CN104313625A - Metal surface cleaning agent containing tea saponin and preparation method of metal surface cleaning agent - Google Patents
Metal surface cleaning agent containing tea saponin and preparation method of metal surface cleaning agent Download PDFInfo
- Publication number
- CN104313625A CN104313625A CN201410622264.0A CN201410622264A CN104313625A CN 104313625 A CN104313625 A CN 104313625A CN 201410622264 A CN201410622264 A CN 201410622264A CN 104313625 A CN104313625 A CN 104313625A
- Authority
- CN
- China
- Prior art keywords
- parts
- metal surface
- water
- surface cleaning
- cleaning agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a metal surface cleaning agent containing tea saponin and a preparation method of the metal surface cleaning agent. The metal surface cleaning agent is characterized by being prepared from the following raw materials in parts by weight: 2-4 parts of tea saponin, 1-2 parts of decyl polyglucoside, 0.1-0.2 part of tartaric acid, 2-4 parts of glycerine, 0.2-0.4 part of eucalyptus oil, 3-5 parts of sodium citrate, 1-2 parts of xanthan gum, 1-2 parts of guar gum, 1-2 parts of water-soluble wool fat, 0.5-1 part of sucrose fatty acid ester, 0.5-1 part of maltitol, 3-5 parts of an additive and 40-50 parts of water. According to the metal surface cleaning agent disclosed by the invention, the natural surfactant of tea saponin serving as a main cleaning ingredient is compounded with other ingredients, so that the characteristics of high cleaning and decontamination capacity, capability of removing various oil contaminations, no secondary pollution, no metal corrosion, environmental protection, safety and harmlessness are realized; the product is good in storage stability and long in quality guarantee period.
Description
Technical field
The present invention relates to metal treatment field, be specifically related to a kind of metal surface cleaning agent containing tea saponin and preparation method thereof.
Background technology
Metal and goods thereof often at the various dirt of surface contamination and impurity, as do not removed in time, can will affect the processing effect of next process, and then have influence on the overall performance of product in the course of processing.The Main Function of metal surface cleaning agent is exactly clean metal material surface oil, wax, rust, glue, paint, powder, carbon distribution, impression of the hand, sweat stain, cutting fluid and other dirt.Traditional metal surface cleaning agent is often solvent-borne type, and cost is high, toxicity is large, security is low and environmental pollution is large.Develop and apply environmental protection, safety, efficiently aqueous based surfactant shaped metal surface cleaning agent, becoming trend of the times.
Tea saponin has another name called TS, is by the class candy glucoside compound extracted in tea tree seed, belongs to saponin class, is a kind of natural nonionic surface active agent of good performance.Tea saponin has good emulsifying, dispersion, foaming, the function such as moistening, also has the booster action of expelling parasite, sterilization, natural environmental-protective, safety non-toxic.
Summary of the invention
The object of this invention is to provide a kind of metal surface cleaning agent containing tea saponin.
The present invention is achieved by the following technical solutions:
Containing a metal surface cleaning agent for tea saponin, it is characterized in that, it is obtained by the raw material of following weight parts:
Tea saponin 2-4, Dodecyl Polyglucosides 1-2, tartrate 0.1-0.2, glycerine 2-4, eucalyptus oil 0.2-0.4, Trisodium Citrate 3-5, xanthan gum 1-2, guar gum 1-2, water-soluble lanolin 1-2, sucrose fatty ester 0.5-1, maltose alcohol 0.5-1, auxiliary agent 3-5, water 40-50
Wherein auxiliary agent is made up of the raw material of following weight part:
Grape skin 15-20, oxalic acid 2-4, citric acid 2-4, tripoly phosphate sodium STPP 1-2, propylene glycol 3-5, polyoxyethylene nonylphenol ether 1-2, silica powder 1-2, water 20-30;
The preparation method of auxiliary agent is:
Stir after grape skin is mixed with the water that 1/3-1/2 measures, supersound process 0.5-1h, add oxalic acid, citric acid, tripoly phosphate sodium STPP and propylene glycol 200-400r/min, 60-80 DEG C of process 12-24h again, after filtration, filter residue is mixed with the water of surplus, add polyoxyethylene nonylphenol ether and silica powder 1000-1200r/min, 60-80 DEG C of process 6-8h, again filter and the filtrate that twice is obtained merging, pH is adjusted to neutrality, obtains final product.
Containing a preparation method for the metal surface cleaning agent of tea saponin, it is characterized in that, comprise the following steps:
(1) xanthan gum, guar gum and tartrate are added in the water of 1/3-1/2 amount, 60-80 DEG C, 200-400r/min stirs 1-2h, then add Dodecyl Polyglucosides and sucrose fatty ester, at same temperature, 800-1000r/min stirring 15-30min, obtains component A;
(2) add in the water of surplus by tea saponin and maltose alcohol, 800-1000r/min adds eucalyptus oil and glycerine after stirring 5-10min, and same rotating speed stirs 15-30min, obtains B component;
(3) 200-400r/min after the mixing of component A, B component and all the other raw materials is stirred 1-2h, after packing and get final product.
