CN104194681A - 陶瓷用胶黏剂及其制备方法 - Google Patents
陶瓷用胶黏剂及其制备方法 Download PDFInfo
- Publication number
- CN104194681A CN104194681A CN201410450653.XA CN201410450653A CN104194681A CN 104194681 A CN104194681 A CN 104194681A CN 201410450653 A CN201410450653 A CN 201410450653A CN 104194681 A CN104194681 A CN 104194681A
- Authority
- CN
- China
- Prior art keywords
- agent
- parts
- ceramic
- adhesive
- toluene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种陶瓷用胶黏剂及其制备方法。具体说,是用来将瓷砖黏贴到水泥地面或墙壁上用的胶黏剂。所述陶瓷用胶黏剂是用聚苯乙烯泡沫塑料、酚醛树脂、橡胶胶液、甲苯、环已酮、乙酸乙烯、填充剂、交联剂、乳化剂、悬浮剂等原料经混合、反应而成。采用本发明来黏贴瓷砖,不仅可降低建筑的承载负荷、建筑装饰成本和工人的劳动强度,还可提高施工效率。
Description
技术领域
本发明涉及一种胶水。具体说,是用来将瓷砖黏贴到水泥地面或墙壁上用的胶黏剂。
背景技术
目前在建筑装饰行业都知道,将瓷砖黏贴到水泥地面或墙壁上的方法都是传统方法,该传统方法是用由水泥、黄沙和水混合而成的泥状混合物先抹在瓷砖的背面,以所述泥状混合物作为粘结剂将瓷砖黏贴到水泥地面或墙壁上。虽然采用这种方法可以实现瓷砖的粘结,但由于需要用由水泥、黄沙和水混合而成的泥状混合物作为粘结剂,而由水泥、黄沙和水混合而成的泥状混合物比较沉重,会增加建筑的承载负荷。又由于需要用由水泥、黄沙和水混合而成的泥状混合物作为粘结剂,需要的建筑材料多,不仅会增加建筑装饰成本,还会增加工人的劳动强度、降低施工效率。
发明内容
本发明要解决的问题是提供一种陶瓷用胶黏剂。采用本发明来黏贴瓷砖,不仅可降低建筑的承载负荷、建筑装饰成本和工人的劳动强度,还可提高施工效率。
本发明要解决的另一个问题是提供一种制备陶瓷用胶黏剂的方法。
为解决上述问题,采取以下技术方案:
本发明的陶瓷用胶黏剂特点是包括以下重量份数的原料:
聚苯乙烯泡沫塑料24~25份;
酚醛树脂4~6份;
橡胶胶液3~5份;
甲苯14~16份;
环已酮13~15份;
乙酸乙烯19~21份;
填充剂28~32份;
交联剂1.4~1.6份;
乳化剂0.9~1.1份;
悬浮剂0.4~0.6份;
其中,所述填充剂是蛋白页岩,交联剂是异氰酸酯,乳化剂是聚氧乙烯蓖麻油醚,悬浮剂是SP-1型悬浮剂。
制备所述陶瓷用胶黏剂的方法特点是包括以下步骤:
先将聚苯乙烯泡沫塑料、甲苯、环已酮和乙酸乙烯加入反应釜内,并加热至58~62摄氏度,溶解成溶液;
然后,加入酚醛树脂、橡胶胶液、交联剂、乳化剂和悬浮剂,经均匀搅拌,使其乳化均匀;
之后,加入填充剂,并以790~810转/分钟的转速进行均匀搅拌;
最后,在38~42摄氏度的温度下,用三辊研磨机进行研磨,得到所述陶瓷用胶黏剂。
采取上述方案,具有以下优点:
