CN104277332A - 一种苯乙烯弹性体土工格栅及其制备方法 - Google Patents
一种苯乙烯弹性体土工格栅及其制备方法 Download PDFInfo
- Publication number
- CN104277332A CN104277332A CN201410575583.0A CN201410575583A CN104277332A CN 104277332 A CN104277332 A CN 104277332A CN 201410575583 A CN201410575583 A CN 201410575583A CN 104277332 A CN104277332 A CN 104277332A
- Authority
- CN
- China
- Prior art keywords
- antioxidant
- styrenic elastomer
- geo
- grid
- minute
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种苯乙烯弹性体土工格栅,由下列重量份的组份原料加工而得:PP树脂70-80、苯乙烯类弹性体20-30、硬脂酸钡0.2-0.4、抗氧剂300 0.2-0.4、抗氧剂10760.1-0.2、紫外线吸收剂UV-90.1-0.3、改性填料25-35。苯乙烯弹性体土工格栅,将配方材料混炼,挤出,熔体通过三辊压光机成型板材,板材经过冲压机进行冲孔,孔板经过升温后拉伸,即制得土工格栅。本发明的加工出的改性土工格栅,拉伸强度高,耐腐蚀,机械性能好,生产加工成本低。
Description
技术领域
本发明涉及土工格栅的制造,具体涉及一种苯乙烯弹性体土工格栅及制备方法。
背景技术
随着土工合成材料行业的发展,越来越多的土工格栅产品推向了市场,土工格栅的主要竞争就是产品性能和价格成本竞争。由于聚丙烯土工格栅领域和使用区域广泛,因此对土工格栅要求其具有多种性能。但是只靠一种聚合物来实现这些性能是很难实现的,因此需要对土工格栅配方进行改性成为这个行业的必然趋势。 在制备高性能材料方面纤维增强是一种普遍而有效的方法,增强所用的纤维一般为玻璃纤维、碳纤维等。由这些纤维填充得到的树脂增强效果明显,能够使得相同规格的土工格栅更薄。但是使用玻璃纤维和碳纤维后,聚合物的拉伸伸长率又会有很大下降,导致土工格栅拉伸很短,产品单位面积重量上升,使得生产成本反而增加,不利于达到低成本化的目的。
在土工格栅中加入改性炭黑等填料,可使其具有较好的耐酸、耐碱、耐腐蚀和抗老化性能,提高抗冲击强度和拉伸强度。强度高、柔软。
发明内容
本发明提供了一种苯乙烯弹性体土工格栅及制备方法。本发明通过配方原材料的改性,从而得到具有强度高、韧性大、耐腐蚀性强等优点的土工格栅。
本发明所采用技术方案如下:
一种苯乙烯弹性体土工格栅,其特征在于,由下列重量份的组份原料加工而得:PP树脂70-80、苯乙烯类弹性体20-30、硬脂酸钡0.2-0.4、抗氧剂300 0.2-0.4、抗氧剂1076 0.1-0.2、紫外线吸收剂UV-9 0.1-0.3、改性填料25-35,
所述的苯乙烯类弹性体为苯乙烯—丁二烯—苯乙烯嵌段共聚物(SBS),
所述的改性填料的制备方法:a、按重量份称取下列组分原料:碳酸钙70-80,高岭土10-20、聚丙烯酸钠 0.3-0.5、白油1-3、抗氧化剂 1010 0.1-0.3、硬脂酸0.2-0.4、浓度为10-15%的氢氧化钠溶液 40-50、吐温80 0.1-0.3、硬脂酸钡2-4、氢氧化铝5-6、三乙醇胺硼酸酯 1-2;b、将碳酸钙、高岭土加入到氢氧化钠溶液,在60-70℃下研磨20-30分钟,然后将聚丙烯酸钠 、白油、硬脂酸加入其中,继续研磨5-10分钟,再加入吐温80、硬脂酸钡继续研磨10-15分钟,最后加入乙醇胺硼酸酯等余下组分,在75-80℃下研磨20-35分钟,然后经脱水、干燥、筛分制得改性填料。
所述的苯乙烯弹性体土工格栅的制备方法,其特征在于,包括以下步骤:
(1)按配方比例将PP树脂、苯乙烯类弹性体、硬脂酸钡、抗氧剂300、抗氧剂1076 、紫外线吸收剂UV-9投入到密炼机中,在120-140℃熔融密炼,得到密炼料A;
