CN102417324A - Inorganic active heat-insulating material for wall insulation, and preparation method thereof - Google Patents
Inorganic active heat-insulating material for wall insulation, and preparation method thereof Download PDFInfo
- Publication number
- CN102417324A CN102417324A CN2011102537578A CN201110253757A CN102417324A CN 102417324 A CN102417324 A CN 102417324A CN 2011102537578 A CN2011102537578 A CN 2011102537578A CN 201110253757 A CN201110253757 A CN 201110253757A CN 102417324 A CN102417324 A CN 102417324A
- Authority
- CN
- China
- Prior art keywords
- parts
- insulating material
- inorganic active
- glass beads
- heat preserving
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an inorganic active heat-insulating material for wall insulation, and a preparation method thereof. The inorganic active heat-insulating material comprises the following components in parts by weight: 28-35 parts of vitrified small balls with the particle size of 30-50 meshes, 12-17 parts of vitrified small balls with the particle size of 200-250 meshes, 30-40 parts of composite silicate, 8-12 parts of quartz sand, 18-22 parts of plant fiber, 2-5 parts of nano waterproof powder, 0.3-0.5 part of dispersible emulsion powder and 0.5-0.6 part of dispersible polyvinyl alcohol. The invention adopts the combination of the composite silicate, two types of vitrified small balls with different particle sizes and quartz sand, thus realizing the aims of increasing the product strength and use effect; grid cloth, anti-crack mortar and other materials are not needed for construction, and the expansion and shrinkage of the constructed wall are small; and the addition of the nano waterproof powder enables the wall material to have a waterproof effect, thus saving a secondary process of brushing waterproof paint.
Description
Technical field
The present invention relates to a kind of material of construction and preparation method thereof, especially a kind of inorganic active wall heat preserving and insulating material and preparation method thereof.
Background technology
At present; The main wall body after construction is accomplished, one deck heat preserving and insulating material of possibly also need constructing again, and present heat preserving and insulating material staple is oarse-grained glass bead; But the excessive clearance between the oarse-grained glass bead, and normally fill with cement.But because the difference of hardness between cement and the glass bead apart from bigger, therefore causes adhesive effect to reduce, and heat insulation effect is also undesirable; And the intensity of wall thermal insulating lagging material is also undesirable now, occurs situation such as cracking easily, and; If also need make body of wall have waterproof effect; Usually also need the brushing waterproof layer, but the brushing of waterproof layer bothers not only, takes a lot of work, and work-ing life and effect are all undesirable.
Summary of the invention
The objective of the invention is: a kind of inorganic active wall heat preserving and insulating material and preparation method thereof is provided, and its heat insulation effect and adhesive effect are good, and material itself also has water-proof function, easy construction, and long service life is to overcome the deficiency of prior art.
The present invention is achieved in that the inorganic active wall heat preserving and insulating material, calculates by weight, and it comprises that particle diameter is 28~35 parts of 30~50 purpose glass beads; Particle diameter is 12~17 parts of 200~250 purpose glass beads; 30~40 parts of composition silicates, 8~12 parts of silica sands, 18~22 parts on vegetable fibre; 2~5 parts in nanometer anti pigment, 0.4~0.6 part of 0.3~0.5 part of dispersibility latex powder and dispersed Z 150PH.
Calculate by weight; It comprises that particle diameter is 28~35 parts of 30~50 purpose glass beads, and particle diameter is 12~17 parts of 200~250 purpose glass beads, 30~40 parts of composition silicates; 8~12 parts of silica sands; 18~22 parts on vegetable fibre, 2~5 parts in nanometer anti pigment, 0.4~0.6 part of 0.3~0.5 part of dispersibility latex powder and dispersed Z 150PH.
Also comprise 2.5~4 parts of 0.2~0.4 part of hydrophober and nonmetal activator.Hydrophober can further improve and firm waterproof effect; Nonmetal activator can fully disperse the nanometer anti pigment, can improve waterproof effect equally.
Also comprise 0.4~0.6 part of 0.3~0.5 part of hardening accelerator and methylcellulose gum.Hardening accelerator produces a desired effect the intensity of body of wall in advance; All moisture when methylcellulose gum keeps construction make the product of preserving period obtain effective moisture protection, also have the rimose of preventing increase and pretend usefulness; Shortened and accomplished the needed time of construction.
Also comprise 0.1~0.3 part of mould inhibitor, 0.8~1 part of 0.9~1.1 part of inhibitor and fire retardant.Mould inhibitor can prevent the body of wall grow mold; Inhibitor can make product have the performance of anti-environmental aging; Fire retardant makes product have anti-flaming function.
The preparation method of inorganic active wall heat preserving and insulating material; Be that 200~250 purpose glass beads, vegetable fibre, nanometer anti pigment, hydrophober and methylcellulose gum mix back stirring 5~10 minutes with particle diameter earlier; Again nonmetal activator, hardening accelerator, mould inhibitor, inhibitor and fire retardant are added; And stirred 2~5 minutes, add 30~50 purpose glass beads, silica sand, composition silicate at last and stirred 3~5 minutes, promptly obtain finished product.
Principle of the present invention is: oarse-grained glass bead is made with short grained that the small-particle vitreous is little to mix use, short grained glass bead can fully be sneaked between the gap of oarse-grained glass bead, can guarantee adhesive effect, can improve heat insulation effect again.Again they are mixed with composition silicate and silica sand, realize the purpose of the intensity of increase product; Having replaced traditional anti-crack fiber, realize that splitting resistance is good, the purpose that cementability is strong, the life-span is long through adding vegetable fibre; Add the nanometer anti pigment and make materials for wall itself have waterproof effect, removed the operation of secondary brushing waterproof paint from, the construction of both having simplified has improved effect again; Make the bonding and homodisperse of mixing between each component through Z 150PH and dispersibility latex powder.