由上述方案可以看出,由于本发明是用聚苯乙烯泡沫塑料、酚醛树脂、橡胶胶液、甲苯、环已酮、乙酸乙烯、填充剂、交联剂、乳化剂、悬浮剂等原料制成的液状粘结剂,使用时,只要将本发明涂抹在瓷砖背面并刮平,即可将瓷砖黏贴带地面或墙壁上,与背景技术中由水泥、黄沙和水混合而成的泥状混合物相比,重量比较轻,不会增加建筑的承载负荷。又由于不需水泥、黄沙和水,需要的建筑材料少,不仅可降低建筑装饰成本、降低工人的劳动强度,还可提高施工效率。
具体实施方式
实施例一
先选取24重量份的聚苯乙烯泡沫塑料、4重量份的酚醛树脂、3重量份的橡胶胶液、14重量份的甲苯、13重量份的环已酮、19重量份的乙酸乙烯、28重量份的填充剂、1.4重量份的交联剂、0.9重量份的乳化剂和0.4重量份的悬浮剂。其中,所述填充剂是蛋白页岩,交联剂是异氰酸酯,乳化剂是聚氧乙烯蓖麻油醚,悬浮剂是SP-1型悬浮剂。
再将聚苯乙烯泡沫塑料、甲苯、环已酮和乙酸乙烯加入反应釜内,并加热至58摄氏度,溶解成溶液。
然后,加入酚醛树脂、橡胶胶液、交联剂、乳化剂和悬浮剂,经均匀搅拌,使其乳化均匀。
之后,加入填充剂,并以790转/分钟的转速进行均匀搅拌;
最后,在38摄氏度的温度下,用三辊研磨机进行研磨,得到所述陶瓷用胶黏剂。
实施例二
先选取25重量份的聚苯乙烯泡沫塑料、5重量份的酚醛树脂、4重量份的橡胶胶液、15重量份的甲苯、14重量份的环已酮、20重量份的乙酸乙烯、30重量份的填充剂、1.5重量份的交联剂、1重量份的乳化剂和0.5重量份的悬浮剂。其中,所述填充剂是蛋白页岩,交联剂是异氰酸酯,乳化剂是聚氧乙烯蓖麻油醚,悬浮剂是SP-1型悬浮剂。
再将聚苯乙烯泡沫塑料、甲苯、环已酮和乙酸乙烯加入反应釜内,并加热至60摄氏度,溶解成溶液。
然后,加入酚醛树脂、橡胶胶液、交联剂、乳化剂和悬浮剂,经均匀搅拌,使其乳化均匀。
之后,加入填充剂,并以800转/分钟的转速进行均匀搅拌;
最后,在40摄氏度的温度下,用三辊研磨机进行研磨,得到所述陶瓷用胶黏剂。
实施例三
先选取26重量份的聚苯乙烯泡沫塑料、6重量份的酚醛树脂、5重量份的橡胶胶液、16重量份的甲苯、15重量份的环已酮、21重量份的乙酸乙烯、32重量份的填充剂、1.6重量份的交联剂、1.1重量份的乳化剂和0.6重量份的悬浮剂。其中,所述填充剂是蛋白页岩,交联剂是异氰酸酯,乳化剂是聚氧乙烯蓖麻油醚,悬浮剂是SP-1型悬浮剂。
再将聚苯乙烯泡沫塑料、甲苯、环已酮和乙酸乙烯加入反应釜内,并加热至62摄氏度,溶解成溶液。
然后,加入酚醛树脂、橡胶胶液、交联剂、乳化剂和悬浮剂,经均匀搅拌,使其乳化均匀。
之后,加入填充剂,并以810转/分钟的转速进行均匀搅拌;
最后,在40摄氏度的温度下,用三辊研磨机进行研磨,得到所述陶瓷用胶黏剂。
Claims (2)
1.陶瓷用胶黏剂,其特征在于包括以下重量份数的原料:
聚苯乙烯泡沫塑料24~25份;
酚醛树脂4~6份;
橡胶胶液3~5份;
甲苯14~16份;
环已酮13~15份;
乙酸乙烯19~21份;
填充剂28~32份;
交联剂1.4~1.6份;
乳化剂0.9~1.1份;
悬浮剂0.4~0.6份;
其中,所述填充剂是蛋白页岩,交联剂是异氰酸酯,乳化剂是聚氧乙烯蓖麻油醚,悬浮剂是SP-1型悬浮剂。
2.制备权利要求1所述陶瓷用胶黏剂的方法,其特征在于包括以下步骤:
先将聚苯乙烯泡沫塑料、甲苯、环已酮和乙酸乙烯加入反应釜内,并加热至58~62摄氏度,溶解成溶液;
然后,加入酚醛树脂、橡胶胶液、交联剂、乳化剂和悬浮剂,经均匀搅拌,使其乳化均匀;
之后,加入填充剂,并以790~810转/分钟的转速进行均匀搅拌;
最后,在38~42摄氏度的温度下,用三辊研磨机进行研磨,得到所述陶瓷用胶黏剂。