CN104005149A - Moisture absorption anti-wrinkle fabric and processing technology thereof - Google Patents

Moisture absorption anti-wrinkle fabric and processing technology thereof Download PDF

Info

Publication number
CN104005149A
CN104005149A CN201410287987.XA CN201410287987A CN104005149A CN 104005149 A CN104005149 A CN 104005149A CN 201410287987 A CN201410287987 A CN 201410287987A CN 104005149 A CN104005149 A CN 104005149A
Authority
CN
China
Prior art keywords
moisture absorption
warp
wrinkle fabric
parallel
processing technology
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410287987.XA
Other languages
Chinese (zh)
Inventor
王素萍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Chang Ya Textile Technology Co Ltd
Original Assignee
Nantong Chang Ya Textile Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nantong Chang Ya Textile Technology Co Ltd filed Critical Nantong Chang Ya Textile Technology Co Ltd
Priority to CN201410287987.XA priority Critical patent/CN104005149A/en
Publication of CN104005149A publication Critical patent/CN104005149A/en
Pending legal-status Critical Current

Abstract

The invention discloses moisture absorption anti-wrinkle fabric which is formed by warp yarns and weft yarns in an interwoven mode. The warp yarns are formed by cotton fibers and spun silk fibers in a blending mode, and the weft yarns are formed by viscose and tencel fibers in a blended woven mode. The blending ratio of the cotton fibers and the spun silk fibers in the warp yarns is 3:1, and the blending ratio of the viscose and the tencel fibers in the weft yarns is 1:1. The moisture absorption anti-wrinkle fabric has the advantages of lightness, thinness, moisture absorption, wrinkle resistance and the like.

Description

A kind of moisture absorption anti-wrinkle fabric and processing technology thereof
Technical field
Patent of the present invention relates to a kind of fabric, is specifically related to a kind of moisture absorption anti-wrinkle fabric and processing technology thereof.
Background technology
Along with scientific and technical development, the textile fabric that meets the different needs of people emerges in an endless stream, and to satisfy the demands of consumers, plays a part more and more important in daily life.
The breathable fabric effect of producing on existing market is poor, wears uncomfortablely, and because comparison of ingredients is single, and the difference of weaving manner, existing breathable fabric is relatively evacuated, and easily damages.
Summary of the invention
The object of invention: the object of the present invention is to provide a kind of moisture absorption anti-wrinkle fabric.
The technical solution used in the present invention: a kind of moisture absorption anti-wrinkle fabric, by warp and parallel, mutually weave and form, described warp is formed by cotton fiber and silk flock blending, described parallel is formed by viscose and silk fiber blended braiding, in described warp, the blending rate of cotton fiber and silk flock is 3:1, and in described parallel, the blending rate of viscose and tencel fiber is 1:1.
Described warp and parallel adopt plain weave or twill weave.
A moisture absorption anti-wrinkle fabric processing technology, specifically comprises the steps:
A, hand over and operation: cotton fiber and silk flock are sent into and in doubling winder, carried out yarn friendship and form mixed and warp, viscose and tencel fiber are sent into and in doubling winder, carried out yarn friendship and form mixed and parallel;
B, winding procedure: by mixed in step a and warp and parallel send in bobbin winder and carry out winder, control groove drum linear velocity is 1000 ~ 1100m/min simultaneously, rolling density is 0.32 ~ 0.37 g/cm 3;
C, warping process: adopt warping machines to carry out section warping to the yarn of winder in step b, the speed of beaming of controlling warping machines is 330 ~ 350 mm/min, and rolling density is 0.5 ~ 0.6 g/cm 3;
D, weaving process: adopt Rapier looms to weave, wherein warp thread and weft yarn are sent into according to preset ratio, and wherein weaving speed is 160~200r/min, and opening time is 300 ~ 320 °;
E, finishing process: the former cloth that steps d has been weaved is tested, the fine hair on burning-off cloth cover then, then send in setting machine and shape, make into cloth and meet the requirements, then carry out perching, packing.
In described step b, groove drum linear velocity is 1000m/min, and rolling density is 0.35 g/cm 3.
In described step c, whole footpath speed is 340 mm/min, and rolling density is 0.52g/cm 3.
In described steps d, manufacturing speed is 180r/min, and opening time is 300 °.
In described step e, perching speed is 18-20m/min.
Beneficial effect: disclosed a kind of moisture absorption anti-wrinkle fabric, specifically frivolous, moisture absorption, the advantage such as crease-resistant.
The specific embodiment
Below in conjunction with specific embodiment, technology contents of the present invention is described in detail:
Disclosed a kind of moisture absorption anti-wrinkle fabric, by warp and parallel, mutually weave and form, its middle longitude is formed by cotton fiber and silk flock blending, described parallel is formed by viscose and silk fiber blended braiding, in described warp, the blending rate of cotton fiber and silk flock is 3:1, and in described parallel, the blending rate of viscose and tencel fiber is 1:1.
Wherein, described warp and parallel adopt plain weave or twill weave.
A moisture absorption anti-wrinkle fabric processing technology, specifically comprises the steps:
A, hand over and operation: cotton fiber and silk flock are sent into and in doubling winder, carried out yarn friendship and form mixed and warp, viscose and tencel fiber are sent into and in doubling winder, carried out yarn friendship and form mixed and parallel;
B, winding procedure: by mixed in step a and warp and parallel send in bobbin winder and carry out winder, control groove drum linear velocity is 1000 ~ 1100m/min simultaneously, rolling density is 0.32 ~ 0.37 g/cm 3;
C, warping process: adopt warping machines to carry out section warping to the yarn of winder in step b, the speed of beaming of controlling warping machines is 330 ~ 350 mm/min, and rolling density is 0.5 ~ 0.6 g/cm 3;
D, weaving process: adopt Rapier looms to weave, wherein warp thread and weft yarn are sent into according to preset ratio, and wherein weaving speed is 160~200r/min, and opening time is 300 ~ 320 °;
E, finishing process: the former cloth that steps d has been weaved is tested, the fine hair on burning-off cloth cover then, then send in setting machine and shape, make into cloth and meet the requirements, then carry out perching, packing.
In described step b, groove drum linear velocity is 1000m/min, and rolling density is 0.35 g/cm 3.
In described step c, whole footpath speed is 340 mm/min, and rolling density is 0.52g/cm 3.
In described steps d, manufacturing speed is 180r/min, and opening time is 300 °.
In described step e, perching speed is 18-20m/min.
The above is only the preferred embodiment of the present invention; be noted that for those skilled in the art; under the premise without departing from the principles of the invention, can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.

