CN104109578A - Eco-friendly aqueous metal cutting fluid and preparation method thereof - Google Patents
Eco-friendly aqueous metal cutting fluid and preparation method thereof Download PDFInfo
- Publication number
- CN104109578A CN104109578A CN201410290917.XA CN201410290917A CN104109578A CN 104109578 A CN104109578 A CN 104109578A CN 201410290917 A CN201410290917 A CN 201410290917A CN 104109578 A CN104109578 A CN 104109578A
- Authority
- CN
- China
- Prior art keywords
- parts
- cutting fluid
- metal cutting
- auxiliary agent
- eco
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an eco-friendly aqueous metal cutting fluid, which is characterized by comprising the following raw materials by weight: 4-5 parts of lauroyl diethanolamine, 3.5-4.5 parts of iso-tridecanol polyoxyethylene ether, 1-2 parts of lauric acid polyoxyethylene, 4-6 parts of coconut oil, 2-4 parts of borax, 1-2 parts of ethyl vanillin, 2-3 parts of 1,2-diethoxyl silyl ethane, 5-7 parts of auxiliary agent and 200 parts of deionized water. The eco-friendly aqueous metal cutting fluid has the advantage of scientific and reasonable formula, an auxiliary agent is added, and the eco-friendly aqueous metal cutting fluid has good wear resistance, dispersion and lubricity, and can cooperate with a surfactant, a protection film can be formed on the metal surface, so that corrosion of surrounding mediums on machine tools, workpieces and cutters can be avoided, an environmental protection formula is employed, no harmful substances such as sodium nitrite and chlorinated paraffin is contained, the eco-friendly aqueous metal cutting fluid is suitable for cutting the metals such as steel, cast iron, stainless steel, copper and aluminium, and copper aluminium alloy, the usage period is long, and deterioration is difficult.
Description
Technical field
The present invention relates to cutting fluid field, particularly a kind of environment amenable water-based metal cutting fluid and preparation method thereof.
Background technology
In mechanical processing industry, be to cut and lubricate with cooling with lubricating oil or with kerosene apply oil substantially.In the course of processing, oil product waste is very serious, and environment and operator are caused to very large injury; And be difficult to obtain desirable finished surface.And it is slow to add man-hour radiating rate, after processing work, very easily upper rust.Be badly in need of now design a kind of environmentally friendly, oilness is good, and rustless property is superior, the cutting fluid that speed of cooling is fast, cleaning performance is good.
Summary of the invention
The object of this invention is to provide a kind of environment amenable water-based metal cutting fluid and preparation method thereof.
In order to realize object of the present invention, the present invention passes through following scheme implementation:
A kind of environment amenable water-based metal cutting fluid, raw material by following weight part is made: lauroyl diethanolamine 4-5, isomerous tridecanol polyoxyethylene ether 3.5-4.5, propyl carbinol 3-4, lauric acid polyoxyethylene ester 1-2, Oleum Cocois 4-6, borax 2-4, vanillal 1-2,1,2-diethoxy estersil base ethane 2-3, auxiliary agent 5-7, deionized water 200;
Described auxiliary agent is made up of the raw material of following weight part: nano aluminum nitride 3-4, graphite 2-3, Sodium dodecylbenzene sulfonate 1-2, borax 2-4, Lauryl Alcohol ester 2-3, xitix 1-2, Microcrystalline Wax 2-3, sodium stearate 3.5-4, water 50-54; First preparation method adds nano aluminum nitride, graphite, Microcrystalline Wax, sodium stearate in the water of half amount, grind 1-2 hour, then slowly add all the other remaining components, be slowly heated to 70 DEG C-80 DEG C, stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product.
The environment amenable water-based metal cutting fluid of one of the present invention, made by following concrete steps:
(1) lauroyl diethanolamine, Oleum Cocois, lauric acid polyoxyethylene ester are mixed, add appropriate deionized water, be heated to 30 DEG C-35 DEG C, stirring reaction 30-40 minute, obtains mixing A material;
(2) all the other remaining components except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 55 DEG C-65 DEG C, insulation 1-1.5 hour, obtains mixing B material;
(3) the mixing B material of insulation is slowly joined while stirring and mixed in A material, after fully stirring, add auxiliary agent, 800-900 rev/min of lower stirring reaction 40-60 minute, is cooled to room temperature and get final product.
