CN104212009B - 一种无卤阻燃橡胶 - Google Patents

一种无卤阻燃橡胶 Download PDF

Info

Publication number
CN104212009B
CN104212009B CN201410488350.7A CN201410488350A CN104212009B CN 104212009 B CN104212009 B CN 104212009B CN 201410488350 A CN201410488350 A CN 201410488350A CN 104212009 B CN104212009 B CN 104212009B
Authority
CN
China
Prior art keywords
parts
halogen
rubber
free fireproof
present
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410488350.7A
Other languages
English (en)
Other versions
CN104212009A (zh
Inventor
张勇
张卫兴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangyin Haida Rubber and Plastic Co Ltd
Original Assignee
Jiangyin Haida Rubber and Plastic Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangyin Haida Rubber and Plastic Co Ltd filed Critical Jiangyin Haida Rubber and Plastic Co Ltd
Priority to CN201410488350.7A priority Critical patent/CN104212009B/zh
Publication of CN104212009A publication Critical patent/CN104212009A/zh
Application granted granted Critical
Publication of CN104212009B publication Critical patent/CN104212009B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种无卤阻燃橡胶，由下列重量份的原料制成：丁苯橡胶50-200份、氧化锌1-10份、硬脂酸1-5份、阻燃剂10-30份、助燃助剂10-20份、补强剂20-50份、软化剂1-10份和硫化促进剂1-10份。本发明所述的无卤阻燃橡胶具有良好阻燃性，并且由于不含卤素，因而对环境造成的伤害较小，因此十分适于工业大规模推广。

Description

一种无卤阻燃橡胶
技术领域
本发明涉及橡胶领域，具体的说，本发明涉及一种无卤阻燃橡胶。
背景技术
橡胶制品由于其耐磨、耐油等特性而得到广泛应用，但是在实际使用中发现，橡胶制品在遇火燃烧时释放出含卤素化合物，因此对环境造成很大破坏。目前，常用的替代阻燃剂有氢氧化镁等，但是其阻燃效果仍然需要进一步提高。因此，工业上需要新的无卤阻燃橡胶，同时其力学性能又不会得到降低。
发明内容
本发明的目的在于提供一种无卤阻燃橡胶。
为了实现本发明的目的，本发明提供一种无卤阻燃橡胶，由下列重量份的原料制成：丁苯橡胶50-200份、氧化锌1-10份、硬脂酸1-5份、阻燃剂10-30份、助燃助剂10-20份、补强剂20-50份、软化剂1-10份和硫化促进剂1-10份。
优选地，本发明所述的无卤阻燃橡胶由下列重量份的原料制成：丁苯橡胶100份、氧化锌6份、硬脂酸3份、阻燃剂20份、阻燃助剂12份、补强剂40份、软化剂5份和硫化促进剂5份。
更优选地，所述阻燃剂为氢氧化镁。
更优选地，所述阻燃助剂为5-(4-羟基苯基)-2H-吡喃-2-酮。
更优选地，所述补强剂为炭黑。
更优选地，所述软化剂为石油树脂。
更优选地，所述硫化促进剂为二硫化四甲基秋兰姆。
本发明还提供5-(4-羟基苯基)-2H-吡喃-2-酮在用作阻燃助剂中的应用。
优选地，所述阻燃助剂可以制成粉末剂。
优选地，所述阻燃助剂可以制成乳剂或喷雾剂。
本发明所述的无卤阻燃橡胶具有良好阻燃性，并且由于不含卤素，因而对环境造成的伤害较小，因此十分适于工业大规模推广。
附图说明
图1：实施例2的样品的断面SEM图；
图2：实施例1的样品的断面SEM图。
具体实施方式
以下通过具体实施方式的描述对本发明作进一步说明，但这并非是对本发明的限制，本领域技术人员根据本发明的基本思想，可以做出各种修改或改进，但是只要不脱离本发明的基本思想，均在本发明的范围之内。
实施例1
称取丁苯橡胶(SBR1502，购自南京扬子石化金浦橡胶有限公司)1000克、氧化锌60克、硬脂酸30克、氢氧化镁200克、5-(4-羟基苯基)-2H-吡喃-2-酮120克、炭黑(炭黑HAF，购自长沙炭黑厂)400克、石油树脂(石油树脂C5，购自南京泛成生物化工有限公司)50克和二硫化四甲基秋兰姆50克；
将丁苯橡胶在SK-160型双辊筒炼塑机中混炼，开炼机前辊135℃，后辊125℃，塑炼15分钟，然后加入氧化锌、硬脂酸、氢氧化镁、5-(4-羟基苯基)-2H-吡喃-2-酮、炭黑、石油树脂和二硫化四甲基秋兰姆，将原料在辊筒上左右交叉打卷使混炼均匀，薄通打包5次，出片，得到分散性较好的胶料，胶料停放8h后，在150℃、10MPa的条件下硫化。
实施例2
按照和实施例1相同的方式制备无卤阻燃橡胶，不同之处在于不使用5-(4-羟基苯基)-2H-吡喃-2-酮。
实验例
性能测试
力学性能：拉伸强度按GB/T528-2009进行。实施例1的样品的拉伸强度为16.9Mpa；实施例2的样品的拉伸强度为11.3Mpa。
SEM观察：将实施例1和2的样品在液氮条件下脆性断裂，其断面形貌由HitachiS530扫描电镜(SEM)观察，结果见图1和图2。
比较图1和图2，不加阻燃助剂的图1中断面形貌粗糙，可清楚看到共混体系分散程度差，而加入阻燃助剂的图2断面形貌模糊程度最高，因为降低共混体系间的界面张力，提高原料之间的相容性，彼此之间作用力更强。这从实施例1的样品的拉伸强度较高也可以得到验证。
氧指数测试：按照GB/T2406-1993标准测定极限氧指数(LOI)，试样尺寸为：110mmx6.5mmx3mm。实施例1的样品的LOI为38.1％，并且燃烧无黑烟，无熔滴，迅速自熄，实施例2的样品的LOI为22.5％，燃烧无黑烟，无熔滴，迅速自熄。由此可见，加入阻燃助剂后，阻燃效果得到显著增强，实施例1的结果与实施例2的结果进行比较，差异具有统计学意义(P＜0.05)。

Claims (1)

1.一种无卤阻燃橡胶，其特征在于，由下列重量份的原料制成：丁苯橡胶100份、氧化锌6份、硬脂酸3份、阻燃剂20份、阻燃助剂12份、补强剂40份、软化剂5份和硫化促进剂5份；
所述阻燃剂为氢氧化镁；
所述阻燃助剂为5-(4-羟基苯基)-2H-吡喃-2-酮；
所述补强剂为炭黑；
所述软化剂为石油树脂；
所述硫化促进剂为二硫化四甲基秋兰姆。
CN201410488350.7A 2014-09-22 2014-09-22 一种无卤阻燃橡胶 Expired - Fee Related CN104212009B (zh)