CN104194629B - 具有阻燃特性的非固化橡胶沥青防水涂料及其制备方法 - Google Patents

具有阻燃特性的非固化橡胶沥青防水涂料及其制备方法 Download PDF

Info

Publication number
CN104194629B
CN104194629B CN201410459750.5A CN201410459750A CN104194629B CN 104194629 B CN104194629 B CN 104194629B CN 201410459750 A CN201410459750 A CN 201410459750A CN 104194629 B CN104194629 B CN 104194629B
Authority
CN
China
Prior art keywords
flame
rubber asphalt
cured rubber
parts
asphalt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410459750.5A
Other languages
English (en)
Other versions
CN104194629A (zh
Inventor
陈晓文
常英
刘金景
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI ORIENTAL YUHONG WATERPROOF TECHNOLOGY CO LTD
Tangshan Dongfang Yuhong Waterproof Technology Co ltd
Beijing Oriental Yuhong Waterproof Technology Co Ltd
Original Assignee
Beijing Oriental Yuhong Waterproof Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beijing Oriental Yuhong Waterproof Technology Co Ltd filed Critical Beijing Oriental Yuhong Waterproof Technology Co Ltd
Priority to CN201410459750.5A priority Critical patent/CN104194629B/zh
Publication of CN104194629A publication Critical patent/CN104194629A/zh
Application granted granted Critical
Publication of CN104194629B publication Critical patent/CN104194629B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种具有阻燃特性的非固化橡胶沥青防水涂料，由下述重量份数的原料组成：石油沥青35～55、软化剂5～25、阻燃剂2～8、防老剂0.1～3、填充剂5～20、改性剂0.1～2。本发明公开的具有阻燃特性的非固化橡胶沥青防水涂料具有阻燃特性，有效解决了热熔型防水材料的阻燃问题，具有施工方便、粘结可靠、自愈性，与自粘型改性沥青防水卷材复合构成防水系统，能够有效解决因基层变形引起的防水层开裂导致的漏水、窜水问题。

