CN103979858B - A kind of anticorrosion light cellular partition board and preparation method thereof - Google Patents
A kind of anticorrosion light cellular partition board and preparation method thereof Download PDFInfo
- Publication number
- CN103979858B CN103979858B CN201410135167.9A CN201410135167A CN103979858B CN 103979858 B CN103979858 B CN 103979858B CN 201410135167 A CN201410135167 A CN 201410135167A CN 103979858 B CN103979858 B CN 103979858B
- Authority
- CN
- China
- Prior art keywords
- powder
- partition board
- cellular partition
- light cellular
- anticorrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of anticorrosion light cellular partition board, it is characterized in that, be made up of the raw material of following weight part: cement 20-26, polypropylene fibre 9-12, copper smelter slag 11-13, polymer dispersion powder 12-14, benzene emulsion 8-10, quartz sand 12-15, diatomite 13-17, sodium alginate 7-9, sepiolite 12-15, propylben 2.4-5.6, sewage disposal mud 13-16, rice straw 17-24, auxiliary agent 3-6, suitable quantity of water; The present invention adds polypropylene fibre, increase product surface intensity, prevent from ftractureing in moulding process, owing to adopting above-mentioned production technique, the features such as obtained partition plate has that intensity is high, light weight, anticorrosion, waterproof, fire prevention, adopt rice straw as this light cellular partition board material main filler of making simultaneously, decrease burning straw pollution on the environment, turn waste into wealth, reduce production cost.
Description
Technical field
The present invention relates to building material field, be specifically related to a kind of anticorrosion light cellular partition board and preparation method thereof.
Background technology
Light cellular partition board is made up of various industrial waste residues such as innoxious phosphogypsum, lightweight slag, flyash, through a kind of novel energy-conserving walling material of frequency conversion steam pressurized maintenance, the walling that it is a kind of external form as the cassette ceiling, but there is male and female falcon groove on its both sides, only sheet material need be erected during installation, male and female falcon is coated after a small amount of filleting mortar assembled.It has the advantages such as quality is light, intensity is high, multiple environmental protection, heat insulating, sound insulation, breathing damping, fire prevention, rapid construction, reduction body of wall cost, so enjoy favor in architecture indoor finishing field, but shortcomings such as the light cellular partition board ultimate compression strength used in the market is low, tensile strength is weak, anti-cracking performance and hanging ability is not good, production cost is high, sound-insulating weak effect.
Summary of the invention
Object of the present invention is just to provide a kind of anticorrosion light cellular partition board and preparation method thereof, to overcome the deficiencies in the prior art.
The object of the present invention is achieved like this:
A kind of anticorrosion light cellular partition board, it is characterized in that, be made up of the raw material of following weight part: cement 20-26, polypropylene fibre 9-12, copper smelter slag 11-13, polymer dispersion powder 12-14, benzene emulsion 8-10, quartz sand 12-15, diatomite 13-17, sodium alginate 7-9, sepiolite 12-15, propylben 2.4-5.6, sewage disposal mud 13-16, rice straw 17-24, auxiliary agent 3-6, suitable quantity of water.
Described auxiliary agent is made up of following raw materials in part by weight: mica powder 5-8, titanium dioxide 3-5, lithium silicate 0.1-0.2, magnesium chloride 2-4, magnesium oxide 1-3, sodium tetraborate 0.02-0.05, Sodium hexametaphosphate 99 0.04-0.08, redispersable latex powder 0.2-0.4, molasses 0.6-2.7, SHP-50 polysiloxane powder hydrophober 1.2-2.4, Oenothera oil 0.02-0.5, dimethyl silicone oil 2.1-3.6, its preparation method to stir adding magnesium oxide powder in 3:2 ratio in 50% magnesium chloride solution to obtain inorganic gel agent, then other leftover materials are pulverized mixing, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product.
The preparation method of described a kind of anticorrosion light cellular partition board, is characterized in that comprising the following steps:
(1) rice straw, sewage disposal mud are sent in charring furnace, calcination processing 3-4 hour at 520-660 DEG C, take out, be ground into powder, the powder to gained makes it seethe spray form benzene emulsion under condition in air blast, makes it mixing;
(2) diatomite, sepiolite, sewage disposal mud are calcined at 605-840 DEG C after 3-6 hour and take out, pulverize, spray 1 ‰ iron(ic) chloride and 0.5 ‰ calcium chloride composite solutions to evenly with spraying gun, dipping 10-12 hour;
(3) step (1), (2) reaction mass and other leftover materials are pulverized add suitable quantity of water stirring and evenly mixing and obtain slip, obtained slurry is added wall slab squeezing former is shaping, cutting, natural curing, to obtain final product.
