CN104354349B - 70%羊毛20%粘胶10%锦纶双面提花布的制备方法 - Google Patents

70%羊毛20%粘胶10%锦纶双面提花布的制备方法 Download PDF

Info

Publication number
CN104354349B
CN104354349B CN201410372132.7A CN201410372132A CN104354349B CN 104354349 B CN104354349 B CN 104354349B CN 201410372132 A CN201410372132 A CN 201410372132A CN 104354349 B CN104354349 B CN 104354349B
Authority
CN
China
Prior art keywords
cloth
wool
speed
polyamide fibre
viscose glue
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410372132.7A
Other languages
English (en)
Other versions
CN104354349A (zh
Inventor
朱炫钊
朱森波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIAXING KINGKAIYUE KNITTING Co Ltd
Original Assignee
JIAXING KINGKAIYUE KNITTING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIAXING KINGKAIYUE KNITTING Co Ltd filed Critical JIAXING KINGKAIYUE KNITTING Co Ltd
Priority to CN201410372132.7A priority Critical patent/CN104354349B/zh
Publication of CN104354349A publication Critical patent/CN104354349A/zh
Application granted granted Critical
Publication of CN104354349B publication Critical patent/CN104354349B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种面料的制备方法。70%羊毛20%粘胶10%锦纶双面提花布的制备方法，该方法包括以下的步骤：原料准备、织造、开幅、清水定型烘干、抓毛和剪毛、空气柔软、上树脂、二次定型、橡毯预缩和汽蒸预缩。制备的双面提花布，同时具备羊毛、粘胶、锦纶的特性，具有良好的保暖性，热定型特性、吸湿性，手感柔和耐用性。

Description

70%羊毛20%粘胶10%锦纶双面提花布的制备方法
技术领域
本发明涉及一种面料的制备方法，尤其涉及一种双面提花布的制备方法。
背景技术
羊毛具有高吸水性：羊毛为非常好的亲水性纤维，穿着非常舒适。保暖性：因羊毛具天然卷曲，可以形成许多不流动的空气区间作为屏障。耐用性：羊毛有非常好的拉伸性及弹性恢复性，并具有特殊的毛鳞结构以及极好的弯曲性，因此它也有很好的外观保持性。粘胶纤维织物的吸湿性能在化纤中最佳，其穿着舒适性与染色性比合成纤维织物好；粘胶纤维织物手感柔软、色泽艳丽，优于其它化纤织物；其色彩夺目，光泽柔和明亮，有华丽高贵之感；普通粘胶织物的悬垂性好。锦纶具有吸湿性和染色性都比涤纶好,耐碱而不耐酸，锦纶有热定型特性,能保持住加热时形成的弯曲变形。
发明内容
本发明的目的是提供一种70%羊毛20%粘胶10%锦纶双面提花布的制备方法，采用该方法制备的双面提花布，同时具备羊毛、粘胶、锦纶的特性，具有良好的保暖性，热定型特性、吸湿性，手感柔和耐用性。
为了实现上述的目的，本发明采用了以下的技术方案：
70%羊毛20%粘胶10%锦纶双面提花布的制备方法，该方法包括以下的步骤：
1）原料准备：41N/1羊毛70/粘胶20/锦纶10色纱；
2）织造：采用34寸24G双面提花机，按72路均匀织入；
3）开幅；采用卧式开幅机，开幅辊线速度<50m/min；
4）清水定型烘干；
5）抓毛、剪毛；抓毛辊的直径采用165~210毫米，转速220~260转/分，线速度140~160米/分，走布速度5~7m/min，抓毛辊与走布速度之比为20:1~30:1，清洁辊直径1~2毫米，转速250~295转/分，清洁辊与抓毛辊隔距，钢针插入30/1000英寸，剪毛刀速度750~900转/分，剪毛高度9~12毫米；
6）空气柔软；以25~45m/min运转机器，当前布端到达机器前部时，停机将织物前后布端缝合成环状；启动机器，加速至330~350m/min，处理温度100℃，处理时间25~40min，冷风降温至40℃，8~15min后停机，开幅出布；
7）上树脂：按重量百分比，1~2%增强树脂PM-150的水溶液，浸渍法使用上浆量为0.5~3%；
8）二次定型：二次定型加40~80g/L蓬松柔软剂、冰凉整理剂58~65g/L、滑爽硅油140~160g/L，温度140~160℃，超喂25m/min；
9）橡毯预缩：橡毯温度应控制在60~70℃，车速在30~35m/min；
10）汽蒸预缩：机械速度，20-30m/min，饱和蒸汽3-3.5Bar，压缩空气5Bar，对面料的横向、纵向缩水率，织物花型、有效门幅作加工调整。
本发明的另外一个目的是提供采用上述的方法制备的双面提花布。
本发明由于采用了上述的技术方案，制备的双面提花布，同时具备羊毛、粘胶、锦纶的特性，具有良好的保暖性，热定型特性、吸湿性，手感柔和耐用性。
具体实施方式
70%羊毛20%粘胶10%锦纶双面提花布的制备方法，该方法包括以下的步骤：
1）原料准备：41N/1羊毛70/粘胶20/锦纶10色纱；
2）织造：采用34寸24G双面提花机，按72路均匀织入；
3）开幅；采用卧式开幅机，开幅辊线速度<50m/min；
4）清水定型烘干；
5）抓毛、剪毛；抓毛辊的直径采用165~210毫米，转速220~260转/分，线速度140~160米/分，走布速度5~7m/min，抓毛辊与走布速度之比为20:1~30:1，清洁辊直径1~2毫米，转速250~295转/分，清洁辊与抓毛辊隔距，钢针插入30/1000英寸，剪毛刀速度750~900转/分，剪毛高度9~12毫米；
6）空气柔软；以25~45m/min运转机器，当前布端到达机器前部时，停机将织物前后布端缝合成环状；启动机器，加速至330~350m/min，处理温度100℃，处理时间25~40min，冷风降温至40℃，8~15min后停机，开幅出布；
7）上树脂：按重量百分比，1~2%增强树脂PM-150的水溶液，浸渍法使用上浆量为0.5~3%；
8）二次定型：二次定型加40~80g/L蓬松柔软剂、冰凉整理剂58~65g/L、滑爽硅油140~160g/L，温度140~160℃，超喂25m/min；
9）橡毯预缩：橡毯温度应控制在60~70℃，车速在30~35m/min；
10）汽蒸预缩：机械速度，20-30m/min，饱和蒸汽3-3.5Bar，压缩空气5Bar，对面料的横向、纵向缩水率，织物花型、有效门幅作加工调整。
上述的方法制备的双面提花布经检测的项目如下表所示。检测标准GB/T22849-2009、GB18401-2003“B”类。

