CN104120015B - Cutting fluid that a kind of antirust, anti-corrosive lubricity cooling is good and preparation method thereof - Google Patents
Cutting fluid that a kind of antirust, anti-corrosive lubricity cooling is good and preparation method thereof Download PDFInfo
- Publication number
- CN104120015B CN104120015B CN201410305509.7A CN201410305509A CN104120015B CN 104120015 B CN104120015 B CN 104120015B CN 201410305509 A CN201410305509 A CN 201410305509A CN 104120015 B CN104120015 B CN 104120015B
- Authority
- CN
- China
- Prior art keywords
- auxiliary agent
- antirust
- cooling
- cutting fluid
- lubricity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses the good cutting fluid of a kind of antirust, anti-corrosive lubricity cooling, it is characterized in that, made by the raw material of following weight portion: dodecenylsuccinic acid 2-3, mercaptobenzothiazoler 1-2, BTA 2-3, magnesia 4-6, methyl oleate 1.5-3, dioctylis sulfosuccinas natricus 4-5, soybean oil 4-6, oleoyl chloride 1-1.5, auxiliary agent 5-7, deionized water 200; The present invention adds dodecenylsuccinic acid, mercaptobenzothiazoler etc. and has antirust, corrosion-resistant effect; Add auxiliary agent, strengthened wear-resistant, disperse, lubricated, film forming; The present invention has excellent lubricated abrasion resistance, cleans cooling and corrosion-resisting resisting resistance, has effectively protected cutter, has improved crudy; Adopt water prescription, good cooling results, greatly takes away the heat producing in process, and cost is low, simple for process.
Description
Technical field
The present invention relates to cutting fluid field, particularly good cutting fluid and the preparation thereof of a kind of antirust, anti-corrosive lubricity coolingMethod.
Background technology
In mechanical processing industry, be substantially with lubricating oil or with kerosene apply oil cut lubricated withCooling. Cutting fluid comprises the oil base cutting fluid that contains mineral oil and additive, contains polyethylene glycol or polypropylene glycol as mainlyThe glycol-based cutting fluid of component, and the water-based cutting fluid of aqueous surfactant solution form. Oil base cutting fluid is at cutting pointCooling effect is poor, and oil base cutting fluid can be polluted workpiece or instrument, need to further clean with organic solvent, to environment notClose friend, aspect the dispersion stabilization of viscosity stability in cutting operation of glycol-based cutting fluid and water-based cutting fluid and abrasive materialShow poor. In process, oil product waste is very serious, and environment and operating personnel are caused to very large injury; And veryThe desirable finished surface of difficult acquisition. And it is slow to add man-hour radiating rate, after processing work, very easily upper rust. Be badly in need of now design lubricatedProperty is good, and rustless property is superior, the cutting fluid that cooling velocity is fast, cleaning performance is good.
Summary of the invention
The object of this invention is to provide cutting fluid that a kind of antirust, anti-corrosive lubricity cooling is good and preparation method thereof.
In order to realize object of the present invention, the present invention passes through following scheme implementation:
The good cutting fluid of antirust, anti-corrosive lubricity cooling, is made up of the raw material of following weight portion: laurylene base fourthDiacid 2-3, mercaptobenzothiazoler 1-2, BTA 2-3, magnesia 4-6, methyl oleate 1.5-3, sodium sulfo-succinate twoMonooctyl ester 4-5, soybean oil 4-6, oleoyl chloride 1-1.5, auxiliary agent 5-7, deionized water 200;
Described auxiliary agent is made up of the raw material of following weight portion: carborundum 2-3, nano zirconium dioxide 2.5-3.5, Angelica oil 1-2, urea 1-2, Lauryl Alcohol ester 2-3, Tissuemat E 2-4, dispersant NNO2-3, emulsion acrylic resin 2.5-3.5, oilSodium sulfonate 2-3, water 50-54; First preparation method adds carborundum, nano zirconium dioxide, dispersant NNO, petroleum sodium sulfonateEnter in the water of half amount, grind 1-2 hour, then slowly add all the other residual components, be slowly heated to 70 DEG C-80 DEG C,Stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product.
The good cutting fluid of a kind of antirust, anti-corrosive lubricity cooling of the present invention, made by following concrete steps:
(1) methyl oleate, dioctylis sulfosuccinas natricus, soybean oil are mixed, add appropriate deionized water, addHeat is to 30 DEG C-35 DEG C, and stirring reaction 30-40 minute, obtains mixing A material;
(2) all the other residual components except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 55DEG C-65 DEG C, insulation 1-1.5 hour, obtains mixing B material;
(3) the mixing B material of insulation is slowly joined while stirring and mixed in A material, after fully stirring, add auxiliary agent, 800-900 revs/min of lower stirring reaction 40-60 minute, are cooled to room temperature and get final product.
