CN104403151A - Elastic rubber floorboard - Google Patents
Elastic rubber floorboard Download PDFInfo
- Publication number
- CN104403151A CN104403151A CN201410817317.4A CN201410817317A CN104403151A CN 104403151 A CN104403151 A CN 104403151A CN 201410817317 A CN201410817317 A CN 201410817317A CN 104403151 A CN104403151 A CN 104403151A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- elastic rubber
- floorboard
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an elastic rubber floorboard, belonging to the field of rubber. The elastic rubber floorboard is prepared from the following components in parts by weight: 90-100 parts of nitrile-butadiene rubber, 30-40 parts of vinyl chloride rubber, 5-9 parts of ethylene propylene diene monomer rubber, 2-4 parts of sulfur, 0.5-1.5 parts of stearic acid, 8-15 parts of silica white, 1-3 parts of anti-aging agent, 3-9 parts of antistatic agent, 1.8-2.4 parts of thiuram type accelerator, 10-15 parts of activated calcium carbonate powder, 0.6-1.2 parts of antioxidant, 1-6 parts of coupling agent and 15-30 parts of flame retardant. By using the nitrile-butadiene rubber as the main rubber and adding the anti-aging agent and flame retardant, the elastic rubber floorboard has excellent oil resistance, flame retardancy and aging resistance; and the antistatic agent is added to further enhance the antistatic property of the floorboard.
Description
Technical field
The invention belongs to rubber materials, specifically a kind of elastic rubber floor.
Background technology
Elastic rubber floor is body material with rubber, then allocate several functions Synergist S-421 95 into, through the pavement that series of process processes, has a very wide range of applications in industry and the field such as civilian.
A kind of synthetic rubber that paracril is obtained by divinyl and acrylonitrile compolymer.Oil resistant (especially alkane oil), the good synthetic rubber of ageing-resistant performance.In paracril, acrylonitrile content (%) has 42 ~ 46,36 ~ 41,31 ~ 35,25 ~ 30,18 ~ 24 etc. five kinds.Acrylonitrile content is more, and oil-proofness is better, but winter hardiness then corresponding decline.It can use for a long time in the air of 120 DEG C or in the oil of 150 DEG C.In addition, it also has good water tolerance, resistance to air loss and excellent adhesive property.Be widely used in system various oil resisting rubber goods, multiple oil seat gasket, pad, sleeve pipe, soft packaging, flexible rubber hose, printer's roll, cable gum material etc., in the industries such as automobile, aviation, oil, duplicating, become requisite resilient material.
In prior art, the application of resiliently-mounted floor is more and more extensive, but the performance of its hardness, the aspect such as anti-aging, fire-retardant, high temperature resistant can't meet service requirements completely.
Summary of the invention
The object of the invention is to overcome prior art defect, a kind of elastic rubber floor is provided.
Object of the present invention can be achieved through the following technical solutions:
A kind of elastic rubber floor, it is characterized in that, described elastic rubber floor is made up of the component of following weight part: paracril 90-100 part, polyvinyl chloride rubber 30-40 part, terpolymer EP rubber 5-9 part, sulphur 2-4 part, stearic acid 0.5-1.5 part, white carbon black 8-15 part, anti-aging agent 1-3 part, static inhibitor 3-9 part, thiuram type accelerator 1.8-2.4 part, active calcium carbonate powder 10-15 part, oxidation inhibitor 0.6-1.2 part, coupling agent 1-6 part, fire retardant 15-30 part.
As further preferred, described elastic rubber floor is made up of the component of following weight part: paracril 95 parts, polyvinyl chloride rubber 35 parts, terpolymer EP rubber 7 parts, 3 parts, sulphur, stearic acid 1 part, white carbon black 12 parts, 2 parts, anti-aging agent, 6 parts, static inhibitor, thiuram type accelerator 2.1 parts, active calcium carbonate powder 12 parts, 0.9 part, oxidation inhibitor, coupling agent 3.5 parts, fire retardant 22 parts.
Anti-aging agent of the present invention is antioxidant 264; Described oxidation inhibitor is irgasfos 168; Described static inhibitor is static inhibitor 129; Described coupling agent is silane coupling agent.
Fire retardant of the present invention is nano-sized magnesium hydroxide, nano-aluminum hydroxide, antimonous oxide are the mixing of 1: 1: 2 with weight ratio.
