CN104130688B - 连续变色室内装饰涂料及制备方法 - Google Patents

连续变色室内装饰涂料及制备方法 Download PDF

Info

Publication number
CN104130688B
CN104130688B CN201410398041.0A CN201410398041A CN104130688B CN 104130688 B CN104130688 B CN 104130688B CN 201410398041 A CN201410398041 A CN 201410398041A CN 104130688 B CN104130688 B CN 104130688B
Authority
CN
China
Prior art keywords
variable color
indoor decorative
decorative paint
speed
acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410398041.0A
Other languages
English (en)
Other versions
CN104130688A (zh
Inventor
龚文龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Foshan New Auckland Chemical Coating Co ltd
Original Assignee
Ningbo Doorbell Household Supplies Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ningbo Doorbell Household Supplies Industry Co Ltd filed Critical Ningbo Doorbell Household Supplies Industry Co Ltd
Priority to CN201410398041.0A priority Critical patent/CN104130688B/zh
Publication of CN104130688A publication Critical patent/CN104130688A/zh
Application granted granted Critical
Publication of CN104130688B publication Critical patent/CN104130688B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及到一种连续变色室内装饰涂料，其包括下述重量组成：

Description

连续变色室内装饰涂料及制备方法
技术领域
本发明涉及到涂料领域，具体指一种连续变色室内装饰涂料及制备方法。
背景技术
光致变色指的是某些化合物在一定的波长和强度的光作用下分子结构会发生变化，从而导致其对光的吸收峰值即颜色的相应改变，且这种改变一般是可逆的。变色涂料是涂层的颜色随环境条件变化的涂料，目前市面上已存在多种类型的变色涂料，根据光源的不同，涂层呈现出不同的颜色，在日常生活中，能够缓解民众的视觉疲劳，带来视觉上的新鲜感，在室内装饰物涂料，室内家具表面涂料等家居用品的使用尤为广泛。
目前大部分变色涂料仅仅是一种颜色变化到另一种颜色，其不能随着周围环境的变化变换为多种颜色。
发明内容
本发明所要解决的技术问题是针对现有技术的现状提供一种能随周围环境变化而该换为多种颜色的连续变色室内装饰涂料。
本发明的所要解决的另一个技术问题是提供一种能随周围环境变化而该换为多种颜色的连续变色室内装饰涂料的制备方法。
本发明解决上述技术问题所采用的技术方案为：该连续变色室内装饰涂料，其特征在于包括下述重量组成：
其中，所述配位化合物为Cu(phen)2(NO3)2或Fe(phen)3(ClO4)2；
所述填料为轻质碳酸钙和/或微细滑石粉；所述轻质碳酸钙含量≥98％，平均粒径≤3μm，吸油量为25～60g/100g，pH值为9-10；所述微细滑石粉粒径为1200-1300目、密度为2.5-3.0g/cm3、折射率为1.5-1.6、吸油量为20-30g/100g；
所述杂多酸光敏剂为硅钨酸H4SiW12O40、磷钨酸H3PW12O40或磷钼酸H3PMo12O40。
上述连续变色室内装饰涂料的制备方法，其特征在于包括下述步骤：
取40-50wt％的聚氨酯乳液置于分散机下，然后依次加入四分之三重量的FoamasterA34和TEGO Disper 752，控制转速为900-1100rpm，搅拌5-7分钟；
然后缓慢加入轻质碳酸钙和微细滑石粉，加入时以不溅起乳液为准，10分钟内提速至1500～2000rpm，搅拌18-22min；得到第一混合物；
将第一混合物料置于三辊机上研磨至粒径≤30μm，出料得透明底漆浆；
将配位化合物、EFC-300和杂多酸合均匀，得到第二混合物；
在900-1100rpm下，将剩余的Foamaster A34加入到剩余的乳液中，然后加入第二混合物，搅拌9-11min；
改变搅拌速率为1500～2000rpm，以1L/min的速度加入所述的底漆浆，搅拌4-7分钟后依次加入SN-thickener 641和Levelling 620，搅拌分散18-22分钟后，降低搅拌速度为900-1100rpm，加入分析纯氨水，调节pH值为7-8；
停止搅拌，待气泡消失后，过滤即得到连续变色室内装饰涂料。
与现有技术相比，本发明所提供的涂料配方能够在不同强度的光照下变换为不同的颜色；并且本申请中各组分协同作用，减少了成膜助剂的使用量，降低了挥发性有毒有机物的使用；该产品在细度，干燥时间，稳定性，涂抹外观和耐水性等各项性能均优于国家标准GB/T 23999-2009《室内装饰装修用水性木器涂料》中关于透明底漆A类和B类(地板、家具类)的规定。
具体实施方式
以下结合实施例对本发明作进一步详细描述。
实施例1
用分析纯氨水调节pH值为7.5。
其中轻质碳酸钙含量≥98％，平均粒径≤3μm，吸油量为25-60g/100g，pH值为9-10，是一种碱性颜料。微细滑石粉的粒径为1250目，密度为2.8g/cm3，折射率为1.59，吸油量为25g/100g。
填料为龙胜三门发龙滑石制品厂生产。
聚氨酯乳液乳液为嘉宝莉公司生产，工业级。
TEGO Disper 752为德国EVONIK-degussa(赢创德固赛)公司生产。
Foamaster A34为德国Cognis(科宁)化工科技有限公司生产。
SN-thickener 641为日本San Nopco(圣诺普科)有限公司生产。
Levelling 620为德国Cognis(科宁)化工科技有限公司生产。
三种杂多酸为吉林省恒汇工贸有限公司生产。
配位化合物为Sigma-Aldrich生产。
制备方法如下：
取所述乳液的40％置于分散机下，然后依次加入四分之三的Foamaster A34、TEGODisper 752，控制转速为1000rpm，搅拌6分钟。
然后缓慢加入轻质碳酸钙和微细滑石粉，加入时以不溅起乳液为要求，10分钟内提速至1500～2000rpm，搅拌18-22min。
将上述混合物料置于三辊机上研磨至粒径≤30μm，出料得透明底漆浆；
将配位化合物、EFC-300和杂多酸混合均匀，得到第一混合物；
在1000rpm下，将剩余的Foamaster A34加入到剩余的乳液中，然后加入第一混合物，搅拌10min；
改变搅拌速度为1700rpm，以1L/min的速度加入所述的底漆浆，搅拌6分钟后依次加入SN-thickener 641和Levelling 620，搅拌分散20分钟后，降低搅拌速度为1000rpm，加入分析纯氨水，调节pH值为7.5；
停止搅拌，待气泡消失后，过滤，出料得到涂料。
实施例2
用分析纯氨水调节pH值为7.5。
其余内容与实施例1相同，检测结果见表1-表3。
实施例3
用分析纯氨水调节pH值为7.5。
其余内容与实施例1相同，检测结果见表1-表3。
实施例4
用分析纯氨水调节pH值为7.5。
其余内容与实施例1相同，检测结果见表1-表3。
对比例1
用分析纯氨水调节pH值为7.5。
其余内容与实施例1相同，检测结果见表1-表3。
对比例2
用分析纯氨水调节pH值为7.5。
其余内容与实施例1相同，检测结果见表1-表3。
对比例3
用分析纯氨水调节pH值为7.5。
其余内容与实施例1相同，检测结果见表1-表3。
对实施例1至实施例4和对比例1至对比例3进行性能测试。
(1)取上述各实施例所制备的木涂料分别置于25ml量筒中，搅拌均匀，记录总体积V，静置30天后，观察分层现象，读取其沉降后的体积Vs，Vs/V即为沉降体积分数。沉降体积分数越大，说明涂料静置后各组分越稳定，水相跟各种助剂均一分散，则说明产品稳定性越好。
(2)按国标GB6783测试涂料性能，且分别考察产品在50℃烘箱中贮存7天和30天的稳定性。贮存稳定性按照优劣分为10级，其中10级最好，0级最差。
(3)按国标GB6783涂布式样后，式样置于暗室，等表干以后，式样放置于不同瓦数的白炽灯下照射，记录涂料变色时间。
表1
表2(Cu配合物)
表3(Fe配合物)
由表1至表3测试结果可以得知，实施例1至实施例4的各项性能均优于国家标准GB/T 23999-2009的规定，尤其是表干小于30 min，实干小于4 h，并且耐水性好和贮存稳定性好。涂料在1小时之内能够实现颜色的变化。表2中，对于含Cu配合物配方，在不同瓦数光照下，颜色从淡绿色，橙黄色，绿色，蓝绿色不断变化，原因在于在光照下杂多酸本身实现变色，Cu配合物则随着光照价态变化，从而使得颜色逐渐变化。对比例2由于不加Cu配合物，颜色为单一的杂多酸光照变为杂多蓝的颜色，对比例3中，Cu配合物量偏少，颜色变化与实施例1，2有所差别。表2为含Fe配合物例子，可见在不同光照强度下，也实现了涂料颜色变化。

