CN104190037B - 一种abc超细干粉灭火剂复合基材及其制备方法 - Google Patents
一种abc超细干粉灭火剂复合基材及其制备方法 Download PDFInfo
- Publication number
- CN104190037B CN104190037B CN201410455414.3A CN201410455414A CN104190037B CN 104190037 B CN104190037 B CN 104190037B CN 201410455414 A CN201410455414 A CN 201410455414A CN 104190037 B CN104190037 B CN 104190037B
- Authority
- CN
- China
- Prior art keywords
- dry powder
- base material
- fine dry
- composite base
- ultra
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及消防灭火领域,公开了一种ABC超细干粉灭火剂复合基材及其制备方法。该复合基材包括以下质量百分比的原料组分:3~5%的云母粉,余料为磷酸乙二胺。制备方法为:将烘干后的磷酸乙二胺和云母粉,经超音速气流粉碎、分级后,即可得到90%粒径小于等于10μm的基材颗粒。由此基材制取的ABC超细干粉灭火剂经加压喷射后,在封闭与半封闭的空间形成类似冷气溶胶的超细干粉灭火剂,它具备优异的淹没式灭火效能,优异的斥水性,贮存周期长,特别适用于水基、干粉复合喷射灭火。
Description
技术领域
本发明涉及消防灭火领域,特别涉及一种制备ABC超细干粉灭火剂的复合基材及其制备方法。
背景技术
目前,市场上销售的ABC干粉灭火剂主要用于A类、B类和C类火灾的灭火。制作ABC超细干粉灭火剂的基材,主要是磷酸二氢铵与硫酸铵复合材料或高聚合度的聚磷酸铵。前两种基材极易吸潮、易溶于水,以这两种基材制备灭火剂工艺较复杂,且灭火剂在较潮湿、振动环境下,易结成硬块,导致失效;后一种高聚合度的聚磷酸铵超细粉碎批量生产产量低,成本大,不适合工业化生产。
发明内容
针对现有技术中存在的问题,本发明的目的在于提供一种制作ABC超细干粉灭火剂的复合基材及其制备方法。本发明的复合基材以云母粉、磷酸乙二胺为材料,按照一定的比例混合,经超音速气流粉碎机粉碎分级后,即得,容易实现批量化超细粉碎。以本发明基材制作的ABC超细干粉灭火剂工艺较简单,各项性能指标符合GA578-2005要求,淹没式灭火效果更好,灭火效能高,小于等于120g/m3(GA578-2005要求的小于等于150g/m3),制取的灭火剂不但斥水性优异,吸湿率低,长期贮存不失效,而且特别适合用作水基、干粉复合喷射灭火剂、制备方法简单。
为了达到上述目的,本发明的技术方案如下。
(1)一种ABC超细干粉灭火剂复合基材,其特征在于,包括以下质量百分比的原料组分:云母粉3~5%,余料为磷酸乙二胺。
优选地,所述ABC超细干粉灭火剂复合基材90%粒径小于等于10μm。
优选地,所述ABC超细干粉灭火剂复合基材颗粒比表面积大于等于2.2m2/g。
优选地,所述磷酸乙二胺的90%粒径小于等于30μm。
优选地,所述云母粉的90%粒径小于等于50μm。
(2)上述ABC超细干粉灭火剂复合基材的制备方法,其特征在于,包括以下步骤:
步骤1,按照上述质量百分比称取各原料组分;
步骤2,磷酸乙二胺、云母粉分别烘干,其含水率分别小于等于0.20%,混合、搅拌均匀,得到中间料A;
步骤3,将中间料A用超音速气流粉碎机粉碎分级,即得90%粒径小于等于10μm的ABC超细干粉灭火剂的复合基材。
在本发明中,以磷酸乙二胺、云母粉为原料,制备ABC超细干粉灭火剂复合基材,用其制备的ABC超细干粉灭火剂的性能指标满足GA578-2005要求,制备的ABC超细干粉灭火剂90%粒径小于等于12μm,灭火效能高、优异的淹没式灭火效能,优异的斥水性,贮存周期长,特别适用于水基、干粉复合喷射灭火。
具体实施方式
以下结合具体实施例对本发明作进一步的详细说明,但本发明不限于这些实施例。
实施例1
制备超细干粉灭火剂的复合基材,具体包括以下步骤:
步骤1,以总原料1吨计称取各原料组分:30kg的云母粉(90%粒径小于等于50μm),余料为磷酸乙二胺(90%粒径小于等于30μm)。
步骤2,将云母粉、磷酸乙二胺分别烘干,满足含水率小于等于0.20%.
