CN104152072B - 高可靠性导热胶带的制备工艺 - Google Patents

高可靠性导热胶带的制备工艺 Download PDF

Info

Publication number
CN104152072B
CN104152072B CN201410357068.5A CN201410357068A CN104152072B CN 104152072 B CN104152072 B CN 104152072B CN 201410357068 A CN201410357068 A CN 201410357068A CN 104152072 B CN104152072 B CN 104152072B
Authority
CN
China
Prior art keywords
heat conduction
parts
adhesive tape
preparation technology
high reliability
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410357068.5A
Other languages
English (en)
Other versions
CN104152072A (zh
Inventor
金闯
梁豪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Taicang Sidike New Material Science and Technology Co Ltd
Original Assignee
Suzhou Sidike New Material Science and Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Sidike New Material Science and Technology Co Ltd filed Critical Suzhou Sidike New Material Science and Technology Co Ltd
Priority to CN201410357068.5A priority Critical patent/CN104152072B/zh
Publication of CN104152072A publication Critical patent/CN104152072A/zh
Application granted granted Critical
Publication of CN104152072B publication Critical patent/CN104152072B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开一种高可靠性导热胶带的制备工艺，包括以下步骤：将0.2~0.5份交联剂与70~135份甲苯、80~85份乙酸乙酯和60~70份丁酮均匀混合获得稀释物；将85份石墨粉与第一步稀释物混合均匀，并在84~86℃条件搅拌形成混合液，此石墨粉直径为3~6微米；将100份丙烯酸酯胶粘剂与第二步的混合液混合，并经高速搅拌器分散2~10小时，从而混合均匀形成导热胶粘混合溶剂；0.4~0.6份偶联剂加入胶黏剂，搅拌0.5-1小时。本发明在长度和厚度方向大大提高了导热性，且克服了长时间导热时大大降低低粘接层的粘度的技术缺陷，能长时间保持与电子器件的接触强度的粘贴强度，实现了散热性能的稳定性，从而进一步提高胶带的使用寿命。

