CN104312300A - 一种防失光油漆及其制备工艺 - Google Patents
一种防失光油漆及其制备工艺 Download PDFInfo
- Publication number
- CN104312300A CN104312300A CN201410591063.9A CN201410591063A CN104312300A CN 104312300 A CN104312300 A CN 104312300A CN 201410591063 A CN201410591063 A CN 201410591063A CN 104312300 A CN104312300 A CN 104312300A
- Authority
- CN
- China
- Prior art keywords
- paint
- silicone oil
- dulling
- loss
- cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防失光油漆的制备工艺,该油漆各组分重量百分比如下:硝化棉(40%-50%)、醇酸树脂(20%-25%)、丙烯酸树脂(10%-15%)、邻苯二甲酸( 10%-15%)、硅油(5%-10%)。本发明通过添加一硅油增光剂,克服硝基漆易失去光泽的缺点;此工艺流程简单,成本低,具有广泛的应用前景。
Description
技术领域
本发明涉及一种油漆的改性方法,特别涉及一种防失光油漆及其制备方法,属于有机化工领域。
背景技术
油漆的使用历史很长,4000多年前,我国劳动人民就利用植物油(如桐油、梓油)和天然生漆涂饰器具表面,干固后形成具有保护性的涂膜。公元前1500 年,埃及人用染料如靛蓝和茜草制造蓝色和红色颜料,但这种油漆还很不完善。18 世纪,由于对亚麻仁油和氧化锌的开发利用,使油漆工业迅速发展。20 世纪,油漆工艺有了重大发展,出现了粘着力更大、光泽度更高、阻燃、抗腐蚀与热稳定性高的各种颜色的油漆。随着科学技术发展,尤其是近几十年来石油化工和有机合成工业的腾飞,许多新型油漆材料相继问世。目前油漆已有几千多种,我国化工部门,现已对油漆的分类以其主要成膜物质为基础,将油漆划分为18大类。按粉刷部位分类,主要分为墙漆、金属漆、木器漆。墙漆包括外墙漆、内墙漆和顶面漆,主要是乳胶漆;金属漆主要是磁漆;木器漆主要有硝基漆、聚酯漆等。
硝基漆是目前比较常见的木器及装修用油漆,主要成膜物是以硝化棉为主,配合醇酸树脂、松香树脂、丙烯酸树脂、氨基树脂等软硬树脂共同组成,溶剂主要有酯类、酮类、醇醚类等溶剂,醇类等助溶剂,以及苯类等稀释剂。硝基漆主要用于木器及家具的涂装、家庭装修、金属涂装、一般水泥涂装等方面。硝基漆干燥迅速,对涂装环境的要求不高,具有较好的硬度和亮度,但其缺点是,使用时间稍长就容易失去光泽。用砂纸把旧漆磨掉,重新刷漆又很麻烦。硅油作为一种增光剂,广泛应用于油漆中,特别是用在硝基漆中。硅油它是一种不同聚合度链状结构的聚有机硅氧烷,由二甲基二氯硅烷加水水解制得初缩聚环体,环体经裂解、精馏制得低环体,然后把环体、封头剂、催化剂放在一起调聚就可得到各种不同聚合度的混合物。加入硅油的有硝基漆,可使硝基漆长期不失去光泽,具有非常好的改善作用。此方法制备的油漆,具有广泛的应用前景。
发明内容
本发明的目的是提供一种防失光油漆的制备工艺。
为实现这一目的,该油漆包括以下重量百分比的物质:
硝化棉 40%-50%
醇酸树脂 20%-25%
丙烯酸树脂 10%-15%
邻苯二甲酸 10%-15%
硅油 5%-10%
一种防失光油漆的制备方法包括如下步骤:
⑴ 按重量比计量,硝化棉:醇酸树脂=2:1的比例放入容器中进行混合;
⑵ 在混合物中依次缓慢滴入丙烯酸树脂乳液进行乳化,并保持温度为50℃环境;
⑶ 把上述乳液的温度冷却到室温,再加入适量邻苯二甲酸,搅拌;
⑷ 再往溶液中加入硅油,进行改性;
⑸ 将所得到的产物隔绝空气密封,保存20天,即得到一种防失去光油漆。
本发明具有下列优点和特性;
⑴ 通过添加一种硅油,克服硝基漆使用一段时间失去光泽的弊端;
⑵ 这种油漆的制备工艺要求不高,流程简单;
⑶ 本油漆制造成本较低、具有广泛的应用前景。
具体实施方式
实施例一:
本发明的一种防失去光油漆,该油漆包括以下重量百分比的物质:
硝化棉 40%-50%
醇酸树脂 20%-25%
丙烯酸树脂 10%-15%
邻苯二甲酸 10%-15%
硅油 5%-10%
一种防失去光油漆的制备方法包括如下步骤:
⑴ 取40份的硝化棉和20份醇酸树脂放入容器中进行混合,搅拌均匀;
⑵ 在混合物中缓慢滴入15份丙烯酸树脂乳液进行乳化,并保持温度为50℃环境;
⑶ 投入10份的邻苯二甲酸到步骤⑵的乳液中,搅拌;
⑷ 往步骤⑶所制备的乳液中继续加入15份的硅油,对其改性;
⑸ 将所得到的混合物隔绝空气密封,保存20天,即得到一种防失光油漆。
实施例二:
本发明的一种防失去光油漆,该油漆包括以下重量百分比的物质:
硝化棉 40%-50%
醇酸树脂 20%-25%
丙烯酸树脂 10%-15%
邻苯二甲酸 10%-15%
硅油 5%-10%
一种防失去光油漆的制备方法包括如下步骤:
⑴ 取50份的硝化棉和25份醇酸树脂放入容器中进行混合,搅拌均匀;
⑵ 在混合物中缓慢滴入10份丙烯酸树脂乳液进行乳化,并保持温度为50℃环境;
⑶ 投入10份的邻苯二甲酸到步骤⑵的乳液中,搅拌;
⑷ 往步骤⑶所制备的乳液中继续加入5份的硅油,对其改性;
⑸ 将所得到的混合物隔绝空气密封,保存20天,即得到一种防失光油漆。
Claims (4)
1.一种防失光油漆的制备工艺,其特征在于包括以下重量百分比的物质:硝化棉(40%-50%)、醇酸树脂 (20%-25%)、丙烯酸树脂 (10%-15%)、邻苯二甲酸 ( 10%-15%)、硅油 (5%-10%)。
2.根据权利要求1所述的一种防失光油漆的制备工艺,其中所用的硝化棉的含氮量为4%-8%。
3.根据权利要求1所述的一种防失光油漆的制备工艺,其特征在于,所述的硝化棉和醇酸树脂,其加入比例(按重量)为2:1。
4.根据权利要求1所述的一种防失光油漆的制备工艺,其特征在于,所用的硅油为二甲基硅油。