CN102775690A - 阻燃型聚苯乙烯保温材料及其制备方法 - Google Patents

阻燃型聚苯乙烯保温材料及其制备方法 Download PDF

Info

Publication number
CN102775690A
CN102775690A CN201210282275XA CN201210282275A CN102775690A CN 102775690 A CN102775690 A CN 102775690A CN 201210282275X A CN201210282275X A CN 201210282275XA CN 201210282275 A CN201210282275 A CN 201210282275A CN 102775690 A CN102775690 A CN 102775690A
Authority
CN
China
Prior art keywords
flame
polystyrene
eps
fire retardant
retarding agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201210282275XA
Other languages
English (en)
Inventor
李斯发
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Boheng Building Materials Technology Development Co.,Ltd.
Original Assignee
SHANGHAI BOHENG BUILDING MATERIALS TECHNOLOGY DEVELOPMENT CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI BOHENG BUILDING MATERIALS TECHNOLOGY DEVELOPMENT CO LTD filed Critical SHANGHAI BOHENG BUILDING MATERIALS TECHNOLOGY DEVELOPMENT CO LTD
Priority to CN201210282275XA priority Critical patent/CN102775690A/zh
Publication of CN102775690A publication Critical patent/CN102775690A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种阻燃型聚苯乙烯保温材料，其特征在于：主要成分及重量百分比为：聚苯乙烯EPS发泡颗粒80％-90％、高效阻燃剂10％-20％，所述高效阻燃剂的成分及重量百分比为：氢氧化镁阻燃剂3-5％、超细石墨1％-6％、高岭土1％-3％、颜料1-3％、水3％；所述的阻燃型聚苯乙烯保温材料制备方法，包括以下步骤：(1)按原料配比将氢氧化镁阻燃剂、超细石墨、高岭土、颜料、水混合搅拌均匀；(2)将制成的高效阻燃剂与聚苯乙烯EPS发泡颗粒进行混合搅拌均匀后在常温下风干3-5分钟，形成高效阻燃剂均匀包裹聚苯乙烯EPS发泡颗粒状态；(3)将步骤(2)中高效阻燃剂均匀包裹聚苯乙烯EPS发泡颗粒的混合物放入模型压制机压制成型，切割成任何尺寸板材。本发明具有制造简单、质轻、防火、保温效果佳的优点。

