CN106079028A

CN106079028A - For the packing box of the rock high-end tea of teas eriocheir sinensis or tank method of manufacturing technology and product

Info

Publication number: CN106079028A
Application number: CN201610592747.XA
Authority: CN
Inventors: 不公告发明人
Original assignee: Individual
Current assignee: Individual
Priority date: 2016-07-26
Filing date: 2016-07-26
Publication date: 2016-11-09

Abstract

Packing box or tank method of manufacturing technology for the rock high-end tea of teas eriocheir sinensis; processing step is as follows: (1) will pulverize after rock teas eriocheir sinensis tea unqualified or after pulverizing rock teas eriocheir sinensis tea is unqualified, pornographic movie, stalky tea mixture; tableware level Moulding powder raw material mix homogeneously, obtains mixing compositions；(2) described mixing compositions is preheated；(3) preheated described mixing compositions is added thermocompression forming in heating die cavity, obtain tea packaging box or the thick embryo of tank；(4) surface of embryo thick to described tea packaging box or tank carries out sanding and polishing process or carries out machining and obtain tea packaging box or tank finished product.

Description

For the packing box of the rock high-end tea of teas eriocheir sinensis or tank method of manufacturing technology and product

Technical field

The present invention relates to tea packaging apparatus, more specifically refer to a kind of packaging for rock teas eriocheir sinensis high-end tea bag dress Box or tank method of manufacturing technology and product.

Background technology

Existing tea packaging box or tank the most do not obtain preferable breakthrough on packaging material.If employing Tea Production In Folium Camelliae sinensis is unqualified or Folium Camelliae sinensis pornographic movie, stalky tea the like waste manufacture tea packaging box or tank, with regard to energy for the main material that manufactures Realize, with tea bag tea, with the tea dress tea packaging box of tea or tank New function, just to make this new tea packaging box or tank, generation Abundant tea culture propagates succession characteristic element, by the extensive welcome of consumer.

Summary of the invention

It is an object of the invention to provide and a kind of use brand-new material to manufacture the manufacturing process of tea-processing packing box or tank Method and product, the i.e. Folium Camelliae sinensis with tea of the same race to be packed are unqualified for mainly to manufacture material, manufacture tea packaging box or tank Method of manufacturing technology and product.The technical scheme is that

For packing box or the tank method of manufacturing technology of the rock high-end tea of teas eriocheir sinensis, it technology is characterized in that

Processing step is as follows: (1) will pulverize after rock teas eriocheir sinensis tea unqualified or pulverize after rock teas eriocheir sinensis tea unqualified, yellow Sheet, stalky tea mixture, tableware level Moulding powder raw material mix homogeneously, obtain mixing compositions；(2) described mixing compositions is carried out Preheating；(3) preheated described mixing compositions is added thermocompression forming in heating die cavity, obtain tea packaging box or tank is thick Embryo；(4) surface of embryo thick to described tea packaging box or tank carries out sanding and polishing process or carries out machining and obtain Folium Camelliae sinensis bag Mounted box or tank finished product.

The described packing box for the rock high-end tea of teas eriocheir sinensis or tank, use above-mentioned method of manufacturing technology to make.

The Folium Camelliae sinensis of the tea of the same race that above-mentioned employing is to be packed is unqualified or Folium Camelliae sinensis pornographic movie, stalky tea are for mainly to manufacture material, comes Manufacture tea packaging box or the process of tank and product.Obtain the most positive technological progress:

1, owing to using Folium Camelliae sinensis unqualified or Folium Camelliae sinensis pornographic movie, stalky tea, tea packaging box or tank are manufactured for the main material that manufactures, real Show twice laid.After in Tea Production, tea dust, Folium Camelliae sinensis pornographic movie, stalky tea separate, general processing method is all discarded or low Valency is sold as the general raw material of industry, is applied in the production of tea packaging box or tank, it is achieved that twice laid.It is manufactured into tea After leaf packing box or tank, substantially increase tea dust, Folium Camelliae sinensis pornographic movie, the added value of stalky tea.

