CN103979859B - A kind of fire-proof light partition plate and preparation method thereof - Google Patents
A kind of fire-proof light partition plate and preparation method thereof Download PDFInfo
- Publication number
- CN103979859B CN103979859B CN201410135231.3A CN201410135231A CN103979859B CN 103979859 B CN103979859 B CN 103979859B CN 201410135231 A CN201410135231 A CN 201410135231A CN 103979859 B CN103979859 B CN 103979859B
- Authority
- CN
- China
- Prior art keywords
- powder
- fire
- partition plate
- sodium
- proof light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of fire-proof light partition plate, it is characterized in that, be made up of the raw material of following weight part: cement 20-25, silicon ash 17-19, sodium bicarbonate 12-17, tungstenalloy aggregate 16-18, anhydrite 13-17, calcite in powder 14-16, Dioctyl Sodium Sulfosuccinate 8-12, epipremnum aureum extracting solution 2-5, sodium dibutyl naphthalene sulfonate 1-3, nut-shell 9-13, auxiliary agent 3-6, suitable quantity of water; The fire-proof light partition plate surfacing that the present invention obtains, attractive in appearance, fire line good, heat-insulating and sound-absorbing effect is good, and not easy to crack, is widely used in the fields such as building.
Description
Technical field
The present invention relates to building material field, be specifically related to a kind of fire-proof light partition plate and preparation method thereof.
Background technology
Light cellular partition board is made up of various industrial waste residues such as innoxious phosphogypsum, lightweight slag, flyash, through a kind of novel energy-conserving walling material of frequency conversion steam pressurized maintenance, the walling that it is a kind of external form as the cassette ceiling, but there is male and female falcon groove on its both sides, only sheet material need be erected during installation, male and female falcon is coated after a small amount of filleting mortar assembled.It has the advantages such as quality is light, intensity is high, multiple environmental protection, heat insulating, sound insulation, breathing damping, fire prevention, rapid construction, reduction body of wall cost, so enjoy favor in architecture indoor finishing field, but shortcomings such as the light cellular partition board ultimate compression strength used in the market is low, tensile strength is weak, anti-cracking performance and hanging ability is not good, production cost is high, sound-insulating weak effect.
Summary of the invention
Object of the present invention is just to provide a kind of fire-proof light partition plate and preparation method thereof, to overcome the deficiencies in the prior art.
The object of the present invention is achieved like this:
A kind of fire-proof light partition plate, it is characterized in that, be made up of the raw material of following weight part: cement 20-25, silicon ash 17-19, sodium bicarbonate 12-17, tungstenalloy aggregate 16-18, anhydrite 13-17, calcite in powder 14-16, Dioctyl Sodium Sulfosuccinate 8-12, epipremnum aureum extracting solution 2-5, sodium dibutyl naphthalene sulfonate 1-3, nut-shell 9-13, auxiliary agent 3-6, suitable quantity of water.
Described auxiliary agent is made up of following raw materials in part by weight: mica powder 5-8, titanium dioxide 3-5, lithium silicate 0.1-0.2, magnesium chloride 2-4, magnesium oxide 1-3, sodium tetraborate 0.02-0.05, Sodium hexametaphosphate 99 0.04-0.08, redispersable latex powder 0.2-0.4, molasses 0.6-2.7, SHP-50 polysiloxane powder hydrophober 1.2-2.4, Oenothera oil 0.02-0.5, dimethyl silicone oil 2.1-3.6, its preparation method to stir adding magnesium oxide powder in 3:2 ratio in 50% magnesium chloride solution to obtain inorganic gel agent, then other leftover materials are pulverized mixing, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product.
The preparation method of described a kind of fire-proof light partition plate, is characterized in that comprising the following steps:
(1) nut-shell, calcite in powder are sent in charring furnace, calcination processing 3-4 hour at 510-635 DEG C, take out, be ground into powder, the powder to gained makes it seethe spray form epipremnum aureum extracting solution under condition in air blast, makes it mixing;
(2) silicon ash, tungstenalloy aggregate, anhydrite are calcined at 610-850 DEG C after 3-6 hour and take out, pulverize, spray 1 ‰ iron(ic) chloride and 0.5 ‰ calcium chloride composite solutions to evenly with spraying gun, dipping 10-12 hour;
(3) step (1), (2) reaction mass and other leftover materials are pulverized add suitable quantity of water stirring and evenly mixing and obtain slip, obtained slurry is added wall slab squeezing former is shaping, cutting, natural curing, to obtain final product.
The present invention has following beneficial effect: the fire-proof light partition plate surfacing that the present invention obtains, attractive in appearance, fire line good, heat-insulating and sound-absorbing effect is good, and not easy to crack, is widely used in the fields such as building.