Claims (7)

1. a moisture absorption anti-wrinkle fabric, by warp and parallel, mutually weave and form, it is characterized in that: described warp is formed by cotton fiber and silk flock blending, described parallel is formed by viscose and silk fiber blended braiding, in described warp, the blending rate of cotton fiber and silk flock is 3:1, and in described parallel, the blending rate of viscose and tencel fiber is 1:1.
2. a kind of moisture absorption anti-wrinkle fabric according to claim 1, is characterized in that: described warp and parallel adopt plain weave or twill weave.
3. a moisture absorption anti-wrinkle fabric processing technology, is characterized in that: specifically comprise the steps:
A, hand over and operation: cotton fiber and silk flock are sent into and in doubling winder, carried out yarn friendship and form mixed and warp, viscose and tencel fiber are sent into and in doubling winder, carried out yarn friendship and form mixed and parallel;
B, winding procedure: by mixed in step a and warp and parallel send in bobbin winder and carry out winder, control groove drum linear velocity is 1000 ~ 1100m/min simultaneously, rolling density is 0.32 ~ 0.37 g/cm 3;
C, warping process: adopt warping machines to carry out section warping to the yarn of winder in step b, the speed of beaming of controlling warping machines is 330 ~ 350 mm/min, and rolling density is 0.5 ~ 0.6 g/cm 3;
D, weaving process: adopt Rapier looms to weave, wherein warp thread and weft yarn are sent into according to preset ratio, and wherein weaving speed is 160~200r/min, and opening time is 300 ~ 320 °;
E, finishing process: the former cloth that steps d has been weaved is tested, the fine hair on burning-off cloth cover then, then send in setting machine and shape, make into cloth and meet the requirements, then carry out perching, packing.
4. a kind of moisture absorption anti-wrinkle fabric processing technology according to claim 3, is characterized in that: in described step b, groove drum linear velocity is 1000m/min, and rolling density is 0.35 g/cm 3.
5. a kind of moisture absorption anti-wrinkle fabric processing technology according to claim 3, is characterized in that: in described step c, whole footpath speed is 340 mm/min, and rolling density is 0.52g/cm 3.
6. a kind of moisture absorption anti-wrinkle fabric processing technology according to claim 3, is characterized in that: in described steps d, manufacturing speed is 180r/min, and opening time is 300 °.
7. a kind of moisture absorption anti-wrinkle fabric processing technology according to claim 3, is characterized in that: in described step e, perching speed is 18-20m/min.
CN201410287987.XA 2014-06-25 2014-06-25 Moisture absorption anti-wrinkle fabric and processing technology thereof Pending CN104005149A (en)