CN104261860A - 一种无机保温墙板及其制备方法 - Google Patents
一种无机保温墙板及其制备方法 Download PDFInfo
- Publication number
- CN104261860A CN104261860A CN201410454600.5A CN201410454600A CN104261860A CN 104261860 A CN104261860 A CN 104261860A CN 201410454600 A CN201410454600 A CN 201410454600A CN 104261860 A CN104261860 A CN 104261860A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat insulation
- activated carbon
- stir
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种无机保温墙板,由下列重量份的原料制成：柠檬酸1-2、石膏3-5、粉煤灰15-20、聚合硫酸铁0.4-0.6、水性氧化叔胺2.2-2.5、锂蒙脱石8-12、重晶石3-4、明矾0.2-0.4、氧化铁2-3、铝粉3-5、水泥30-35、生石灰9-12、核桃壳粉2-3、碱式碳酸镁2-3、耐碱玻璃纤维网格布适量、改性活性炭25-30、水适量；本发明保温墙板具有较高的强度、低的导热系数，密度小，施工方便，耐热性能好，耐腐蚀，无污染，可以广泛用于民用、工业建筑的非承重内墙或外墙；通过使用改性活性炭，增加了保温性能，还具有持久抗菌、释放香气、有益人体健康的效果。
Description
技术领域
本发明属于建筑材料领域，尤其涉及一种无机保温墙板及其制备方法。
背景技术
随着建筑业的蓬勃发展，能源的不断枯竭，还有全球变暖的影响，降低建筑能耗，提高能源利用率，已受到全社会的关注和重视。目前建筑用的保温材料性能良莠不齐，存在强度低、保温性不够好、价格高、耐久性差、耐水和耐腐蚀性不好、对环境有污染、阻燃性不好等缺点，需要进行改进。
活性炭具有质量轻，孔隙发达，吸附性好的特点，如果加入保温材料中，不仅具有良好的保温性能。活性炭具有良好的吸附性能，能够吸附有益的物质、气味，再缓慢释放，起到有益于健康的作用。
发明内容
本发明的目的在于提供一种无机保温墙板及其制备方法，该保温墙板
本发明的技术方案如下：
一种无机保温墙板,其特征在于由下列重量份的原料制成：柠檬酸1-2、石膏3-5、粉煤灰15-20、聚合硫酸铁0.4-0.6、水性氧化叔胺2.2-2.5、锂蒙脱石8-12、重晶石3-4、明矾0.2-0.4、氧化铁2-3、铝粉3-5、水泥30-35、生石灰9-12、核桃壳粉2-3、碱式碳酸镁2-3、耐碱玻璃纤维网格布适量、改性活性炭25-30、水适量；
所述改性活性炭由下列重量份的原料制成：艾叶2-3、茶树叶2-3、樟树皮2-3、硅藻土2-3、檀木碎屑3-5、50-60%乙醇水溶液适量、活性炭20-25、硅烷偶联剂KH-550 0.5-0.7；制备方法为：将艾叶、茶树叶、樟树皮、檀木碎屑粉碎，加入25-30倍重量的50-60%乙醇水溶液，加热至70-80℃，搅拌30-40分钟，过滤得浆料，加入硅藻土，搅拌均匀；将活性炭粉碎成1-5mm的颗粒，加入所述浆料中，浸泡6-8个小时，烘干备用；将硅烷偶联剂KH-550加入5-6倍重量的50-60%乙醇水溶液，搅拌均匀，再均匀地喷洒在活性炭颗粒表面，边烘干边不停翻动活性炭颗粒，防止粘连，烘干至绝干，即得。
所述的无机保温墙板的制备方法，其特征在于包括以下步骤：
（1）将锂蒙脱石、重晶石、明矾、氧化铁混合，粉碎成100-200目颗粒，加入核桃壳粉，混合均匀，加入7-9%重量份的水，造粒，粒径在3-9mm，送入煅烧炉中，在300-400℃下预烧10-20分钟，在800-1000℃下烧结，取出得到颗粒；
（2）将水泥、石膏、粉煤灰、生石灰、改性活性炭、第（1）步得到的颗粒混合，送入砂浆搅拌机中搅拌均匀，按照水料比为0.3-0.5加入水，搅拌均匀得到浆料；
（3）将除铝粉、柠檬酸以外的其他剩余成分混合，加入第（2）步得到的浆料中搅拌均匀，加入铝粉、柠檬酸，搅拌均匀，得到保温芯材浆料；
（4）将墙板模具底层涂布一层耐碱玻璃纤维网格布，将保温芯材浆料浇筑到模具中，校平，再在上面涂布一层耐碱玻璃纤维网格布，经振捣成型、发泡、脱模、养护，即得。
