CN104212390A - High-efficient ceramic binding agent - Google Patents
High-efficient ceramic binding agent Download PDFInfo
- Publication number
- CN104212390A CN104212390A CN201410321798.XA CN201410321798A CN104212390A CN 104212390 A CN104212390 A CN 104212390A CN 201410321798 A CN201410321798 A CN 201410321798A CN 104212390 A CN104212390 A CN 104212390A
- Authority
- CN
- China
- Prior art keywords
- parts
- bentonite
- phthalates
- methyl
- barium sulfate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-efficient ceramic binding agent which is composed of following raw materials including 2-3 parts of silicon powder, 3-5 parts of diatom ooze, 6-8 parts of mica powder, 9-12 parts of bentonite, 5-10 parts of magnesium oxide, 10-12 parts of barium sulfate, 3-6 parts of calcium carbonate, 4-8 parts of calcium oxide, 2-6 parts of tetraethoxysilane, 3-5 parts of vinyltrimethoxysilane, 1-3 parts of aminopropyltriethoxysilane, 3-5 parts of 2-bromoisobutyryl bromide, 6-10 parts of diethylene triamine pentamethylene phosphonic acid, 3-5 parts of pentamethyldiethylenetriamine, 5-8 parts of diisobutyl phthalate, 3-5 parts of 2-methyl-2-propanol, 4-6 parts of potassium biphthalate, 100-120 parts of phenol-formaldehyde resin and 50-80 parts of petroleum resin. The high-efficient ceramic binding agent is used for binding and repairing of a ceramic product, can cure at normal temperature, is high in binding strength, and is acid-resistant, alkali-resistant and corrosion-resistant.
Description
Technical field
The present invention relates to a kind of technical field of tackiness agent, particularly relate to a kind of ceramic high-efficiency tackiness agent.
Background technology
Pottery is the general name of pottery and porcelain, and material is oxide compound, nitride, boride and carbide etc. mostly.Common stupalith clay, aluminum oxide and kaolin etc., general hardness is higher, but plasticity-is poor.Except using on common tableware, ornament, in the development of science, technology, also play important role.Present ceramic smooth surface, has good erosion resistance, but easily damaged, and slight shock just may occur slight crack or partial exfoliation, repairs timely and can retrieve partial loss, avoid occurring more serious damage.
Summary of the invention
The object of the invention is the shortcoming in order to overcome above-mentioned prior art, providing a kind of ceramic high-efficiency tackiness agent, this ceramic high-efficiency tackiness agent is used for the bonding of ceramic or repairing, have ambient temperature curing, cohesive strength is high, acid and alkali-resistance and the advantage such as corrosion-resistant.
The technical solution adopted for the present invention to solve the technical problems is: a kind of ceramic high-efficiency tackiness agent, be made up of the feed composition of following number: 2-3 part silica flour, 3-5 part diatom ooze, 6-8 part mica powder, 9-12 part bentonite, 5-10 part magnesium oxide, 10-12 part barium sulfate, 3-6 part calcium carbonate, 4-8 part calcium oxide, 2-6 part tetraethoxy, 3-5 part vinyltrimethoxy silane, 1-3 part aminopropyl triethoxysilane, 3-5 part 2-bromine isobutyl acylbromide, 6-10 part diethylene triamine pentamethylene phosphonic, 3-5 part pentamethyl-diethylenetriamine, 5-8 part diisobutyl phthalate, 3-5 part 2-methyl-2-propanol, 4-6 part Potassium Hydrogen Phthalate, 100-120 part resol, 50-80 part petroleum resin.
Further, the number of each feed composition is: 2 parts of silica flours, 3 parts of diatom oozes, 6 parts of mica powders, 9 parts of bentonite, 5 parts of magnesium oxide, 10 parts of barium sulfate, 3 parts of calcium carbonate, 4 parts of calcium oxide, 2 parts of tetraethoxys, 3 parts of vinyltrimethoxy silanes, 1 part of aminopropyl triethoxysilane, 3 parts of 2-bromine isobutyl acylbromides, 6 parts of diethylene triamine pentamethylene phosphonics, 3 parts of pentamethyl-diethylenetriamines, 5 parts of diisobutyl phthalates, 3 parts of 2-methyl-2-propanols, 4 parts of Potassium Hydrogen Phthalates, 100 parts of resol, 50 parts of petroleum resin.
Or the number of each feed composition is: 3 parts of silica flours, 5 parts of diatom oozes, 8 parts of mica powders, 12 parts of bentonite, 10 parts of magnesium oxide, 12 parts of barium sulfate, 6 parts of calcium carbonate, 8 parts of calcium oxide, 6 parts of tetraethoxys, 5 parts of vinyltrimethoxy silanes, 3 parts of aminopropyl triethoxysilanes, 5 parts of 2-bromine isobutyl acylbromides, 10 parts of diethylene triamine pentamethylene phosphonics, 5 parts of pentamethyl-diethylenetriamines, 8 parts of diisobutyl phthalates, 5 parts of 2-methyl-2-propanols, 6 parts of Potassium Hydrogen Phthalates, 120 parts of resol, 80 parts of petroleum resin.