Advantage of the present invention is:
Adopt natural surface active agent tea saponin as principal cleaning ingredients and other compositions composite, there is clean strong detergency, multiple greasy dirt, not corroding metal, non-secondary pollution, environmental protection, safe and harmless feature can be removed, product excellent storage stability, long quality-guarantee period.
Embodiment
Non-limiting examples of the present invention is as follows:
Containing a metal surface cleaning agent for tea saponin, be prepared from by the component raw material of following weight (kg):
Tea saponin 3, Dodecyl Polyglucosides 1.5, tartrate 0.15, glycerine 3, eucalyptus oil 0.3, Trisodium Citrate 4, xanthan gum 1.5, guar gum 1.5, water-soluble lanolin 1.5, sucrose fatty ester 0.8, maltose alcohol 0.8, auxiliary agent 4, water 45;
Wherein, auxiliary agent is made up of the raw material of following weight (kg):
Grape skin 18, oxalic acid 3, citric acid 3, tripoly phosphate sodium STPP 1.5, propylene glycol 4, polyoxyethylene nonylphenol ether 1.5, silica powder 1.5, water 25;
The preparation method of auxiliary agent:
Stir after grape skin is mixed with the water of 1/2 amount, supersound process 0.5h, add oxalic acid, citric acid, tripoly phosphate sodium STPP and propylene glycol 400r/min, 80 DEG C of process 24h again, after filtration, filter residue is mixed with the water of surplus, add polyoxyethylene nonylphenol ether and silica powder 1200r/min, 60 DEG C of process 8h, again filter and the filtrate that twice is obtained merging, pH is adjusted to neutrality, obtains final product.
Preparation method containing the metal surface cleaning agent of tea saponin comprises the following steps:
(1) xanthan gum, guar gum and tartrate are added in the water of 1/3 amount, 80 DEG C, 400r/min stirs 1h, then add Dodecyl Polyglucosides and sucrose fatty ester, at same temperature, 1000r/min stirs 15min, obtains component A;
(2) add in the water of surplus by tea saponin and maltose alcohol, 1000r/min adds eucalyptus oil and glycerine after stirring 5min, and same rotating speed stirs 15min, obtains B component;
(3) 400r/min after the mixing of component A, B component and all the other raw materials is stirred 1h, after packing and get final product.
Through inspection, clean-out system cleaning rate >=95% of the present embodiment.
Claims (2)
1., containing a metal surface cleaning agent for tea saponin, it is characterized in that, it is obtained by the raw material of following weight parts:
Tea saponin 2-4, Dodecyl Polyglucosides 1-2, tartrate 0.1-0.2, glycerine 2-4, eucalyptus oil 0.2-0.4, Trisodium Citrate 3-5, xanthan gum 1-2, guar gum 1-2, water-soluble lanolin 1-2, sucrose fatty ester 0.5-1, maltose alcohol 0.5-1, auxiliary agent 3-5, water 40-50;
Described auxiliary agent is made up of the raw material of following weight part:
Grape skin 15-20, oxalic acid 2-4, citric acid 2-4, tripoly phosphate sodium STPP 1-2, propylene glycol 3-5, polyoxyethylene nonylphenol ether 1-2, silica powder 1-2, water 20-30;
The preparation method of described auxiliary agent is:
Stir after grape skin is mixed with the water that 1/3-1/2 measures, supersound process 0.5-1h, add oxalic acid, citric acid, tripoly phosphate sodium STPP and propylene glycol 200-400r/min, 60-80 DEG C of process 12-24h again, after filtration, filter residue is mixed with the water of surplus, add polyoxyethylene nonylphenol ether and silica powder 1000-1200r/min, 60-80 DEG C of process 6-8h, again filter and the filtrate that twice is obtained merging, pH is adjusted to neutrality, obtains final product.
2. the preparation method of a kind of metal surface cleaning agent containing tea saponin according to claim 1, is characterized in that, comprise the following steps:
(1) xanthan gum, guar gum and tartrate are added in the water of 1/3-1/2 amount, 60-80 DEG C, 200-400r/min stirs 1-2h, then add Dodecyl Polyglucosides and sucrose fatty ester, at same temperature, 800-1000r/min stirring 15-30min, obtains component A;
(2) add in the water of surplus by tea saponin and maltose alcohol, 800-1000r/min adds eucalyptus oil and glycerine after stirring 5-10min, and same rotating speed stirs 15-30min, obtains B component;
(3) 200-400r/min after the mixing of component A, B component and all the other raw materials is stirred 1-2h, after packing and get final product.