CN104120015A - Cutting fluid with good rust prevention, corrosion prevention, lubricity and cooling capability and preparation method thereof - Google Patents
Cutting fluid with good rust prevention, corrosion prevention, lubricity and cooling capability and preparation method thereof Download PDFInfo
- Publication number
- CN104120015A CN104120015A CN201410305509.7A CN201410305509A CN104120015A CN 104120015 A CN104120015 A CN 104120015A CN 201410305509 A CN201410305509 A CN 201410305509A CN 104120015 A CN104120015 A CN 104120015A
- Authority
- CN
- China
- Prior art keywords
- parts
- cutting fluid
- prevention
- auxiliary agent
- slowly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses cutting fluid with good rust prevention, corrosion prevention, lubricity and cooling capability. The cutting fluid is characterized by being prepared from the following raw materials in parts by weight: 2-3 parts of dodecatylene succinic acid, 1-2 parts of mercaptobenzothiazole, 2-3 parts of benzotriazole, 4-6 parts of magnesium oxide, 1.5-3 parts of methyl oleate, 4-5 parts of sodium di(2-ethylhexyl) sulfosuccinate, 4-6 parts of soybean oil, 1-1.5 parts of oleoyl chloride, 5-7 parts of additives and 200 parts of deionized water. Due to dodecatylene succinic acid, mercaptobenzothiazole and the like, the cutting fluid has the functions of rust prevention and anti-corrosion; due to the additives, the abrasion prevention, the dispersity, the lubricity and the film-forming property are improved; the cutting fluid is excellent in lubrication and anti-abrasion property, washing and cooling capability and rust prevention and corrosion prevention, a cutter is effectively protected, and the machining quality is improved; due to an adopted aqueous formula, the cooling effect is good, the heat generated in the machining process can be greatly carried away, the cost is low, and the process is simple and practicable.
Description
Technical field
The present invention relates to cutting fluid field, cutting fluid that particularly a kind of antirust, anti-corrosive oilness cooling is good and preparation method thereof.
Background technology
In mechanical processing industry, be to cut and lubricate with cooling with lubricating oil or with kerosene apply oil substantially.Cutting fluid comprises the oil base cutting fluid that contains mineral oil and additive, contains polyoxyethylene glycol or polypropylene glycol as the glycol-based cutting fluid of main ingredient, and the water-based cutting fluid of water phase surfactant mixture form.Oil base cutting fluid is poor at the cooling performance of cutting point, oil base cutting fluid can be polluted workpiece or instrument, need to further clean with organic solvent, unfriendly to environment, performance is poor aspect the dispersion stabilization of viscosity stability in cutting operation of glycol-based cutting fluid and water-based cutting fluid and abrasive material.In the course of processing, oil product waste is very serious, and environment and operator are caused to very large injury; And be difficult to obtain desirable finished surface.And it is slow to add man-hour radiating rate, after processing work, very easy upper rust.Be badly in need of now design oilness good, rustless property is superior, the cutting fluid that speed of cooling is fast, cleaning performance is good.
Summary of the invention
The object of this invention is to provide cutting fluid that a kind of antirust, anti-corrosive oilness cooling is good and preparation method thereof.
In order to realize object of the present invention, the present invention passes through following scheme implementation:
The good cutting fluid of antirust, anti-corrosive oilness cooling, is made by the raw material of following weight part: dodecenylsuccinic acid 2-3, mercaptobenzothiazole 1-2, benzotriazole 2-3, magnesium oxide 4-6, Witconol 2301 1.5-3, Dioctyl Sodium Sulfosuccinate 4-5, soybean oil 4-6, oleoyl chloride 1-1.5, auxiliary agent 5-7, deionized water 200;
Described auxiliary agent is made by the raw material of following weight part: silicon carbide 2-3, nano zirconium dioxide 2.5-3.5, Radix Angelicae Sinensis oil 1-2, urea 1-2, Lauryl Alcohol ester 2-3, polyethylene wax 2-4, dispersion agent NNO 2-3, Emulsion acrylic resin 2.5-3.5, petroleum sodium sulfonate 2-3, water 50-54; First preparation method adds silicon carbide, nano zirconium dioxide, dispersion agent NNO, petroleum sodium sulfonate in the water of half amount, grind 1-2 hour, then slowly add all the other remaining components, slowly be heated to 70 ℃-80 ℃, stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product.
