CN104231458A - Epsa改性保温隔热防火材料 - Google Patents
Epsa改性保温隔热防火材料 Download PDFInfo
- Publication number
- CN104231458A CN104231458A CN201310242592.3A CN201310242592A CN104231458A CN 104231458 A CN104231458 A CN 104231458A CN 201310242592 A CN201310242592 A CN 201310242592A CN 104231458 A CN104231458 A CN 104231458A
- Authority
- CN
- China
- Prior art keywords
- epsa
- agent
- heat preservation
- water
- percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种EPSA改性保温隔热防火材料由77%EPS聚苯颗粒、3%促进剂、10%胶炼剂,加入添加剂:5%粉剂、1%偶联剂、1%发泡剂、3%防水剂配方组成。经混合产生化学反应发泡膨胀形成制品,同时制品能抗折抗压,具备保温、隔热、防火、防水功能,其防火性能指标达到A级。是一种十分理想的轻型的保温隔热防火材料。
Description
技术领域:
本发明涉及内外墙保温隔热防火材料,适用于建筑物内外墙保温隔热防火。也可以用于管道、锅炉、热水箱等的保温隔热。
背景技术
能源和材料是我国国民经济的基础,同时也是我国国民经济发展的瓶颈,节能已经成为我国的基本国策。我国的建筑能耗约总全国总能耗的30%,在我国建筑业飞速发展的今天,如果不注意节能产品的使用,建筑能耗比例将随着建筑物的增加而增大。使用轻质、保温、隔热的建筑材料是降低能耗的有效措施之一。住建部和公安部于2009年46号及2011年公安部消防局65文规定凡建筑物外墙必须安装使用保温隔热防火达到A级要求的装饰材料。现市场上仅采用国家标准B级的装饰材料,所以研发国家标准A级水平的保温隔热防火材料迫在眉睫。
发明内容
本发明的目的是提供一种经济型、重量轻、且保温、隔热、防火、防水的EPS聚苯内外墙保温隔热材料。其技术指标达到国家标准A级水平。
本发明的技术是这样完成的。
一种内外墙保温隔热防火材料,其特征在于采用下述原材料配方组成。
77%EPS聚苯颗粒、3%促进剂、10%胶炼剂为主体,加入添加剂:5%粉剂、1%偶联剂、1%发泡剂、3%防水剂。
EPS聚苯颗粒、促进剂、胶炼剂为主体混合后产生化学反应迅速发泡膨胀,具备保温隔热防火阻燃功能。外墙隔热保温材料首先要有良好的阻燃性,我们用明火直接对试验件燃烧,经20分钟后试验件仍完好无损,既未熔化也未变软,仅出现碳化点。
而加入发泡剂可以将制品密度降低到0.18g/cm3-0.26g/cm3,并有较高的强度以满足成型和施工需要。
掺和粉剂提高制品的抗折和抗压强度,防止收缩裂缝,同时制品密度没有明显变化,提高强度。
偶联剂不与其他材料产生化学反应,完全是通过物理作用改善制品的工作性能和力学性能,对制品的稳定性能起到很好作用。
防水剂防止雨水进入制品。使制品有良好的防水性能,我们将试件放入水中浸泡经过一小时取出,吸水量仅占10%。
上述配方组成起到很好的保温、隔热、防火、防水、隔音的作用,同时有良好的抗折抗压强度,轻质、剥离性能好、粘接强度高、导热系数低等特点,制品达到国家标准保温隔热防火材料A级水平。
具体实施方式:
我们经过30多次的试制,制定了成熟的工艺路线,将原材料77%EPS聚苯颗粒、3%促进剂、10%胶炼剂为主体,加入添加剂:5%粉剂、1%偶联剂、1%发泡剂、3%防水剂按比例称出重量,放入搅拌机混合均匀好后发泡膨胀。
将混合好的原浆流入模具中经加温加压成型后养护24小时以上即可取出待用。制品可做成30mm,40mm,50mm厚度满足各种环境的需要。
原材料----搅拌----成型----加温加压----养护----裁剪----包装出厂。
Claims (5)
1.一种EPSA改性保温隔热防火材料,采用77%EPS聚苯颗粒、3%促进剂、10%胶炼剂,添加剂:5%粉剂、1%偶联剂、1%发泡剂、3%防水剂配方组成,其特征在于采用EPS聚苯颗粒,促进剂,胶炼剂为主体,经化学反应发泡膨胀,加入添加剂:粉剂、偶联剂、发泡剂、防水剂,使其制品能抗折、抗压、重量轻,具备保温、隔热、防火、防水功能,其防火性能指标达到A级。
2.根据权利要求1所述EPSA改性保温隔热防火材料,其特征在于添加了偶联剂,有效防止制品吸潮反卤。
3.根据权利要求1所述EPSA改性保温隔热防火材料,其特征在于加入了粉剂对制品性能起稳定作用,以防止收缩裂缝,提高抗折、抗压强度。
4.根据权利要求1所述EPSA改性保温隔热防火材料,其特征在于加入了发泡剂,降低了制品密度,使制品达到0.180g/cm3~0.260g/cm3,从而使制品降低导热系数,其导热系数达到0.048w/m.k-0.08w/m.k。
5.根据权利要求1所述EPSA改性保温隔热防火材料,其特征在于加入了防水剂,使其制品降低了吸水率,提高粘接强度及剥离性能。