In sum, ceramic high-efficiency tackiness agent of the present invention is used for the bonding of ceramic or repairing, have ambient temperature curing, cohesive strength is high, acid and alkali-resistance and the advantage such as corrosion-resistant.
Embodiment
Embodiment 1
A kind of ceramic high-efficiency tackiness agent described by the present embodiment 1, be made up of the feed composition of following number: 2 parts of silica flours, 3 parts of diatom oozes, 6 parts of mica powders, 9 parts of bentonite, 5 parts of magnesium oxide, 10 parts of barium sulfate, 3 parts of calcium carbonate, 4 parts of calcium oxide, 2 parts of tetraethoxys, 3 parts of vinyltrimethoxy silanes, 1 part of aminopropyl triethoxysilane, 3 parts of 2-bromine isobutyl acylbromides, 6 parts of diethylene triamine pentamethylene phosphonics, 3 parts of pentamethyl-diethylenetriamines, 5 parts of diisobutyl phthalates, 3 parts of 2-methyl-2-propanols, 4 parts of Potassium Hydrogen Phthalates, 100 parts of resol, 50 parts of petroleum resin.
Embodiment 2
A kind of ceramic high-efficiency tackiness agent described by the present embodiment 2, be made up of the feed composition of following number: 3 parts of silica flours, 5 parts of diatom oozes, 8 parts of mica powders, 12 parts of bentonite, 10 parts of magnesium oxide, 12 parts of barium sulfate, 6 parts of calcium carbonate, 8 parts of calcium oxide, 6 parts of tetraethoxys, 5 parts of vinyltrimethoxy silanes, 3 parts of aminopropyl triethoxysilanes, 5 parts of 2-bromine isobutyl acylbromides, 10 parts of diethylene triamine pentamethylene phosphonics, 5 parts of pentamethyl-diethylenetriamines, 8 parts of diisobutyl phthalates, 5 parts of 2-methyl-2-propanols, 6 parts of Potassium Hydrogen Phthalates, 120 parts of resol, 80 parts of petroleum resin.
The above is only preferred embodiment of the present invention, not does any pro forma restriction to technical scheme of the present invention.Every above embodiment is done according to technical spirit of the present invention any simple modification, equivalent variations and modification, all still belong in the scope of technical scheme of the present invention.
Claims (3)
1. a ceramic high-efficiency tackiness agent, it is characterized in that, be made up of the feed composition of following number: 2-3 part silica flour, 3-5 part diatom ooze, 6-8 part mica powder, 9-12 part bentonite, 5-10 part magnesium oxide, 10-12 part barium sulfate, 3-6 part calcium carbonate, 4-8 part calcium oxide, 2-6 part tetraethoxy, 3-5 part vinyltrimethoxy silane, 1-3 part aminopropyl triethoxysilane, 3-5 part 2-bromine isobutyl acylbromide, 6-10 part diethylene triamine pentamethylene phosphonic, 3-5 part pentamethyl-diethylenetriamine, 5-8 part diisobutyl phthalate, 3-5 part 2-methyl-2-propanol, 4-6 part Potassium Hydrogen Phthalate, 100-120 part resol, 50-80 part petroleum resin.
2. a kind of ceramic high-efficiency tackiness agent according to claim 1, it is characterized in that, the number of each feed composition is: 2 parts of silica flours, 3 parts of diatom oozes, 6 parts of mica powders, 9 parts of bentonite, 5 parts of magnesium oxide, 10 parts of barium sulfate, 3 parts of calcium carbonate, 4 parts of calcium oxide, 2 parts of tetraethoxys, 3 parts of vinyltrimethoxy silanes, 1 part of aminopropyl triethoxysilane, 3 parts of 2-bromine isobutyl acylbromides, 6 parts of diethylene triamine pentamethylene phosphonics, 3 parts of pentamethyl-diethylenetriamines, 5 parts of diisobutyl phthalates, 3 parts of 2-methyl-2-propanols, 4 parts of Potassium Hydrogen Phthalates, 100 parts of resol, 50 parts of petroleum resin.
3. a kind of ceramic high-efficiency tackiness agent according to claim 1, it is characterized in that, the number of each feed composition is: 3 parts of silica flours, 5 parts of diatom oozes, 8 parts of mica powders, 12 parts of bentonite, 10 parts of magnesium oxide, 12 parts of barium sulfate, 6 parts of calcium carbonate, 8 parts of calcium oxide, 6 parts of tetraethoxys, 5 parts of vinyltrimethoxy silanes, 3 parts of aminopropyl triethoxysilanes, 5 parts of 2-bromine isobutyl acylbromides, 10 parts of diethylene triamine pentamethylene phosphonics, 5 parts of pentamethyl-diethylenetriamines, 8 parts of diisobutyl phthalates, 5 parts of 2-methyl-2-propanols, 6 parts of Potassium Hydrogen Phthalates, 120 parts of resol, 80 parts of petroleum resin.