CN104163432A - 酸化后的蛭石 - Google Patents
酸化后的蛭石 Download PDFInfo
- Publication number
- CN104163432A CN104163432A CN201410358767.1A CN201410358767A CN104163432A CN 104163432 A CN104163432 A CN 104163432A CN 201410358767 A CN201410358767 A CN 201410358767A CN 104163432 A CN104163432 A CN 104163432A
- Authority
- CN
- China
- Prior art keywords
- vermiculite
- batching
- acidifying
- acidized
- flap
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种酸化后的蛭石,其技术方案的要点是,酸化后的蛭石配料由膨胀蛭石、凹凸棒石粘土、氧化镁、硫酸、速溶硅酸钠、聚乙烯醇、羟丙基甲基纤维素和碳酸钠组成;将酸化后的蛭石配料输入磨机中磨粉,磨粉后的粉状物为酸化后的蛭石。酸化后的蛭石的生产方法采取先酸化再进行复合配料,可以避免硫酸与速溶硅酸钠、聚乙烯醇、羟丙基甲基纤维素和碳酸钠发生化学反应;蛭石经过酸化处理后,pH值控制在5.0~7.0,可以提高膨胀蛭石的利用率。酸化后的蛭石具有较好的吸附性、触变性、热稳定性、可塑性和粘结性的特点。酸化后的蛭石适用于生产环保材料、园林材料、建筑材料、发泡剂和消防产品。
Description
技术领域
本发明涉及酸化处理,具体涉及一种酸化后的蛭石。
背景技术
蛭石是一种天然、无毒的矿物质,在高温作用下会膨胀的矿物。它是一种比较少见的矿物,属于硅酸盐。其晶体结构为单斜晶系,从外形上它看上去像云母。由于蛭石有离子交换的能力,它对土壤的营养有极大的作用。
蛭石是一种与蒙脱石相似的粘土矿物,为层状结构的硅酸盐。一般由黑云母经热液蚀变或风化形成。它有时以粗大的黑云母样子出现有时则细微得成为土壤状。把蛭石加热到300℃时,它能膨胀20倍并发生弯曲。蛭石一般为褐、黄、暗绿色,有油一样的光泽,加热后变成灰色。生蛭石片经过高温焙烧后,其体积能迅速膨胀数倍至数十倍,体积膨胀后的蛭石就叫膨胀蛭石,
在自然界里在温泉的溶液中由黑云母等矿物产生。在自然界里它们与土壤中的粘土混合在一起,而且无法从粘土中分出来。
为了提高蛭石的应用质量,需要对蛭石进行酸化处理。
发明内容
本发明的目的是克服现有技术中不足之处,提供一种酸化后的蛭石。
酸化后的蛭石配料由膨胀蛭石、凹凸棒石粘土、氧化镁、硫酸、速溶硅酸钠、聚乙烯醇、羟丙基甲基纤维素和碳酸钠组成。
酸化后的蛭石的生产方法:将酸化后的蛭石配料输入磨机中磨粉,磨粉后的粉状物为酸化后的蛭石。
蛭石是一种天然、无毒的硅酸盐矿物质,在高温作用下会膨胀的矿物,生蛭石片经过高温焙烧后,其体积能迅速膨胀数倍至数十倍,体积膨胀后的蛭石叫膨胀蛭石,是世界上最轻的矿物之一。
膨胀蛭石具有很强的保温隔热性能、阳离子交换性和吸附性,还具有良好的吸水性、隔音性、耐冻性、隔热性和耐火性,膨胀蛭石的化学性质稳定。本发明选用粉碎后的膨胀蛭石,膨胀蛭石的颗粒细度≤0.5毫米。
凹凸棒石粘土具有独特的层链状结构特征,晶体呈针状,纤维状或纤维集合状。凹凸棒石粘土具有独特的分散、耐高温、抗盐碱等良好的胶体性质和较高的吸附能力,并具有一定的可塑性及粘结力,本发明选用凹凸棒石粘土的颗粒细度≤5毫米。
氧化镁具有碱性氧化物的通性,属于胶凝材料,能提高蛭石的胶体性能。
硫酸选用浓度为98%的浓硫酸。
速溶硅酸钠为白色粉状物料,能快速溶解于水,具有粘结力强、强度较高,耐酸性、耐热性好,耐碱性和耐水性差的特点。
聚乙烯醇系白色固体,外型分絮状、颗粒状、粉末状三种;无毒无味、颗粒状可在80--90℃水中溶解,粉末状的在其他粉料的预分散后可在常温下溶解。具有较好的粘稠度、聚合性、粘结性及保水性。
羟丙基甲基纤维素具有增稠能力、排盐性、pH稳定性、保水性、尺寸稳定性、优良的成膜性以及广泛的耐酶性、分散性和粘结性等特点。
碳酸钠具有盐的通性和热稳定性,易溶于水,其水溶液呈碱性,在本发明中用于调整酸化后的蛭石pH值。
本发明通过下述技术方案予以实现:
1、酸化后的蛭石配料按重量百分比由下列组分组成:酸化后的蛭石半成品90~98%、速溶硅酸钠0.1~5%、聚乙烯醇0.1~5%、羟丙基甲基纤维素0.01~3%和碳酸钠0~3%。
2、酸化后的蛭石的生产方法:将酸化后的蛭石配料输入磨机中磨粉,颗粒细度≤0.074毫米,磨粉后的粉状物为酸化后的蛭石成品。
3、酸化后的蛭石半成品的生产方法:⑴将蛭石混合物的配料输入已经运转的搅拌机中搅拌,再将稀硫酸缓慢加入蛭石混合物中进行酸化处理;⑵将酸化处理后的蛭石混合物,通过对辊机挤压为蛭石片状物,蛭石片状物的厚度≤3毫米;⑶将蛭石片状物输送到回转式烘干炉内焙烧,焙烧时间为1~3小时,焙烧温度控制在300~400℃,焙烧后的蛭石片状物含水量≤2%,焙烧后的蛭石片状物为酸化后的蛭石半成品,含水量百分比为重量百分比。
4、蛭石片状物的配料按重量百分比由下列组分组成:蛭石混合物75~95%和稀硫酸5~25%。
5、蛭石混合物的配料按重量百分比由下列组分组成:膨胀蛭石68~92%、凹凸棒石粘土5~30%和氧化镁0.1~3%。
6、稀硫酸的配料按重量百分比由下列组分组成:浓度为98%的浓硫酸1~25%和水75~99%,浓度为98%的浓硫酸百分比为重量百分比。
酸化后的蛭石的生产方法采取先酸化再进行复合配料,可以避免硫酸与速溶硅酸钠、聚乙烯醇、羟丙基甲基纤维素和碳酸钠发生化学反应,充分发挥配料中原材料的各自特性,并得到互补,确保酸化后的蛭石内在质量。
根据产品质量的需要,采用碳酸钠调整酸化后的蛭石pH值,方法简单易行。
膨胀蛭石经过酸化处理后,pH值控制在5.0~7.0,可以提高膨胀蛭石的利用率。
酸化后的蛭石具有较好的吸附性、触变性、热稳定性、可塑性和粘结性的特点。
酸化后的蛭石适用于生产环保材料、园林材料、建筑材料、发泡剂和消防产品。
具体实施方式
下面结合实施例对本发明作进一步的描述:
1、酸化后的蛭石配料按重量百分比由下列组分组成:酸化后的蛭石半成品95%、速溶硅酸钠2%、聚乙烯醇2.2%、羟丙基甲基纤维素0.8%和碳酸钠0%。
2、酸化后的蛭石的生产方法:将酸化后的蛭石配料输入磨机中磨粉,颗粒细度≤0.074毫米,磨粉后的粉状物为酸化后的蛭石成品。
3、酸化后的蛭石半成品的生产方法:⑴将蛭石混合物的配料输入已经运转的搅拌机中搅拌,再将稀硫酸缓慢加入蛭石混合物中进行酸化处理;⑵将酸化处理后的蛭石混合物,通过对辊机挤压为蛭石片状物,蛭石片状物的厚度≤3毫米;⑶将蛭石片状物输送到回转式烘干炉内焙烧,焙烧时间为2小时,焙烧温度控制在300~350℃,焙烧后的蛭石片状物含水量≤2%,焙烧后的蛭石片状物为酸化后的蛭石半成品。
4、蛭石片状物的配料按重量百分比由下列组分组成:蛭石混合物78%和稀硫酸22%。
5、蛭石混合物的配料按重量百分比由下列组分组成:膨胀蛭石7476%、凹凸棒石粘土22%和氧化镁2%。
6、稀硫酸的配料按重量百分比由下列组分组成:浓度为98%的浓硫酸6%和水94%。
Claims (7)
1.一种酸化后的蛭石,其特征在于,酸化后的蛭石配料按重量百分比由下列组分组成:酸化后的蛭石半成品90~98%、速溶硅酸钠0.1~5%、聚乙烯醇0.1~5%、羟丙基甲基纤维素0.01~3%和碳酸钠0~3%。
2.根据权利要求1所述酸化后的蛭石的生产方法,其特征在于,将酸化后的蛭石配料输入磨机中磨粉,颗粒细度≤0.074毫米,磨粉后的粉状物为酸化后的蛭石成品。
3.根据权利要求1所述酸化后的蛭石半成品的生产方法,其特征在于,⑴将蛭石混合物的配料输入已经运转的搅拌机中搅拌,再将稀硫酸缓慢加入蛭石混合物中进行酸化处理;⑵将酸化处理后的蛭石混合物,通过对辊机挤压为蛭石片状物,蛭石片状物的厚度≤3毫米;⑶将蛭石片状物输送到回转式烘干炉内焙烧,焙烧时间为1~3小时,焙烧温度控制在300~400℃,焙烧后的蛭石片状物含水量≤2%,焙烧后的蛭石片状物为酸化后的蛭石半成品。
4.根据权利要求3所述蛭石片状物的配料,其特征在于,蛭石片状物的配料按重量百分比由下列组分组成:蛭石混合物75~95%和稀硫酸5~25%。
5.根据权利要求4所述蛭石混合物的配料,其特征在于,蛭石混合物的配料按重量百分比由下列组分组成:膨胀蛭石68~92%、凹凸棒石粘土5~30%和氧化镁0.1~3%。
6.根据权利要求4所述稀硫酸的配料,其特征在于,稀硫酸的配料按重量百分比由下列组分组成:浓度为98%的浓硫酸1~25%和水75~99%。
7.根据权利要求5所述蛭石混合物的配料,其特征在于,选用膨胀蛭石的颗粒细度≤0.5毫米,凹凸棒石粘土的颗粒细度≤5毫米。