Description

具有阻燃特性的非固化橡胶沥青防水涂料及其制备方法
技术领域
本发明涉及一种自愈性非固化防水涂料，尤其是一种具有阻燃特性的非固化橡胶沥青防水涂料，属于建筑防水材料，土木建筑工程防水领域。
背景技术
近年来，非固化橡胶沥青防水涂料在建筑防水领域得到了极大的应用和推广，但是目前市场上生产的非固化沥青涂料虽具有很好的防水效果，却均不具有阻燃性能，限制了其应用范围，增加了热熔施工危险性的同时加大了建筑物发生火灾的危险性。
发明内容
针对现有技术和市场的需要，本发明了一种具有阻燃特性的非固化橡胶沥青防水涂料，同时具有防水和阻燃特性，解决了现有非固化涂料在施工及应用中可能发生火灾的危险性。
本发明是通过下述技术方案实现的：
一种具有阻燃特性的非固化橡胶沥青防水涂料，由如下重量份数的原料组成：石油沥青35～55、软化剂5～25、阻燃剂2～8、防老剂0.1～3、填充剂5～20、改性剂0.1～2。
相应的，本发明公开了所述具有阻燃特性的非固化橡胶沥青防水涂料的制备方法，包括下述步骤：将石油沥青加热到140～160℃，然后加入软化剂、改性剂和阻燃剂，搅拌均匀，继续升温至160～180℃，在此温度下发育30～45min，开启胶体磨加速溶胀过程，并使改性剂均化完全后加入防老剂，停止胶体磨，匀速搅拌，加入填充剂，继续发育45～90min，即得。
其中，所用的石油沥青优选为环烷基石油沥青，更优选A级环烷基石油沥青，针入度为70～200(以0.1mm计)，最优选A级环烷基石油沥青，针入度为100～120(以0.1mm计)。
其中，软化剂为减线机油、糠醛抽出油、环烷油、芳烃油中的一种或多种的混合物，优选为减一线机油。
其中，阻燃剂为氢氧化镁、氢氧化铝、聚磷酸铵、磷酸三苯酯、六溴环十二烷中的一种或多种的混合物，优选为聚磷酸铵、磷酸三苯酯。
其中，改性剂为苯乙烯-丁二烯-苯乙烯嵌段共聚物(SBS)、苯乙烯-异戊二烯-苯乙烯嵌段共聚物(SIS)、苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物(SEBS)、苯乙烯-乙烯-丙烯-苯乙烯型嵌段共聚物(SEPS)、聚烯烃弹性体(POE LC670)、再生橡胶粉、丁基再生胶、丁腈再生胶中的-种或多种的混合物，优选为SBS、POE LC670、SEBS。
其中，防老剂为水杨酸苯酯、紫外线吸收剂(如UV-P、UV-0、UV-531)、光稳定剂(如GW-540、ZX-70、HS-944)、硫磺、含硫有机物或有机过氧化物中的一种或多种的混合物，优选为光稳定剂、有机过氧化物(过氧化苯甲酰BPO、二叔丁基过氧化物DTBP、叔丁基过氧化氢TBHP)。
其中，填充剂为轻质碳酸钙、重质碳酸钙、石粉、石灰粉、粉煤灰、滑石粉、炭黑中的一种或几种的混合物，优选为轻质碳酸钙、重质碳酸钙、滑石粉。
具体实施方式
为了能更清楚地理解本发明的技术实质，申请人在下面对本发明的具体实施方式作详细说明。这些说明均不是构成对本发明方案的限制，因此，任何人只要在本发明方案的启示下所做出的纯属形式上的而并非为实质性的等效变化和改型都应当视为本发明所公开的技术方案范畴并且视为主张权利保护的范围。
实施例1
制备方法：将石油沥青加热到140℃，然后加入软化剂、改性剂和阻燃剂，搅拌均匀，继续升温至160℃，在此温度下发育30min，开启胶体磨加速溶胀过程，并使改性剂均化更完全，1h后加入防老剂，停止胶体磨，匀速搅拌2h，加入填充剂，继续发育45min，出料即制得。
本实例的阻燃型非固化橡胶沥青防水涂料各项性能参数如下：固含量99.9％，耐热性70℃无流淌、滑动、滴落，低温柔性-30℃以下，-5℃下延伸性30mm，干燥基面和潮湿基面粘结性均100％内聚破坏，自愈性合格，热老化、化学腐蚀168h后基本无变化，遇明火阻燃。
实施例2
制备方法：将石油沥青加热到160℃，然后加入软化剂、改性剂和阻燃剂，搅拌均匀，继续升温至180℃，在此温度下发育40min，开启胶体磨加速溶胀过程，并使改性剂均化更完全，1.5h后加入防老剂，停止胶体磨，匀速搅拌1.5h，加入填充剂，继续发育80min，出料即制得。
本实例的阻燃型非固化橡胶沥青防水涂料各项性能参数如下：固含量99.9％，耐热性75℃无流淌、滑动、滴落，低温柔性-30℃以下，-5℃下延伸性30mm，干燥基面和潮湿基面粘结性均100％内聚破坏，自愈性合格，热老化、化学腐蚀160h后基本无变化，遇明火阻燃。
实施例3
制备方法：将石油沥青加热到160℃，然后加入软化剂、改性剂和阻燃剂，搅拌均匀，继续升温至180℃，在此温度下发育50min，开启胶体磨加速溶胀过程，并使改性剂均化更完全，1.5h后加入防老剂，停止胶体磨，匀速搅拌2h，加入填充剂，继续发育80min，出料即制得。
本实例的阻燃型非固化橡胶沥青防水涂料各项性能参数如下：固含量99.9％，耐热性85℃无流淌、滑动、滴落，低温柔性-30℃以下，-5℃下延伸性30mm，干燥基面和潮湿基面粘结性均100％内聚破坏，自愈性合格，热老化、化学腐蚀200h后无变化，遇明火阻燃。
实施例4
环烷基石油沥青，针入度11540
制备方法：将石油沥青加热到150℃，然后加入软化剂、改性剂和阻燃剂，搅拌均匀，继续升温至180℃，在此温度下发育45min，开启胶体磨加速溶胀过程，并使改性剂均化更完全，1.5h后加入防老剂，停止胶体磨，匀速搅拌2h，加入填充剂，继续发育90min，出料即制得。
本实例的阻燃型非固化橡胶沥青防水涂料各项性能参数如下：固含量99.9％，耐热性85℃无流淌、滑动、滴落，低温柔性-30℃以下，-5℃下延伸性30mm，干燥基面和潮湿基面粘结性均100％内聚破坏，自愈性合格，热老化、化学腐蚀200h后无变化，遇明火阻燃。
实施例5
制备方法：将石油沥青加热到140℃，然后加入软化剂、改性剂和阻燃剂，搅拌均匀，继续升温至160℃，在此温度下发育30min，开启胶体磨加速溶胀过程，并使改性剂均化更完全，1h后加入防老剂，停止胶体磨，匀速搅拌2h，加入填充剂，继续发育45min，出料即制得。
本实例的阻燃型非固化橡胶沥青防水涂料各项性能参数如下：固含量99.9％，耐热性85℃无流淌、滑动、滴落，低温柔性-30℃以下，-5℃下延伸性30mm，干燥基面和潮湿基面粘结性均100％内聚破坏，自愈性合格，热老化、化学腐蚀200H后无变化，遇明火阻燃。
由上述可见，本发明的涂料具有良好的自愈性和阻燃特性。同时在优选的情况下(即A级环烷基石油沥青，针入度为100～120(以0.1mm计)；减一线机油；阻燃剂为聚磷酸铵、磷酸三苯酯；改性剂为苯乙烯-丁二烯嵌段共聚物、氢化苯乙烯-丁二烯嵌段共聚物；防老剂为光稳定剂、有机过氧化物(过氧化苯甲酰BPO、二叔丁基过氧化物DTBP、叔丁基过氧化氢TBHP)；填充剂为轻质碳酸钙、重质碳酸钙、滑石粉。

