CN105219275B - A kind of plastic products modify processing antiscuffing paste - Google Patents
A kind of plastic products modify processing antiscuffing paste Download PDFInfo
- Publication number
- CN105219275B CN105219275B CN201510599038.XA CN201510599038A CN105219275B CN 105219275 B CN105219275 B CN 105219275B CN 201510599038 A CN201510599038 A CN 201510599038A CN 105219275 B CN105219275 B CN 105219275B
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- plastic products
- modification
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Processing antiscuffing paste is modified the invention discloses a kind of plastic products, is related to plastic products processing technique field, is made up of the raw material of following parts by weight：80 90 parts of modified alta-mud, 30 35 parts of soap powder, 25 30 parts of zeolite powder, 15 20 parts of flyash, 15 20 parts of coarse colza meal, 13 18 parts of tea seed powder, 12 16 parts of tung oil, 10 15 parts of modification of microcrystalline paraffin, 8 12 parts of activated carbon, 8 12 parts of silicon powder, 6 10 parts of vaseline, 58 parts of tallow, 50 60 parts of ethanol, 300 350 parts of water.The present invention is using modified alta-mud as primary raw material; plastic products modification processing antiscuffing paste is made, the antiscuffing paste can directly be coated on surface of plastic products, can not only effectively improve polishing effect; the dimensional accuracy of plastic products can also be protected to greatest extent, prevent excessive polishing.
Description
Technical field：
The present invention relates to plastic products processing technique field, and in particular to a kind of plastic products modify processing antiscuffing paste.
Background technology：
Plastic products are to use plastics for the daily necessities of main Raw material processing, the general designation of industrial goods.Including with
Plastics are the product of all techniques such as injection, the plastic uptake of raw material.Plastic products produce the dispensing for generally comprising plastics, shaping, machine
Tool processing, engagement, modification and assembling etc..Four processes are carried out after plastics are molded for product or semi-products afterwards, also known as
For plastics secondary operation., it is necessary to remove the cold shut of surface of plastic products, spot and micro useless by polishing in modification processing
Side.It is general to be polished using polishing machine, because polishing wheel is directly contacted with surface of plastic products, therefore easily occur polished
Spend or polish situation not in place.Product appearance will excessively be directly affected and waste raw material by such as polishing, and be polished not in place
Percent defective will be increased, so as to increase input cost.
The content of the invention：
The technical problems to be solved by the invention are to provide a kind of polishing effect good and easy to use material products modification
Processing antiscuffing paste.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of plastic products modify processing antiscuffing paste, are made up of the raw material of following parts by weight：
80-90 parts of modified alta-mud, 30-35 parts of soap powder, 25-30 parts of zeolite powder, 15-20 parts of flyash, coarse colza meal
15-20 parts, 13-18 parts of tea seed powder, 12-16 parts of tung oil, 10-15 parts of modification of microcrystalline paraffin, 8-12 parts of activated carbon, silicon powder 8-12
Part, 6-10 parts of vaseline, 5-8 parts of tallow, 50-60 parts of ethanol, 300-350 parts of water；
Its preparation method is as follows：
(1) first well mixed modified alta-mud, zeolite powder and flyash are placed in 70-80 DEG C of baking oven and dry 8-12h,
Then in calcining 2-3h at 300-350 DEG C, 1-2h is calcined at 500-550 DEG C, mixed powder is produced；
(2) soap powder and tea seed powder are added in ethanol, then in ultrasonically treated under supersonic frequency 22kHz, power 100W
15-20min, adds tung oil, modification of microcrystalline paraffin, vaseline and tallow, and mixture is warming up to 60-65 DEG C of insulated and stirred 10-
15min, produces material I；
(3) coarse colza meal, activated carbon and silicon powder mixed powder are added to the water, stand and material I is added after 15-20min,
Ball mill is transferred to after well mixed, fineness is milled to less than 0.1mm, the finally heated water content that is concentrated into is 12-15%.
The modified alta-mud is formed by the material modification of following parts by weight：60-70 parts of bentonite, carboxymethyl cellulose
5-8 parts of sodium, 0.2-0.5 parts of nano boric acid aluminium, 90-100 parts of ethanol, its method of modifying are：First by bentonite and carboxymethyl cellulose
Plain sodium is scattered in ethanol, is added nano boric acid aluminium after grinding 15min, is well mixed after microwave frequency 2450MHz, power
Microwave treatment 12min under 600W, powder is ground into after last concentrated, drying.Alta-mud modification can improve stickiness, from
And strengthen polishing effect.
