CN104120017B - Water-base cutting fluid of the strong good antirust property of a kind of penetration and preparation method thereof - Google Patents
Water-base cutting fluid of the strong good antirust property of a kind of penetration and preparation method thereof Download PDFInfo
- Publication number
- CN104120017B CN104120017B CN201410305552.3A CN201410305552A CN104120017B CN 104120017 B CN104120017 B CN 104120017B CN 201410305552 A CN201410305552 A CN 201410305552A CN 104120017 B CN104120017 B CN 104120017B
- Authority
- CN
- China
- Prior art keywords
- water
- cutting fluid
- auxiliary agent
- penetration
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses the water-base cutting fluid of the strong good antirust property of a kind of penetration, it is characterized in that, made by the raw material of following weight portion: oleic diethanola mide borate ester 2-3, HEDP 2-3, zinc naphthenate 1-2, glycerine 3-5, acrylonitrile 2-3, petroleum sodium sulfonate 4-5, tetradecyl trimethyl ammonium chloride 1-2, stannous sulfate 0.8-1.4, turkey red oil 3-5, auxiliary agent 5-7, deionized water 200; The present invention adds kinds of surface activating agent, has good permeability, cleaning, adds auxiliary agent, have good wear-resistant, disperse, lubricated, film forming, collaborative HEDP, prevents that surface of the work is by air corrosion; Cutting fluid of the present invention adopts water-based formulation, and cooling performance excellence, greatly takes away the heat producing in process, reduces the temperature of machined surface, and crimping and the distortion of effectively avoiding workpiece Yin Gaowen to produce, improved production efficiency.
Description
Technical field
The present invention relates to cutting fluid field, particularly water-base cutting fluid and the preparation thereof of the strong good antirust property of a kind of penetrationMethod.
Background technology
In mechanical processing industry, be substantially with lubricating oil or with kerosene apply oil cut lubricated withCooling. In process, oil product waste is very serious, and environment and operating personnel are caused to very large injury; And be difficult to obtainObtain desirable finished surface. And it is slow to add man-hour radiating rate, after processing work, very easily upper rust. Cutting fluid should possess good coldBut performance, greasy property, rustless property, oil removing cleaning function, anti-corrosion function, easily dilutable feature. Cutting fluid can be divided into two at presentClass, oil-soluble cutting fluid and water-soluble metalworking liquid. General oil-soluble cutting fluid lubrication performance is good, but poor cooling performance, and containLarge amount of organic, contaminated environment. Although some water-soluble metalworking liquid cooling performances are good, exist again lubricity and rust-proof effect poorProblem, therefore research and development have lubricity, cooling, rust-preventing characteristic, easy cleaning, nontoxic, tasteless, non-corrosive to human body, to equipment not concurrentlyThe cutting fluid of corrosion just seems very important.
Summary of the invention
The object of this invention is to provide water-base cutting fluid of the strong good antirust property of a kind of penetration and preparation method thereof.
In order to realize object of the present invention, the present invention passes through following scheme implementation:
A water-base cutting fluid for the strong good antirust property of penetration, is made up of the raw material of following weight portion: oleic acid diethanolAcid amides borate 2-3, HEDP 2-3, zinc naphthenate 1-2, glycerine 3-5, acrylonitrile 2-3, petroleum sodium sulfonate 4-5,Tetradecyl trimethyl ammonium chloride 1-2, stannous sulfate 0.8-1.4, turkey red oil 3-5, auxiliary agent 5-7, deionized water 200;
Described auxiliary agent is made up of the raw material of following weight portion: carborundum 2-3, nano zirconium dioxide 2.5-3.5, Angelica oil 1-2, urea 1-2, Lauryl Alcohol ester 2-3, Tissuemat E 2-4, dispersant NNO2-3, emulsion acrylic resin 2.5-3.5, oilSodium sulfonate 2-3, water 50-54; First preparation method adds carborundum, nano zirconium dioxide, dispersant NNO, petroleum sodium sulfonateEnter in the water of half amount, grind 1-2 hour, then slowly add all the other residual components, be slowly heated to 70 DEG C-80 DEG C,Stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product.
The water-base cutting fluid of the strong good antirust property of a kind of penetration of the present invention, made by following concrete steps:
(1) petroleum sodium sulfonate, turkey red oil, tetradecyl trimethyl ammonium chloride are mixed, add appropriate deionizationWater, is heated to 30 DEG C-35 DEG C, and stirring reaction 30-40 minute obtains mixing A material;
(2) all the other residual components except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 55DEG C-65 DEG C, insulation 1-1.5 hour, obtains mixing B material;
(3) the mixing B material of insulation is slowly joined while stirring and mixed in A material, after fully stirring, add auxiliary agent, 800-900 revs/min of lower stirring reaction 40-60 minute, are cooled to room temperature and get final product.