Claims (4)

1.一种具有阻燃特性的非固化橡胶沥青防水涂料，其特征在于由下述重量份数的原料组成：石油沥青35～55、软化剂5～25、阻燃剂2～8、防老剂0.1～3、填充剂5～20、改性剂0.1～2；其中，石油沥青为环烷基石油沥青，针入度为70～200，以0.1mm计；软化剂为减线机油、糠醛抽出油、环烷油、芳烃油中的一种或多种的混合物；改性剂为苯乙烯-丁二烯嵌段共聚物、氢化苯乙烯-丁二烯嵌段共聚物、丁苯橡胶、氯丁橡胶、聚乙烯、聚丙烯、热塑性弹性体、再生橡胶粉、丁基再生胶、丁腈再生胶中的一种或多种的混合物；阻燃剂为氢氧化镁、氢氧化铝、聚磷酸铵、磷酸三苯酯、六溴环十二烷中的一种或多种的混合物。
2.根据权利要求1的具有阻燃特性的非固化橡胶沥青防水涂料，其特征在于防老剂为水杨酸苯酯、紫外线吸收剂、光稳定剂、硫磺、含硫有机物或有机过氧化物中的一种或几种的混合物。
3.根据权利要求1的具有阻燃特性的非固化橡胶沥青防水涂料，其特征在于填充剂为轻质碳酸钙、重质碳酸钙、石灰粉、粉煤灰、滑石粉中的一种或几种的混合物。
4.权利要求1所述的阻燃特性的非固化橡胶沥青防水涂料的制备方法，其特征在于包括下述步骤：将石油沥青加热到140～160℃，然后加入软化剂、改性剂和阻燃剂，搅拌均匀，继续升温至160～180℃，在此温度下发育30～45min，开启胶体磨加速溶胀过程，并使改性剂均化完全后加入防老剂，停止胶体磨，匀速搅拌，加入填充剂，继续发育45～90min，即得。
CN201410459750.5A 2014-09-11 2014-09-11 具有阻燃特性的非固化橡胶沥青防水涂料及其制备方法 Active CN104194629B (zh)