CN104192886A - 一种超细改性硫酸钡的制备工艺 - Google Patents

一种超细改性硫酸钡的制备工艺 Download PDF

Info

Publication number
CN104192886A
CN104192886A CN201410426387.7A CN201410426387A CN104192886A CN 104192886 A CN104192886 A CN 104192886A CN 201410426387 A CN201410426387 A CN 201410426387A CN 104192886 A CN104192886 A CN 104192886A
Authority
CN
China
Prior art keywords
barium sulfate
modified barium
grinding
fine
superfine modified
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410426387.7A
Other languages
English (en)
Inventor
李斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGDONG YUFENG POWDER MATERIAL Co Ltd
Original Assignee
GUANGDONG YUFENG POWDER MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGDONG YUFENG POWDER MATERIAL Co Ltd filed Critical GUANGDONG YUFENG POWDER MATERIAL Co Ltd
Priority to CN201410426387.7A priority Critical patent/CN104192886A/zh
Publication of CN104192886A publication Critical patent/CN104192886A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种超细改性硫酸钡的制备工艺,其特征在于,包括以下步骤:(1)破碎、(2)磨粉、(3)制浆、(4)超细研磨、(5)干燥、(6)研磨改性,最终得到所述的超细改性硫酸钡。本发明一种超细改性硫酸钡的制备工艺,其生产方法简单,成本低,且生出来的硫酸钡粉白度、流平性、光泽、耐水性都非常好,更加适用于工业生产中。

