CN104250792A - 一种高精度铸铁件涂装前皮膜钝化液的配制方法 - Google Patents
一种高精度铸铁件涂装前皮膜钝化液的配制方法 Download PDFInfo
- Publication number
- CN104250792A CN104250792A CN201310268948.0A CN201310268948A CN104250792A CN 104250792 A CN104250792 A CN 104250792A CN 201310268948 A CN201310268948 A CN 201310268948A CN 104250792 A CN104250792 A CN 104250792A
- Authority
- CN
- China
- Prior art keywords
- acid
- benzotriazole
- high precision
- preparation
- sodium carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高精度铸铁件涂装前皮膜钝化液的配制方法，该钝化液组成为：植酸10-12％，酒石酸1-2％，柠檬酸0.5-1.5％，溴酸0.5-0.7％，苯甲酸钠2.5-3.5％，苯骈三氮唑0.35-0.55％，三乙醇胺3.5-4.5％，碳酸钠2.3-2.7％，异噻咪唑酮0.4-0.6％，工业酒精1-2％，余量为水；配制方法为：将水加入到反应釜中，开动搅拌器，按300-400转/min的速度搅拌，再依次加入酒石酸、柠檬酸、溴酸、苯甲酸钠、碳酸钠、三乙醇胺、植酸，每加一种材料都要连续搅拌6-12min；再用工业酒精将苯骈三氮唑和异噻咪唑酮溶解好后也加入到反应釜中，加完后继续搅拌30-40分钟即可。
Description
技术领域
本发明涉及表面处理技术领域，尤其涉及一种高精度铸铁件涂装前皮膜钝化液的配制方法。
背景技术
铸铁工件在喷涂涂装前应该通过磷化处理，使其表面生成一层有一定粗糙度，具有多孔性吸附性的磷化膜。这层磷化膜的主要作用在于：一是增强铸铁工件基本表面与喷涂涂层之间的附着力；二是提高联合涂层的综合耐大气中腐蚀性介质的侵蚀。但是对于高精度铸铁件，技术条件规定不允许采用磷化工艺进行前处理，而要求进行钝化处理形成达标的皮膜钝化层。
一般对加工工件的技术要求是：铸铁毛坯经过机械加工后表面先进行喷丸处理；经喷处理后的零部件必须进行皮膜钝化处理；对于做好的皮膜钝化膜层进行防锈，要求采用水剂防锈处理，不得采用防锈油；对于铸铁工件经过上述处理后得保证三个月的防锈期，并且通过海上运输不能生锈；对工件进行组合装配成整机后，直接喷涂环氧基底漆和面漆，不能影响喷涂涂装漆层的结合力。
达到上述的技术要求，需要解决的核心技术主要有两点：一是在常温条件下，在工艺规定的时间内，在工艺参数确定的工作液中，能够在铸铁工件表面上实现连接完整致密的皮膜钝化的化学反应，生成膜，膜厚达标。具有可靠的吸附性、附着性、防锈性以及满足喷涂涂层结合强度的皮膜钝化膜。二是在皮膜钝化膜表面上再覆盖一层水剂防锈保护膜，同时要求这层保护膜不仅对钝化膜实施固膜处理，保证工件表面六个月的周期内并通过海上运输不生锈，更重要的是直接实施喷涂涂装不影响漆层的结合力。
发明内容
本发明的目的在于提出一种高精度铸铁件涂装前皮膜钝化液的配制方法，该方法配制的钝化液通过对组份的调整，满足高精度铸铁件的涂装前技术要求。
为达此目的，本发明采用以下技术方案：