Excellent effect of the present invention is: the present invention adds dodecenylsuccinic acid, mercaptobenzothiazoler etc. and has antirust, anti-Rotten effect; Add auxiliary agent, strengthened wear-resistant, disperse, lubricated, film forming; The present invention has excellent lubricated abrasion resistance, clearWash cooling and corrosion-resisting resisting resistance, effectively protected cutter, improved crudy; Adopt water prescription, cooling effectGood, greatly take away the heat producing in process, cost is low, simple for process.
Detailed description of the invention
Below by instantiation, the present invention is described in detail.
The good cutting fluid of antirust, anti-corrosive lubricity cooling, by following weight portion (kilogram) raw material make: 12Alkenyl succinic acid 2, mercaptobenzothiazoler 1, BTA 2, magnesia 4, methyl oleate 1.5, dioctylis sulfosuccinas natricus4, soybean oil 4, oleoyl chloride 1, auxiliary agent 5, deionized water 200;
Described auxiliary agent by following weight portion (kilogram) raw material make: carborundum 2, nano zirconium dioxide 2.5, Angelica oil 1,Urea 1, Lauryl Alcohol ester 2, Tissuemat E 2, dispersant NNO2, emulsion acrylic resin 2.5, petroleum sodium sulfonate 2, water 50; SystemPreparation Method is first carborundum, nano zirconium dioxide, dispersant NNO, petroleum sodium sulfonate to be added in the water of half amount, grinds 1-2 hours, then slowly add all the other residual components, be slowly heated to 70 DEG C-80 DEG C, under 300-500 rev/min of condition, stir anti-Answer 30-50 minute, be cooled to room temperature and get final product.
The good cutting fluid of a kind of antirust, anti-corrosive lubricity cooling of the present invention, made by following concrete steps:
(1) methyl oleate, dioctylis sulfosuccinas natricus, soybean oil are mixed, add appropriate deionized water, addHeat is to 30 DEG C-35 DEG C, and stirring reaction 30-40 minute, obtains mixing A material;
(2) all the other residual components except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 55DEG C-65 DEG C, insulation 1-1.5 hour, obtains mixing B material;
(3) the mixing B material of insulation is slowly joined while stirring and mixed in A material, after fully stirring, add auxiliary agent, 800-900 revs/min of lower stirring reaction 40-60 minute, are cooled to room temperature and get final product.
After tested, cutting fluid of the present invention can reach following technical requirement:
Claims (2)
1. the good cutting fluid of antirust, anti-corrosive lubricity cooling, is characterized in that, is made up: ten of the raw material of following weight portionDialkylene succinic acid 2-3, mercaptobenzothiazoler 1-2, BTA 2-3, magnesia 4-6, methyl oleate 1.5-3, sulfo group fourthDiacid sodium dioctyl ester 4-5, soybean oil 4-6, oleoyl chloride 1-1.5, auxiliary agent 5-7, deionized water 200;
Described auxiliary agent is made up of the raw material of following weight portion: carborundum 2-3, nano zirconium dioxide 2.5-3.5, Angelica oil 1-2, urineElement 1-2, Lauryl Alcohol ester 2-3, Tissuemat E 2-4, dispersant NNO2-3, emulsion acrylic resin 2.5-3.5, mahogany acidSodium 2-3, water 50-54; The preparation method of auxiliary agent is first by carborundum, nano zirconium dioxide, dispersant NNO, petroleum sodium sulfonateAdd in the water of half amount, grind 1-2 hour, then slowly add all the other residual components, be slowly heated to 70 DEG C-80 DEG C,Stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product.
2. the good cutting fluid of a kind of antirust, anti-corrosive lubricity cooling according to claim 1, is characterized in that, by following toolBody step is made:
(1) methyl oleate, dioctylis sulfosuccinas natricus, soybean oil are mixed, add appropriate deionized water, be heated to30 DEG C-35 DEG C, stirring reaction 30-40 minute, obtains mixing A material;
(2) all the other residual components except auxiliary agent are joined in reactor, are uniformly mixed, be slowly heated to 55 DEG C-65 DEG C, insulation 1-1.5 hour, obtains mixing B material;
(3) the mixing B material of insulation is slowly joined while stirring and mixed in A material, after fully stirring, add auxiliary agent, 800-900Rev/min lower stirring reaction 40-60 minute, is cooled to room temperature and get final product.