Claims (1)

1.连续变色室内装饰涂料，其特征在于包括下述重量组成：
其中，所述配位化合物为Cu(phen)2(NO3)2或Fe(phen)3(ClO4)2；
所述填料为轻质碳酸钙和/或微细滑石粉；所述轻质碳酸钙含量≥98％，平均粒径≤3μm，吸油量为25～60g/100g，pH值为9-10；所述微细滑石粉粒径为1200-1300目、密度为2.5-3.0g/cm3、折射率为1.5-1.6、吸油量为20-30g/100g；
所述杂多酸光敏剂为硅钨酸H4SiW12O40、磷钨酸H3PW12O40或磷钼酸H3PMo12O40；
该连续变色室内装饰涂料的制备方法如下：
取40-50wt％的聚氨酯乳液置于分散机下，然后依次加入四分之三重量的Foamaster A34和TEGO Disper 752，控制转速为900-1100rpm，搅拌5-7分钟；
然后缓慢加入轻质碳酸钙和微细滑石粉，加入时以不溅起乳液为准，10分钟内提速至1500～2000rpm，搅拌18-22min；得到第一混合物；
将第一混合物料置于三辊机上研磨至粒径≤30μm，出料得透明底漆浆；
将配位化合物、EFC-300和杂多酸光敏剂混合均匀，得到第二混合物；
在900-1100rpm下，将剩余的Foamaster A34加入到剩余的乳液中，然后加入第二混合物，搅拌9-11min；
改变搅拌速率为1500～2000rpm，以1L/min的速度加入所述的底漆浆，搅拌4-7分钟后依次加入SN-thickener 641和Levelling 620，搅拌分散18-22分钟后，降低搅拌速度为900-1100rpm，加入分析纯氨水，调节pH值为7-8；
停止搅拌，待气泡消失后，过滤即得到连续变色室内装饰涂料。
CN201410398041.0A 2014-08-13 2014-08-13 连续变色室内装饰涂料及制备方法 Active CN104130688B (zh)