CN105565707A - Glass fiber reinforced composite material - Google Patents
Glass fiber reinforced composite material Download PDFInfo
- Publication number
- CN105565707A CN105565707A CN201510914450.6A CN201510914450A CN105565707A CN 105565707 A CN105565707 A CN 105565707A CN 201510914450 A CN201510914450 A CN 201510914450A CN 105565707 A CN105565707 A CN 105565707A
- Authority
- CN
- China
- Prior art keywords
- parts
- oxide
- glass fiber
- composite material
- fiber reinforced
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a glass fiber reinforced composite material, which is prepared from the following raw materials in parts by weight: 50 to 60 parts of silicon dioxide, 5 to 10 parts of silicon carbide, 5 to 10 parts of phenolic resin, 1 to 6 parts of polypropylene, 5 to 10 parts of bisphenol A epoxy resin, 2 to 7 parts of barium titanate, 6 to 10 parts of boric oxide, 3 to 9 parts of calcium oxide, 3 to 6 parts of aluminium oxide, 2 to 6 parts of magnesium oxide, 2 to 6 parts of sodium oxide, 7 to 10 parts of limestone, 1 to 3 parts of titanium dioxide, 0.3 to 0.5 part of ferric oxide, and 6 to 10 parts of sodium carbonate. According to the glass fiber reinforced composite material provided by the invention, the components and the matching ratio of the components are optimized, so that the prepared glass fiber composite material not only has excellent water resistance, but also has better acid resistance, electric property and mechanical property, and is extensive in material sources, low in price, stable in product quality, and long in service life.
Description
Technical field
The invention belongs to glass fiber material field, be specifically related to a kind of glass fibre reinforced composion.
Background technology
Glass fibre belongs to ceramic, and have the plurality of advantages such as good insulating, thermotolerance is strong, erosion resistance good, physical strength is high, therefore become the class body material that application quantity in reinforced composite is maximum, but quality is crisp, wear resistance is poor.Therefore, need to improve glass fibre, develop a kind of matrix material, improve the over-all properties of glass fibre.
Summary of the invention
The object of the present invention is to provide a kind of glass fibre reinforced composion.
The technical solution used in the present invention is, a kind of glass fibre reinforced composion, is made up of the raw material of following parts by weight: silicon-dioxide 50-60 part, silicon carbide 5-10 part, resol 5-10 part, polypropylene 1-6 part, bisphenol A type epoxy resin 5-10 part, barium titanate 2-7 part, boron oxide 6-10 part, calcium oxide 3-9 part, aluminum oxide 3-6 part, magnesium oxide 2-6 part, sodium oxide 2-6 part, Wingdale 7-10 part, titanium dioxide 1-3 part, ferric oxide 0.3-0.5 part, sodium carbonate 6-10 part.
The present invention has the following advantages: the preferably proportioning of each component and each component, the glass fiber compound material prepared not only has excellent water resistance, simultaneously, acid resistance, electric property and mechanical property are all better, material source is extensive, cheap, constant product quality, long service life.
Embodiment
Below in conjunction with embodiment, the present invention is further elaborated.
Embodiment 1
A kind of glass fibre reinforced composion, is made up of the raw material of following parts by weight: silicon-dioxide 50 parts, 5 parts, silicon carbide, 5 parts, resol, polypropylene 1 part, bisphenol A type epoxy resin 5 parts, barium titanate 2 parts, boron oxide 6 parts, 3 parts, calcium oxide, 3 parts, aluminum oxide, 2 parts, magnesium oxide, sodium oxide 2 parts, 7 parts, Wingdale, titanium dioxide 1 part, ferric oxide 0.3 part, 6 parts, sodium carbonate.
Embodiment 2
A kind of glass fibre reinforced composion, is made up of the raw material of following parts by weight: silicon-dioxide 55 parts, 7 parts, silicon carbide, 7 parts, resol, polypropylene 4 parts, bisphenol A type epoxy resin 7 parts, barium titanate 5 parts, boron oxide 8 parts, 5 parts, calcium oxide, 5 parts, aluminum oxide, 5 parts, magnesium oxide, sodium oxide 5 parts, 8 parts, Wingdale, titanium dioxide 2 parts, ferric oxide 0.4 part, 8 parts, sodium carbonate.
Embodiment 3
A kind of glass fibre reinforced composion, is made up of the raw material of following parts by weight: silicon-dioxide 60 parts, 10 parts, silicon carbide, 10 parts, resol, polypropylene 6 parts, bisphenol A type epoxy resin 10 parts, barium titanate 7 parts, boron oxide 10 parts, 9 parts, calcium oxide, 6 parts, aluminum oxide, 6 parts, magnesium oxide, sodium oxide 6 parts, 10 parts, Wingdale, titanium dioxide 3 parts, ferric oxide 0.5 part, 10 parts, sodium carbonate.
Although above-mentioned, the specific embodiment of the present invention is described; but not limiting the scope of the invention; one of ordinary skill in the art should be understood that; on the basis of technical scheme of the present invention, those skilled in the art do not need to pay various amendment or distortion that creative work can make still within protection scope of the present invention.
Claims (1)
1. a glass fibre reinforced composion, is characterized in that: be made up of the raw material of following parts by weight: silicon-dioxide 50-60 part, silicon carbide 5-10 part, resol 5-10 part, polypropylene 1-6 part, bisphenol A type epoxy resin 5-10 part, barium titanate 2-7 part, boron oxide 6-10 part, calcium oxide 3-9 part, aluminum oxide 3-6 part, magnesium oxide 2-6 part, sodium oxide 2-6 part, Wingdale 7-10 part, titanium dioxide 1-3 part, ferric oxide 0.3-0.5 part, sodium carbonate 6-10 part.