Owing to adopted above-mentioned technical scheme; Compared with prior art; The present invention adopts the different glass bead of composition silicate, two kinds of particle diameters and the combination of silica sand; Realized increasing the intensity of product and the purpose of result of use, do not needed the materials such as grid cloth, anticracking grout to construct, and the expansion and the shrinking percentage of the body of wall that obtains of construction are little; Also make materials for wall itself have waterproof effect, removed the operation of secondary brushing waterproof paint from through adding the nanometer anti pigment.Material source of the present invention is extensive, and is easy to implement, and result of use is good.
Embodiment
Embodiments of the invention 1: the preparation of inorganic active wall heat preserving and insulating material; Be that 15 parts of 200~250 purpose glass beads, 20 parts on vegetable fibre, 3 parts in nanometer anti pigment, 0.3 part of hydrophober and methylcellulose gum are put into stirring 8 minutes (adopting conventional stirring velocity) in the composite machine of horizontal sealing for 0.5 part with particle diameter earlier; Again with 3 parts of nonmetal activator, 0.4 part of hardening accelerator, 0.2 part of mould inhibitor, 1.0 parts of inhibitors and 0.9 part of adding of fire retardant; And stirred 4 minutes; Add 32 parts of 30~50 purpose glass beads, 10 parts of silica sands and composition silicate at last and stirred 4 minutes for 35 parts, promptly obtain finished product.
Embodiments of the invention 2: the preparation of inorganic active wall heat preserving and insulating material; Be that 12 parts of 200~250 purpose glass beads, 18 parts on vegetable fibre, 2 parts in nanometer anti pigment, 0.2 part of hydrophober and methylcellulose gum are put into stirring 5 minutes (adopting conventional stirring velocity) in the composite machine of horizontal sealing for 0.4 part with particle diameter earlier; Again with 2.5 parts of nonmetal activator, 0.3 part of hardening accelerator, 0.1 part of mould inhibitor, 0.9 part of inhibitor and 0.8 part of adding of fire retardant; And stirred 2 minutes; Add 28 parts of 30~50 purpose glass beads, 8 parts of silica sands and composition silicate at last and stirred 3 minutes for 30 parts, promptly obtain finished product.
Embodiments of the invention 3: the preparation of inorganic active wall heat preserving and insulating material; Be that 17 parts of 200~250 purpose glass beads, 22 parts on vegetable fibre, 5 parts in nanometer anti pigment, 0.4 part of hydrophober and methylcellulose gum are put into stirring 10 minutes (adopting conventional stirring velocity) in the composite machine of horizontal sealing for 0.6 part with particle diameter earlier; Again with 4 parts of nonmetal activator, 0.5 part of hardening accelerator, 0.3 part of mould inhibitor, 1.1 parts of inhibitors and 1 part of adding of fire retardant; And stirred 5 minutes; Add 35 parts of 30~50 purpose glass beads, 12 parts of silica sands and composition silicate at last and stirred 5 minutes for 40 parts, promptly obtain finished product.
The product that glass bead can adopt Guizhou Ai Si to produce than type material ltd; Composition silicate adopts the Yizhang, Hunan to build the Hunan ox board composition silicate that English white cement ltd produces; The nanometer anti pigment are the product that Taiwan land of happiness Materials Co., Ltd produces.
All the other components all can adopt commercially available conventional raw material.
Claims (6)
1. inorganic active wall heat preserving and insulating material is characterized in that: calculate by weight, it comprises that particle diameter is 28~35 parts of 30~50 purpose glass beads; Particle diameter is 12~17 parts of 200~250 purpose glass beads; 30~40 parts of composition silicates, 8~12 parts of silica sands, 18~22 parts on vegetable fibre; 2~5 parts in nanometer anti pigment, 0.4~0.6 part of 0.3~0.5 part of dispersibility latex powder and dispersed Z 150PH.
2. inorganic active wall heat preserving and insulating material according to claim 1 is characterized in that: calculate by weight, it comprises that particle diameter is 28~35 parts of 30~50 purpose glass beads; Particle diameter is 12~17 parts of 200~250 purpose glass beads; 30~40 parts of composition silicates, 8~12 parts of silica sands, 18~22 parts on vegetable fibre; 2~5 parts in nanometer anti pigment, 0.4~0.6 part of 0.3~0.5 part of dispersibility latex powder and dispersed Z 150PH.
3. inorganic active wall heat preserving and insulating material according to claim 1 and 2 is characterized in that: also comprise 2.5~4 parts of 0.2~0.4 part of hydrophober and nonmetal activator.
4. inorganic active wall heat preserving and insulating material according to claim 1 and 2 is characterized in that: also comprise 0.4~0.6 part of 0.3~0.5 part of hardening accelerator and methylcellulose gum.
5. inorganic active wall heat preserving and insulating material according to claim 1 and 2 is characterized in that: also comprise 0.1~0.3 part of mould inhibitor, 0.8~1 part of 0.9~1.1 part of inhibitor and fire retardant.
6. the preparation method of an inorganic active wall heat preserving and insulating material; It is characterized in that: be that 200~250 purpose glass beads, vegetable fibre, nanometer anti pigment, hydrophober and methylcellulose gum mix back stirring 5~10 minutes with particle diameter earlier; Again nonmetal activator, hardening accelerator, mould inhibitor, inhibitor and fire retardant are added; And stirred 2~5 minutes, add 30~50 purpose glass beads, silica sand, composition silicate at last and stirred 3~5 minutes, promptly obtain finished product.