CN104310872A - A light thermally-insulating waterproof partition plate and a manufacturing method thereof - Google Patents
A light thermally-insulating waterproof partition plate and a manufacturing method thereof Download PDFInfo
- Publication number
- CN104310872A CN104310872A CN201410501738.6A CN201410501738A CN104310872A CN 104310872 A CN104310872 A CN 104310872A CN 201410501738 A CN201410501738 A CN 201410501738A CN 104310872 A CN104310872 A CN 104310872A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- partition plate
- suitable quantity
- flue dust
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A light thermally-insulating waterproof partition plate is disclosed. The partition plate is characterized in that: the partition plate is prepared from following raw materials by weight: 20-25 parts of cement, 1-3 parts of aluminum oxide, 11-14 parts of nanometer graphite, 0.7-1.4 parts of calcium sulfate, 1-3 parts of borax, 0.2-0.4 part of saponin, 0.8-2.4 parts of iron oxide yellow, 1-3 parts of a lemon extract liquid, 13-17 parts of zeolite, 8-13 parts of paraffin, 11-14 parts of octadecyl trimethyl ammonium chloride, 15-18 parts of electric-plant flue dust, 16-18 parts of litchi leaves, 3-6 parts of an auxiliary agent and a proper amount of water; the electric-plant flue dust, the nanometer graphite, and the like are processed and then added into the raw materials, thus reducing the production cost and achieving comprehensive economic effects of waste reutilization on the one hand, and enhancing thermal insulation and sound insulation effects of baffle bricks on the other hand; and a prepared light baffle brick has high strength and good waterproofness and is free of maintenance in production. In addition, the partition plate is simple in production process, free of special equipment and easy to manufacture.
Description
Technical field
The present invention relates to building material field, be specifically related to a kind of light thermal-insulation retention wall plate and preparation method thereof.
Background technology
Light cellular partition board is made up of various industrial waste residues such as innoxious phosphogypsum, lightweight slag, flyash, through a kind of novel energy-conserving walling material of frequency conversion steam pressurized maintenance, the walling that it is a kind of external form as the cassette ceiling, but there is male and female falcon groove on its both sides, only sheet material need be erected during installation, male and female falcon is coated after a small amount of filleting mortar assembled.It has the advantages such as quality is light, intensity is high, multiple environmental protection, heat insulating, sound insulation, breathing damping, fire prevention, rapid construction, reduction body of wall cost, so enjoy favor in architecture indoor finishing field, but shortcomings such as the light cellular partition board ultimate compression strength used in the market is low, tensile strength is weak, anti-cracking performance and hanging ability is not good, production cost is high, sound-insulating weak effect.
Summary of the invention
Object of the present invention is just to provide a kind of light thermal-insulation retention wall plate and preparation method thereof, to overcome the deficiencies in the prior art.
The object of the present invention is achieved like this:
A kind of light thermal-insulation retention wall plate, it is characterized in that, be made up of the raw material of following weight part: cement 20-25, aluminum oxide 1-3, nano-graphite 11-14, calcium sulfate 0.7-1.4, borax 1-3, saponin 0.2-0.4, iron oxide yellow 0.8-2.4, lemon extracting solution 1-3, zeolite 13-17, paraffin 8-13, octadecyl trimethyl ammonium chloride 11-14, power plant flue dust 15-18, Lychee leaf 16-18, auxiliary agent 3-6, suitable quantity of water.
Described auxiliary agent is made up of following raw materials in part by weight: mica powder 5-8, titanium dioxide 3-5, lithium silicate 0.1-0.2, magnesium chloride 2-4, magnesium oxide 1-3, sodium tetraborate 0.02-0.05, Sodium hexametaphosphate 99 0.04-0.08, redispersable latex powder 0.2-0.4, molasses 0.6-2.7, SHP-50 polysiloxane powder hydrophober 1.2-2.4, Oenothera oil 0.02-0.5, dimethyl silicone oil 2.1-3.6, its preparation method to stir adding magnesium oxide powder in 50% magnesium chloride solution to obtain inorganic gel agent, then other leftover materials are pulverized mixing, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product.
The preparation method of described a kind of light thermal-insulation retention wall plate, is characterized in that comprising the following steps:
(1) send in charring furnace by Lychee leaf, at 504-637 DEG C, charing process 3-4 hour, takes out, is ground into powder, and the powder to gained makes it seethe spray form paraffin under condition in air blast, makes it mixing;
(2) zeolite, power plant's flue dust are calcined at 605-840 DEG C after 3-6 hour and take out, pulverizing, adds lemon extracting solution and octadecyl trimethyl ammonium chloride stirs, granulation;
(3) get calcium sulfate and add suitable quantity of water stirring 5-10 minute, put into nano-graphite and soak 3-5 hour, take out oven dry and pulverize;
(4) step (1), (2), (3) reaction mass and other leftover materials are pulverized add suitable quantity of water stirring and evenly mixing and obtain slip, obtained slurry is added wall slab squeezing former is shaping, cutting, natural curing, to obtain final product.
