CN104058775A - Refractory ceramic fiber board - Google Patents
Refractory ceramic fiber board Download PDFInfo
- Publication number
- CN104058775A CN104058775A CN201410314868.9A CN201410314868A CN104058775A CN 104058775 A CN104058775 A CN 104058775A CN 201410314868 A CN201410314868 A CN 201410314868A CN 104058775 A CN104058775 A CN 104058775A
- Authority
- CN
- China
- Prior art keywords
- parts
- oxide
- fibers
- ceramic fiber
- fiber board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a refractory ceramic fiber board. The refractory ceramic fiber board comprises, by weight, 20-60 parts of glass fibers, 30-50 parts of mineral fibers, 5-7 parts of aluminum oxide, 5-8 parts of chromic oxide, 6-10 parts of polyester fibers, 80-100 parts of linen fibers, 40-50 parts of carbon fibers, 3-8 parts of magnesium oxide, 5-10 parts of silicon oxide, 5-10 parts of polyethylene glycol, 3-5 parts of sodium hexametaphosphate, 5-8 parts of lauryl sodium sulfate, 10-15 parts of organic silicon defoaming agents, 3-8 parts of paraffin, 5-10 parts of rubber, 10-25 parts of resin, 12-20 parts of polybutadiene latex and 15-18 parts of butylbenzene latex. When at high temperature, the refractory ceramic fiber board can bear high temperature more than 1000 DEG C, and binding force is not lost; when at low temperature, the refractory ceramic fiber board has good binding and dispersing performance, fibers are evenly dispersed in the whole product manufacturing technological process, and service life is effectively prolonged.
Description
Technical field
The present invention relates to the technical field of ceramic beaverboard, relate in particular to a kind of pyroceram fibre plate.
Background technology
At present, ceramic limiting plate is except having corresponding loose shape ceramic fiber cotton premium properties, and product quality is hard, and toughness and good strength have good weather-proof ability.Heating is not expanded, quality is light, easy construction, and shear-bow is arbitrarily the ideal energy saving material of cellar for storing things stove, pipeline and other heat-preserving equipments.
When ceramic beaverboard prepared by prior art runs into high temperature, itself has just lost bonding force, presents loose condition (of surface).
Summary of the invention
The object of the invention is the shortcoming in order to overcome above-mentioned prior art, a kind of pyroceram fibre plate is provided, this pyroceram fibre plate, in the time running into high temperature, can bear 1000 DEG C of above high temperature, and not lose cohesive force; In the time of low temperature, there is good combination and dispersing property, in whole production technological process, play fiber dispersion and evenly wait effect.
The technical solution adopted for the present invention to solve the technical problems is: a kind of pyroceram fibre plate, composition of raw materials component by following umber forms: 20-60 part glass fibre, 30-50 part mineral fibre, 5-7 part aluminum oxide, 5-8 part chromic oxide, 6-10 part trevira, 80-100 part flax fiber, 40-50 part carbon fiber, 3-8 part magnesium oxide, 5-10 part silicon oxide, 5-10 part polyoxyethylene glycol, 3-5 part Sodium hexametaphosphate 99, 5-8 part sodium lauryl sulphate, 10-15 part silicone antifoam agent, 3-8 part paraffin, 5-10 part rubber, 10-25 part resin, 12-20 part polyhutadiene latex, 15-18 part butadiene-styrene latex.
Further, each composition of raw materials component is: 20 parts of glass fibre, 30 parts of mineral fibre, 5 parts of aluminum oxide, 5 parts of chromic oxide, 6 parts of trevira, 80 parts of flax fibers, 40 parts of carbon fibers, 3 parts of magnesium oxide, 5 parts of silicon oxide, 5 parts of polyoxyethylene glycol, 3 parts of Sodium hexametaphosphate 99s, 5 parts of sodium lauryl sulphate, 10 parts of silicone antifoam agents, 3 parts of paraffin, 5 parts of rubber, 10 parts of resins, 12 parts of polyhutadiene latexes, 15 parts of butadiene-styrene latexes.
Or each composition of raw materials component is: 60 parts of glass fibre, 50 parts of mineral fibre, 7 parts of aluminum oxide, 8 parts of chromic oxide, 10 parts of trevira, 100 parts of flax fibers, 50 parts of carbon fibers, 8 parts of magnesium oxide, 10 parts of silicon oxide, 10 parts of polyoxyethylene glycol, 5 parts of Sodium hexametaphosphate 99s, 8 parts of sodium lauryl sulphate, 15 parts of silicone antifoam agents, 8 parts of paraffin, 10 parts of rubber, 25 parts of resins, 20 parts of polyhutadiene latexes, 18 parts of butadiene-styrene latexes.