Description

阻燃型聚苯乙烯保温材料及其制备方法
技术领域
本发明涉及一种防火保温材料，尤其涉及一种阻燃型聚苯乙烯(EPS)保温材料，还涉及该阻燃型聚苯乙烯(EPS)保温材料的制备方法。
背景技术
在我国大力推广建筑节能的形势下，所有的建筑都应达到相应的节能标准，但目前绝大多少保温材料为有机物，在具体实施过程中，保温和防火的矛盾十分突出，目前占据我国建筑物外墙保温材料市场约80％份额为有机材料，外墙保温工程中应用最广泛的发泡聚苯(EPS)板、挤塑聚苯板(XPS)，以及喷涂聚氨酯(SPU)、聚苯颗粒等，然而有机材料的易燃性很难解决，也因此酿成多起重大火灾事故；防火性能好的多为无机材料，如膨胀珍珠岩、中空玻化微珠、闭孔珍珠岩、岩棉、矿棉、玻璃棉等，而无机材料的保温效果又比较差，无法达到目前建筑物外墙保温要求的节能标准。有机材料不防火，与无机材料保温性能差一直是建筑物外墙保温材料突出的矛盾，因此提供和推广一种阻燃型保温材料非常有必要。
发明内容
有鉴于此，本发明所要解决的技术问题是：提供一种节能、含有高效阻燃剂的颗粒状可发性聚苯乙烯(EPS)保温材料，来达到防火保温的要求。
为了达到上述目的，本发明采用如下技术方案来实现的：一种阻燃型聚苯乙烯保温材料，主要成分及重量百分比为：聚苯乙烯EPS发泡颗粒80％-90％、高效阻燃剂10％-20％，所述高效阻燃剂的成分及重量百分比为：氢氧化镁阻燃剂3-5％、超细石墨1％-6％、高岭土1％-3％、颜料1-3％、水3％。作为优选，所述颜料为镉红。
阻燃型聚苯乙烯保温材料制备方法，包括以下步骤：
(1)高效阻燃剂的制作：按原料配比将氢氧化镁阻燃剂、超细石墨、高岭土、颜料、水混合搅拌均匀。
(2)按原料配比将步骤(1)制成的高效阻燃剂与聚苯乙烯EPS发泡颗粒进行混合搅拌均匀后在常温下风干3-5分钟，形成高效阻燃剂均匀包裹聚苯乙烯EPS发泡颗粒状态。
(3)成型：将步骤(2)中高效阻燃剂均匀包裹聚苯乙烯EPS发泡颗粒的混合物放入模型压制机压制成型，切割成任何尺寸板材。
本发明的中聚苯乙烯EPS发泡颗粒具有很好的保温性能，氢氧化镁具有阻燃作用，石墨也具有隔离空气起着阻燃的效果，加入高岭土使得整个阻燃剂有着很好的粘结作用，氢氧化镁阻燃剂、超细石墨、颜料、高岭土、水按一定比例混合搅拌均匀制得高效阻燃剂具有很好的阻燃效果和粘结性能。本发明通过将高效阻燃剂与聚苯乙烯EPS发泡颗粒进行混合搅拌均匀后在常温下风干，形成阻燃剂均匀包裹聚苯乙烯EPS发泡颗粒状态，这使得聚苯乙烯EPS发泡颗粒整体被高效阻燃剂给包裹，形成了很好的与空气隔离效果，起着阻燃、保温和抗压作用。采用建筑材料不燃性试验方法国家标准对本发明的材料进行试验为A级不燃物。
由上述技术方案可在，本发明的有益效果是：
相比现有技术，本发明通过将高效阻燃剂均匀包裹聚苯乙烯EPS发泡颗粒，使得聚苯乙烯EPS发泡颗粒与空气隔离的更彻底，因而阻燃效果更好、保温效果也更好，制造简单、质轻、防火、保温效果佳。
具体实施方式
为了使本领域技术人员能更进一步了解本发明的特征及技术内容，本发明将通过以下实施例进行说明。
原料配比：
Figure BSA00000761769000021
混合搅拌均匀制得高效阻燃剂；
将制成的高效阻燃剂与43kg的聚苯乙烯EPS发泡颗粒进行混合搅拌均匀后在常温下风干3-5分钟，形成阻燃剂均匀包裹聚苯乙烯EPS发泡颗粒状态，然后将高效阻燃剂均匀包裹聚苯乙烯EPS发泡颗粒的混合物放入模型压制机压制成型，切割成任何尺寸板材。

Claims (3)

1.阻燃型聚苯乙烯保温材料，其特征在于：主要成分及重量百分比为：聚苯乙烯EPS发泡颗粒80％-90％、高效阻燃剂10％-20％，所述高效阻燃剂的成分及重量百分比为：氢氧化镁阻燃剂3-5％、超细石墨1％-6％、高岭土1％-3％、颜料1-3％、水3％。
2.如权利要求1所述的阻燃型聚苯乙烯保温材料，其特征在于：所述颜料为镉红。
3.如权利要求1所述的阻燃型聚苯乙烯保温材料制备方法，包括以下步骤：
(1)高效阻燃剂的制作：按原料配比将氢氧化镁阻燃剂、超细石墨、高岭土、颜料、水混合搅拌均匀。
(2)按原料配比将步骤(1)制成的高效阻燃剂与聚苯乙烯EPS发泡颗粒进行混合搅拌均匀后在常温下风干3-5分钟，形成高效阻燃剂均匀包裹聚苯乙烯EPS发泡颗粒状态。
(3)成型：将步骤(2)中高效阻燃剂均匀包裹聚苯乙烯EPS发泡颗粒的混合物放入模型压制机压制成型，切割成任何尺寸板材。
CN201210282275XA 2012-08-09 2012-08-09 阻燃型聚苯乙烯保温材料及其制备方法 Pending CN102775690A (zh)