Embodiment
Described a kind of fire-proof light partition plate, it is characterized in that, be made up of the raw material of following weight part: cement 20, silicon ash 18, sodium bicarbonate 12, tungstenalloy aggregate 16, anhydrite 13, calcite in powder 14, Dioctyl Sodium Sulfosuccinate 8, epipremnum aureum extracting solution 2, sodium dibutyl naphthalene sulfonate 3, nut-shell 13, auxiliary agent 6, suitable quantity of water.
Described auxiliary agent is made up of following raw materials in part by weight: mica powder 5, titanium dioxide 5, lithium silicate 0.1, magnesium chloride 2, magnesium oxide 1, sodium tetraborate 0.02, Sodium hexametaphosphate 99 0.04, redispersable latex powder 0.2, molasses 0.6, SHP-50 polysiloxane powder hydrophober 1.2, Oenothera oil 0.02, dimethyl silicone oil 2.1, its preparation method to stir adding magnesium oxide powder in 3:2 ratio in 50% magnesium chloride solution to obtain inorganic gel agent, then other leftover materials are pulverized mixing, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter is at 2-5mm, dry and get final product.
Making method comprises the following steps:
(1) nut-shell, calcite in powder are sent in charring furnace, calcination processing 3-4 hour at 510-635 DEG C, take out, be ground into powder, the powder to gained makes it seethe spray form epipremnum aureum extracting solution under condition in air blast, makes it mixing;
(2) silicon ash, tungstenalloy aggregate, anhydrite are calcined at 610-850 DEG C after 3-6 hour and take out, pulverize, spray 1 ‰ iron(ic) chloride and 0.5 ‰ calcium chloride composite solutions to evenly with spraying gun, dipping 10-12 hour;
(3) step (1), (2) reaction mass and other leftover materials are pulverized add suitable quantity of water stirring and evenly mixing and obtain slip, obtained slurry is added wall slab squeezing former is shaping, cutting, natural curing, to obtain final product.
The technical indicator of being processed the light cellular partition board obtained by above-described embodiment is as follows:
(1) unit weight: 514kg/m
3;
(2) thermal conductivity (medial temperature 25 ± 2 DEG C): 0.072W/ (mk);
(3) ultimate compression strength: 5.1Mpa.
Claims (2)
1. a fire-proof light partition plate, it is characterized in that, comprise the raw material of following weight part: cement 20-25, silicon ash 17-19, sodium bicarbonate 12-17, tungstenalloy aggregate 16-18, anhydrite 13-17, calcite in powder 14-16, Dioctyl Sodium Sulfosuccinate 8-12, epipremnum aureum extracting solution 2-5, sodium dibutyl naphthalene sulfonate 1-3, nut-shell 9-13, auxiliary agent 3-6, suitable quantity of water;
Described auxiliary agent comprises the raw material of following weight part: mica powder 5-8, titanium dioxide 3-5, lithium silicate 0.1-0.2, magnesium chloride 2-4, magnesium oxide 1-3, sodium tetraborate 0.02-0.05, Sodium hexametaphosphate 99 0.04-0.08, redispersable latex powder 0.2-0.4, molasses 0.6-2.7, SHP-50 polysiloxane powder hydrophober 1.2-2.4, Oenothera oil 0.02-0.5, dimethyl silicone oil 2.1-3.6
The preparation method of described auxiliary agent to stir adding magnesium oxide powder in 3:2 ratio in 50% magnesium chloride solution to obtain inorganic gel agent, then other leftover materials are pulverized mixing, add suitable quantity of water and stir 30-40 minute pulping, granulation, balling-up particle diameter, at 2-5mm, is dried and be get final product.
2. the making method of a kind of fire-proof light partition plate according to claim 1, is characterized in that comprising the following steps:
(1) nut-shell, calcite in powder are sent in charring furnace, calcination processing 3-4 hour at 510-635 DEG C, take out, be ground into powder, the powder to gained makes it seethe spray form epipremnum aureum extracting solution under condition in air blast, makes it mixing;
(2) silicon ash, tungstenalloy aggregate, anhydrite are calcined at 610-850 DEG C after 3-6 hour and take out, pulverize, spray 1 ‰ iron(ic) chloride and 0.5 ‰ calcium chloride composite solutions to evenly with spraying gun, dipping 10-12 hour;
(3) step (1), (2) reaction mass and other leftover materials are pulverized add suitable quantity of water stirring and evenly mixing and obtain slip, obtained slurry is added wall slab squeezing former is shaping, cutting, natural curing, to obtain final product.