The modification of microcrystalline paraffin is formed by the material modification of following parts by weight：90-100 parts of microcrystalline wax, β-ring paste
Smart 6-10 parts, 2-3 parts of citric acid, 100-120 parts of water, its method of modifying is：First citric acid is added in microcrystalline wax, grinding
Beta-schardinger dextrin and water are added after 15min, is well mixed after microwave treatment 8min under microwave frequency 2450MHz, power 600W, most
By concentration, drying after be ground into powder.The modification of microcrystalline wax can improve lubricant effect, prevent excessive polishing.
The beneficial effects of the invention are as follows：Plastic products modification processing is made using modified alta-mud as primary raw material in the present invention
With antiscuffing paste, the antiscuffing paste can directly be coated on surface of plastic products, can not only effectively improve polishing effect, moreover it is possible to greatest extent
The dimensional accuracy of plastic products is protected on ground, prevents excessive polishing.
Embodiment：
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1
(1) well mixed 80 parts of modified alta-muds, 25 parts of zeolite powders and 15 parts of flyash are first placed in 70-75 DEG C of baking oven
Middle dry 12h, then in calcining 3h at 350 DEG C, calcines 2h at 550 DEG C, produces mixed powder；
(2) 30 parts of soap powder and 18 parts of tea seed powder are added in 50 parts of ethanol, then in supersonic frequency 22kHz, power
Ultrasonically treated 20min under 100W, adds 12 parts of tung oil, 10 parts of modification of microcrystalline paraffin, 7 parts of vaseline and 5 parts of tallows, mixture
60-65 DEG C of insulated and stirred 15min is warming up to, material I is produced；
(3) 15 parts of coarse colza meals, 8 parts of activated carbons and 8 parts of silicon powder mixed powders are added in 300 parts of water, stands 15min
Material I is added afterwards, ball mill is transferred to after being well mixed, and is milled to fineness less than 0.1mm, the finally heated water content that is concentrated into is
12-15%.
The preparation of modified alta-mud：First 60 parts of bentonites and 5 parts of sodium carboxymethylcelluloses are scattered in 90 parts of ethanol, ground
Grind and 0.3 part of nano boric acid aluminium is added after 15min, be well mixed after microwave treatment under microwave frequency 2450MHz, power 600W
12min, powder is ground into after last concentrated, drying.
The preparation of modification of microcrystalline paraffin：First 2 parts of citric acids are added in 90 parts of microcrystalline waxes, 6 parts are added after grinding 15min
Beta-schardinger dextrin and 100 parts of water, are well mixed after microwave treatment 8min under microwave frequency 2450MHz, power 600W, most afterwards through dense
Powder is ground into after contracting, drying.
Embodiment 2
(1) well mixed 85 parts of modified alta-muds, 30 parts of zeolite powders and 18 parts of flyash are first placed in 75-80 DEG C of baking oven
Middle dry 12h, then in calcining 3h at 350 DEG C, calcines 2h at 500 DEG C, produces mixed powder；
(2) 35 parts of soap powder and 15 parts of tea seed powder are added in 55 parts of ethanol, then in supersonic frequency 22kHz, power
Ultrasonically treated 20min under 100W, adds 15 parts of tung oil, 12 parts of modification of microcrystalline paraffin, 8 parts of vaseline and 7 parts of tallows, mixture
60-65 DEG C of insulated and stirred 15min is warming up to, material I is produced；
(3) 18 parts of coarse colza meals, 10 parts of activated carbons and 8 parts of silicon powder mixed powders are added in 350 parts of water, stood
Material I is added after 15min, ball mill is transferred to after being well mixed, fineness is milled to less than 0.1mm, the finally heated water that is concentrated into contains
Measure as 12-15%.
The preparation of modified alta-mud：First 65 parts of bentonites and 7 parts of sodium carboxymethylcelluloses are scattered in 95 parts of ethanol, ground
Grind and 0.4 part of nano boric acid aluminium is added after 15min, be well mixed after microwave treatment under microwave frequency 2450MHz, power 600W
12min, powder is ground into after last concentrated, drying.
The preparation of modification of microcrystalline paraffin：First 3 parts of citric acids are added in 95 parts of microcrystalline waxes, 8 parts are added after grinding 15min
Beta-schardinger dextrin and 110 parts of water, are well mixed after microwave treatment 8min under microwave frequency 2450MHz, power 600W, most afterwards through dense
Powder is ground into after contracting, drying.
