CN104312155A - 一种阻燃硅橡胶混炼胶及其制备方法 - Google Patents

一种阻燃硅橡胶混炼胶及其制备方法 Download PDF

Info

Publication number
CN104312155A
CN104312155A CN201410481946.4A CN201410481946A CN104312155A CN 104312155 A CN104312155 A CN 104312155A CN 201410481946 A CN201410481946 A CN 201410481946A CN 104312155 A CN104312155 A CN 104312155A
Authority
CN
China
Prior art keywords
parts
silicone rubber
powder
rubber
rubber compound
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410481946.4A
Other languages
English (en)
Inventor
李保生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIANCHANG RONGSHENG ORGANOSILICON SCIENCE & TECHNOLOGY Co Ltd
Original Assignee
TIANCHANG RONGSHENG ORGANOSILICON SCIENCE & TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANCHANG RONGSHENG ORGANOSILICON SCIENCE & TECHNOLOGY Co Ltd filed Critical TIANCHANG RONGSHENG ORGANOSILICON SCIENCE & TECHNOLOGY Co Ltd
Priority to CN201410481946.4A priority Critical patent/CN104312155A/zh
Publication of CN104312155A publication Critical patent/CN104312155A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种阻燃硅橡胶混炼胶及其制备方法。其由以下重量份的原料制成：二甲基硅橡胶80-100、甲基三乙酰氧基硅烷3-6、聚苯硫醚15-25、钼酸钙5-10、三硬脂酸甘油酯2-4、沉淀白炭黑15-20、过氧化二苯甲酰2-3、轻烧粉10-15、妥尔油5-10、羟基锡酸锌8-12、聚a-烯烃4-7、勃姆石粉5-10、过氧化新癸酸叔丁酯1.5-2.5、牛油树脂5-10、4-叔丁基苯硫酚2-3、N,N-二环己基-2-苯并噻唑次磺酰胺1-2、2-巯基甲基苯并咪唑1-2、助剂3-5。本发明硅橡胶混炼胶阻燃性能优异，阻燃级别能够达到FV-0，且不含卤族元素，物燃烧时烟密度很低，不产生有毒有害气体和烟雾，不会给环境带来污染，同时具有优良的耐高温性、耐辐射性、耐化学药品性和抗老化性，安全环保，经久耐用。

Description

一种阻燃硅橡胶混炼胶及其制备方法
技术领域
本发明涉及一种阻燃硅橡胶混炼胶及其制备方法，属于硅橡胶技术领域。
背景技术
硅橡胶是以聚硅烷为主链的高分子材料，由于主链硅氧链段的非极性和弱的分子间相互作用，具有良好的热稳定性、耐候性、耐老化性和电气性能，在很宽的温度内（-50~120℃）其力学性能相当稳定，在航天航空、电子电气工业等领域中得到广泛的应用。目前市场上的硅橡胶混炼胶存在着阻燃性差的缺点，且多添加含有卤族元素的阻燃剂，燃烧时释放出大量的有害气体，严重影响人们的身体健康，无法满足市场的需求，因此，需要对硅橡胶进行改性，以获得阻燃性能优异、安全环保的硅橡胶混炼胶。
发明内容
本发明目的在于提供一种无卤、低烟、安全环保、阻燃性能优异的阻燃硅橡胶混炼胶及其制备方法。
为实现上述目的，本发明采用如下技术方案：
    一种阻燃硅橡胶混炼胶，由以下重量份的原料制成：二甲基硅橡胶80-100、甲基三乙酰氧基硅烷3-6、聚苯硫醚15-25、钼酸钙5-10、三硬脂酸甘油酯2-4、沉淀白炭黑15-20、过氧化二苯甲酰2-3、轻烧粉10-15、妥尔油5-10、羟基锡酸锌8-12、聚a-烯烃4-7、勃姆石粉5-10、过氧化新癸酸叔丁酯1.5-2.5、牛油树脂5-10、4-叔丁基苯硫酚2-3、N,N-二环己基-2-苯并噻唑次磺酰胺1-2、2-巯基甲基苯并咪唑1-2、助剂3-5；
所述助剂的制备方法如下:a、取以下重量份的原料：松香季戊四醇酯3-7、4,5-环氧环己烷-1,2-二甲酸二缩水甘油酯 2-5、氟化锆5-10、硫代磷酸三苯基异氰酸酯2-4、4 ,4′- 联苯二酚1-2、三异丙醇胺环硼酸酯3-5、2,2-二噻吩基乙醇酸甲酯2-3、骨胶粉4-8、碳化钨6-12、癸基十四醇鲸蜡硬脂酸酯2.5-4.5、2-(4-吗啉基二硫代)苯并噻唑 2-3；b、将氟化锆、碳化钨、骨胶粉、松香季戊四醇酯、癸基十四醇鲸蜡硬脂酸酯、4,5-环氧环己烷-1,2-二甲酸二缩水甘油酯加入高速搅拌机内，3000-4000rpm高速搅拌3-6min，然后加入余下原料，1000-1500rpm高速搅拌4-8min，即可。
    本发明的阻燃硅橡胶混炼胶的制备方法，包括以下步骤：按配方配比将二甲基硅橡胶、甲基三乙酰氧基硅烷、妥尔油、轻烧粉、勃姆石粉一同投入到捏合机中,在50-60℃下混炼2-3h；然后加入聚苯硫醚、三硬脂酸甘油酯、牛油树脂、聚a-烯烃、钼酸钙、沉淀白炭黑，升温至70-80℃，混炼1-2h，最后加入余下原料，升温至145-165℃,抽真空，真空度控制在0.05-0.07MPa，混炼0.5-1h，降温至60℃以下出料，即得本发明硅橡胶混炼胶。
本发明的有益效果：
本发明硅橡胶混炼胶阻燃性能优异，阻燃级别能够达到FV-0，且不含卤族元素，物燃烧时烟密度很低，不产生有毒有害气体和烟雾，不会给环境带来污染，同时具有优良的耐高温性、耐辐射性、耐化学药品性和抗老化性，安全环保，经久耐用。
具体实施方式
    一种阻燃硅橡胶混炼胶，由以下重量（kg）的原料制成：二甲基硅橡胶100、甲基三乙酰氧基硅烷5、聚苯硫醚20、钼酸钙8、三硬脂酸甘油酯3、沉淀白炭黑18、过氧化二苯甲酰2.5、轻烧粉15、妥尔油8、羟基锡酸锌10、聚a-烯烃6、勃姆石粉7、过氧化新癸酸叔丁酯2、牛油树脂8、4-叔丁基苯硫酚2.5、N,N-二环己基-2-苯并噻唑次磺酰胺2、2-巯基甲基苯并咪唑1、助剂4.5；
    所述助剂的制备方法如下:a、取以下重量份的原料：松香季戊四醇酯7、4,5-环氧环己烷-1,2-二甲酸二缩水甘油酯3、氟化锆8、硫代磷酸三苯基异氰酸酯3、4 ,4′- 联苯二酚1-2、三异丙醇胺环硼酸酯4、2,2-二噻吩基乙醇酸甲酯2.5、骨胶粉6、碳化钨8、癸基十四醇鲸蜡硬脂酸酯3.5、2-(4-吗啉基二硫代)苯并噻唑 2.5；b、将氟化锆、碳化钨、骨胶粉、松香季戊四醇酯、癸基十四醇鲸蜡硬脂酸酯、4,5-环氧环己烷-1,2-二甲酸二缩水甘油酯加入高速搅拌机内，4000rpm高速搅拌3min，然后加入余下原料，1500rpm高速搅拌5min，即可。
    阻燃硅橡胶混炼胶的制备方法，包括以下步骤：按配方配比将二甲基硅橡胶、甲基三乙酰氧基硅烷、妥尔油、轻烧粉、勃姆石粉一同投入到捏合机中,在55℃下混炼3h；然后加入聚苯硫醚、三硬脂酸甘油酯、牛油树脂、聚a-烯烃、钼酸钙、沉淀白炭黑，升温至75℃，混炼1.5h，最后加入余下原料，升温至155℃,抽真空，真空度控制在0.06MPa，混炼1h，降温至60℃以下出料，即得本发明硅橡胶混炼胶。
上述实施例制得的阻燃硅橡胶混炼胶的性能测试结果如下表所示：
表1   阻燃硅橡胶混炼胶的性能测试结果

