CN104368781A - 一种高压法兰离心铸造工艺 - Google Patents

一种高压法兰离心铸造工艺 Download PDF

Info

Publication number
CN104368781A
CN104368781A CN201410434412.6A CN201410434412A CN104368781A CN 104368781 A CN104368781 A CN 104368781A CN 201410434412 A CN201410434412 A CN 201410434412A CN 104368781 A CN104368781 A CN 104368781A
Authority
CN
China
Prior art keywords
centrifugal casting
pressure flange
high pressure
roughing
technology
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410434412.6A
Other languages
English (en)
Inventor
尹志华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUSONG HENGDA ELECTRICAL FITTINGS CO Ltd
Original Assignee
SUSONG HENGDA ELECTRICAL FITTINGS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUSONG HENGDA ELECTRICAL FITTINGS CO Ltd filed Critical SUSONG HENGDA ELECTRICAL FITTINGS CO Ltd
Priority to CN201410434412.6A priority Critical patent/CN104368781A/zh
Publication of CN104368781A publication Critical patent/CN104368781A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种高压法兰离心铸造工艺，其步骤包括熔炼过程、离心浇注、冷却、粗加工工艺、热处理工艺。离心浇注提高了铸件的冷却速度和金属的利用率，在加强合金液精炼除气，提高合金液纯净度的情况下，离心铸造可以加强合金液的冷却，同时在离心力场的作用下，使合金液中的氧化夹渣浮于铸件的内表面，实现铸件定向凝固。

Description

一种高压法兰离心铸造工艺
技术领域
本发明涉及法兰制造领域，更具体的说是一种高压法兰离心铸造工艺。 
背景技术
高压法兰于20世纪50年代诞生以来，广泛应用于石油石化、油气开采、工业煤气生产、石油精炼、食品加工、化工工业、环境工程、矿物及核电、航空航天、船舶工业、合成燃料加工、煤的氧化和液化等领域。在中国市场上，此类产品完全依靠进口，国内无一家可以设计、生产，直至2005年，这一局面才被国内的成都植源机械科技所打破。高压法兰主要应用在管道的安装中，高压法兰连接是管道施工的重要连接方式，主要连接管与管之间的连接，起到重要的作用和价值。高压法兰连接就是把两个管道、管件或器材，先各自固定在一个法兰盘上，两个法兰盘之间，加上法兰垫，用螺栓紧固在一起，完成了连接。 
发明内容
    本发明提供一种高压法兰离心铸造工艺，为实现本发明的目的，本发明的技术方案如下： 
一种高压法兰离心铸造工艺,其具体步骤为：
(1)熔炼过程:将铜、回炉料同时装入感应炉中，快速熔化，铜温度达到1150-1200℃时，加入预热的Al-Fe中间合金，加入时应把中间合金压入铜液中，进行搅拌助熔，之后加入Al，用钟罩压入二氯化锌脱水除气精炼，仔细搅拌，炉前检验合格后，除净浮渣，出炉浇注；
（2）离心浇注：离心铸造时，模具内表面喷刷氧化锌涂料，浇注温度控制在1100-1200℃，采用先快后慢的方式，浇注速度为5-8kg/s，离心转速为630-680r/min；
（3）冷却：冷却到铸件表面呈暗黑红色，即600-700℃才能停机，脱模；
（4）粗加工工艺：对铸件进行粗加工，粗加工时，法兰两侧薄壁处，直径方向单面留量3-5mm，长度方向单边留量3-5mm；
（5）热处理工艺。
优选的，步骤（2）中涂料配比为7%的氧化锌、2%水玻璃，余量为水。 
优选的，步骤（5）热处理工艺中，淬火温度控制在830-870℃、回火温度在590-630℃。 
有益效果：本发明提供了一种高压法兰离心铸造工艺，其步骤包括熔炼过程、离心浇注、冷却、粗加工工艺、热处理工艺。离心浇注提高了铸件的冷却速度和金属的利用率，在加强合金液精炼除气，提高合金液纯净度的情况下，离心铸造可以加强合金液的冷却，同时在离心力场的作用下，使合金液中的氧化夹渣浮于铸件的内表面，实现铸件定向凝固。 
具体实施方式
为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施方式，进一步阐述本发明。 
一种高压法兰离心铸造工艺，其具体步骤为： 
(1)熔炼过程:将铜、回炉料同时装入感应炉中，快速熔化，铜温度达到1150℃时，加入预热的Al-Fe中间合金，加入时应把中间合金压入铜液中，进行搅拌助熔，之后加入Al，用钟罩压入二氯化锌脱水除气精炼，仔细搅拌，炉前检验合格后，除净浮渣，出炉浇注；
（2）离心浇注：离心铸造时，模具内表面喷刷氧化锌涂料，浇注温度控制在1100℃，采用先快后慢的方式，浇注速度为5kg/s，离心转速为630r/min，涂料配比为7%的氧化锌、2%水玻璃，余量为水；
（3）冷却：冷却到铸件表面呈暗黑红色，即600℃才能停机，脱模；
（4）粗加工工艺：对铸件进行粗加工，粗加工时，法兰两侧薄壁处，直径方向单面留量3mm，长度方向单边留量3mm；
（5）热处理工艺：其中淬火温度控制在830℃、回火温度在590℃。
本发明提供了一种高压法兰离心铸造工艺，其步骤包括熔炼过程、离心浇注、冷却、粗加工工艺、热处理工艺。离心浇注提高了铸件的冷却速度和金属的利用率，在加强合金液精炼除气，提高合金液纯净度的情况下，离心铸造可以加强合金液的冷却，同时在离心力场的作用下，使合金液中的氧化夹渣浮于铸件的内表面，实现铸件定向凝固。 
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。 

Claims (3)

1.一种高压法兰离心铸造工艺，其特征在于，其具体步骤为：
(1)熔炼过程:将铜、回炉料同时装入感应炉中，快速熔化，铜温度达到1150-1200℃时，加入预热的Al-Fe中间合金，加入时应把中间合金压入铜液中，进行搅拌助熔，之后加入Al，用钟罩压入二氯化锌脱水除气精炼，仔细搅拌，炉前检验合格后，除净浮渣，出炉浇注；
（2）离心浇注：离心铸造时，模具内表面喷刷氧化锌涂料，浇注温度控制在1100-1200℃，采用先快后慢的方式，浇注速度为5-8kg/s，离心转速为630-680r/min；
（3）冷却：冷却到铸件表面呈暗黑红色，即600-700℃才能停机，脱模；
（4）粗加工工艺：对铸件进行粗加工，粗加工时，法兰两侧薄壁处，直径方向单面留量3-5mm，长度方向单边留量3-5mm；
（5）热处理工艺。
2.根据权利要求1所述的一种高压法兰离心铸造工艺，其特征在于，步骤（2）中涂料配比为7%的氧化锌、2%水玻璃，余量为水。
3. 根据权利要求1所述的一种高压法兰离心铸造工艺，其特征在于，步骤（5）热处理工艺中，淬火温度控制在830-870℃、回火温度在590-630℃。
 
CN201410434412.6A 2014-08-29 2014-08-29 一种高压法兰离心铸造工艺 Pending CN104368781A (zh)