregal O -20, peregal O-25, peregal SA20, peregal A20, paregal O S15, peregal C-125, OP-
10th, at least one of OP-25.
4. automobile polishing wax according to claim 1, it is characterised in that described grinding agent is nano aluminium oxide.
5. automobile polishing wax according to claim 4, it is characterised in that the preparation method of described nano aluminium oxide is such as
Under：
(1) under the conditions of being stirred at room temperature, the Aluminum Chloride Hexahydrate aqueous solution is added drop-wise in aqueous sodium carbonate, then by filtering,
Wash, be dried to obtain presoma；
(2) solid precursor that step (1) obtains is added in Muffle furnace, calcines 2~3 hours, obtain in 500~600 DEG C
Nano-sized Alumina Powder.
6. automobile polishing wax according to claim 5, it is characterised in that in step (1), in described aqueous sodium carbonate
Add PEG2000.
7. automobile polishing wax according to claim 1, it is characterised in that described brightener is dimethyl silicone polymer.
A kind of 8. manufacture method of automobile polishing wax as described in any one of claim 1~7, it is characterised in that including：Will be solid
Body paraffin and grinding agent are added to the water, and stir, then add that emulsifying agent and brightener are well mixed and obtain described in
Automobile polishing wax.