步骤3,将烘干后的云母粉、磷酸乙二胺加入高混机内混合、搅拌均匀得中间料A。
步骤4,将中间料A用超音速气流粉碎机粉碎分级,即得90%粒径小于等于10μm的ABC超细干粉灭火剂的复合基材。
实施例2
制备超细干粉灭火剂的复合基材,具体包括以下步骤:
步骤1,以总原料1吨计称取各原料组分:40kg的云母粉(90%粒径小于等于50μm),余料为磷酸乙二胺(90%粒径小于等于30μm)。
步骤2,将云母粉、磷酸乙二胺分别烘干,满足含水率小于等于0.20%。
步骤3,将烘干后的云母粉、磷酸乙二胺加入高混机内混合、搅拌均匀得中间料A。
步骤4,将中间料A用超音速气流粉碎机粉碎分级,即得90%粒径小于等于10μm的ABC超细干粉灭火剂的复合基材。
实施例3
制备超细干粉灭火剂的复合基材,具体包括以下步骤:
步骤1,以总原料1吨计称取各原料组分:45kg的云母粉(90%粒径小于等于50μm),余料为磷酸乙二胺(90%粒径小于等于30μm)。
步骤2,将云母粉、磷酸乙二胺分别烘干,满足含水率小于等于0.20%.
步骤3,将烘干后的云母粉、磷酸乙二胺加入高混机内混合、搅拌均匀得中间料A。
步骤4,将中间料A用超音速气流粉碎机粉碎分级,即得90%粒径小于等于10μm的ABC超细干粉灭火剂的复合基材。
实施例4
制备超细干粉灭火剂的复合基材,具体包括以下步骤:
步骤1,以总原料1吨计称取各原料组分:50kg的云母粉(90%粒径小于等于50μm),余料为磷酸乙二胺(90%粒径小于等于30μm)。
步骤2,将云母粉、磷酸乙二胺分别烘干,满足含水率小于等于0.20%.
步骤3,将烘干后的云母粉、磷酸乙二胺加入高混机内混合、搅拌均匀得中间料A。
步骤4,将中间料A用超音速气流粉碎机粉碎分级,即得90%粒径小于等于10μm的ABC超细干粉灭火剂的复合基材。
将实施例1-4得到的复合基材按同样的工艺进一步加工成ABC超细干粉灭火剂,对灭火剂各项性能进行检测,性能如下表1所示:
表1 ABC超细干粉灭火剂性能
实施例1-4所制备的超细干粉灭火剂的灭火特性如下表2所示。
表2 ABC超细干粉灭火剂灭火特性
表1的粉体综合特性、性能和表2的灭火性能,说明实施例1-4所制备的超细干粉灭火剂具有优良的灌装、贮存、输送、喷射和灭火性能;并且实验表明该超细干粉灭火剂通过压缩气体喷射后形成的冷气溶胶灭火剂,不仅具有优异的灭火效能,而且具有可压缩性、流动性和弥散性等气体灭火剂灭火应用的典型特点,能够实现全淹没的灭火方式。当射入有限空间内的冷气溶胶灭火剂达到灭火浓度时,可使火焰在极短时间内熄灭,即使火源被障碍物遮蔽,冷气溶胶灭火剂也会绕开障碍物而快速扑灭有限空间内的ABC类火灾,满足GA578-2005的相关要求。如果将该干粉灭火剂应用于移动式灭火装置,将超细干粉灭火剂射流对准火灾的火源根部喷射,使得局部产生较高的灭火剂浓度,更有利于快速扑灭火灾。
此外,此基材制成的超细干粉灭火剂吸湿率值小,斥水性能优异,不但利于长期贮存,而且特别适应用作水基、干粉复合喷射灭火设备的灭火剂。
Claims (6)
1.一种ABC超细干粉灭火剂复合基材,其特征在于,包括以下质量百分比的原料组分:云母粉3~5%,余料为磷酸乙二胺。
2.根据权利要求1所述的ABC超细干粉灭火剂复合基材,其特征在于,所述ABC超细干粉灭火剂复合基材90%粒径小于等于10μm。
3.根据权利要求1或2所述的ABC超细干粉灭火剂复合基材,其特征在于,所述ABC超细干粉灭火剂复合基材颗粒比表面积大于等于2.2m2/g。
4.根据权利要求1所述的ABC超细干粉灭火剂复合基材,其特征在于,所述磷酸乙二胺的90%粒径小于等于30μm。
5.根据权利要求1所述的ABC超细干粉灭火剂复合基材,其特征在于,所述云母粉的90%粒径小于等于50μm。
6.一种ABC超细干粉灭火剂复合基材的制备方法,其特征在于,包括以下步骤:
步骤1,按照权利要求1所述的超细干粉灭火剂复合基材的质量百分比称取各原料组分;
步骤2,磷酸乙二胺、云母粉分别烘干,其含水率分别小于等于0.20%;
步骤3,将烘干后的磷酸乙二胺、云母粉加入高混机内,混合均匀,得中间料A;
步骤4,将中间料A用超音速气流粉碎机粉碎分级,即得90%粒径小于等于10μm的ABC超细干粉灭火剂的复合基材。