Description

一种超细改性硫酸钡的制备工艺
技术领域
本发明涉及化工领域,具体为一种超细改性硫酸钡的制备工艺。 
背景技术
硫酸钡具有独特的物理性质,其性能:微黄色粉末,相对密度4.0-4.6,不溶于水、酸、碱及其他溶剂,耐热耐酸、碱、无毒,可用于与食品接触的制品,被广泛用于工业生产中,可以作为橡胶的补强填充剂,也可用于耐酸橡胶制品和一般制品,还可用作表面涂布剂、上浆剂、加重剂,亦用于颜料、陶瓷、蓄电池、搪瓷、油漆、涂料等。 
 发明内容     
本发明针对上述问题提出一种白度、流平性、光泽、耐水性都非常好的超细改性硫酸钡,且生产方法简单的一种超细改性硫酸钡的制备工艺。
     本发明的技术方案是 :一种超细改性硫酸钡的制备工艺,包括以下步骤 : 
(1)破碎
将大块重晶石矿用颚式破碎机、锤式破碎机进行破碎得到均匀大小颗粒;
(2) 磨粉
 将得到的破碎均匀大小颗粒的重晶石矿用硫酸钡雷蒙磨磨粉至平均颗粒为 400 目 ;
(3) 制浆
 将磨粉后的物料加水制浆固含量 45%-60% ;
(4) 超细研磨
将制浆后的浆料加入上述浆料重量的 2.5% 的聚乙二醇, 搅拌均匀, 反应 15min,然后将上述物料进行湿式超细精磨 8小时;
(5) 干燥
 对超细研磨后的物料进行干燥得到超细硫酸钡粉末制品。
(6)、研磨改性 
将收集得到的硫酸钡粉再利用干法研磨打散,研磨速率为 1460r/min,并在研磨过程中加入改性剂,最终得到所述的超细改性硫酸钡。
所述的聚乙二醇的相对分子质量为4000。 
所述的改性剂为有机硅。 
本发明的技术方案,一种超细改性硫酸钡的制备工艺,其生产方法简单,成本低,且生出来的硫酸钡粉白度、流平性、光泽、耐水性都非常好,更加适用于工业生产中。 
具体实施方式
本发明的技术方案是 :一种超细改性硫酸钡的制备工艺, 其特征在于, 包括以下步骤 : 
(1)破碎
将大块重晶石矿用颚式破碎机、锤式破碎机进行破碎均匀大小颗粒;
(2) 磨粉
 将破碎均匀大小颗粒的重晶石矿用硫酸钡雷蒙磨磨粉至平均颗粒为 400 目 ;
(3) 制浆
 将磨粉后的物料加水制浆固含量 45%-60% ;
(4) 超细研磨
将制浆后的浆料加入上述浆料重量的 2.5% 的聚乙二醇, 搅拌均匀, 反应 15min,然后将上述物料进行湿式超细精磨 8小时;
(5) 干燥
 对超细研磨后的物料进行干燥得到超细硫酸钡粉末制品。
(6)、研磨改性 
将收集得到的硫酸钡粉再利用干法研磨打散,研磨速率为 1460r/min,并在研磨过程中加入改性剂,最终得到所述的超细改性硫酸钡。
所述的聚乙二醇的相对分子质量为4000。 
所述的改性剂为有机硅。 
本发明的技术方案,一种超细改性硫酸钡的制备工艺: 
第一步,将大块重晶石矿用颚式破碎机、锤式破碎机进行破碎均匀大小颗粒,此步骤为下部工序的的磨粉奠定了基础,使磨粉的颗粒大小更加均匀,粉粒更细,减少磨粉时间;第二步,将破碎均匀大小颗粒的重晶石矿用硫酸钡雷蒙磨磨粉至平均颗粒为 400 目,为制备料浆奠定了基础;第三步,将磨粉后的物料加水制浆固含量 45%-60%,其固含量应严格控制在45%-60%的范围内,保证了料浆的充分混合;第四步,将制浆后的浆料加入上述浆料重量的 2.5% 的聚乙二醇, 搅拌均匀,反应 15min,然后将上述物料进行湿式超细精磨 8小时,起反应时间不宜超过15min,否则会降低硫酸钡粉末的光泽度和白度,研磨时间为8小时可以充分保证产品的细度,时间过长反而增加生产本;第五步,干燥可采用利用喷雾干燥设备将浆料进行喷雾干燥,浆料的喷射速率为 46kg/min,干燥温度为 250-300℃, 利用旋风分离器收集外加布袋除尘器收集硫酸钡粉 ;最后一步,研磨改性,将收集得到的硫酸钡粉再利用干法研磨打散,研磨速率为 1460r/min,并在研磨过程中加入改性剂,最终得到所述的超细改性硫酸钡,其改性剂为有机硅提高了产品的流平性、光泽、耐水性。
本发明一种超细改性硫酸钡的制备工艺,其生产方法简单,成本低,且生出来的硫酸钡粉白度、流平性、光泽、耐水性都非常好,更加适用于工业生产中。 
对于本领域技术人员而言,显然本发明不限于上述示范性实施例的细节,而且在不背离本发明的精神或基本特征的情况下,能够以其他的具体形式实现本发明。因此,无论从哪一点来看,均应将实施例看作是示范性的,而且是非限制性的,本发明的范围由所附权利要求而不是上述说明限定,因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。 
  

Claims (3)

1.一种超细改性硫酸钡的制备工艺, 其特征在于, 包括以下步骤 :
(1)破碎
将大块重晶石矿用颚式破碎机、锤式破碎机进行破碎得到均匀大小颗粒;
(2) 磨粉
 将得到的破碎均匀大小颗粒的重晶石矿用硫酸钡雷蒙磨磨粉至平均颗粒为 400 目 ;
(3) 制浆
 将磨粉后的物料加水制浆固含量 45%-60% ;
(4) 超细研磨
将制浆后的浆料加入上述浆料重量的 2.5% 的聚乙二醇, 搅拌均匀, 反应 15min,然后将上述物料进行湿式超细精磨 8小时;
(5) 干燥
 对超细研磨后的物料进行干燥得到超细硫酸钡粉末制品;
(6)、研磨改性
将收集得到的硫酸钡粉再利用干法研磨打散,研磨速率为 1460r/min,并在研磨过程中加入改性剂,最终得到所述的超细改性硫酸钡。
2.根据权利要求 1 所述的一种超细改性硫酸钡的制备工艺, 其特征在于,所述的聚乙二醇的相对分子质量为4000。
3.根据权利要求 1 所述的一种超细改性硫酸钡的制备工艺, 其特征在于,所述的改性剂为有机硅。
CN201410426387.7A 2014-08-27 2014-08-27 一种超细改性硫酸钡的制备工艺 Pending CN104192886A (zh)