CN104310872B - A kind of light thermal-insulation retention wall plate and preparation method thereof - Google Patents

A kind of light thermal-insulation retention wall plate and preparation method thereof Download PDF

Info

Publication number
CN104310872B
CN104310872B CN201410501738.6A CN201410501738A CN104310872B CN 104310872 B CN104310872 B CN 104310872B CN 201410501738 A CN201410501738 A CN 201410501738A CN 104310872 B CN104310872 B CN 104310872B
Authority
CN
China
Prior art keywords
powder
water
suitable quantity
stir
add
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410501738.6A
Other languages
Chinese (zh)
Other versions
CN104310872A (en
Inventor
彭庆付
孟玲琳
王英
崔玉凤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI ZHONGKUNYUAN NEW BUILDING MATERIALS Co Ltd
Original Assignee
ANHUI ZHONGKUNYUAN NEW BUILDING MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI ZHONGKUNYUAN NEW BUILDING MATERIALS Co Ltd filed Critical ANHUI ZHONGKUNYUAN NEW BUILDING MATERIALS Co Ltd
Priority to CN201410501738.6A priority Critical patent/CN104310872B/en
Publication of CN104310872A publication Critical patent/CN104310872A/en
Application granted granted Critical
Publication of CN104310872B publication Critical patent/CN104310872B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a kind of light thermal-insulation retention wall plate, it is characterized in that, made by the raw material of following weight portion: cement 20-25, aluminium oxide 1-3, nano-graphite 11-14, calcium sulfate 0.7-1.4, borax 1-3, saponin 0.2-0.4, iron oxide yellow 0.8-2.4, lemon extract 1-3, zeolite 13-17, paraffin 8-13, OTAC 11-14, the flue dust 15-18 of power plant, lychee leaf 16-18, auxiliary agent 3-6, suitable quantity of water; The present invention will add in raw material after the processing such as power plant's flue dust, nano-graphite, one side has reduced production cost, has realized the Economic model of refuse reclamation, strengthened on the other hand the heat preservation and soundproof effect of partition block, the light partition wall brick making have that intensity is good, water proofing property is good and produce in exempt from care action. Meanwhile, production process of the present invention is simple, without special installation, easy to manufacture.

Description

A kind of light thermal-insulation retention wall plate and preparation method thereof
Technical field
The present invention relates to building material field, be specifically related to a kind of light thermal-insulation retention wall plate and preparation method thereof.
Background technology
Light cellular partition board is made up of various industrial waste residues such as innoxious ardealite, lightweight slag, flyash, a kind of novel energy-conserving walling material forming through the maintenance of frequency conversion steam pressurized, the walling that it is a kind of external form as the cassette ceiling, but there is male and female falcon groove on its both sides, when installation, only sheet material need be erected, male and female falcon is coated after a small amount of filleting mortar assembled. It has the advantages such as quality is light, intensity is high, multiple environmental protection, insulation, sound insulation, breathing damping, fire prevention, rapid construction, reduction body of wall cost, so enjoy favor in architecture indoor finishing field, but the shortcomings such as the light cellular partition board compression strength using is in the market low, tensile strength weak, anti-cracking performance and hanging ability is not good, production cost is high, sound-insulating weak effect.
Summary of the invention
Object of the present invention is just to provide a kind of light thermal-insulation retention wall plate and preparation method thereof, to overcome the deficiencies in the prior art.
The object of the present invention is achieved like this:
A kind of light thermal-insulation retention wall plate, it is characterized in that, made by the raw material of following weight portion: cement 20-25, aluminium oxide 1-3, nano-graphite 11-14, calcium sulfate 0.7-1.4, borax 1-3, saponin 0.2-0.4, iron oxide yellow 0.8-2.4, lemon extract 1-3, zeolite 13-17, paraffin 8-13, OTAC 11-14, the flue dust 15-18 of power plant, lychee leaf 16-18, auxiliary agent 3-6, suitable quantity of water.
Described auxiliary agent is made up of following raw materials in part by weight: mica powder 5-8, titanium dioxide 3-5, lithium metasilicate 0.1-0.2, magnesium chloride 2-4, magnesia 1-3, sodium tetraborate 0.02-0.05, calgon 0.04-0.08, redispersable latex powder 0.2-0.4, molasses 0.6-2.7, SHP-50 polysiloxanes powder hydrophober 1.2-2.4, evening primrose oil 0.02-0.5, dimethicone 2.1-3.6, its preparation method is in 50% magnesium chloride solution, to add the magnesium oxide powder inorganic gel agent that stirs to obtain, then other leftover materials are pulverized and mixed, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product.
The preparation method of described a kind of light thermal-insulation retention wall plate, is characterized in that comprising the following steps:
(1) lychee leaf is sent in retort, at 504-637 DEG C, 3-4 hour is processed in charing, takes out, and is ground into powder, makes it seethe spray form paraffin under condition to the powder of gained in air blast, makes it to mix;
(2) zeolite, power plant's flue dust are calcined at 605-840 DEG C after 3-6 hour and taken out, pulverize, add lemon extract and OTAC to stir, granulation;
(3) get calcium sulfate and add suitable quantity of water to stir 5-10 minute, put into nano-graphite and soak 3-5 hour, take out to dry and pulverize;
(4) step (1), (2), (3) reaction mass and the pulverizing of other leftover materials are added to suitable quantity of water and stir and evenly mix to obtain slip, the slurry making is added to wall slab squeezing former moulding, cutting, natural curing, to obtain final product.
The present invention has following beneficial effect: the present invention will add in raw material after the processing such as power plant's flue dust, nano-graphite, one side has reduced production cost, has realized the Economic model of refuse reclamation, strengthened on the other hand the heat preservation and soundproof effect of partition block, the light partition wall brick making have that intensity is good, water proofing property is good and produce in exempt from care action. Meanwhile, production process of the present invention is simple, without special installation, easy to manufacture.
Detailed description of the invention
Described a kind of light thermal-insulation retention wall plate, it is characterized in that, made by the raw material of following weight portion: cement 25, aluminium oxide 1, nano-graphite 14, calcium sulfate 0.7, borax 1, saponin 0.2, iron oxide yellow 0.9, lemon extract 1, zeolite 13, paraffin 8, OTAC 11, power plant's flue dust 15, lychee leaf 16, auxiliary agent 3, suitable quantity of water.
Described auxiliary agent is made up of following raw materials in part by weight: mica powder 5, titanium dioxide 3, lithium metasilicate 0.1, magnesium chloride 2, magnesia 1, sodium tetraborate 0.02, calgon 0.04, redispersable latex powder 0.4, molasses 0.6, SHP-50 polysiloxanes powder hydrophober 1.2, evening primrose oil 0.02, dimethicone 2.1, its preparation method is in 50% magnesium chloride solution, to add the magnesium oxide powder inorganic gel agent that stirs to obtain, then other leftover materials are pulverized and mixed, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter, at 2-5mm, is dried and be get final product.
Preparation method comprises the following steps:
(1) lychee leaf is sent in retort, at 504-637 DEG C, 3-4 hour is processed in charing, takes out, and is ground into powder, makes it seethe spray form paraffin under condition to the powder of gained in air blast, makes it to mix;
(2) zeolite, power plant's flue dust are calcined at 605-840 DEG C after 3-6 hour and taken out, pulverize, add lemon extract and OTAC to stir, granulation;
(3) get calcium sulfate and add suitable quantity of water to stir 5-10 minute, put into nano-graphite and soak 3-5 hour, take out to dry and pulverize;
(4) step (1), (2), (3) reaction mass and the pulverizing of other leftover materials are added to suitable quantity of water and stir and evenly mix to obtain slip, the slurry making is added to wall slab squeezing former moulding, cutting, natural curing, to obtain final product.
The technical indicator of processing the light cellular partition board obtaining by above-described embodiment is as follows:
(1) unit weight: 512kg/m3
(2) thermal conductivity factor (25 ± 2 DEG C of mean temperatures): 0.074W/ (mk);
(3) high temperature resistant, flat appearance is smooth.

