CN104120018B - Multifunctional aqueous cutting fluid that a kind of bactericidal effect is good and preparation method thereof - Google Patents
Multifunctional aqueous cutting fluid that a kind of bactericidal effect is good and preparation method thereof Download PDFInfo
- Publication number
- CN104120018B CN104120018B CN201410305910.0A CN201410305910A CN104120018B CN 104120018 B CN104120018 B CN 104120018B CN 201410305910 A CN201410305910 A CN 201410305910A CN 104120018 B CN104120018 B CN 104120018B
- Authority
- CN
- China
- Prior art keywords
- good
- auxiliary agent
- cutting fluid
- bactericidal effect
- mixing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses the multifunctional aqueous cutting fluid that a kind of bactericidal effect is good, it is characterized in that, be made up of the raw material of following weight portion: poly-aspartate 2-3, octadecylamine 2.5-3.5, formalin 0.5-1, mica powder 4-6, white carbon 2-4, ethanol 3-4, sodium stearate 4-5, sulfuration Oleum Gossypii semen 2-3.5, auxiliary agent 5-7, deionized water 200；The present invention adds formalin as antibacterial; prevent cutting fluid from going bad; extend the resting period; add auxiliary agent; there is good wear-resistant, dispersion, lubrication, film property; the interpolation of matching surface activating agent, can not only form protecting film at surface of the work, and has good permeability, cleaning；Water prescription of the present invention, cooling is good, greatly takes away the heat produced in the course of processing, reduces the temperature of machined surface, is effectively protected cutter, improves crudy。
Description
Technical field
The present invention relates to cutting fluid field, multifunctional aqueous cutting fluid that particularly a kind of bactericidal effect is good and preparation method thereof。
Background technology
Because modern mechanical processing is all pursued develop to high speed, direction powerful, accurate, the frictional force in cutting process, frictional heat is caused to increase substantially, this just requires that metal working fluid has better lubrication, cooling, cleaning, rustless property, in order to obtain desirable finished surface。The lubrication of mineral lubricating oil, rustless property are superior, but cooling, cleaning performance poor；Emulsion and the cooling of water-base cutting fluid, cleaning performance are excellent, but lubrication, rustless property are poor。And traditional emulsion fouling apt to deteriorate in summer, winter is easily dilutable not, just researches and develops now a kind of multifunctional aqueous cutting fluid with sterilizing and anti-foul effect。
Summary of the invention
It is an object of the invention to provide good multifunctional aqueous cutting fluid of a kind of bactericidal effect and preparation method thereof。
In order to realize the purpose of the present invention, the present invention is implemented by below scheme:
The multifunctional aqueous cutting fluid that a kind of bactericidal effect is good, is made up of the raw material of following weight portion: poly-aspartate 2-3, octadecylamine 2.5-3.5, formalin 0.5-1, mica powder 4-6, white carbon 2-4, ethanol 3-4, sodium stearate 4-5, sulfuration Oleum Gossypii semen 2-3.5, auxiliary agent 5-7, deionized water 200；
Described auxiliary agent is made up of the raw material of following weight portion: artificial diamond stone powder 2-3, corundum 1-2, acrylonitrile 1-2, Oleum Bupleuri 3-4, Lauryl Alcohol ester 2-3, abienol 2-3, hexamethyl disiloxane 1-1.5, dodecylbenzene sodium sulfonate 3.5-4, water 50-54；Preparation method be first by artificial diamond's stone powder, corundum, Oleum Bupleuri, dodecylbenzene sodium sulfonate add half amount water in, grind 1-2 hour, it is then slowly added into all the other residual componentss, it is slowly heated to 70 DEG C-80 DEG C, stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product。
The multifunctional aqueous cutting fluid that a kind of bactericidal effect of the present invention is good, is made up of step in detail below:
(1) by mica powder, white carbon, sodium stearate, sulfuration Oleum Gossypii semen mix homogeneously, adding appropriate deionized water, heating, to 30 DEG C-35 DEG C, is ground 30-40 minute, obtains mixing A material；
(2) all the other residual componentss except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 55 DEG C-65 DEG C, be incubated 1-1.5 hour, obtain mixing B material；
