CN104326674A - 一种白色微晶石 - Google Patents
一种白色微晶石 Download PDFInfo
- Publication number
- CN104326674A CN104326674A CN201310309866.6A CN201310309866A CN104326674A CN 104326674 A CN104326674 A CN 104326674A CN 201310309866 A CN201310309866 A CN 201310309866A CN 104326674 A CN104326674 A CN 104326674A
- Authority
- CN
- China
- Prior art keywords
- parts
- microlite
- oxide
- white micro
- color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种白色微晶石,其组成成分及重量份数如下:二氧化硅30~40份;三氧化二铝6~10份;氧化钙10~15份;氧化锌3~5份;氧化硼4~6份;氧化钡4~6份;氧化钾0.3~0.7份;氧化钠1~3份;二氧化钛0.5~1.5份;氧化镁0.5~1.5份。本发明微晶石的颜色稳定、色泽鲜亮、使用期长,而且成本低廉,制作方便,填补了现有微晶石的图案和色彩的种类,该微晶石图案新颖、色彩独特,大大满足了人们在生活及生产中对微晶石的需求。
Description
技术领域
本发明属于建材技术领域,涉及微晶石,尤其是一种白色微晶石。
背景技术
随着建材行业的飞速发展,各类建材产品与日俱增,微晶石以其优越的性也越来越受到人们的关注和青睐。
微晶石是通过控制玻璃的结晶而得到的一种多晶材料。目前微晶石已经形成了一种特别门类的材料,其品种繁多,性能各异,具有十分广泛的用途。微晶石是微晶玻璃众多品种中的一种,它是一种新型高档建筑装饰材料,具有强度高、抗磨损、耐腐蚀、耐风化、不吸水、清洁维护方便、无放射性污染等理化特性以及色调均匀,光泽柔和晶莹,表面致密无暇等优异的外观特点。因此微晶石各方面性能均优于天然石材,现在已经被广泛用于建筑内外墙、地面及廊柱等高档装修饰面。
目前,随着微晶石日益受到人们的青睐,因此人们对人造石英石的图案及色彩的要求也越来越高,现有的人造石英石已经不能完全满足人们的需要。
通过检索,发现与本发明专利申请相关的如下专利公开文献:
1、用高硅铁尾矿制造微晶石的方法(CN101817640A),公开了一种利用铁尾矿制造微晶石的方法,其特征在于:铁尾矿占配合料的30~70%,其余成分是石英砂、氧化铝、氧化锌、碳酸钡、氧化铜、三氧化二铬等。本发明利用废弃物制造微晶石,不仅减少了尾矿的堆存量,减轻了环境污染、还能够提高产品性能、降低生产成本,因此具有好的社会效益和经济效益。
2、环保型纳米复合微晶石(CN102021987A),涉及一种环保型纳米复合微晶石,有一个基板层,所述基板层上复合有微晶石装饰层,所述基板层内设置增强花板,该增强花板上均布多个结合孔和多个凸钉,所述复合微晶石板周缘处设置金属边框,所述基板层是水泥与膨胀珍珠岩复合层,所述微晶石装饰层包括树脂、氢氧化铝粗粉、氢氧化铝细粉、玻璃微粒、颜料、细石粉;本发明外表具有玛瑙石材效果、防水、耐酸碱,可用于墙壁、天花板、地板、家具的装饰。
3、一种微晶石及制备方法(CN1247879),公开了一种微晶石,其成分由不饱和聚酯树脂为:45—55%、轻质碳酸钙为:35—45%、色浆为:1—10%、促进剂为:1—4%、固化剂为:1—4%,通过把不饱和聚酯树脂、色浆、轻质碳酸钙分成二等份,并拌匀后分别加入促进剂和固化剂后拌匀,再整个混合拌匀注模,经脱模、打磨、抛光后成品,这种微晶石具有原料成本低、成型容易、成品后耐冲击、触感好,适用于批量生产。
通过对比,本发明专利申请与上述专利公开文献存在本质的不同。
发明内容
本发明的目的是克服现有技术的不足之处,提供一种颜色稳定、色泽鲜亮、使用期长,而且成本低廉,制作方便的白色微晶石。
本发明实现目的的技术方案是:
一种白色微晶石,其组成成分及重量份数如下:
而且,所述的白色微晶石,其组成成分及重量份数如下:
一种白色微晶石,其组成成分及重量如下:
而且,所述白色微晶石的制备方法的步骤如下:将各原料准确称量后,在1600℃的熔炉中将天然无机材料熔成玻璃液、水淬,再经1200℃结晶形成微晶石,然后再经磨抛、切割、深加工、检验合格后,即得白色微晶石成品。
本发明的优点和有益效果为:
1、本发明微晶石的颜色稳定、色泽鲜亮、使用期长,而且成本低廉,制作方便,填补了现有微晶石的图案和色彩的种类,该微晶石图案新颖、色彩独特,大大满足了人们在生活及生产中对微晶石的需求。
2、本发明微晶石的制备方法过程方便简单、操作简单、原料来源广泛,降低了生产成本,提高了企业的生产效率。
具体实施方式
下面通过具体实施例对本发明作进一步详述,以下实施例只是描述性的,不是限定性的,不能以此限定本发明的保护范围。
如无特殊说明,本发明中所使用的试剂为常规试剂;如无特殊说明,所使用的方法为常规方法。
实施例1
一种白色微晶石,其组成成分及重量份数如下:
上述白色微晶石的制备方法,步骤如下:
将各原料准确称量后,在高达1600℃的熔炉中将天然无机材料熔成玻璃液(岩浆)、水淬,再经1200℃结晶形成微晶石(石头),然后再经磨抛、切割、深加工、检验合格后,即得白色微晶石成品。
实施例2
一种白色微晶石,其组成成分及重量份数如下:
上述白色微晶石的制备方法同实施例1。
实施例3
一种白色微晶石,其组成成分及重量份数如下:
上述白色微晶石的制备方法同实施例1。
Claims (3)
1.一种白色微晶石,其特征在于:其组成成分及重量份数如下:
2.根据权利要求1所述的白色微晶石,其特征在于:其组成成分及重量份数如下:
3.根据权利要求1所述的白色微晶石,其特征在于:所述白色微晶石的制备方法的步骤如下:将各原料准确称量后,在1600℃的熔炉中将天然无机材料熔成玻璃液、水淬,再经1200℃结晶形成微晶石,然后再经磨抛、切割、深加工、检验合格后,即得白色微晶石成品。