一种高精度铸铁件涂装前皮膜钝化液的配制方法，该钝化液以重量百分数计由下列组份组成：植酸10-12％，酒石酸1-2％，柠檬酸0.5-1.5％，溴酸0.5-0.7％，苯甲酸钠2.5-3.5％，苯骈三氮唑0.35-0.55％，三乙醇胺3.5-4.5％，碳酸钠2.3-2.7％，异噻咪唑酮0.4-0.6％，工业酒精1-2％，余量为水；所述配制方法为：将计量的水加入到反应釜中，在常温常压下开动搅拌器，按300-400转/min的速度进行搅拌，并依次加入酒石酸、柠檬酸、溴酸、苯甲酸钠、碳酸钠、三乙醇胺、植酸，每加一种材料都要连续搅拌6-12min；再用工业酒精将苯骈三氮唑和异噻咪唑酮溶解好后也加入到反应釜中，加完所有的材料后继续搅拌30-40分钟即可。
本发明具有如下技术效果：
本发明配制的钝化液为常温钝化液，其中无铬酸，磷酸，重铬酸钾，重铬酸钠，钼酸钠或亚硝酸盐等有毒有害物质，对操作人员及环境没有任何影响。
采用本发明配制的钝化液生成的皮膜厚度适宜，不影响铸铁件的精度，同时具有可靠的吸附性、附着性、防锈性，并且满足喷涂涂层结合强度的要求。
具体实施方式
实施例一
一种高精度铸铁件涂装前皮膜钝化液的配制方法，该钝化液以重量百分数计由下列组份组成：植酸10％，酒石酸2％，柠檬酸0.5％，溴酸0.7％，苯甲酸钠2.5％，苯骈三氮唑0.55％，三乙醇胺3.5％，碳酸钠2.7％，异噻咪唑酮0.4％，工业酒精2％，余量为水；所述配制方法为：将计量的水加入到反应釜中，在常温常压下开动搅拌器，按300转/min的速度进行搅拌，并依次加入酒石酸、柠檬酸、溴酸、苯甲酸钠、碳酸钠、三乙醇胺、植酸，每加一种材料都要连续搅拌12min；再用工业酒精将苯骈三氮唑和异噻咪唑酮溶解好后也加入到反应釜中，加完所有的材料后继续搅拌30分钟即可。
实施例二
一种高精度铸铁件涂装前皮膜钝化液的配制方法，该钝化液以重量百分数计由下列组份组成：植酸12％，酒石酸1％，柠檬酸1.5％，溴酸0.5％，苯甲酸钠3.5％，苯骈三氮唑0.35％，三乙醇胺4.5％，碳酸钠2.3％，异噻咪唑酮0.6％，工业酒精1％，余量为水；所述配制方法为：将计量的水加入到反应釜中，在常温常压下开动搅拌器，按400转/min的速度进行搅拌，并依次加入酒石酸、柠檬酸、溴酸、苯甲酸钠、碳酸钠、三乙醇胺、植酸，每加一种材料都要连续搅拌6min；再用工业酒精将苯骈三氮唑和异噻咪唑酮溶解好后也加入到反应釜中，加完所有的材料后继续搅拌40分钟即可。
实施例三
一种高精度铸铁件涂装前皮膜钝化液的配制方法，该钝化液以重量百分数计由下列组份组成：植酸11％，酒石酸1.5％，柠檬酸1.0％，溴酸0.6％，苯甲酸钠3.0％，苯骈三氮唑0.45％，三乙醇胺4.0％，碳酸钠2.5％，异噻咪唑酮0.5％，工业酒精1-2％，余量为水；所述配制方法为：将计量的水加入到反应釜中，在常温常压下开动搅拌器，按350转/min的速度进行搅拌，并依次加入酒石酸、柠檬酸、溴酸、苯甲酸钠、碳酸钠、三乙醇胺、植酸，每加一种材料都要连续搅拌8min；再用工业酒精将苯骈三氮唑和异噻咪唑酮溶解好后也加入到反应釜中，加完所有的材料后继续搅拌35分钟即可。
Claims (1)
1.一种高精度铸铁件涂装前皮膜钝化液的配制方法，其特征在于，该钝化液以重量百分数计由下列组份组成：植酸10-12％，酒石酸1-2％，柠檬酸0.5-1.5％，溴酸0.5-0.7％，苯甲酸钠2.5-3.5％，苯骈三氮唑0.35-0.55％，三乙醇胺3.5-4.5％，碳酸钠2.3-2.7％，异噻咪唑酮0.4-0.6％，工业酒精1-2％，余量为水；所述配制方法为：将计量的水加入到反应釜中，在常温常压下开动搅拌器，按300-400转/min的速度进行搅拌，并依次加入酒石酸、柠檬酸、溴酸、苯甲酸钠、碳酸钠、三乙醇胺、植酸，每加一种材料都要连续搅拌6-12min；再用工业酒精将苯骈三氮唑和异噻咪唑酮溶解好后也加入到反应釜中，加完所有的材料后继续搅拌30-40分钟即可。