Excellent effect of the present invention is: the present invention adds kinds of surface activating agent, has good permeability, cleaning,Add auxiliary agent, have good wear-resistant, disperse, lubricated, film forming, collaborative HEDP, prevents that surface of the work is by skyGas corrosion; Cutting fluid of the present invention adopts water-based formulation, and cooling performance excellence, greatly takes away the heat producing in process,Reduce the temperature of machined surface, crimping and the distortion of effectively avoiding workpiece Yin Gaowen to produce, improved production efficiency.
Detailed description of the invention
Below by instantiation, the present invention is described in detail.
A water-base cutting fluid for the strong good antirust property of penetration, by following weight portion (kilogram) raw material make: oleic acidDiglycollic amide borate 2, HEDP 2, zinc naphthenate 1, glycerine 3, acrylonitrile 2, petroleum sodium sulfonate 4, the tetradecaneBase trimethyl ammonium chloride 1, stannous sulfate 0.8, turkey red oil 3, auxiliary agent 5, deionized water 200;
Described auxiliary agent by following weight portion (kilogram) raw material make: carborundum 2, nano zirconium dioxide 2.5, Angelica oil 1,Urea 1, Lauryl Alcohol ester 2, Tissuemat E 2, dispersant NNO2, emulsion acrylic resin 2.5, petroleum sodium sulfonate 2, water 50; SystemPreparation Method is first carborundum, nano zirconium dioxide, dispersant NNO, petroleum sodium sulfonate to be added in the water of half amount, grinds 1-2 hours, then slowly add all the other residual components, be slowly heated to 70 DEG C-80 DEG C, under 300-500 rev/min of condition, stir anti-Answer 30-50 minute, be cooled to room temperature and get final product.
The water-base cutting fluid of the strong good antirust property of a kind of penetration of the present invention, made by following concrete steps:
(1) petroleum sodium sulfonate, turkey red oil, tetradecyl trimethyl ammonium chloride are mixed, add appropriate deionizationWater, is heated to 30 DEG C-35 DEG C, and stirring reaction 30-40 minute obtains mixing A material;
(2) all the other residual components except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 55DEG C-65 DEG C, insulation 1-1.5 hour, obtains mixing B material;
(3) the mixing B material of insulation is slowly joined while stirring and mixed in A material, after fully stirring, add auxiliary agent, 800-900 revs/min of lower stirring reaction 40-60 minute, are cooled to room temperature and get final product.
After tested, cutting fluid of the present invention can reach following technical requirement:
Claims (1)
1. a water-base cutting fluid for the strong good antirust property of penetration, is characterized in that, is made up: oil of the raw material of following weight portionAcid diglycollic amide borate 2-3, HEDP 2-3, zinc naphthenate 1-2, glycerine 3-5, acrylonitrile 2-3, oil sulphurAcid sodium 4-5, tetradecyl trimethyl ammonium chloride 1-2, stannous sulfate 0.8-1.4, turkey red oil 3-5, auxiliary agent 5-7, deionized water200；
Described auxiliary agent is made up of the raw material of following weight portion: carborundum 2-3, nano zirconium dioxide 2.5-3.5, Angelica oil 1-2, urineElement 1-2, Lauryl Alcohol ester 2-3, Tissuemat E 2-4, dispersant NNO2-3, emulsion acrylic resin 2.5-3.5, mahogany acidSodium 2-3, water 50-54; First preparation method adds one by carborundum, nano zirconium dioxide, dispersant NNO, petroleum sodium sulfonateIn the water of half amount, grind 1-2 hour, then slowly add all the other residual components, be slowly heated to 70 DEG C-80 DEG C, at 300-500Stirring reaction 30-50 minute under rev/min condition, is cooled to room temperature and get final product;
The water-base cutting fluid of the strong good antirust property of described penetration is made up of following concrete steps:
(1) petroleum sodium sulfonate, turkey red oil, tetradecyl trimethyl ammonium chloride are mixed, add appropriate deionized water, addHeat is to 30 DEG C-35 DEG C, and stirring reaction 30-40 minute, obtains mixing A material;
(2) all the other residual components except auxiliary agent are joined in reactor, are uniformly mixed, be slowly heated to 55 DEG C-65 DEG C, insulation 1-1.5 hour, obtains mixing B material;
(3) the mixing B material of insulation is slowly joined while stirring and mixed in A material, after fully stirring, add auxiliary agent, 800-900Rev/min lower stirring reaction 40-60 minute, is cooled to room temperature and get final product.