Embodiment 3
(1) well mixed 90 parts of modified alta-muds, 30 parts of zeolite powders and 20 parts of flyash are first placed in 75-80 DEG C of baking oven
Middle dry 12h, then in calcining 3h at 350 DEG C, calcines 2h at 550 DEG C, produces mixed powder；
(2) 35 parts of soap powder and 18 parts of tea seed powder are added in 60 parts of ethanol, then in supersonic frequency 22kHz, power
Ultrasonically treated 20min under 100W, adds 16 parts of tung oil, 15 parts of modification of microcrystalline paraffin, 10 parts of vaseline and 8 parts of tallows, mixing
Thing is warming up to 60-65 DEG C of insulated and stirred 15min, produces material I；
(3) 20 parts of coarse colza meals, 12 parts of activated carbons and 8 parts of silicon powder mixed powders are added in 350 parts of water, stood
Material I is added after 15min, ball mill is transferred to after being well mixed, fineness is milled to less than 0.1mm, the finally heated water that is concentrated into contains
Measure as 12-15%.
The preparation of modified alta-mud：First 70 parts of bentonites and 8 parts of sodium carboxymethylcelluloses are scattered in 100 parts of ethanol,
Grind and 0.5 part of nano boric acid aluminium is added after 15min, be well mixed after microwave treatment under microwave frequency 2450MHz, power 600W
12min, powder is ground into after last concentrated, drying.
The preparation of modification of microcrystalline paraffin：First 3 parts of citric acids are added in 100 parts of microcrystalline waxes, 10 are added after grinding 15min
Part beta-schardinger dextrin and 120 parts of water, are well mixed after microwave treatment 8min under microwave frequency 2450MHz, power 600W, most pass through afterwards
Powder is ground into after concentration, drying.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (2)
1. a kind of plastic products modify processing antiscuffing paste, it is characterised in that be made up of the raw material of following parts by weight：
80-90 parts of modified alta-mud, 30-35 parts of soap powder, 25-30 parts of zeolite powder, 15-20 parts of flyash, coarse colza meal 15-20
It is part, 13-18 parts of tea seed powder, 12-16 parts of tung oil, 10-15 parts of modification of microcrystalline paraffin, 8-12 parts of activated carbon, 8-12 parts of silicon powder, all
6-10 parts of intellectual circle, 5-8 parts of tallow, 50-60 parts of ethanol, 300-350 parts of water；
Its preparation method is as follows：
(1) first well mixed modified alta-mud, zeolite powder and flyash are placed in 70-80 DEG C of baking oven and dry 8-12h, then
In calcining 2-3h at 300-350 DEG C, 1-2h is calcined at 500-550 DEG C, mixed powder is produced；
(2) soap powder and tea seed powder are added in ethanol, then in ultrasonically treated 15- under supersonic frequency 22kHz, power 100W
20min, adds tung oil, modification of microcrystalline paraffin, vaseline and tallow, and mixture is warming up to 60-65 DEG C of insulated and stirred 10-
15min, produces material I；
(3) coarse colza meal, activated carbon and silicon powder mixed powder are added to the water, stand and material I is added after 15-20min, mixing
Ball mill is transferred to after uniform, fineness is milled to less than 0.1mm, the finally heated water content that is concentrated into is 12-15%；
The modified alta-mud is formed by the material modification of following parts by weight：60-70 parts of bentonite, sodium carboxymethylcellulose 5-
8 parts, 0.2-0.5 parts of nano boric acid aluminium, 90-100 parts of ethanol, its method of modifying be：First by bentonite and sodium carboxymethylcellulose
It is scattered in ethanol, adds nano boric acid aluminium after grinding 15min, be well mixed after under microwave frequency 2450MHz, power 600W
Microwave treatment 12min, powder is ground into after last concentrated, drying.
2. plastic products according to claim 1 modify processing antiscuffing paste, it is characterised in that：The modification of microcrystalline paraffin
Formed by the material modification of following parts by weight：90-100 parts of microcrystalline wax, 6-10 parts of beta-schardinger dextrin, 2-3 parts of citric acid, water
100-120 parts, its method of modifying is：First citric acid is added in microcrystalline wax, beta-schardinger dextrin and water are added after grinding 15min,
It is well mixed after microwave treatment 8min under microwave frequency 2450MHz, power 600W, powder is ground into after last concentrated, drying
End.