The present invention has following beneficial effect: the present invention will add in starting material after the process such as power plant's flue dust, nano-graphite, reduce production cost on the one hand, realize the Economic model of refuse reclamation, enhance on the other hand the heat preservation and soundproof effect of partition block, obtained light partition wall brick has that intensity is good, water-repellancy is good and exempt from care action in producing.Meanwhile, production process of the present invention is simple, without the need to specific installation, easy to manufacture.
Embodiment
Described a kind of light thermal-insulation retention wall plate, it is characterized in that, be made up of the raw material of following weight part: cement 25, aluminum oxide 1, nano-graphite 14, calcium sulfate 0.7, borax 1, saponin 0.2, iron oxide yellow 0.9, lemon extracting solution 1, zeolite 13, paraffin 8, octadecyl trimethyl ammonium chloride 11, power plant's flue dust 15, Lychee leaf 16, auxiliary agent 3, suitable quantity of water.
Described auxiliary agent is made up of following raw materials in part by weight: mica powder 5, titanium dioxide 3, lithium silicate 0.1, magnesium chloride 2, magnesium oxide 1, sodium tetraborate 0.02, Sodium hexametaphosphate 99 0.04, redispersable latex powder 0.4, molasses 0.6, SHP-50 polysiloxane powder hydrophober 1.2, Oenothera oil 0.02, dimethyl silicone oil 2.1, its preparation method to stir adding magnesium oxide powder in 50% magnesium chloride solution to obtain inorganic gel agent, then other leftover materials are pulverized mixing, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter, at 2-5mm, is dried and be get final product.
Making method comprises the following steps:
(1) send in charring furnace by Lychee leaf, at 504-637 DEG C, charing process 3-4 hour, takes out, is ground into powder, and the powder to gained makes it seethe spray form paraffin under condition in air blast, makes it mixing;
(2) zeolite, power plant's flue dust are calcined at 605-840 DEG C after 3-6 hour and take out, pulverizing, adds lemon extracting solution and octadecyl trimethyl ammonium chloride stirs, granulation;
(3) get calcium sulfate and add suitable quantity of water stirring 5-10 minute, put into nano-graphite and soak 3-5 hour, take out oven dry and pulverize;
(4) step (1), (2), (3) reaction mass and other leftover materials are pulverized add suitable quantity of water stirring and evenly mixing and obtain slip, obtained slurry is added wall slab squeezing former is shaping, cutting, natural curing, to obtain final product.
The technical indicator of being processed the light cellular partition board obtained by above-described embodiment is as follows:
(1) unit weight: 512kg/m
3;
(2) thermal conductivity (medial temperature 25 ± 2 DEG C): 0.074W/ (mk);
(3) high temperature resistant, flat appearance is smooth.
Claims (2)
1. a light thermal-insulation retention wall plate, it is characterized in that, be made up of the raw material of following weight part: cement 20-25, aluminum oxide 1-3, nano-graphite 11-14, calcium sulfate 0.7-1.4, borax 1-3, saponin 0.2-0.4, iron oxide yellow 0.8-2.4, lemon extracting solution 1-3, zeolite 13-17, paraffin 8-13, octadecyl trimethyl ammonium chloride 11-14, power plant flue dust 15-18, Lychee leaf 16-18, auxiliary agent 3-6, suitable quantity of water, described auxiliary agent is made up of following raw materials in part by weight: mica powder 5-8, titanium dioxide 3-5, lithium silicate 0.1-0.2, magnesium chloride 2-4, magnesium oxide 1-3, sodium tetraborate 0.02-0.05, Sodium hexametaphosphate 99 0.04-0.08, redispersable latex powder 0.2-0.4, molasses 0.6-2.7, SHP-50 polysiloxane powder hydrophober 1.2-2.4, Oenothera oil 0.02-0.5, dimethyl silicone oil 2.1-3.6, its preparation method to stir adding magnesium oxide powder in 50% magnesium chloride solution to obtain inorganic gel agent, then other leftover materials are pulverized mixing, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product.
2. the making method of a kind of light thermal-insulation retention wall plate according to claim 1, is characterized in that comprising the following steps:
(1) send in charring furnace by Lychee leaf, at 504-637 DEG C, charing process 3-4 hour, takes out, is ground into powder, and the powder to gained makes it seethe spray form paraffin under condition in air blast, makes it mixing;
(2) zeolite, power plant's flue dust are calcined at 605-840 DEG C after 3-6 hour and take out, pulverizing, adds lemon extracting solution and octadecyl trimethyl ammonium chloride stirs, granulation;
(3) get calcium sulfate and add suitable quantity of water stirring 5-10 minute, put into nano-graphite and soak 3-5 hour, take out oven dry and pulverize;
(4) step (1), (2), (3) reaction mass and other leftover materials are pulverized add suitable quantity of water stirring and evenly mixing and obtain slip, obtained slurry is added wall slab squeezing former is shaping, cutting, natural curing, to obtain final product.