The good cutting fluid of a kind of antirust, anti-corrosive oilness cooling of the present invention, by following concrete steps, made:
(1) Witconol 2301, Dioctyl Sodium Sulfosuccinate, soybean oil are mixed, add appropriate deionized water, be heated to 30 ℃-35 ℃, stirring reaction 30-40 minute, obtains mixing A material;
(2) all the other remaining components except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 55 ℃-65 ℃, insulation 1-1.5 hour, obtains mixing B material;
(3) the mixing B material of insulation is slowly joined while stirring and mixed in A material, after fully stirring, add auxiliary agent, 800-900 rev/min of lower stirring reaction 40-60 minute, is cooled to room temperature and get final product.
Excellent effect of the present invention is: the present invention adds dodecenylsuccinic acid, mercaptobenzothiazole etc. and has antirust, rot-resistant effect; Add auxiliary agent, strengthened wear-resistant, disperse, lubricated, film-forming properties; The present invention has excellent lubricated abrasion resistance, cleans cooling and corrosion-resisting resisting resistance, has effectively protected cutter, has improved processing quality; Adopt water prescription, good cooling results, greatly takes away the heat producing in the course of processing, and cost is low, simple for process.
Embodiment
Below by specific examples, the present invention is described in detail.
The good cutting fluid of antirust, anti-corrosive oilness cooling, by following weight part (kilogram) raw material make: dodecenylsuccinic acid 2, mercaptobenzothiazole 1, benzotriazole 2, magnesium oxide 4, Witconol 2301 1.5, Dioctyl Sodium Sulfosuccinate 4, soybean oil 4, oleoyl chloride 1, auxiliary agent 5, deionized water 200;
Described auxiliary agent by following weight part (kilogram) raw material make: silicon carbide 2, nano zirconium dioxide 2.5, Radix Angelicae Sinensis oil 1, urea 1, Lauryl Alcohol ester 2, polyethylene wax 2, dispersion agent NNO 2, Emulsion acrylic resin 2.5, petroleum sodium sulfonate 2, water 50; First preparation method adds silicon carbide, nano zirconium dioxide, dispersion agent NNO, petroleum sodium sulfonate in the water of half amount, grind 1-2 hour, then slowly add all the other remaining components, slowly be heated to 70 ℃-80 ℃, stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product.
The good cutting fluid of a kind of antirust, anti-corrosive oilness cooling of the present invention, by following concrete steps, made:
(1) Witconol 2301, Dioctyl Sodium Sulfosuccinate, soybean oil are mixed, add appropriate deionized water, be heated to 30 ℃-35 ℃, stirring reaction 30-40 minute, obtains mixing A material;
(2) all the other remaining components except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 55 ℃-65 ℃, insulation 1-1.5 hour, obtains mixing B material;
(3) the mixing B material of insulation is slowly joined while stirring and mixed in A material, after fully stirring, add auxiliary agent, 800-900 rev/min of lower stirring reaction 40-60 minute, is cooled to room temperature and get final product.
After tested, cutting fluid of the present invention can reach following technical requirements:
Claims (2)
1. the good cutting fluid of antirust, anti-corrosive oilness cooling, it is characterized in that, by the raw material of following weight part, made: dodecenylsuccinic acid 2-3, mercaptobenzothiazole 1-2, benzotriazole 2-3, magnesium oxide 4-6, Witconol 2301 1.5-3, Dioctyl Sodium Sulfosuccinate 4-5, soybean oil 4-6, oleoyl chloride 1-1.5, auxiliary agent 5-7, deionized water 200;
Described auxiliary agent is made by the raw material of following weight part: silicon carbide 2-3, nano zirconium dioxide 2.5-3.5, Radix Angelicae Sinensis oil 1-2, urea 1-2, Lauryl Alcohol ester 2-3, polyethylene wax 2-4, dispersion agent NNO 2-3, Emulsion acrylic resin 2.5-3.5, petroleum sodium sulfonate 2-3, water 50-54; First preparation method adds silicon carbide, nano zirconium dioxide, dispersion agent NNO, petroleum sodium sulfonate in the water of half amount, grind 1-2 hour, then slowly add all the other remaining components, slowly be heated to 70 ℃-80 ℃, stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product.
2. the good cutting fluid of a kind of antirust, anti-corrosive oilness cooling according to claim 1, is characterized in that, by following concrete steps, is made:
(1) Witconol 2301, Dioctyl Sodium Sulfosuccinate, soybean oil are mixed, add appropriate deionized water, be heated to 30 ℃-35 ℃, stirring reaction 30-40 minute, obtains mixing A material;
(2) all the other remaining components except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 55 ℃-65 ℃, insulation 1-1.5 hour, obtains mixing B material;
(3) the mixing B material of insulation is slowly joined while stirring and mixed in A material, after fully stirring, add auxiliary agent, 800-900 rev/min of lower stirring reaction 40-60 minute, is cooled to room temperature and get final product.