2, above-mentioned employing tea dust, Folium Camelliae sinensis pornographic movie, stalky tea are mainly to manufacture tea packaging box or the tank that material manufactures, mainly Composition is tea dust, Folium Camelliae sinensis pornographic movie, stalky tea, easily degrades, and compared with the tea packaging box of other materials manufacture or tank, can produce The biggest ecological, environmental protective benefit.

3, owing to have employed, Folium Camelliae sinensis is unqualified, Folium Camelliae sinensis pornographic movie, stalky tea, for main manufacture material manufacture tea packaging box or Tank, generation significantly have the technical effect that in the case of using, Folium Camelliae sinensis pornographic movie, stalky tea unqualified with kind Folium Camelliae sinensis, packing box or tank band There is the fragrance of same kind tea, for packaging with kind Folium Camelliae sinensis, overcome the other materials packing boxes such as generation taint of odour or tank is had Defect, it is possible to keep very well the quality of packaging Folium Camelliae sinensis.

4, the Folium Camelliae sinensis of above-mentioned employing tea of the same race is unqualified is the main tea packaging box manufacturing material manufacture or tank, proposes first With tea bag tea, with tea dress tea, with same kind tea bag dress with the tea packaging new concept of kind tea, there is abundant tea culture and propagate Succession characteristic element, especially for the packaging of all kinds of high-end tea, can be welcome by market.

Embodiment

It is exemplified below:

Embodiment 1:

As follows for packing box or tank method of manufacturing technology, processing step and the condition of rock teas eriocheir sinensis high-end tea bag dress: (1) will Rock teas eriocheir sinensis tea after pulverizing unqualified or after pulverizing rock teas eriocheir sinensis tea is unqualified, pornographic movie, stalky tea mixture, tableware level three Poly cyanamid Moulding powder (also referred to as melamine moulding powder) raw material is (5～8) in mass ratio: the ratio mix homogeneously of (2～5), is mixed Even compositions；(2) described mixing compositions is preheated；(3) preheated described mixing compositions is added heating die cavity Middle thermocompression forming, obtains tea packaging box or the thick embryo of tank；(4) surface of embryo thick to described tea packaging box or tank carries out polishing throwing Optical processing or carry out machining and obtain tea packaging box or tank finished product.

The temperature upper limit preheating described mixing compositions is 130 DEG C.

Described mixing compositions is carried out the temperature range of thermocompression forming be 140～150 DEG C, pressure limit be 5～ 40MPa。

The described packing box for rock teas eriocheir sinensis high-end tea bag dress or tank, use above-mentioned method of manufacturing technology to make.

Embodiment 2:

As follows for packing box or tank method of manufacturing technology, processing step and the condition of rock teas eriocheir sinensis high-end tea bag dress: (1) will Rock teas eriocheir sinensis tea after pulverizing unqualified or after pulverizing rock teas eriocheir sinensis tea is unqualified, pornographic movie, stalky tea mixture, tableware level urea Aldehyde Moulding powder raw material is (5～8) in mass ratio: the ratio mix homogeneously of (2～5), obtains mixing compositions；(2) to described mixed Even compositions preheats；(3) preheated described mixing compositions is added thermocompression forming in heating die cavity, obtain Folium Camelliae sinensis bag Mounted box or the thick embryo of tank；(4) surface of embryo thick to described tea packaging box or tank carries out sanding and polishing process or carries out machining Obtain tea packaging box or tank finished product.

Described mixing compositions is carried out the temperature range of thermocompression forming be 140～150 DEG C, pressure limit be 10～ 40MPa。

Claims

1., for packing box or the tank method of manufacturing technology of the rock high-end tea of teas eriocheir sinensis, it technology is characterized in that

Packing box for the rock high-end tea of teas eriocheir sinensis the most according to claim 1 or tank method of manufacturing technology, its technology Feature is:

Described tableware level Moulding powder is tableware level tripolycyanamide Moulding powder or tableware level urea aldehyde Moulding powder.

Rock teas eriocheir sinensis tea after pulverizing unqualified or after pulverizing rock teas eriocheir sinensis tea is unqualified, pornographic movie, stalky tea mixture and meal The mass ratio of tool level Moulding powder is (5～8): (2～5).

4., for packing box or the tank of the rock high-end tea of teas eriocheir sinensis, it technology is characterized in that described in employing claim 1 or 2 or 3 Method of manufacturing technology make.