(3) expect the mixing B of insulation to be slowly added into while stirring in mixing A material, after being sufficiently stirred for, add auxiliary agent, 800-900 rev/min of lower stirring reaction 50-60 minute, it is cooled to room temperature and get final product。
The excellent effect of the present invention is: the present invention adds formalin as antibacterial; prevent cutting fluid from going bad; extend the resting period; add auxiliary agent; there is good wear-resistant, dispersion, lubrication, film property; the interpolation of matching surface activating agent, can not only form protecting film at surface of the work, and has good permeability, cleaning；Water prescription of the present invention, cooling is good, greatly takes away the heat produced in the course of processing, reduces the temperature of machined surface, is effectively protected cutter, improves crudy。
Detailed description of the invention
Below by instantiation, the present invention is described in detail。
The multifunctional aqueous cutting fluid that a kind of bactericidal effect is good, is made up of the raw material of following weight portion (kilogram): poly-aspartate 2, octadecylamine 2.5, formalin 0.5, mica powder 4, white carbon 2, ethanol 3, sodium stearate 4, sulfuration Oleum Gossypii semen 2, auxiliary agent 5, deionized water 200；
Described auxiliary agent is made up of the raw material of following weight portion (kilogram): artificial diamond's stone powder 2, corundum 1, acrylonitrile 1, Oleum Bupleuri 3, Lauryl Alcohol ester 2, abienol 2, hexamethyl disiloxane 1, dodecylbenzene sodium sulfonate 3.5, water 50；Preparation method be first by artificial diamond's stone powder, corundum, Oleum Bupleuri, dodecylbenzene sodium sulfonate add half amount water in, grind 1-2 hour, it is then slowly added into all the other residual componentss, it is slowly heated to 70 DEG C-80 DEG C, stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product。
The multifunctional aqueous cutting fluid that a kind of bactericidal effect of the present invention is good, is made up of step in detail below:
(1) by mica powder, white carbon, sodium stearate, sulfuration Oleum Gossypii semen mix homogeneously, adding appropriate deionized water, heating, to 30 DEG C-35 DEG C, is ground 30-40 minute, obtains mixing A material；
(2) all the other residual componentss except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 55 DEG C-65 DEG C, be incubated 1-1.5 hour, obtain mixing B material；
(3) expect the mixing B of insulation to be slowly added into while stirring in mixing A material, after being sufficiently stirred for, add auxiliary agent, 800-900 rev/min of lower stirring reaction 50-60 minute, it is cooled to room temperature and get final product。
After tested, cutting fluid of the present invention can reach the requirement of following technology:
Claims (2)
1. the multifunctional aqueous cutting fluid that a bactericidal effect is good, it is characterized in that, be made up of the raw material of following weight portion: poly-aspartate 2-3, octadecylamine 2.5-3.5, formalin 0.5-1, mica powder 4-6, white carbon 2-4, ethanol 3-4, sodium stearate 4-5, sulfuration Oleum Gossypii semen 2-3.5, auxiliary agent 5-7, deionized water 200；
Described auxiliary agent is made up of the raw material of following weight portion: artificial diamond stone powder 2-3, corundum 1-2, acrylonitrile 1-2, Oleum Bupleuri 3-4, Lauryl Alcohol ester 2-3, abienol 2-3, hexamethyl disiloxane 1-1.5, dodecylbenzene sodium sulfonate 3.5-4, water 50-54；Preparation method be first by artificial diamond's stone powder, corundum, Oleum Bupleuri, dodecylbenzene sodium sulfonate add half amount water in, grind 1-2 hour, it is then slowly added into all the other residual componentss, it is slowly heated to 70 DEG C-80 DEG C, stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product。
2. the multifunctional aqueous cutting fluid that a kind of bactericidal effect is good according to claim 1, it is characterised in that be made up of step in detail below:
(1) by mica powder, white carbon, sodium stearate, sulfuration Oleum Gossypii semen mix homogeneously, adding appropriate deionized water, heating, to 30 DEG C-35 DEG C, is ground 30-40 minute, obtains mixing A material；
(2) all the other residual componentss except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 55 DEG C-65 DEG C, be incubated 1-1.5 hour, obtain mixing B material；
(3) expect the mixing B of insulation to be slowly added into while stirring in mixing A material, after being sufficiently stirred for, add auxiliary agent, 800-900 rev/min of lower stirring reaction 50-60 minute, it is cooled to room temperature and get final product。