CN104358005B - The cotton 15% big tmaterial of spun silk one side and the preparation method of 35% Lyocell fibers 30% real silk 20% - Google Patents

The cotton 15% big tmaterial of spun silk one side and the preparation method of 35% Lyocell fibers 30% real silk 20% Download PDF

Info

Publication number
CN104358005B
CN104358005B CN201410546678.XA CN201410546678A CN104358005B CN 104358005 B CN104358005 B CN 104358005B CN 201410546678 A CN201410546678 A CN 201410546678A CN 104358005 B CN104358005 B CN 104358005B
Authority
CN
China
Prior art keywords
silk
fabric
cotton
shrinkage
real
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410546678.XA
Other languages
Chinese (zh)
Other versions
CN104358005A (en
Inventor
朱炫钊
朱森波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIAXING KINGKAIYUE KNITTING Co Ltd
Original Assignee
JIAXING KINGKAIYUE KNITTING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIAXING KINGKAIYUE KNITTING Co Ltd filed Critical JIAXING KINGKAIYUE KNITTING Co Ltd
Priority to CN201410546678.XA priority Critical patent/CN104358005B/en
Publication of CN104358005A publication Critical patent/CN104358005A/en
Application granted granted Critical
Publication of CN104358005B publication Critical patent/CN104358005B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The preparation method that the present invention relates to a kind of fabric.The preparation method of the cotton 15% big tmaterial of spun silk one side of 35% Lyocell fibers 30% real silk 20%, the method comprises the following steps: open-width, clear water shaping and drying, mercerising, second time sizing, rubber blanket preshrunk, decatizing and steam-shrinkage.The big tmaterial of one side of preparation, is provided simultaneously with the characteristic of Lyocell fibers, real silk, cotton, spun silk, have moisture absorption by force, higher swellability, water absorption, breathability, warmth retention property, skin-protection and health-care, gloss profit U.S., the soft ruggedness of feel.

Description

The cotton 15% big tmaterial of spun silk one side and the preparation method of 35% Lyocell fibers 30% real silk 20%
Technical field
The preparation method that the present invention relates to a kind of fabric, the preparation method particularly relating to the big tmaterial of a kind of one side.
Background technology
Lyocell fibers has high brute force dry, wet, has higher swellability, good spinnability.
Real silk has good moisture absorption, permeability, has skin-protection and health-care effect.Soft, smooth, abundant, plentiful, elastic excellent.
Cotton feature is that moisture absorption is strong---cotton fiber is porous material, interior molecules arrangement very irregular, and containing substantial amounts of hydrophilic-structure in molecule.Warmth retention property----cotton fiber is the non-conductor of heat, and the inner chamber of cotton fiber is filled with immobilising air, comfortable and easy to wear---electrostatic, good air permeability, anti-sensitivity will not be produced, it is easy to clean.
Spun silk has number height, and gloss profit is beautiful, and feel is soft, is suitable to manufacture light and soft fine fabrics.
Summary of the invention
The preparation method that it is an object of the invention to provide the cotton 15% big tmaterial of spun silk one side of a kind of 35% Lyocell fibers 30% real silk 20%, adopt the big tmaterial of one side prepared by the method, it is provided simultaneously with the characteristic of Lyocell fibers, real silk, cotton, spun silk, have moisture absorption by force, higher swellability, water absorption, breathability, warmth retention property, skin-protection and health-care, gloss profit is beautiful, the soft ruggedness of feel.
In order to realize above-mentioned purpose, present invention employs following technical scheme:
The preparation method of the cotton 15% big tmaterial of spun silk one side of 35% Lyocell fibers 30% real silk 20%, the method comprises the following steps:
1) raw material prepares: cotton 20/ thin,tough silk 15 dyed yarn of 120N/2 tencel 35/, 3 strands of real silk color silks;
2) weaving: install additional at 34 cun of 30G single-side jacquards and special add shuttle triangle, by 48 road pricking with needle, the good flower pattern of compilation and design in computer software, by computerized version figure and color matching, dyed yarn is accessed into yarn way accordingly, wherein 3 strands of real silks are made to add shuttle and are used;
3) open-width;Adopt horizontal scutcher, expander linear velocity < 50m/min;
4) clear water shaping and drying;
5) mercerization: dry body cloth open-width joint is directly gone up machine and done gently alkali mercerized, first adds Fe by 100g/L in mercerising process3+Chelated dispersants improves water quality, NaOH concentration 200-260g/L, 0.2% silkete penetrating agent, and by 25m/min room temperature mercerising, alkali liquor rolls and adds 90g/L glacial acetic acid after washing when open washing and carry out acid-base neutralization, and pH value 7 is, and play tint retention;
6) secondary sizing: secondary sizing adds 40 ~ the fluffy softening agent of 70g/L, ice-cold finishing agent 60 ~ 65g/L, smooth silicone oil 130 ~ 160g/L, temperature 140 ~ 165 DEG C, overfeeding 25m/min;
7) rubber blanket preshrunk: rubber blanket temperature should control at 55 ~ 70 DEG C, and speed is at 30 ~ 35m/min;
8) decatizing and preshrinking process: fabric after mercerising and sizing is entered continuous pressure decator and carries out decatizing, more than steam pressure 6Pa, 20m/min, expects the washing shrinkage horizontal, longitudinal to fabric by steam-shrinkage machine and woollen blanket preshrinking machine after decatizing, patterns of fabric, effective gate width are done processing and adjusted;
9) steam-shrinkage: mechanical speed, 20-30m/min, saturated vapor 3-3.5Bar, compress air 5Bar, the washing shrinkage horizontal, longitudinal to fabric, patterns of fabric, effective gate width are done processing and are adjusted.
Another object of the present invention is to provide adopts the big tmaterial of the one side prepared with the aforedescribed process.
Due to the fact that and have employed above-mentioned technical scheme, the big tmaterial of one side of preparation, is provided simultaneously with the characteristic of Lyocell fibers, real silk, cotton, spun silk, have moisture absorption by force, higher swellability, water absorption, breathability, warmth retention property, skin-protection and health-care, gloss profit is beautiful, the soft ruggedness of feel.
Detailed description of the invention
The preparation method of the cotton 15% big tmaterial of spun silk one side of 35% Lyocell fibers 30% real silk 20%, it is characterised in that the method comprises the following steps:
1) raw material prepares: cotton 20/ thin,tough silk 15 dyed yarn of 120N/2 tencel 35/, 3 strands of real silk color silks;
2) weaving: install additional at 34 cun of 30G single-side jacquards and special add shuttle triangle, by 48 road pricking with needle, the good flower pattern of compilation and design in computer software, by computerized version figure and color matching, dyed yarn is accessed into yarn way accordingly, wherein 3 strands of real silks are made to add shuttle and are used;
3) open-width;Adopt horizontal scutcher, expander linear velocity < 50m/min;
4) clear water shaping and drying;
5) mercerization: dry body cloth open-width joint is directly gone up machine and done gently alkali mercerized, first adds Fe by 100g/L in mercerising process3+Chelated dispersants improves water quality, NaOH concentration 230g/L, 0.2% silkete penetrating agent, and by 25m/min room temperature mercerising, alkali liquor rolls and adds 90g/L glacial acetic acid after washing when open washing and carry out acid-base neutralization, and pH value 7 is, and play tint retention;
6) secondary sizing: secondary sizing adds the fluffy softening agent of 60g/L, ice-cold finishing agent 60g/L, smooth silicone oil 150g/L, temperature 150 DEG C, overfeeding 25m/min;
7) rubber blanket preshrunk: rubber blanket temperature should control at 60 DEG C, and speed is at 33m/min;
8) decatizing and preshrinking process: fabric after mercerising and sizing is entered continuous pressure decator and carries out decatizing, more than steam pressure 6Pa, 20m/min, expects the washing shrinkage horizontal, longitudinal to fabric by steam-shrinkage machine and woollen blanket preshrinking machine after decatizing, patterns of fabric, effective gate width are done processing and adjusted;
9) steam-shrinkage: mechanical speed, 25m/min, saturated vapor 3.3Bar, compress air 5Bar, the washing shrinkage horizontal, longitudinal to fabric, patterns of fabric, effective gate width are done processing and are adjusted.
The big tmaterial of one side prepared by above-mentioned method project after testing is as shown in the table.Examination criteria GB/T22849-2009, GB18401-2003 " B " class.