Excellent effect of the present invention is: scientific formulation of the present invention is reasonable; add auxiliary agent, there is good wear-resistant, dispersion, oilness, matching surface promoting agent; and can be at film-forming properties; can on metallic surface, form protective membrane, make lathe, workpiece, cutter avoid the corrosion of surrounding medium, adopt environmental protection formulae; not containing the harmful material such as Sodium Nitrite, clorafin; the machining that is applicable to the metals such as steel, cast iron, stainless steel, copper aluminium and alloy thereof, life cycle is long, not perishable.
Embodiment
Below by specific examples, the present invention is described in detail.
A kind of environment amenable water-based metal cutting fluid, by following weight part (kilogram) raw material make: lauroyl diethanolamine 4, isomerous tridecanol polyoxyethylene ether 3.5, propyl carbinol 3, lauric acid polyoxyethylene ester 1, Oleum Cocois 4, borax 2, vanillal 1,1,2-diethoxy estersil base ethane 2, auxiliary agent 5, deionized water 200;
Described auxiliary agent by following weight part (kilogram) raw material make: nano aluminum nitride 3, graphite 2, Sodium dodecylbenzene sulfonate 1, borax 2, Lauryl Alcohol ester 2, xitix 1, Microcrystalline Wax 2, sodium stearate 3.5, water 50; First preparation method adds nano aluminum nitride, graphite, Microcrystalline Wax, sodium stearate in the water of half amount, grind 1-2 hour, then slowly add all the other remaining components, be slowly heated to 70 DEG C-80 DEG C, stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product.
The environment amenable water-based metal cutting fluid of one of the present invention, made by following concrete steps:
(1) lauroyl diethanolamine, Oleum Cocois, lauric acid polyoxyethylene ester are mixed, add appropriate deionized water, be heated to 30 DEG C-35 DEG C, stirring reaction 30-40 minute, obtains mixing A material;
(2) all the other remaining components except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 55 DEG C-65 DEG C, insulation 1-1.5 hour, obtains mixing B material;
(3) the mixing B material of insulation is slowly joined while stirring and mixed in A material, after fully stirring, add auxiliary agent, 800-900 rev/min of lower stirring reaction 40-60 minute, is cooled to room temperature and get final product.
After tested, cutting fluid of the present invention can reach following technical requirements:
Claims (2)
1. an environment amenable water-based metal cutting fluid, it is characterized in that, raw material by following weight part is made: lauroyl diethanolamine 4-5, isomerous tridecanol polyoxyethylene ether 3.5-4.5, propyl carbinol 3-4, lauric acid polyoxyethylene ester 1-2, Oleum Cocois 4-6, borax 2-4, vanillal 1-2,1,2-diethoxy estersil base ethane 2-3, auxiliary agent 5-7, deionized water 200;
Described auxiliary agent is made up of the raw material of following weight part: nano aluminum nitride 3-4, graphite 2-3, Sodium dodecylbenzene sulfonate 1-2, borax 2-4, Lauryl Alcohol ester 2-3, xitix 1-2, Microcrystalline Wax 2-3, sodium stearate 3.5-4, water 50-54; First preparation method adds nano aluminum nitride, graphite, Microcrystalline Wax, sodium stearate in the water of half amount, grind 1-2 hour, then slowly add all the other remaining components, be slowly heated to 70 DEG C-80 DEG C, stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product.
2. a kind of environment amenable water-based metal cutting fluid according to claim 1, is characterized in that, is made up of following concrete steps:
(1) lauroyl diethanolamine, Oleum Cocois, lauric acid polyoxyethylene ester are mixed, add appropriate deionized water, be heated to 30 DEG C-35 DEG C, stirring reaction 30-40 minute, obtains mixing A material;
(2) all the other remaining components except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 55 DEG C-65 DEG C, insulation 1-1.5 hour, obtains mixing B material;
(3) the mixing B material of insulation is slowly joined while stirring and mixed in A material, after fully stirring, add auxiliary agent, 800-900 rev/min of lower stirring reaction 40-60 minute, is cooled to room temperature and get final product.