Description

高可靠性导热胶带的制备工艺
技术领域
本发明涉及一种高可靠性导热胶带的制备工艺，属于胶粘材料技术领域。
背景技术
从普通的台式电脑，到笔记本电脑，平板电脑，智能手机，科技创新突飞猛进。电子产品携带越来越轻便化，体积越来越小，功能越来越强大，这样导致集成度越来越高。这样导致体积在缩小，功能变强大，直接导致电子元器件的散热要求越来越高。而以前采用的风扇式散热，由于体积大，会产生噪音等问题，逐渐被市场淘汰。进而产生了其它的散热材料，如铜箔、铝箔类散热，但是由于资源有限，而且价格昂贵，散热效果也没有想象中的好，慢慢的，都在寻找新的高效的散热材料。其次，由于电子产品的多样性，现有的产品往往需要定制，从而难适用具体的使用场合且限制了其应用的推广；因此，如果设计一种针对电子产品特点的具有高性能散热胶带，成为本领域普通技术人员努力的方向。
发明内容
本发明目的是提供一种高可靠性导热胶带的制备工艺，该制备工艺获得的导热胶带在长度和厚度方向大大提高了导热性，且克服了长时间导热时大大降低粘接层的粘度的技术缺陷，能长时间保持与电子器件的接触强度的粘贴强度，实现了散热性能的稳定性。
为达到上述目的，本发明采用的技术方案是：一种高可靠性导热胶带的制备工艺，其特征在于：包括以下步骤：
第一步，将0.2~0.5份交联剂与70~135份甲苯、80~85份乙酸乙酯和60~70份丁酮均匀混合获得稀释物，此交联剂选自以下通式（）的化合物，
（）；
式中，R1、R2、R3各自独立地代表碳原子数为3~8的酮的碳链上去除一个氢原子后的残基，M为Al；
第二步：将85份石墨粉与第一步稀释物混合均匀，并在84~86℃条件搅拌形成混合液，此石墨粉直径为3~6微米；
第三步：将100份丙烯酸酯胶粘剂与第二步的混合液混合，并经高速搅拌器分散2~10小时，从而混合均匀形成导热胶粘混合溶剂；
第四步：0.4~0.6份偶联剂加入胶黏剂，搅拌0.5-1小时；
第五步：将第三步获得的导热胶粘混合溶剂涂布于上表面具有铝箔层的PET薄膜的下表面；
第六步：对第四步中的导热胶粘混合溶剂进行烘烤形成导热胶粘层；
第七步：将第五步中经过烘烤的导热胶粘层另一表面贴合离型材料；
第八步：收卷。
上述技术方案中进一步改进的方案如下：
1、上述方案中，所述PET薄膜、导热胶粘层和铝箔层的厚度比为100：100~300：10~100。
2、上述方案中，所述第二步的搅拌温度为85℃。
3、上述方案中，所述PET薄膜厚度为0.004mm~0.025mm。
由于上述技术方案运用，本发明与现有技术相比具有下列优点和效果：
1、本发明制备工艺获得高可靠性导热胶带在长度和厚度方向大大提高了导热性，且克服了长时间导热时大大降低低粘接层的粘度的技术缺陷，能长时间保持与电子器件的接触强度的粘贴强度，实现了散热性能的稳定性，从而进一步提高胶带的使用寿命。
2、本发明配方中添加特定的交联剂，克服了长时间导热时大大降低低粘接层的粘度的技术缺陷，能长时间保持与电子器件的接触强度的粘贴强度，实现了散热性能的稳定性，从而进一步提高胶带的使用寿命
3、本发明采用三种特定含量的组分作为溶剂，有效避免了石墨颗粒在后续工艺丙烯酸酯胶粘体系中团聚现象，从而有利于长度和厚度方向导热同步提高；
4、本发明根据其配方特定，采用直径为3~6微米的石墨和厚度比为10：10~30：1~10依次叠加的PET薄膜、导热胶粘层和铝箔层的导热贴膜，在兼顾现有贴膜性能同时，更有利于电子器件的热量分散和传输，从而进一步避免了胶带局部热量的集中，提高了产品的使用寿命。
具体实施方式
下面结合实施例对本发明作进一步描述：
实施例：一种高可靠性导热胶带的制备工艺，包括以下步骤：
第一步，将0.4份交联剂与90份甲苯、80份乙酸乙酯和60份丁酮均匀混合获得稀释物，此交联剂选自以下通式（）的化合物，
（）；
式中，R1、R2、R3各自独立地代表碳原子数为3~8的酮的碳链上去除一个氢原子后的残基，M为Al；
第二步：将85份石墨粉与第一步稀释物混合均匀，并在84~86℃条件搅拌形成混合液，此石墨粉直径为4.8~5微米；
第三步：将100份丙烯酸酯胶粘剂与第二步的混合液混合，并经高速搅拌器分散2~10小时，从而混合均匀形成导热胶粘混合溶剂；
第四步：0.4~0.6份偶联剂加入胶黏剂，搅拌0.5-1小时；
第五步：将第三步获得的导热胶粘混合溶剂涂布于上表面具有铝箔层的PET薄膜的下表面；
第六步：对第四步中的导热胶粘混合溶剂进行烘烤形成导热胶粘层；
第七步：将第五步中经过烘烤的导热胶粘层另一表面贴合离型材料；
第八步：收卷。
上述PET薄膜、导热胶粘层和铝箔层的厚度比为10：28：5。
上述第二步的搅拌温度为85℃；上述PET薄膜厚度为0.004mm~0.025mm。
上述实施例只为说明本发明的技术构思及特点，其目的在于让熟悉此项技术的人士能够了解本发明的内容并据以实施，并不能以此限制本发明的保护范围。凡根据本发明精神实质所作的等效变化或修饰，都应涵盖在本发明的保护范围之内。

Claims (4)

1.一种高可靠性导热胶带的制备工艺，其特征在于：包括以下步骤：
第一步，将0.2~0.5份交联剂与70~135份甲苯、80~85份乙酸乙酯和60~70份丁酮均匀混合获得稀释物，此交联剂选自以下通式（）的化合物，
（）；
式中，R1、R2、R3各自独立地代表碳原子数为3~8的酮的碳链上去除一个氢原子后的残基，M为Al；
第二步：将85份石墨粉与第一步稀释物混合均匀，并在84~86℃条件搅拌形成混合液，此石墨粉直径为3~6微米；
第三步：将100份丙烯酸酯胶粘剂与第二步的混合液混合，并经高速搅拌器分散2~10小时，从而混合均匀形成胶黏剂；
第四步：0.4~0.6份偶联剂加入步骤三的胶黏剂获得导热胶粘混合物，搅拌0.5-1小时；
第五步：将第四步获得的导热胶粘混合物涂布于上表面具有铝箔层的PET薄膜的下表面；
第六步：对第五步中的导热胶粘混合物进行烘烤形成导热胶粘层；
第七步：将第六步中经过烘烤的导热胶粘层另一表面贴合离型材料；
第八步：收卷。
2.根据权利要求1所述高可靠性导热胶带的制备工艺，其特征在于：所述PET薄膜、导热胶粘层和铝箔层的厚度比为100：100~300：10~100。
3.根据权利要求1所述高可靠性导热胶带的制备工艺，其特征在于：所述第二步的搅拌温度为85℃。
4.根据权利要求1所述高可靠性导热胶带的制备工艺，其特征在于：所述PET薄膜厚度为0.004mm~0.025mm。
CN201410357068.5A 2012-12-18 2012-12-18 高可靠性导热胶带的制备工艺 Active CN104152072B (zh)