Claims (2)

  1. The preparation method of the cotton 15% big tmaterial of spun silk one side of 1.35% Lyocell fibers 30% real silk 20%, it is characterised in that the method comprises the following steps:
    1) raw material prepares: cotton 20/ thin,tough silk 15 dyed yarn of 120N/2 tencel 35/, 3 strands of real silk color silks;
    2) weaving: install additional at 34 cun of 30G single-side jacquards and special add shuttle triangle, by 48 road pricking with needle, the good flower pattern of compilation and design in computer software, by computerized version figure and color matching, dyed yarn is accessed into yarn way accordingly, wherein 3 strands of real silks are made to add shuttle and are used;
    3) open-width: adopt horizontal scutcher, expander linear velocity < 50m/min;
    4) clear water shaping and drying;
    5) mercerization: dry body cloth open-width joint is directly gone up machine and done gently alkali mercerized, first adds Fe by 100g/L in mercerising process3+Chelated dispersants improves water quality, NaOH concentration 200-260g/L, 0.2% silkete penetrating agent, and by 25m/min room temperature mercerising, alkali liquor rolls and adds 90g/L glacial acetic acid after washing when open washing and carry out acid-base neutralization, and pH value 7 is, and play tint retention;
    6) secondary sizing: secondary sizing adds 40 ~ the fluffy softening agent of 70g/L, ice-cold finishing agent 60 ~ 65g/L, smooth silicone oil 130 ~ 160g/L, temperature 140 ~ 165 DEG C, overfeeding 25m/min;
    7) rubber blanket preshrunk: rubber blanket temperature should control at 55 ~ 70 DEG C, and speed is at 30 ~ 35m/min;
    8) decatizing and preshrinking process: fabric after mercerising and sizing is entered continuous pressure decator and carries out decatizing, more than steam pressure 6Pa, 20m/min, expects after decatizing to be done processing adjusted by washing shrinkage horizontal, longitudinal to fabric of steam-shrinkage machine and woollen blanket preshrinking machine and patterns of fabric, effective gate width;
    9) steam-shrinkage: mechanical speed 20-30m/min, saturated vapor 3-3.5Bar, compress air 5Bar, the washing shrinkage horizontal, longitudinal to fabric, patterns of fabric, effective gate width are done processing and are adjusted.
  2. 2. the big tmaterial of one side that prepared by method according to claim 1.
CN201410546678.XA 2014-10-16 2014-10-16 The cotton 15% big tmaterial of spun silk one side and the preparation method of 35% Lyocell fibers 30% real silk 20% Active CN104358005B (en)