Claims (2)

1.一种阻燃硅橡胶混炼胶，其特征在于，由以下重量份的原料制成：二甲基硅橡胶80-100、甲基三乙酰氧基硅烷3-6、聚苯硫醚15-25、钼酸钙5-10、三硬脂酸甘油酯2-4、沉淀白炭黑15-20、过氧化二苯甲酰2-3、轻烧粉10-15、妥尔油5-10、羟基锡酸锌8-12、聚a-烯烃4-7、勃姆石粉5-10、过氧化新癸酸叔丁酯1.5-2.5、牛油树脂5-10、4-叔丁基苯硫酚2-3、N,N-二环己基-2-苯并噻唑次磺酰胺1-2、2-巯基甲基苯并咪唑1-2、助剂3-5；
    所述助剂的制备方法如下:a、取以下重量份的原料：松香季戊四醇酯3-7、4,5-环氧环己烷-1,2-二甲酸二缩水甘油酯 2-5、氟化锆5-10、硫代磷酸三苯基异氰酸酯2-4、4 ,4′- 联苯二酚1-2、三异丙醇胺环硼酸酯3-5、2,2-二噻吩基乙醇酸甲酯2-3、骨胶粉4-8、碳化钨6-12、癸基十四醇鲸蜡硬脂酸酯2.5-4.5、2-(4-吗啉基二硫代)苯并噻唑 2-3；b、将氟化锆、碳化钨、骨胶粉、松香季戊四醇酯、癸基十四醇鲸蜡硬脂酸酯、4,5-环氧环己烷-1,2-二甲酸二缩水甘油酯加入高速搅拌机内，3000-4000rpm高速搅拌3-6min，然后加入余下原料，1000-1500rpm高速搅拌4-8min，即可。
2.一种如权利要求1所述的阻燃硅橡胶混炼胶的制备方法，其特征在于包括以下步骤：按配方配比将二甲基硅橡胶、甲基三乙酰氧基硅烷、妥尔油、轻烧粉、勃姆石粉一同投入到捏合机中,在50-60℃下混炼2-3h；然后加入聚苯硫醚、三硬脂酸甘油酯、牛油树脂、聚a-烯烃、钼酸钙、沉淀白炭黑，升温至70-80℃，混炼1-2h，最后加入余下原料，升温至145-165℃,抽真空，真空度控制在0.05-0.07MPa，混炼0.5-1h，降温至60℃以下出料，即得本发明硅橡胶混炼胶。
CN201410481946.4A 2014-09-19 2014-09-19 一种阻燃硅橡胶混炼胶及其制备方法 Pending CN104312155A (zh)