本发明的有益效果
本发明保温墙板具有较高的强度、低的导热系数，密度小，施工方便，耐热性能好，耐腐蚀，无污染，可以广泛用于民用、工业建筑的非承重内墙或外墙；通过使用改性活性炭，增加了保温性能，还具有持久抗菌、释放香气、有益人体健康的效果。
具体实施方式
一种无机保温墙板,由下列重量份（公斤）的原料制成：柠檬酸1.5、石膏4、粉煤灰18、聚合硫酸铁0.5、水性氧化叔胺2.3、锂蒙脱石10、重晶石3.5、明矾0.3、氧化铁2.5、铝粉4、水泥33、生石灰11、核桃壳粉2.5、碱式碳酸镁2.5、耐碱玻璃纤维网格布适量、改性活性炭28、水适量；
所述改性活性炭由下列重量份（公斤）的原料制成：艾叶2.5、茶树叶2.5、樟树皮2.5、硅藻土2.5、檀木碎屑4、55%乙醇水溶液适量、活性炭23、硅烷偶联剂KH-550 0.6；制备方法为：将艾叶、茶树叶、樟树皮、檀木碎屑粉碎，加入28倍重量的55%乙醇水溶液，加热至75℃，搅拌35分钟，过滤得浆料，加入硅藻土，搅拌均匀；将活性炭粉碎成1-5mm的颗粒，加入所述浆料中，浸泡7个小时，烘干备用；将硅烷偶联剂KH-550加入5.5倍重量的55%乙醇水溶液，搅拌均匀，再均匀地喷洒在活性炭颗粒表面，边烘干边不停翻动活性炭颗粒，防止粘连，烘干至绝干，即得。
所述的无机保温墙板的制备方法，包括以下步骤：
（1）将锂蒙脱石、重晶石、明矾、氧化铁混合，粉碎成100-200目颗粒，加入核桃壳粉，混合均匀，加入8%重量份的水，造粒，粒径在3-9mm，送入煅烧炉中，在350℃下预烧15分钟，在900℃下烧结，取出得到颗粒；
（2）将水泥、石膏、粉煤灰、生石灰、改性活性炭、第（1）步得到的颗粒混合，送入砂浆搅拌机中搅拌均匀，按照水料比为0.4加入水，搅拌均匀得到浆料；
（3）将除铝粉、柠檬酸以外的其他剩余成分混合，加入第（2）步得到的浆料中搅拌均匀，加入铝粉、柠檬酸，搅拌均匀，得到保温芯材浆料；
（4）将墙板模具底层涂布一层耐碱玻璃纤维网格布，将保温芯材浆料浇筑到模具中，校平，再在上面涂布一层耐碱玻璃纤维网格布，经振捣成型、发泡、脱模、养护，即得。
实验数据：
测得厚度为120mm的保温墙板的性能如下：抗冲击性能(次)为19，抗弯破坏载荷（自重倍数）≥6，吊挂力（N）为1640，传热系数为0.45b/w/m.k，空气声隔声量（dB）为55，抗压强度（MPa）为5.5。
Claims (2)
1.一种无机保温墙板,其特征在于由下列重量份的原料制成：柠檬酸1-2、石膏3-5、粉煤灰15-20、聚合硫酸铁0.4-0.6、水性氧化叔胺2.2-2.5、锂蒙脱石8-12、重晶石3-4、明矾0.2-0.4、氧化铁2-3、铝粉3-5、水泥30-35、生石灰9-12、核桃壳粉2-3、碱式碳酸镁2-3、耐碱玻璃纤维网格布适量、改性活性炭25-30、水适量；
所述改性活性炭由下列重量份的原料制成：艾叶2-3、茶树叶2-3、樟树皮2-3、硅藻土2-3、檀木碎屑3-5、50-60%乙醇水溶液适量、活性炭20-25、硅烷偶联剂KH-550 0.5-0.7；制备方法为：将艾叶、茶树叶、樟树皮、檀木碎屑粉碎，加入25-30倍重量的50-60%乙醇水溶液，加热至70-80℃，搅拌30-40分钟，过滤得浆料，加入硅藻土，搅拌均匀；将活性炭粉碎成1-5mm的颗粒，加入所述浆料中，浸泡6-8个小时，烘干备用；将硅烷偶联剂KH-550加入5-6倍重量的50-60%乙醇水溶液，搅拌均匀，再均匀地喷洒在活性炭颗粒表面，边烘干边不停翻动活性炭颗粒，防止粘连，烘干至绝干，即得。
2.根据权利要求1所述的无机保温墙板的制备方法，其特征在于包括以下步骤：
（1）将锂蒙脱石、重晶石、明矾、氧化铁混合，粉碎成100-200目颗粒，加入核桃壳粉，混合均匀，加入7-9%重量份的水，造粒，粒径在3-9mm，送入煅烧炉中，在300-400℃下预烧10-20分钟，在800-1000℃下烧结，取出得到颗粒；
（2）将水泥、石膏、粉煤灰、生石灰、改性活性炭、第（1）步得到的颗粒混合，送入砂浆搅拌机中搅拌均匀，按照水料比为0.3-0.5加入水，搅拌均匀得到浆料；
（3）将除铝粉、柠檬酸以外的其他剩余成分混合，加入第（2）步得到的浆料中搅拌均匀，加入铝粉、柠檬酸，搅拌均匀，得到保温芯材浆料；
（4）将墙板模具底层涂布一层耐碱玻璃纤维网格布，将保温芯材浆料浇筑到模具中，校平，再在上面涂布一层耐碱玻璃纤维网格布，经振捣成型、发泡、脱模、养护，即得。