(2)将密炼料A和改性填料按比例混合后,投入挤出机加料斗中,再通过挤出机在低于 220℃温度下挤出,熔体通过三辊压光机成型板材,板材经过冲压机进行冲孔,孔板经过升温到80℃-98℃后拉伸,即制得苯乙烯弹性体土工格栅。
本发明取得的有益效果在于:
本发明与普通的土工格栅相比, 本发明在配方中将乙烯弹性体和聚丙烯混合改性,再添加改性填料,适量的助剂,调整适当的工艺参数,加工出的改性土工格栅 ,拉伸强度高,耐腐蚀,机械性能好,生产加工成本低。 改性土工格栅使得相同规格的土工格栅更薄,伸长率提高,消除了普通的土工格栅脆性大、易开裂的问题。 生产出的格栅在在相同厚度下,产品的强度提高 10%-13%;单肋长度提高 18%-20%;冲击强度提高 20%-30%。
具体实施方式
以下结合实施例对本发明作进一步说明,
一种苯乙烯弹性体土工格栅,由下列重量(kg)的组份原料加工而得:PP树脂75、所述的苯乙烯类弹性体为苯乙烯—丁二烯—苯乙烯嵌段共聚物(SBS) 25、硬脂酸钡0.3、抗氧剂300 0.3、抗氧剂1076 0.15、紫外线吸收剂UV-9 0.2、改性填料30,
其中,改性填料的制备方法:a、按重量份称取下列组分原料:碳酸钙75,高岭土15、聚丙烯酸钠 0.4、白油2、抗氧化剂 1010 0.2、硬脂酸0.3、浓度为14%的氢氧化钠溶液 45、吐温80 0.2、硬脂酸钡3、 氢氧化铝5、三乙醇胺硼酸酯 1.5; b、将碳酸钙、高岭土加入到氢氧化钠溶液,在60-70℃下研磨20-30分钟,然后将聚丙烯酸钠 、白油、硬脂酸加入其中,继续研磨5-10分钟,再加入吐温80、硬脂酸钡继续研磨10-15分钟,最后加入乙醇胺硼酸酯等余下组分,在75-80℃下研磨20-35分钟,然后经脱水、干燥、筛分制得改性填料。
苯乙烯弹性体土工格栅的制备方法,包括以下步骤:
(1)按配方比例将PP树脂、所述的苯乙烯类弹性体为苯乙烯—丁二烯—苯乙烯嵌段共聚物(SBS)、硬脂酸钡、抗氧剂300、抗氧剂1076 、紫外线吸收剂UV-9投入到密炼机中,在120-140℃熔融密炼,得到密炼料A;
(2)将密炼料A和改性填料按比例混合后,投入挤出机加料斗中,再通过挤出机在低于 220℃温度下挤出,熔体通过三辊压光机成型板材,板材经过冲压机进行冲孔,孔板经过升温到80℃-98℃后拉伸,即制得苯乙烯弹性体土工格栅。
本发明的土工格栅不同规格的性能检测值如下表:
Claims (2)
1.一种苯乙烯弹性体土工格栅,其特征在于,由下列重量份的组份原料加工而得:PP树脂70-80、苯乙烯类弹性体20-30、硬脂酸钡0.2-0.4、抗氧剂300 0.2-0.4、抗氧剂1076 0.1-0.2、紫外线吸收剂UV-9 0.1-0.3、改性填料25-35,
所述的苯乙烯类弹性体为苯乙烯—丁二烯—苯乙烯嵌段共聚物(SBS),
所述的改性填料的制备方法:a、按重量份称取下列组分原料:碳酸钙70-80,高岭土10-20、聚丙烯酸钠 0.3-0.5、白油1-3、抗氧化剂 1010 0.1-0.3、硬脂酸0.2-0.4、浓度为10-15%的氢氧化钠溶液 40-50、吐温80 0.1-0.3、硬脂酸钡2-4、氢氧化铝5-6、三乙醇胺硼酸酯 1-2;b、将碳酸钙、高岭土加入到氢氧化钠溶液,在60-70℃下研磨20-30分钟,然后将聚丙烯酸钠 、白油、硬脂酸加入其中,继续研磨5-10分钟,再加入吐温80、硬脂酸钡继续研磨10-15分钟,最后加入乙醇胺硼酸酯等余下组分,在75-80℃下研磨20-35分钟,然后经脱水、干燥、筛分制得改性填料。
2.根据权利要求1所述的苯乙烯弹性体土工格栅的制备方法,其特征在于,包括以下步骤:
(1)按配方比例将PP树脂、苯乙烯类弹性体、硬脂酸钡、抗氧剂300、抗氧剂1076 、紫外线吸收剂UV-9投入到密炼机中,在120-140℃熔融密炼,得到密炼料A;
(2)将密炼料A和改性填料按比例混合后,投入挤出机加料斗中,再通过挤出机在低于 220℃温度下挤出,熔体通过三辊压光机成型板材,板材经过冲压机进行冲孔,孔板经过升温到80℃-98℃后拉伸,即制得苯乙烯弹性体土工格栅。