In sum, the invention has the beneficial effects as follows: pyroceram fibre plate of the present invention, in the time running into high temperature, can bear 1000 DEG C of above high temperature, and not lose cohesive force; In the time of low temperature, there is good combination and dispersing property, in whole production technological process, play fiber dispersion and evenly wait effect, effectively extended work-ing life.
Embodiment
Embodiment 1
The described a kind of pyroceram fibre plate of the present embodiment 1, is made up of the composition of raw materials component of following umber: 20 parts of glass fibre, 30 parts of mineral fibre, 5 parts of aluminum oxide, 5 parts of chromic oxide, 6 parts of trevira, 80 parts of flax fibers, 40 parts of carbon fibers, 3 parts of magnesium oxide, 5 parts of silicon oxide, 5 parts of polyoxyethylene glycol, 3 parts of Sodium hexametaphosphate 99s, 5 parts of sodium lauryl sulphate, 10 parts of silicone antifoam agents, 3 parts of paraffin, 5 parts of rubber, 10 parts of resins, 12 parts of polyhutadiene latexes, 15 parts of butadiene-styrene latexes.
Embodiment 2
The described a kind of pyroceram fibre plate of the present embodiment 2, is made up of the composition of raw materials component of following umber: 60 parts of glass fibre, 50 parts of mineral fibre, 7 parts of aluminum oxide, 8 parts of chromic oxide, 10 parts of trevira, 100 parts of flax fibers, 50 parts of carbon fibers, 8 parts of magnesium oxide, 10 parts of silicon oxide, 10 parts of polyoxyethylene glycol, 5 parts of Sodium hexametaphosphate 99s, 8 parts of sodium lauryl sulphate, 15 parts of silicone antifoam agents, 8 parts of paraffin, 10 parts of rubber, 25 parts of resins, 20 parts of polyhutadiene latexes, 18 parts of butadiene-styrene latexes.
The above, be only preferred embodiment of the present invention, not principle of the present invention done to any pro forma restriction.Any simple modification, equivalent variations and modification that every foundation technical spirit of the present invention is done above embodiment, all still belong in the scope of technical scheme of the present invention.
Claims (3)
1. a pyroceram fibre plate, it is characterized in that, composition of raw materials component by following umber forms: 20-60 part glass fibre, 30-50 part mineral fibre, 5-7 part aluminum oxide, 5-8 part chromic oxide, 6-10 part trevira, 80-100 part flax fiber, 40-50 part carbon fiber, 3-8 part magnesium oxide, 5-10 part silicon oxide, 5-10 part polyoxyethylene glycol, 3-5 part Sodium hexametaphosphate 99, 5-8 part sodium lauryl sulphate, 10-15 part silicone antifoam agent, 3-8 part paraffin, 5-10 part rubber, 10-25 part resin, 12-20 part polyhutadiene latex, 15-18 part butadiene-styrene latex.
2. a kind of pyroceram fibre plate according to claim 1, it is characterized in that, each composition of raw materials component is: 20 parts of glass fibre, 30 parts of mineral fibre, 5 parts of aluminum oxide, 5 parts of chromic oxide, 6 parts of trevira, 80 parts of flax fibers, 40 parts of carbon fibers, 3 parts of magnesium oxide, 5 parts of silicon oxide, 5 parts of polyoxyethylene glycol, 3 parts of Sodium hexametaphosphate 99s, 5 parts of sodium lauryl sulphate, 10 parts of silicone antifoam agents, 3 parts of paraffin, 5 parts of rubber, 10 parts of resins, 12 parts of polyhutadiene latexes, 15 parts of butadiene-styrene latexes.
3. a kind of pyroceram fibre plate according to claim 1, it is characterized in that, each composition of raw materials component is: 60 parts of glass fibre, 50 parts of mineral fibre, 7 parts of aluminum oxide, 8 parts of chromic oxide, 10 parts of trevira, 100 parts of flax fibers, 50 parts of carbon fibers, 8 parts of magnesium oxide, 10 parts of silicon oxide, 10 parts of polyoxyethylene glycol, 5 parts of Sodium hexametaphosphate 99s, 8 parts of sodium lauryl sulphate, 15 parts of silicone antifoam agents, 8 parts of paraffin, 10 parts of rubber, 25 parts of resins, 20 parts of polyhutadiene latexes, 18 parts of butadiene-styrene latexes.