Claims (2)

1.70%羊毛20%粘胶10%锦纶双面提花布的制备方法，其特征在于该方法包括以下的步骤：
1）原料准备：41N/1羊毛70/粘胶20/锦纶10色纱；
2）织造：采用34寸24G双面提花机，按72路均匀织入；
3）开幅；采用卧式开幅机，开幅辊线速度<50m/min；
4）清水定型烘干；
5）抓毛、剪毛；抓毛辊的直径采用165~210毫米，转速220~260转/分，线速度140~160米/分，走布速度5~7m/min，抓毛辊与走布速度之比为20:1~30:1，清洁辊直径1~2毫米，转速250~295转/分，清洁辊与抓毛辊的钢针插入30/1000英寸，剪毛刀速度750~900转/分，剪毛高度9~12毫米；
6）空气柔软；以25~45m/min运转机器，当前布端到达机器前部时，停机将织物前后布端缝合成环状；启动机器，加速至330~350m/min，处理温度100℃，处理时间25~40min，冷风降温至40℃，8~15min后停机，开幅出布；
7）上树脂：按重量百分比，1~2%增强树脂PM-150的水溶液，浸渍法使用上浆量为0.5~3%；
8）二次定型：二次定型加40~80g/L蓬松柔软剂、冰凉整理剂58~65g/L、滑爽硅油140~160g/L，温度140~160℃，超喂25m/min；
9）橡毯预缩：橡毯温度应控制在60~70℃，车速在30~35m/min；
10）汽蒸预缩：机械速度20-30m/min，饱和蒸汽3-3.5Bar，压缩空气5Bar，对面料的横向、纵向缩水率及织物花型、有效门幅作加工调整。
2.根据权利要求1所述的方法制备的双面提花布。
CN201410372132.7A 2014-07-31 2014-07-31 70%羊毛20%粘胶10%锦纶双面提花布的制备方法 Active CN104354349B (zh)