The present invention has following beneficial effect: the present invention adds polypropylene fibre, increase product surface intensity, prevent from ftractureing in moulding process, owing to adopting above-mentioned production technique, the features such as obtained partition plate has that intensity is high, light weight, anticorrosion, waterproof, fire prevention, adopt rice straw as this light cellular partition board material main filler of making simultaneously, decrease burning straw pollution on the environment, turn waste into wealth, reduce production cost.
Embodiment
The anticorrosion light cellular partition board of described one, it is characterized in that, be made up of the raw material of following weight part: cement 20, polypropylene fibre 9, copper smelter slag 11, polymer dispersion powder 12, benzene emulsion 8, quartz sand 12, diatomite 13, sodium alginate 7, sepiolite 12, propylben 2.4, sewage disposal mud 13, rice straw 24, auxiliary agent 3, suitable quantity of water.
Described auxiliary agent is made up of following raw materials in part by weight: mica powder 5, titanium dioxide 3, lithium silicate 0.1, magnesium chloride 2, magnesium oxide 3, sodium tetraborate 0.02, Sodium hexametaphosphate 99 0.04, redispersable latex powder 0.2, molasses 0.7, SHP-50 polysiloxane powder hydrophober 1.4, Oenothera oil 0.02, dimethyl silicone oil 2.6, its preparation method to stir adding magnesium oxide powder in 3:2 ratio in 50% magnesium chloride solution to obtain inorganic gel agent, then other leftover materials are pulverized mixing, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product.
Making method comprises the following steps:
(1) rice straw, sewage disposal mud are sent in charring furnace, calcination processing 3-4 hour at 520-660 DEG C, take out, be ground into powder, the powder to gained makes it seethe spray form benzene emulsion under condition in air blast, makes it mixing;
(2) diatomite, sepiolite, sewage disposal mud are calcined at 605-840 DEG C after 3-6 hour and take out, pulverize, spray 1 ‰ iron(ic) chloride and 0.5 ‰ calcium chloride composite solutions to evenly with spraying gun, dipping 10-12 hour;
(3) step (1), (2) reaction mass and other leftover materials are pulverized add suitable quantity of water stirring and evenly mixing and obtain slip, obtained slurry is added wall slab squeezing former is shaping, cutting, natural curing, to obtain final product.
The technical indicator of being processed the light cellular partition board obtained by above-described embodiment is as follows:
(1) unit weight: 496kg/m
3;
(2) ultimate compression strength: 4.98MPa;
(3) high temperature resistant, flat appearance is smooth.
Claims (1)
1. an anticorrosion light cellular partition board, it is characterized in that, be made up of the raw material of following weight part: cement 20-26, polypropylene fibre 9-12, copper smelter slag 11-13, polymer dispersion powder 12-14, benzene emulsion 8-10, quartz sand 12-15, diatomite 13-17, sodium alginate 7-9, sepiolite 12-15, propylben 2.4-5.6, sewage disposal mud 13-16, rice straw 17-24, auxiliary agent 3-6, suitable quantity of water, described auxiliary agent is made up of following raw materials in part by weight: mica powder 5-8, titanium dioxide 3-5, lithium silicate 0.1-0.2, magnesium chloride 2-4, magnesium oxide 1-3, sodium tetraborate 0.02-0.05, Sodium hexametaphosphate 99 0.04-0.08, redispersable latex powder 0.2-0.4, molasses 0.6-2.7, SHP-50 polysiloxane powder hydrophober 1.2-2.4, Oenothera oil 0.02-0.5, dimethyl silicone oil 2.1-3.6, its preparation method to stir adding magnesium oxide powder in 3:2 ratio in 50% magnesium chloride solution to obtain inorganic gel agent, then other leftover materials are pulverized mixing, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product,
The making method of described a kind of anticorrosion light cellular partition board, comprises the following steps:
(1) rice straw, sewage disposal mud are sent in charring furnace, calcination processing 3-4 hour at 520-660 DEG C, take out, be ground into powder, the powder to gained makes it seethe spray form benzene emulsion under condition in air blast, makes it mixing;
(2) diatomite, sepiolite, sewage disposal mud are calcined at 605-840 DEG C after 3-6 hour and take out, pulverize, spray 1 ‰ iron(ic) chloride and 0.5 ‰ calcium chloride composite solutions to evenly with spraying gun, dipping 10-12 hour;
(3) step (1), (2) reaction mass and other leftover materials are pulverized add suitable quantity of water stirring and evenly mixing and obtain slip, obtained slurry is added wall slab squeezing former is shaping, cutting, natural curing, to obtain final product.