Beneficial effect of the present invention: elastic rubber floor of the present invention selects paracril to be primary elastomeric, add antiaging agent, fire retardant, there is excellent oil resistant, fire-retardant, ageing resistance, add static inhibitor simultaneously, further increase the antistatic property on floor.
Embodiment
For the ease of it will be appreciated by those skilled in the art that the present invention is further illustrated below in conjunction with specific embodiment.
Embodiment 1
A kind of elastic rubber floor, is made up of the component of following weight part: paracril 95 parts, polyvinyl chloride rubber 35 parts, terpolymer EP rubber 7 parts, 3 parts, sulphur, stearic acid 1 part, white carbon black 12 parts, antioxidant 264 2 parts, 129 6 parts, static inhibitor, thiuram type accelerator 2.1 parts, active calcium carbonate powder 12 parts, irgasfos 168 0.9 part, silane coupling agent 3.5 parts, nano-sized magnesium hydroxide 5.5 parts, nano-aluminum hydroxide 5.5 parts, antimonous oxide 11 parts.
Embodiment 2
A kind of elastic rubber floor, is made up of the component of following weight part: paracril 90 parts, polyvinyl chloride rubber 30 parts, terpolymer EP rubber 5 parts, 2 parts, sulphur, stearic acid 0.5 part, white carbon black 9 parts, antioxidant 264 1 part, 129 4 parts, static inhibitor, thiuram type accelerator 1.8 parts, active calcium carbonate powder 10 parts, irgasfos 168 0.6 part, silane coupling agent 2 parts, nano-sized magnesium hydroxide 4 parts, nano-aluminum hydroxide 4 parts, antimonous oxide 8 parts.
Embodiment 3
A kind of elastic rubber floor, is made up of the component of following weight part: paracril 100 parts, polyvinyl chloride rubber 40 parts, terpolymer EP rubber 9 parts, 4 parts, sulphur, stearic acid 1.5 parts, white carbon black 15 parts, antioxidant 264 3 parts, 129 9 parts, static inhibitor, thiuram type accelerator 2.4 parts, active calcium carbonate powder 15 parts, irgasfos 168 1.2 parts, silane coupling agent 6 parts, nano-sized magnesium hydroxide 7 parts, nano-aluminum hydroxide 7 parts, antimonous oxide 14 parts.
Above content is only citing made for the present invention and explanation; affiliated those skilled in the art make various amendment to described specific embodiment or supplement or adopt similar mode to substitute; only otherwise depart from invention or surmount this scope as defined in the claims, protection scope of the present invention all should be belonged to.
Claims (4)
1. an elastic rubber floor, it is characterized in that, described elastic rubber floor is made up of the component of following weight part: paracril 90-100 part, polyvinyl chloride rubber 30-40 part, terpolymer EP rubber 5-9 part, sulphur 2-4 part, stearic acid 0.5-1.5 part, white carbon black 8-15 part, anti-aging agent 1-3 part, static inhibitor 3-9 part, thiuram type accelerator 1.8-2.4 part, active calcium carbonate powder 10-15 part, oxidation inhibitor 0.6-1.2 part, coupling agent 1-6 part, fire retardant 15-30 part.
2. elastic rubber floor according to claim 1, it is characterized in that, described elastic rubber floor is made up of the component of following weight part: paracril 95 parts, polyvinyl chloride rubber 35 parts, terpolymer EP rubber 7 parts, 3 parts, sulphur, stearic acid 1 part, white carbon black 12 parts, 2 parts, anti-aging agent, 6 parts, static inhibitor, thiuram type accelerator 2.1 parts, active calcium carbonate powder 12 parts, 0.9 part, oxidation inhibitor, coupling agent 3.5 parts, fire retardant 22 parts.
3. elastic rubber floor according to claim 1, is characterized in that, described anti-aging agent is antioxidant 264; Described oxidation inhibitor is irgasfos 168; Described static inhibitor is static inhibitor 129; Described coupling agent is silane coupling agent.
4. elastic rubber floor according to claim 1, is characterized in that, described fire retardant is nano-sized magnesium hydroxide, nano-aluminum hydroxide, antimonous oxide are the mixing of 1: 1: 2 with weight ratio.