Claims (2)

1. a light thermal-insulation retention wall plate, it is characterized in that, made by the raw material of following weight portion: cement 20-25, aluminium oxide 1-3, nano-graphite 11-14, calcium sulfate 0.7-1.4, borax 1-3, saponin 0.2-0.4, iron oxide yellow 0.8-2.4, lemon extract 1-3, zeolite 13-17, paraffin 8-13, OTAC 11-14, the flue dust 15-18 of power plant, lychee leaf 16-18, auxiliary agent 3-6, suitable quantity of water, described auxiliary agent is made up of following raw materials in part by weight: mica powder 5-8, titanium dioxide 3-5, lithium metasilicate 0.1-0.2, magnesium chloride 2-4, magnesia 1-3, sodium tetraborate 0.02-0.05, calgon 0.04-0.08, redispersable latex powder 0.2-0.4, molasses 0.6-2.7, SHP-50 polysiloxanes powder hydrophober 1.2-2.4, evening primrose oil 0.02-0.5, dimethicone 2.1-3.6, its preparation method is in 50% magnesium chloride solution, to add the magnesium oxide powder inorganic gel agent that stirs to obtain, then other leftover materials are pulverized and mixed, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product.
2. the preparation method of a kind of light thermal-insulation retention wall plate according to claim 1, is characterized in that comprising the following steps:
(1) lychee leaf is sent in retort, at 504-637 DEG C, 3-4 hour is processed in charing, takes out, and is ground into powder, makes it seethe spray form paraffin under condition to the powder air blast of gained, makes it to mix;
(2) zeolite, power plant's flue dust are calcined at 605-840 DEG C after 3-6 hour and taken out, pulverize, add lemon extract and OTAC to stir, granulation;
(3) get calcium sulfate and add suitable quantity of water to stir 5-10 minute, put into nano-graphite and soak 3-5 hour, take out to dry and pulverize;
(4) step (1), (2), (3) reaction mass and the pulverizing of other leftover materials are added to suitable quantity of water and stir and evenly mix to obtain slip, the slurry making is added to wall slab squeezing former moulding, cutting, natural curing, to obtain final product.
CN201410501738.6A 2014-09-27 2014-09-27 A kind of light thermal-insulation retention wall plate and preparation method thereof Active CN104310872B (en)