CN104275294A - 一种铝材喷涂工艺 - Google Patents

一种铝材喷涂工艺 Download PDF

Info

Publication number
CN104275294A
CN104275294A CN201410513281.0A CN201410513281A CN104275294A CN 104275294 A CN104275294 A CN 104275294A CN 201410513281 A CN201410513281 A CN 201410513281A CN 104275294 A CN104275294 A CN 104275294A
Authority
CN
China
Prior art keywords
aluminum profiles
parts
aluminium
aluminum
spray coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410513281.0A
Other languages
English (en)
Inventor
王寿高
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410513281.0A priority Critical patent/CN104275294A/zh
Publication of CN104275294A publication Critical patent/CN104275294A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种铝材喷涂工艺，包括以下步骤：用80%的磷酸溶液对铝材表面进行冲洗，除去铝型材表面的油脂；常温下，用100-200g/L的NaOH冲洗除油后的铝材；用水清洗铝材表面；打砂表面光滑，无刺感；涂抹一道底漆；利用红外线照射对底漆进行烘烤；喷刷涂料，采用自动喷涂机对铝材表面喷涂，厚度为5-8μm；喷罩光漆，干膜厚度为2-4μm；常温下自然风干；检测、包装入库。喷涂工艺步骤简单、加工方便、成品质量高、大大降低成产成本；表面平整光洁、耐寒、耐腐蚀。

Description

一种铝材喷涂工艺
技术领域
本发明涉及一种金属表面的喷涂技术，具体涉及一种铝材喷涂工艺。
背景技术
工业中，喷漆工艺到处可见，喷漆的工艺也是多种多样，比较散乱无统一标准，以前的铝型材喷涂工艺不但步序繁琐，加工出来的铝板表面的漆面还不平整，底漆含较多有害成分，长期使用，对身体有害，不具备耐寒和防锈双重功能。
发明内容
本发明的目的在于克服现有技术存在的不足，提供一种铝材喷涂工艺。
为达到上述目的，本发明采取了如下的技术方案：一种铝材喷涂工艺，包括以下步骤：
a、清洗铝材表面：用80%的磷酸溶液对铝材表面进行冲洗，除去铝型材表面的油脂；
b、碱洗：常温下，用100-200g/L 的NaOH 冲洗除油后的铝材； 
c、水洗：用水清洗；
d、打砂表面光滑，无刺感；
e、涂抹一道底漆；
f、利用红外线照射对底漆进行烘烤；
g、喷刷涂料，采用自动喷涂机对铝材表面喷涂，厚度为5-8μm；
h、喷罩光漆，干膜厚度为2-4μm；
i、常温下自然风干；
j、检测、包装入库。
进一步，底漆成分包括氧化硅5份，硬脂酸丁酯5份，环烷酸锌5份，防沉剂1份，丙烯酸树脂5份，碳酸钙80份，盐酸10份。
本发明的有益效果是：喷涂工艺步骤简单、加工方便、成品质量高、大大降低成产成本；表面平整光洁、耐寒、耐腐蚀。
具体实施方式
下面结合具体实施例来对本发明作进一步的描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
一种铝材喷涂工艺，包括以下步骤：
a、清洗铝材表面：用80%的磷酸溶液对铝材表面进行冲洗，除去铝型材表面的油脂；
b、碱洗：常温下，用100-200g/L 的NaOH 冲洗除油后的铝材； 
c、水洗：用水清洗；
d、打砂表面光滑，无刺感；
e、涂抹一道底漆；
f、利用红外线照射对底漆进行烘烤；
g、喷刷涂料，采用自动喷涂机对铝材表面喷涂，厚度为5-8μm；
h、喷罩光漆，干膜厚度为2-4μm；
i、常温下自然风干；
j、检测、包装入库。
底漆成分包括氧化硅5份，硬脂酸丁酯5份，环烷酸锌5份，防沉剂1份，丙烯酸树脂5份，碳酸钙80份，盐酸10份。
上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进，这些改进也应视为本发明的保护范围。

Claims (2)

1. 一种铝材喷涂工艺，其特征在于：包括以下步骤：
a、清洗铝材表面：用80%的磷酸溶液对铝材表面进行冲洗，除去铝型材表面的油脂；
b、碱洗：常温下，用100-200g/L 的NaOH 冲洗除油后的铝材； 
c、水洗：用水清洗；
d、打砂表面光滑，无刺感；
e、涂抹一道底漆；
f、利用红外线照射对底漆进行烘烤；
g、喷刷涂料，采用自动喷涂机对铝材表面喷涂，厚度为5-8μm；
h、喷罩光漆，干膜厚度为2-4μm；
i、常温下自然风干；
j、检测、包装入库。
2.根据权利要求1所述的一种铝材喷涂工艺，其特征在于：所述底漆成分包括氧化硅5份，硬脂酸丁酯5份，环烷酸锌5份，防沉剂1份，丙烯酸树脂5份，碳酸钙80份，盐酸10份。
CN201410513281.0A 2014-09-29 2014-09-29 一种铝材喷涂工艺 Pending CN104275294A (zh)